DE29522138U1 - Geschäumte Stärkezusammensetzungen und Gegenstände - Google Patents
Geschäumte Stärkezusammensetzungen und GegenständeInfo
- Publication number
- DE29522138U1 DE29522138U1 DE29522138U DE29522138U DE29522138U1 DE 29522138 U1 DE29522138 U1 DE 29522138U1 DE 29522138 U DE29522138 U DE 29522138U DE 29522138 U DE29522138 U DE 29522138U DE 29522138 U1 DE29522138 U1 DE 29522138U1
- Authority
- DE
- Germany
- Prior art keywords
- starch
- fibers
- based composition
- fiber
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Claims (47)
1. Gegenstand mit einer faserverstärkten, Stärke-gebundenen Zellmatrix und einer
Laminatbeschichtung aufgebracht auf mindestens einem Teil davon, wobei die Stärke
gebundene Zellmatrix einen gelierten Binder auf Stärke-Basis und in der gesamten Stärke
gebundenen Zellmatrix dispergierte Fasern umfaßt, die eine durchschnittliche Länge von
mindestens etwa 0,3 mm und ein durchschnittliches Seitenverhältnis größer als etwa 25 : 1
aufweisen und in einer Konzentration in einem Bereich von etwa 2 Gew.-% bis etwa 80
Gew.-% der Stärke-gebundenen Zellmatrix vorliegen.
2. Gegenstand gemäß Anspruch 1, wobei die Stärke-gebundene Zellmatrix eine Dichte
in einem Bereich von etwa 0,05 g/cm3 bis etwa 1 g/cm3, vorzugsweise in einem Bereich von
etwa 0,15 g/cm3 bis etwa 0,25 g/cm3 aufweist.
3. Gegenstand gemäß Anspruch 1, wobei die Stärke-gebundene Zellmatrix eine äußere
Hautschicht mit einer Dichte und einen inneren Schaumabschnitt mit einer Dichte beinhaltet,
die deutlich geringer ist als die Dichte der äußeren Hautschicht.
4. Gegenstand gemäß Anspruch 1, mit einer Dicke bis zu etwa 10 cm, vorzugsweise mit
einer Dicke in einem Bereich von etwa 0,5 mm bis etwa 5 mm und insbesondere in einem
Bereich von etwa 1 mm bis etwa 3 mm.
5. Gegenstand gemäß Anspruch 1, wobei der Binder auf Stärke-Basis während des
Formens gelatiniert wurde und mindestens eine Stärke ausgewählt aus unmodifizierter
Stärke, Kartoffelstärke, Kartoffelstärkederivat, wachsartiger Maisstärke und wachsartigem
Maisstärkederivat einschließt.
6. Gegenstand gemäß Anspruch 1, wobei der Binder auf Stärke-Basis einen
Amylosegehalt von weniger als etwa 45%, vorzugsweise von weniger als etwa 25% aufweist.
7. Gegenstand gemäß Anspruch 1, wobei der Binder auf Stärke-Basis eine modifizierte
Stärke einschließt, vorzugsweise eine modifizierte Stärke, die modifiziert wurde durch
mindestens ein Verfahren der Veresterung, Veretherung, Oxidation, Säurehydrolyse,
Vernetzung und Enzymumwandlung.
8. Gegenstand gemäß Anspruch 1, wobei der Binder auf Stärke-Basis in einer
Konzentration in einem Bereich von etwa 10 Gew.-% bis etwa 80 Gew.-% der Stärke
gebundenen Zellmatrix, vorzugsweise in einem Bereich von etwa 30 Gew.-% bis etwa 70
Gew.-% der Stärke-gebundenen Zellmatrix vorliegt.
9. Gegenstand gemäß Anspruch 1, wobei die Fasern mindestens einen Fasertyp von
Cellulosederivat-Fasern, Hartholzfasern, Weichholzfasern, recycelten Papierfasern,
Hanffasern, Baumwollfasern, Sisalfasern, Abacafasern, Bagassefasern, Graphitfasern,
Silicafasern, Keramikfasern und Metallfasern einschließen.
10. Gegenstand gemäß Anspruch 1, wobei die Fasern in einer Konzentration in einem
Bereich von etwa 4 Gew.-% bis etwa 40 Gew.-% der Stärke-gebundenen Zellmatrix,
vorzugsweise in einem Bereich von etwa 5 Gew.-% bis etwa 20 Gew.-% der Stärke
gebundenen Zellmatrix vorliegen.
11. Gegenstand gemäß Anspruch 1, wobei die Fasern ein Seitenverhältnis von
mindestens 100 : 1 aufweisen.
12. Gegenstand gemäß Anspruch 1, wobei die Fasern eine durchschnittliche Länge von
mindestens etwa 2 mm, vorzugsweise von mindestens etwa 3,5 mm und insbesondere von
mindestens etwa 6,5 mm aufweisen.
13. Gegenstand gemäß Anspruch 1, des weiteren umfassend einen anorganischen
Aggregat-Füllstoff, vorzugsweise einen anorganischen Aggregat-Füllstoff ausgewählt aus der
Gruppe bestehend aus Calciumcarbonat, Sand, Kies, Fels (Gestein), Kalkstein, Sandstein,
Glaskügelchen, Mica, Ton, Kaolin, synthetischem Ton, Aluminiumoxid, Silica, Flugasche,
Quarzglas, tafelförmigem Aluminiumoxid, Mikrokügelchen, Calciumsulfatdihydrat
Calciumaluminat, hydratisierten hydraulischen Zementteilchen, unhydratisierten
hydraulischen Zementteilchen, Perlit, Vermiculit, hohlen Glaskügelchen, Aerogelen,
Xerogelen, porösen Keramikkügelchen, Xonotlit, leichtgewichtigen expandierten Tonen,
Bimsstein und abgebröckeltem Fels.
14. Gegenstand gemäß Anspruch 1, des weiteren umfassend einen anorganischen
Aggregat-Füllstoff in einer Konzentration in einem Bereich von etwa 20 Gew.-% bis etwa 80
Gew.-% der Stärke-gebundenen Zellmatrix, vorzugsweise in einem Bereich von etwa 30
Gew.-% bis etwa 70 Gew.-% der Stärke-gebundenen Zellmatrix, insbesondere in einem
Bereich von etwa 40 Gew.-% bis etwa 60 Gew.-% der Stärke-gebundenen Zellmatrix.
15. Gegenstand gemäß Anspruch 1, wobei die Laminatbeschichtung eine organische
Beschichtung umfaßt, gebildet aus mindestens einem Material ausgewählt aus Wachsen,
Schellack, Trockenölen, Kolophonium, Kolophoniumderivaten, Polyesterharzen,
Epoxyharzen, Terpenharzen, harzartigen Vinylverbindungen, vorzugsweise Polyvinylacetat
und Polyvinylalkohol, Cellulose(derivat)materialien, vorzugsweise Celluloseacetat,
Polyethylen, Polyethylen-Copolymeren, Acrylharzderivaten, Acrylharzderivat-Copolymeren,
Melamin, Polyamiden, Polymilchsäure, Polyhydroxybutyrat-Hydroxyvalerat-Copolymer,
Sojabohnenprotein, bioabbaubaren Polymeren, Elastomeren und Gemischen der
vorstehenden.
16. Gegenstand gemäß Anspruch 1, wobei die Laminatbeschichtung als im wesentlichen
gleichmäßiger Film aufgebracht ist.
17. Gegenstand gemäß Anspruch 1, wobei die Stärke-gebundene Zellmatrix des
weiteren Polyvinylalkohol umfaßt.
18. Gegenstand gemäß Anspruch 1, wobei der Gegenstand einen
Nahrungsmittelbehälter, Getränkebehälter oder einen flüssigkeitsfesten Behälter umfaßt.
19. Gegenstand gemäß Anspruch 1, wobei der Gegenstand in Form eines "clam shell"-
Behälters, einer Schachtel, einer Kiste, einer Tasse, eines Tellers, einer Schale oder eines
Tabletts vorliegt.
20. Eine fasergefüllte Zusammensetzung auf Stärke-Basis zum Formen in einen
Gegenstand mit einer Stärke-gebundenen Zellmatrix, wobei die Zusammensetzung auf
Stärke-Basis eine ungelatinierte Stärke, Wasser, ein Verdickungsmittel und Fasern mit
einem durchschnittlichen Seitenverhältnis größer als etwa 25 : 1 umfaßt, wobei das Wasser
und das Verdickungsmittel eine fluide Fraktion umfaßt mit einer Fließspannung, derart, daß
die Fasern im wesentlichen gleichmäßig in der gesamten Zusammensetzung auf Stärke-
Basis dispergiert sind, wobei die Zusammensetzung die Stärke-gebundene Zellmatrix durch
Gelierung der Stärkekörnchen und nachfolgende Entfernung von mindestens einem Teil des
Wassers aus der Zusammensetzung auf Stärke-Basis durch Verdampfen bildet.
21. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei die
fluide Fraktion eine Fließspannung in einem Bereich von etwa 10 Pa bis etwa 5000 Pa,
vorzugsweise in einem Bereich von etwa 100 Pa bis etwa 500 Pa aufweist.
22. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei die
fluide Fraktion eine scheinbare Viskosität gemessen bei einer Schergeschwindigkeit von 5 Pa.s
in einem Bereich von etwa 5 Pa.s bis etwa 1000 Pa.s, vorzugsweise in einem Bereich von
etwa 30 Pa.s bis etwa 200 Pa.s aufweist.
23. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei die
Zusammensetzung auf Stärke-Basis eine Fließspannung in einem Bereich von etwa 250 Pa
bis etwa 4000 Pa aufweist.
24. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei die
Zusammensetzung auf Stärke-Basis eine scheinbare Viskosität gemessen bei einer
Schergeschwindigkeit von 5 s-1 in einem Bereich von etwa 50 Pa.s bis etwa 2000 Pa.s
aufweist.
25. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei der
Stärkebinder ausgewählt ist aus der Gruppe bestehend aus Kartoffelstärke, Kar
toffelstärkederivat, wachsartiger Maisstärke und wachsartigem Maisstärkederivat.
26. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei der
Stärkebinder in einer Konzentration in einem Bereich von etwa 5 Gew.-% bis etwa 50
Gew.-% der Zusammensetzung auf Stärke-Basis, vorzugsweise in einem Bereich von etwa
10 Gew.-% bis etwa 40 Gew.-% der Zusammensetzung auf Stärke-Basis vorliegt.
27. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei der
Stärkebinder in einer Konzentration in einem Bereich von etwa 10 Gew.-% bis etwa 80
Gew.-% der Gesamffeststoffe in der Zusammensetzung auf Stärke-Basis, vorzugsweise in
einem Bereich von etwa 30 Gew.-% bis etwa 70 Gew.-% der Gesamtfeststoffe in der
Zusammensetzung auf Stärke-Basis vorliegt.
28. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei die
Stärkekörnchen einen Amylosegehalt von weniger als etwa 45%, vorzugsweise von weniger
als etwa 25% aufweisen.
29. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei das
Wasser in einer Konzentration in einem Bereich von etwa 15 Gew.-% bis etwa 80 Gew.-%
der Zusammensetzung auf Stärke-Basis, vorzugsweise in einem Bereich von etwa 30
Gew.-% bis etwa 70 Gew.-% der Zusammensetzung auf Stärke-Basis vorliegt.
30. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei das
Verdickungsmittel einen im wesentlichen gelatinierten Binder auf Stärke-Basis umfaßt.
31. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei das
Verdickungsmittel eine modifizierte Stärke ist, vorzugsweise eine modifizierte Stärke, die
modifiziert wurde durch mindestens ein Verfahren der Veresterung, Veretherung, Oxidation,
Säurehydrolyse, Vernetzung und Enzymumwandlung.
32. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei das
Verdickungsmittel einen Cellulosederivatether umfaßt, vorzugsweise einen
Cellulosederivatether ausgewählt aus der Gruppe bestehend aus Methyl
hydroxyethylcellulose, Hydroxymethylethylcellulose, Carboxymethylcellulose, Methylcellu
lose, Ethylcellulose, Hydroxyethylcellulose, Hydroxyethylpropylcellulose, Hydroxypropylme
thylcellulose und Gemischen oder Derivaten davon.
33. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei das
Verdickungsmittel ein Polysaccharid oder ein Polysaccharidderivat umfaßt, vorzugsweise ein
Polysaccharid oder Polysaccharidderivat ausgewählt aus der Gruppe bestehend aus
Alginsäure, Phycocolloiden, Agar, Gummi arabicum, Guargum, Johannisbrotgummi, Karaya-
Gummi, Xanthangummi, Tragant-Gummi und Gemischen oder Derivaten davon.
34. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei das
Verdickungsmittel ein Protein oder ein Proteinderivat ist, vorzugsweise ein Protein oder
Proteinderivat ausgewählt aus der Gruppe bestehend aus Prolamin, Kollagen, Gelatine,
Kasein und Gemischen oder Derivaten davon.
35. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei das
Verdickungsmittel ein synthetisches organisches Material ist, vorzugsweise ein synthetisches
organisches Material ausgewählt aus der Gruppe bestehend aus Polyvinylpyrrolidon,
Polyethylenglykol, Polyvinylalkohol, Polyvinylmethylether, Polyacrylsäuren,
Polyacrylsäuresalzen, Polyvinylacrylsäuren, Polyvinylacrylsäuresalzen, Polyacrylamiden,
Ethylenoxid-Polymeren, Polymilchsäure, Latex und Gemischen oder Derivaten davon.
36. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei die
Fasern natürlich vorkommende organische Fasern einschließen, vorzugsweise
Cellulosederivat-Fasern, insbesondere Fasern abgeleitet von einer Faserquelle, ausgewählt
aus der Gruppe bestehend aus Hartholz, Weichholz, recycelten Papierfasern, Hanf,
Baumwolle, Sisal, Abaca und Bagasse.
37. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei die
Fasern anorganische Fasern einschließen, vorzugsweise anorganische Fasern ausgewählt
aus der Gruppe bestehend aus Glasfasern, Graphitfasern, Silicafasern, Keramikfasern und
Metallfasern.
38. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei die
Fasern in einer Konzentration in einem Bereich von etwa 1 Gew.-% bis etwa 40 Gew.-% der
Zusammensetzung auf Stärke-Basis, vorzugsweise in einem Bereich von etwa 2 Gew.-% bis
etwa 20 Gew.-% der Zusammensetzung auf Stärke-Basis vorliegen.
39. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei die
Fasern in einer Konzentration in einem Bereich von etwa 2 Gew.-% bis etwa 80 Gew.-% der
Gesamtfeststoffe in der Zusammensetzung auf Stärke-Basis, vorzugsweise in einem Bereich
von etwa 5 Gew.-% bis etwa 20 Gew.-% der Gesamtfeststoffe in der Zusammensetzung auf
Stärke-Basis vorliegen.
40. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei die
Fasern ein Seitenverhältnis von mindestens etwa 100 : 1, vorzugsweise von mindestens etwa
250 : 1 aufweisen.
41. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei die
Fasern eine durchschnittliche Länge in einem Bereich von etwa 0,3 mm bis etwa 2 mm
aufweisen.
42. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, wobei die
Fasern eine durchschnittliche Länge von mindestens etwa 2 mm, vorzugsweise von
mindestens etwa 3,5 mm und insbesondere von mindestens etwa 6,5 mm aufweisen.
43. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, des weiteren
einen anorganischen Aggregat-Füllstoff umfassend, vorzugsweise einen anorganischen
Aggregat-Füllstoff ausgewählt aus der Gruppe bestehend aus Calciumcarbonat, Sand, Kies,
Fels (Gestein), Kalkstein, Sandstein, Glaskügelchen, Mica, Ton, Kaolin, synthetischem Ton,
Aluminiumoxid, Silica, Flugasche, Quarzglas, tafelförmigem Aluminiumoxid, Mikrokügelchen,
Calciumsulfatdihydrat, Calciumaluminat, hydratisierten hydraulischen Zementteilchen,
unhydratisierten hydraulischen Zementteilchen, Perlit, Vermiculit, hohlen Glaskügelchen,
Aerogelen, Xerogelen, porösen Keramikkügelchen, Xonotlit, leichtgewichtigen expandierten
Tonen, Bimsstein und abgebröckeltem Fels.
44. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, des weiteren
umfassend einen anorganischen Aggregat-Füllstoff in einer Konzentration in einem Bereich
von etwa 20 Gew.-% bis etwa 80 Gew.-% der Gesamtfeststoffe in der Zusammensetzung auf
Stärke-Basis, vorzugsweise in einem Bereich von etwa 30 Gew.-% bis etwa 70 Gew.-% der
Gesamtfeststoffe in der Zusammensetzung auf Stärke-Basis, insbesondere in einem Bereich
von etwa 40 Gew.-% bis etwa 60 Gew.-% der Gesamtfeststoffe in der Zusammensetzung auf
Stärke-Basis.
45. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, des weiteren
ein Formentrennmittel umfassend, vorzugsweise ein Formentrennmittel ausgewählt aus der
Gruppe bestehend aus mittelkettigen Fettsäuren, langkettigen Fettsäuren und
Magnesiumstearat.
46. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, des weiteren
ein inneres Beschichtungsmaterial umfassend, vorzugsweise ein inneres
Beschichtungsmaterial ausgewählt aus der Gruppe bestehend aus Wachs, Polymilchsäure
und Schellack.
47. Fasergefüllte Zusammensetzung auf Stärke-Basis gemäß Anspruch 20, des weiteren
einen Weichmacher umfassend, vorzugsweise einen Weichmacher ausgewählt aus der
Gruppe bestehend aus Mono- und Diglyceriden, Polyethylenglycol, Glycerin und Sorbitol.