DE19644673A1 - Rotationsgeräte aus Edel- und/oder Nichtedelmetall - Google Patents
Rotationsgeräte aus Edel- und/oder NichtedelmetallInfo
- Publication number
- DE19644673A1 DE19644673A1 DE1996144673 DE19644673A DE19644673A1 DE 19644673 A1 DE19644673 A1 DE 19644673A1 DE 1996144673 DE1996144673 DE 1996144673 DE 19644673 A DE19644673 A DE 19644673A DE 19644673 A1 DE19644673 A1 DE 19644673A1
- Authority
- DE
- Germany
- Prior art keywords
- molten glass
- stirrer
- devices
- precious
- plunger
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Description
Die Erfindung bezieht sich auf Vorrichtungen zum Verrühren und/oder
portionsweisem Ausstoßen von geschmolzenem Glas.
Um homogene, schlierenfreie Gläser herzustellen, finden Stirrergeräte
Anwendung, mit denen das Glas in zähflüssigen Zustand gerührt und
durchgemischt wird.
Weiterhin werden Plungergeräte dazu benutzt, die Glasmasse in Form von
Tropfen nach unten in automatisch arbeitende Maschinen geführt wird.
Es ist bekannt, daß oben erwähnte Geräte aus reinem Platin und/oder Pla
tiniegierungen hergestellt werden. Desweiteren sind Geräte bekannt, die
als Kernmaterial Molybdän, Wolfram oder Legierungen beider mit einem
Überzug aus Platin oder Platinlegierungen versehen sind.
Dieselben haben den Nachteil ungenügender Festigkeit bei hohen Tempe
raturen als auch zu kostenintensiv zu sein. Im Falle von Kernmaterialien
mit Platinüberzug besteht der Nachteil in der Möglichkeit einer Undich
tigkeit bei Verlust des Vakuums.
Durch die Erfindung werden die Mängel der bekannten Geräte auf
zweckmäßige Weise vermieden.
Gemäß der vorliegenden Erfindung bestehen die in Berührung mit dem
geschmolzenen Glas stehenden Geräteteile aus
A) Edelmetallen wie Pla tin, Rhodium, Palladium, Gold, Silber, Ruthenium, Iridium, Osmium bzw. deren Legierungen oder aus Kombinationen dieser Werkstoffe,
B) Nicht-Edelmetalle wie Nickel, Eisen und Chrom bzw. deren Legierun gen oder Kombinationen sind für geeignete Glasschmelztemperaturen und/oder Glaszusammensetzungen ebenfalls Gegenstand dieser Erfin dung.
A) Edelmetallen wie Pla tin, Rhodium, Palladium, Gold, Silber, Ruthenium, Iridium, Osmium bzw. deren Legierungen oder aus Kombinationen dieser Werkstoffe,
B) Nicht-Edelmetalle wie Nickel, Eisen und Chrom bzw. deren Legierun gen oder Kombinationen sind für geeignete Glasschmelztemperaturen und/oder Glaszusammensetzungen ebenfalls Gegenstand dieser Erfin dung.
Konsequenterweise werden diese Edel- und Nichtedelmetalle nicht in
Vollmaterial Anwendung finden, sondern sind im Innern mit einem oder
mehreren Kühlkanälen durchsetzt.
Geeignete Stabilisierung im Innern der Rotationsgeräte sind in Form von
Stangen, Bändern, Blechen, Waben oder in sonstiger Querschnittsform
vorgesehen. Weiteren geeigneten stabilisierungstechnischen Möglichkei
ten sind keine Grenzen gesetzt.
Durch die Ausbildung der Edel- und/oder Nichtedelmetallgeräte gemäß
der Erfindung sind die Achsen der Rotationsbehälter und/oder der Flügel,
Paddel, Fahnen mit Wasser-, Luft- und/oder Gaskühlkanälen versehen,
was die Stabilisieren erhöht und Edelmetallkosten erheblich senkt.
Auf den erwähnten Nachteil eines Vakuums kann in diesem Fall verzich
tet werden.
Claims (6)
1. Stirrer- und Plungergeräte für geschmolzenes Glas,
dadurch gekennzeichnet, daß die Rotationsgeräte aus
Edel- und/oder Nichtedelmetall mit einem oder mehreren
Kühlkanälen ausgeführt sind.
2. Stirrer- und Plungergeräte für geschmolzenes Glas,
dadurch gekennzeichnet, daß Edelmetalle wie Platin,
Rhodium, Palladium, Gold, Silber, Ruthenium, Iridium,
Osmium bzw. deren Legierungen oder Kombinationen
Anwendung finden.
3. Stirrer- und Plungergeräte für geschmolzenes Glas,
dadurch gekennzeichnet, daß Nicht-Edelmetalle wie
Nickel, Eisen und Chrom bzw. deren Legierungen oder
Kombinationen Anwendung finden.
4. Stirrer- und Plungergeräte für geschmolzenes Glas,
dadurch gekennzeichnet, daß zur Stabilisierung
der Kühlkanäle Stangen, Bänder, Bleche, Waben oder sonstige
Querschnittsformen Anwendung finden.
5. Stirrer- und Plungergeräte für geschmolzenes Glas,
dadurch gekennzeichnet, daß zur Stabilisierung
des Innenraumes der Rotationsgeräte eine Wasser-
Luft- und/oder Gas-Kühlung vorgesehen sein kann.
6. Stirrer- und Plungergeräte für geschmolzenes Glas,
dadurch gekennzeichnet, daß zur Stabilisierung
der Edelmetallgeräte Quarzglas oder Zirkonmaterialien
verwendet werden.