DE596513C - Optisches Glas mit einer Brechungszahl ueber 1,60 - Google Patents
Optisches Glas mit einer Brechungszahl ueber 1,60Info
- Publication number
- DE596513C DE596513C DE1930596513D DE596513DA DE596513C DE 596513 C DE596513 C DE 596513C DE 1930596513 D DE1930596513 D DE 1930596513D DE 596513D A DE596513D A DE 596513DA DE 596513 C DE596513 C DE 596513C
- Authority
- DE
- Germany
- Prior art keywords
- refractive index
- glasses
- optical glass
- oxide
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
DEUTSCHES REICH
19 JUN. 1934
AUSGEGEBEN AM 3. MAI 1934
REICHSPATENTAMT
PATENTSCHRIFT
M 596513 KLASSE 32 b GRUPPEl
Jenaer Glaswerk Schott & Gen. in Jena
Patentiert im Deutschen Reiche vom 6. November 1930 ab
Es ist bekannt, daß sich Gläser mit einer Brechungszahl über 1,60 durch Vermehrung
des Bleioxydgehaltes auf Kosten des Gehaltes an Kieselsäure und an einwertigen Metal 1-oxyden
(Alkalien) erzeugen lassen. Bei solchen Gläsern ist aber der Zuwachs der Brechungszahl
verknüpft mit einer erheblichen Erhöhung der Farbenzerstreuung. So haben Bleioxydgläser mit nD = 1,60 den Wert
v = 38, solche mit nD = 1,75 den Wert ν = 28,
es fällt also schon bei einer Erhöhung des- nD
um 0,015 das ν um eine Einheit. Ein ähnliches
Verhalten zeigen Gläser, in denen das Bleioxyd teilweise oder ganz durch Antimonoxyd
(Sb2O1) ersetzt ist. Es ist ferner bekannt,
daß sich Gläser mit einer Brechungszahl über 1,60 und einer gegenüber den erwähnten
Blei-Antimon-Gläsern verminderten "." Farbenzerstreuung erzielen lassen, indem man
ao den Gehalt an Bleioxyd und Antimonoxyd ganz oder teilweise durch zweiwertige Oxyde,
. wie Ba O, Sr O, Ca O, Mg O, Zn O, ersetzt.' Da
jedoch dabei zweckmäßig ein Teil des SiOs
durch dreiwertige Oxyde, wie B2O3 oder
Al2O3,' ersetzt wird, um die Kristallisationsneigung solcher Gläser zu vermindern, so
wird der Gehalt an SiO2 mehr oder weniger stark herabgedrückt, womit eine Erhöhung
der Säurelöslichkeit (Fleckenempfindlichkeit) ■30 der erzeugten Gläser einhergeht.
. Es hat sich nun gezeigt, daß sich Gläser mit verhältnismäßig hohem Kieselsäuregehalt
mit B rech werten über 1,60 und einer Farbenzerstreuung, die kleiner ist als bei entsprechend
brechenden Blei-Antimon-Gläsern, erzeugen lassen, wenn man den Gehalt an Erdalkalioxyden
(BeO, MgO, CaO, SrO, BaO), gegebenenfalls neben einwertigen, anderen
zweiwertigen und dreiwertigen Oxyden, mindestens 10 "/„ betragen läßt und noch bis zu
20% Titanoxyd (TiO2) in das Glas einführt. Mit einem Gehalt an Titanoxyd von 25 °/0
und darüber oder einem Gehalt an Germaniumoxyd von 27 °)0 hat man schon Gläser
von hoher Brechung erzielt, jedoch steigt dann die Farbenzerstreuung ebenfalls in solchem
Maße an, daß sich die Gläser in.ihrem Zusammenhang zwischen Brechwert und
Farbenzerstreuung wie Blei-Antimon-Gläser verhalten. Auch tritt bei einem Gehalt an
Titanoxyd von 25 °/0 wegen der unvermeidlichen Verunreinigungen durch Eisenoxyd
schon eine Gelb- bis Braunfärbung des Glases ein. Anderseits genügt schon ein Gehalt von
weit weniger als 20 °('o Ti O2, um die Säurelöslichkeit
(Fleckenempfindlichkeit) des Glases sehr stark herabzudrücken. Es empfiehlt sich, bei den neuen Gläsern den Gehalt an
zweiwertigen Oxyden und Antimonoxyd zusammen mindestens 35 °/„ betragen zu lassen,
um bei der Erreichung einer hohen Brechung einen zu hohen Titangehalt und damit eine
Annäherung der Farbenzerstreuung an die der Blei-Antimon-Gläser zu vermeiden.
Man kann in den neuen Gläsern den Gehalt an Titanoxyd teilweise durch Thoriumoxyd
(ThO2), Hafniumoxyd (HfO2), Zirkonoxyd
(ZrO2) oder eine Mischung von ihnen ersetzen. Auch Germaniumoxyd (GeO2) und
Zinnoxyd (SnO2) wirken in ähnlicher Weise.
Vier Beispiele der neuen Gläser zeigt folgende Tafel:
SiO, · 32,0 32,0 32,0 32,0
B2O3 .... ■ . 8,0 8,0 8,0 7,5
Al2O3
— — - —- 0,5
Na2O .... 0,2 — — —
CaO ...... 10,0 10,0 10,0 10,0
BaO 43,5 37,2 37,2 36,2
ZnO 3,0 3,0 3,0 2,0
PbO .... 0,3 3,5 6;5 . 0,3
Sb2O3 ... — 3,0 — —
TiO. 2,s 3,0 3,0 rr,o
As2O3 0,5 0,3 0,3 0,5
η ο 1,658 1,668 ι ,6/i 1,696
ν 5i,4 48,o 47,3 42,0
Claims (2)
1. Optisches Glas mit einer Brechungszahl über 1,60, dadurch gekennzeichnet,
daß es Kieselsäure, mindestens io°/0 an Erdalkalioxyden, gegebenenfalls neben
einwertigen, anderen zweiwertigen und dreiwertigen Oxyden, sowie Titanoxyd bis zur Höhe von 20 °/0 enthält.
2. Optisches Glas nach Anspruch 1, dadurch gekennzeichnet, daß es an zweiwertigen Oxyden und Antimonoxyd zusam-1
men mindestens 35 °/0 enthält.