DE102007029600A1 - Novel piezoceramic composition is prepared by utilizing piezoceramic material, and green body is supplied with piezoceramic composition - Google Patents

Novel piezoceramic composition is prepared by utilizing piezoceramic material, and green body is supplied with piezoceramic composition Download PDF

Info

Publication number
DE102007029600A1
DE102007029600A1 DE102007029600A DE102007029600A DE102007029600A1 DE 102007029600 A1 DE102007029600 A1 DE 102007029600A1 DE 102007029600 A DE102007029600 A DE 102007029600A DE 102007029600 A DE102007029600 A DE 102007029600A DE 102007029600 A1 DE102007029600 A1 DE 102007029600A1
Authority
DE
Germany
Prior art keywords
piezoceramic
composition
composition according
electrode material
content
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE102007029600A
Other languages
German (de)
Inventor
Francois Bamiere
Katrin Benkert
Carsten Dr. Schuh
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Siemens AG
Original Assignee
Siemens AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Siemens AG filed Critical Siemens AG
Priority to DE102007029600A priority Critical patent/DE102007029600A1/en
Publication of DE102007029600A1 publication Critical patent/DE102007029600A1/en
Withdrawn legal-status Critical Current

Abstract

The piezoceramic composition is new. The piezoceramic composition of formula (I), is new. Pb 1 - aRE bAE cAL d[Zr xTi y(Sc sW) z]O 3(I) RE : rare-earth metal with a rare-earth metal part of b; AE : alkaline earth metal with an alkaline earth metal part of c; AL : alkali metal with an alkali metal portion of d; a : not > 1; b : 0-0.4; c : 0-0.5; d : 0-0.5; s : not less than 0; x : not less than 0; y : not less than 0; z : not less than 0; and x+y+z : 1. An independent claim is also included for a method for manufacturing a piezoceramic component, which involves utilizing piezoceramic composition with piezoceramic material, and a green body is supplied with the piezoceramic composition.

Description

Die Erfindung betrifft eine piezokeramische Zusammensetzung mit einer nominalen Summenformel eines Bleizirkonattitanats (Pb(Ti, Zr)O3, PZT). Daneben werden ein Verfahren zum Herstellen eines piezokeramischen Bauteils unter Verwendung der piezokeramischen Zusammensetzung und eine Verwendung des piezokeramischen Bauteils angegeben.The invention relates to a piezoceramic composition having a nominal composition of lead zirconate titanate (Pb (Ti, Zr) O 3 , PZT). In addition, a method for producing a piezoceramic component using the piezoceramic composition and a use of the piezoceramic component are specified.

Bleizirkonattitanat ist ein Perowskit, bei dem die A-Plätze des Perowskits mit zweiwertigem Blei (Pb2+) und die B-Plätze des Perowskits mit vierwertigem Zirkonium (Zr4+) und vierwertigem Titan (Ti4+) besetzt sind. Zur Beeinflussung einer elektrischen oder piezoelektrischen Eigenschaft wie Permittivität, Curietemperatur, Kopplungsfaktor oder piezoelektrische Ladungskonstante (beispielsweise d33-Koeffizient) wird PZT dotiert.Lead zirconate titanate is a perovskite in which Perovskite A sites of divalent lead (Pb 2+ ) and perovskite B sites are occupied by tetravalent zirconium (Zr 4+ ) and tetravalent titanium (Ti 4+ ). To influence an electrical or piezoelectric property such as permittivity, Curie temperature, coupling factor or piezoelectric charge constant (for example, d 33 coefficient) PZT is doped.

Aus der EP 0 894 341 B1 ist ein piezokeramisches Bauteil in Form eines monolithischen Vielschichtaktors bekannt. Der Vielschichtaktor besteht aus einer Vielzahl von übereinander zu einem monolithischen Stapel angeordneten Piezoelementen. Jedes der Piezoelemente weist eine Elektrodenschicht, eine weitere Elektrodenschicht und eine zwischen den Elektrodenschichten angeordnete Piezokeramikschicht auf. Im Stapel benachbarte Piezoelemente weisen jeweils eine gemeinsame Elektrodenschicht auf. Das Elektrodenmaterial der Elektrodenschichten besteht aus einer Silber-Palladium-Legierung. Die Piezokeramikschichten weisen einen piezokeramischen Werkstoff aus PZT auf. Die nominale Summenformel des piezokeramischen Werkstoffs lautet Pb0,99Ag0,01La0,01[Zr0,30Ti0,36(Ni1/3Nb2/3)0,34]O3. Dieses PZT weist mit Nickel und Niob eine komplexe B-Platzdotierung auf.From the EP 0 894 341 B1 is a piezoceramic component known in the form of a monolithic multilayer actuator. The multilayer actuator consists of a plurality of piezo elements arranged one above the other in a monolithic stack. Each of the piezoelectric elements has an electrode layer, a further electrode layer and a piezoceramic layer arranged between the electrode layers. In the stack adjacent piezoelectric elements each have a common electrode layer. The electrode material of the electrode layers consists of a silver-palladium alloy. The piezoceramic layers have a piezoceramic material of PZT. The nominal empirical formula of the piezoceramic material is Pb 0.99 Ag 0.01 La 0.01 [Zr 0.30 Ti 0.36 (Ni 1/3 Nb 2/3 ) 0.34] O 3 . This PZT exhibits complex B-doping with nickel and niobium.

Zum Herstellen des Vielschichtaktors werden pulverförmige, oxidische Metallverbindungen zu einer piezokeramischen Zusammensetzung mit der formalen Summenformel Pb0,99La0,01[Zr0,30Ti0,36(Ni1/3Nb2/3)0,34]O3,005 gemischt. Die piezokeramische Zusammensetzung besteht aus einer Mischung pulverförmiger Metalloxide. Diese Mischung wird in einem Formgebungsprozess zu keramischen Grünfolien verarbeitet. Die keramischen Grünfolien werden mit Elektrodenmaterial aus einer Silber-Palladium-Legierung mit einem Palladium-Anteil von etwa 30 Gew.-% bedruckt. Die bedruckten Grünfolien werden übereinander gestapelt, entbindert und gesintert. Beim Sintern entstehen aus den Grünfolien mit der piezokeramischen Zusammensetzung die Piezokeramikschichten mit dem piezokeramischen Werkstoff. Aus den auf die Grünfolien gedruckten Elektrodenmaterialien entstehen die Elektrodenschichten (Innenelektroden). Durch das gemeinsame Sintern der Piezokeramikschichten und der Elektrodenschichten (Cofiring) entsteht der monolithische Vielschichtaktor.For producing the multilayer actuator, powdery oxide metal compounds become a piezoceramic composition having the formal molecular formula Pb 0.99 La 0.01 [Zr 0.30 Ti 0.36 (Ni 1/3 Nb 2/3 ) 0.34] O 3.005 mixed. The piezoceramic composition consists of a mixture of powdered metal oxides. This mixture is processed into ceramic green sheets in a molding process. The ceramic green sheets are printed with electrode material of a silver-palladium alloy having a palladium content of about 30 wt .-%. The printed green sheets are stacked, debinded and sintered. During sintering, the green films with the piezoceramic composition form the piezoceramic layers with the piezoceramic material. The electrode layers (internal electrodes) are produced from the electrode materials printed on the green sheets. The monolithic multilayer actuator is produced by the common sintering of the piezoceramic layers and the electrode layers (cofiring).

Die Zusammensetzung des beim Sintern resultierenden piezokeramischen Werkstoffs ist stöchiometrisch. Die Stöchiometrie ergibt sich dadurch, dass beim Sintern überschüssiges Blei in Form von Bleioxid (PbO) entweicht. Überschüssig vorhandenes, heterovalentes Lanthan wird durch den Einbau von Silber des Elektrodenmaterials auf den A-Plätzen des PZTs ausgeglichen.The Composition of the resulting piezoceramic during sintering Material is stoichiometric. The stoichiometry results from the fact that surplus during sintering Lead in the form of lead oxide (PbO) escapes. surplus Existing, heterovalent lanthanum is formed by the incorporation of silver of the electrode material on the A-sites of the PZT balanced.

Der resultierende Vielschichtaktor zeichnet sich durch gute piezoelektrische Eigenschaften aus. Beispielsweise beträgt die Curie-Temperatur Tc etwa 170°C. Allerdings liegt die Sintertemperatur zum Erzielen der guten piezoelektrischen Eigenschaften bei über 1100°C. Um ein Aufschmelzen des Elektrodenmaterials bei diesen hohen Sintertemperaturen zu vermeiden, muss der Palladiumanteil am Elektrodenmaterial mindestens 30 Gew.-% betragen.The resulting multilayer actuator is characterized by good piezoelectric properties. For example, the Curie temperature T c is about 170 ° C. However, the sintering temperature for achieving the good piezoelectric properties is over 1100 ° C. In order to avoid a melting of the electrode material at these high sintering temperatures, the palladium content of the electrode material must be at least 30% by weight.

Aus Kostengründen ist es wünschenswert, den Palladiumanteil am Elektrodenmaterial zu erniedrigen oder generell billigeres Elektrodenmaterial wie Kupfer oder reines Silber zu verwenden. Diese Metalle weisen jeweils einen Schmelzpunkt von unter 1100°C auf. Dies bedeutet, dass die Sintertemperatur erniedrigt werden muss. Die bekannte piezokeramische Zusammensetzung eignet sich nicht zum Verdichten bei einer Sintertemperatur von unter 1100°C. Bei einer solch niedrigen Sintertemperatur werden die verbesserten piezoelektrischen Eigenschaften nicht erzielt.Out For cost reasons, it is desirable to have the palladium content on the electrode material or generally cheaper electrode material such as To use copper or pure silver. These metals each have a melting point of less than 1100 ° C on. This means, that the sintering temperature must be lowered. The well-known piezoceramic Composition is not suitable for compacting at a sintering temperature from below 1100 ° C. At such a low sintering temperature the improved piezoelectric properties are not achieved.

Aufgabe der Erfindung ist es, eine piezokeramische Zusammensetzung anzugeben, die bei einer Sintertemperatur von unter 1100°C verdichtet und die sich zu einem piezokeramischen Werkstoff verarbeiten lässt, der im Vergleich zum Stand der Technik ähnliche oder bessere piezoelektrische Eigenschaften aufweist.task the invention is to provide a piezoceramic composition, which compacts at a sintering temperature of below 1100 ° C and which can be processed to a piezoceramic material, the similar or better compared to the prior art having piezoelectric properties.

Zur Lösung der Aufgabe wird eine piezokeramische Zusammensetzung mit einer nominalen Summenformel Pb1-aREbAEcALd[ZrxTiy(ScsWw)z]O3, angegeben, wobei RE ein Seltenerdmetall mit einem Seltenerdmetallanteil b ist, AE ein Erdalkalimetall mit einem Erdalkalimetallanteil c ist, AL ein Alkalimetall mit einem Alkalimetallanteil d ist, Scandium mit einem Scandiumanteil s·z vorhanden ist und Wolfram mit einem Wolframanteil w·z vorhanden ist. Darüber hinaus gelten folgende Zusammenhänge:
a < 1
0 ≤ b ≤ 0,4
0 ≤ c ≤ 0,5
0 ≤ d ≤ 0,5
s > 0
w > 0
0,1 ≤ s/w ≤ 5
x > 0
y > 0
z > 0
x + y + z = 1.To achieve the object, a piezoceramic composition having a nominal empirical formula Pb 1-a RE b AE c AL d [Zr x Ti y (Sc s W w ) z ] O 3 is given, where RE is a rare earth metal having a rare earth metal content b, AE is an alkaline earth metal having an alkaline earth metal content c, AL is an alkali metal having an alkali metal content d, scandium is present with a scandium content s · z and tungsten with a tungsten content w · z is present. In addition, the following relationships apply:
a <1
0 ≤ b ≤ 0.4
0 ≤ c ≤ 0.5
0 ≤ d ≤ 0.5
s> 0
w> 0
0.1 ≤ s / w ≤ 5
x> 0
y> 0
z> 0
x + y + z = 1.

Die angegebenen Anteile sind molare Anteile. s/w gibt das Verhältnis der molaren Anteile von Scandium und Wolfram an.The specified proportions are molar proportions. b / w gives the ratio the molar proportions of scandium and tungsten.

Zur Lösung der Aufgabe wird auch ein Verfahren zum Herstellen eines piezokeramischen Bauteils mit einem piezokeramischen Werkstoff unter Verwendung der piezokeramischen Zusammensetzung mit folgenden Verfahrensschritten angegeben: a) Bereitstellen eines Grünkörpers mit der piezokeramischen Zusammensetzung und b) Wärmebehandeln des Grünkörpers, wobei aus der piezokeramischen Zusammensetzung der piezokeramische Werkstoff des Bauteils entsteht. Der Grünkörper ist ein Formkörper, der beispielsweise aus homogen vermischten, zusammen verpressten Oxiden der angegebenen Metalle besteht. Ebenso kann der Grünkörper ein organisches Additiv aufweisen, das mit den Oxiden der Metalle zu einem Schlicker verarbeitet ist. Das organische Additiv ist beispielsweise ein Binder oder ein Dispergator. Aus dem Schlicker wird ein Grünkörper, beispielsweise in Form einer Grünfolie durch Folienziehen erzeugt. Der beim Formgebungsprozess hergestellte Grünkörper mit der piezokeramischen Zusammensetzung wird einer Wärmebehandlung unterzogen. Das Wärmebehandeln des Grünkörpers beinhaltet ein Kalzinieren und/oder ein Sintern. Es kommt zur Bildung und zum Verdichten des sich bildenden piezokeramischen Werkstoffs. Beim Verdichten entweicht Bleioxid. Daher wird Blei mit einem stöchiometrischen Bleiüberschuss von bis zu 0,1 (10 mol%) und vorzugsweise bis zu 0,05 (5 mol%) zugegeben. Der Bleiüberschuss beträgt beispielsweise 0,03 (3 mol%).to Solution to the problem is also a method of manufacturing a piezoceramic component with a piezoceramic material using the piezoceramic composition with the following Process steps indicated: a) providing a green body with the piezoceramic composition and b) heat treating of the green body, leaving from the piezoceramic Composition of the piezoceramic material of the component arises. The green body is a shaped body that for example, homogeneously mixed, co-compressed oxides the specified metals. Likewise, the green body have an organic additive with the oxides of the metals processed into a slurry. The organic additive is for example a binder or a dispersant. The slip becomes a green body, for example in the form of a green sheet by film drawing generated. The green body produced during the molding process with the piezoceramic composition becomes a heat treatment subjected. The heat treatment of the green body includes calcination and / or sintering. It comes to education and for compacting the forming piezoceramic material. At the Compaction escapes lead oxide. Therefore, lead with a stoichiometric Lead excess of up to 0.1 (10 mol%) and preferably up to 0.05 (5 mol%) was added. The lead surplus is for example, 0.03 (3 mol%).

Der Erfindung liegt die Erkenntnis zugrunde, dass sich ein Bleizirkonattitanat mit komplexer 3-Platz-Dotierung mit Scandium und Wolfram bei einer relativ niedrigen Sintertemperatur verdichten lässt. Es wird vermutet, dass sich während des Sinterprozesses intermediär eine bei niedriger Temperatur schmelzende eutektische Phase aus Bleioxid und Wolframoxid (PbO·WO3) bildet. Diese eutektische Phase kann die Sinterung der piezokeramischen Zusammensetzung zum piezokeramischen Werkstoff begünstigen (Schmelzphasen unterstütze Sinterung). Die Bildung und das Verdichten des piezokeramischen Werkstoffs finden bereits bei Temperaturen von 1000°C statt. Da aus XRD-Messungen nach dem Sintern keine Hinweise auf das Vorhandensein einer weiteren Phase zu entnehmen sind, wird davon ausgegangen, dass ein Anteil der flüssigen Phase sehr gering ist. In Folge des geringen Anteils werden die piezoelektrischen Eigenschaften des resultierenden piezokeramischen Werkstoffs kaum beeinflusst. Zudem werden die Komponenten der flüssigen Phase vermutlich beim Fortgang des Sinterns in das PZT eingebaut.The invention is based on the finding that a lead zirconate titanate with complex 3-site doping with scandium and tungsten can be compacted at a relatively low sintering temperature. It is assumed that a low-melting eutectic phase of lead oxide and tungsten oxide (PbO.WO 3 ) forms as an intermediate during the sintering process. This eutectic phase may favor the sintering of the piezoceramic composition to the piezoceramic material (melt phases assist sintering). The formation and densification of the piezoceramic material take place even at temperatures of 1000 ° C. Since XRD measurements after sintering give no indication of the presence of another phase, it is assumed that a proportion of the liquid phase is very small. Due to the low proportion, the piezoelectric properties of the resulting piezoceramic material are hardly affected. In addition, the components of the liquid phase are believed to be incorporated into the PZT as sintering progresses.

Ein weiterer, die Sinterung begünstigender Effekt, ist in einer Leerstellenkompensation zu sehen, die bei dieser komplexen B-Platz-Dotierung auftritt: Akzeptor-Ionen, wie beispielsweise Sc3+, bewirken die Bildung von Sauerstoff-Leerstellen. Donator-Ionen, wie beispielsweise W3+, W4+ und W6+, bewirken Blei-Leerstellen. Leerstellen sind Gitterdefekte im PZT, die eine Mobilität der Korngrenzen und somit den Verdichtungsprozess beim Sintern behindern. Durch die Zugabe der Dotierungs-Ionen werden Sauerstoff-Leerstellen und Blei-Leerstellen gebildet. Aufgrund der unterschiedlichen Ladungsvorzeichen kompensieren sich die Sauerstoffleerstellen und die Bleileerstellen. Die Verdichtung beim Sintern wird begünstigt.Another effect favoring sintering is to be seen in a vacancy compensation that occurs in this complex B-site doping: acceptor ions, such as Sc 3+ , cause the formation of oxygen vacancies. Donor ions such as W 3+ , W 4+ and W 6+ cause lead vacancies. Voids are lattice defects in the PZT, which impede the mobility of the grain boundaries and thus the compression process during sintering. The addition of the doping ions forms oxygen vacancies and lead vacancies. Due to the different signs of charge, the oxygen vacancies and the lead generation sites compensate each other. The compression during sintering is favored.

Prinzipiell ist ein beliebiges Verhältnis des Scandiumanteils und des Wolframanteils zueinander denkbar. Vorzugsweise gilt: 0,5 ≤ s/w ≤ 3. Beispielsweise ist das Verhältnis s/w gleich 1. In einer besonderen Ausgestaltung gilt s/w = 2. Das Verhältnis des Scandiumanteils und des Wolframanteils beträgt im Wesentlichen 2. Dabei ist eine Abweichung von 10% (1,8 ≤ s/w ≤ 1,2) bis hin zu 20% möglich (1,6 ≤ s/w ≤ 2,4). Bei diesem Verhältnis sind die Anzahlen der Sauerstoff-Leerstellen und der Blei-Leerstellen annähernd gleich. Es findet eine optimale Leerstellen-Kompensation statt.in principle is any ratio of the scandium content and the Wolframanteils conceivable to each other. Preferably, 0.5 ≦ s / w ≦ 3. For example, the ratio s / w is 1. In one special design applies s / w = 2. The ratio of the Scandiumanteils and the tungsten content is substantially 2. Here is a deviation of 10% (1.8 ≤ s / w ≤ 1.2) up to 20% possible (1.6 ≤ s / w ≤ 2.4). At this ratio, the numbers of oxygen vacancies and the lead vacancies are approximately equal. It finds one optimal vacancy compensation takes place.

Vorzugsweise beträgt der Scandiumanteil 2/3·z. Es gilt: s = 2/3. Auch hier sind Abweichungen von 10% bis hin zu 20% möglich. Mit diesen Anteilen lässt sich eine besonders niedrige Sintertemperatur bei relativ guten piezoelektrischen Eigenschaften des resultierenden piezokeramischen Werkstoffs erzielen. Aber auch mit dem Zusammenhang s = w = 0,5 werden sehr gute Ergebnisse erzielt.Preferably the scandium content is 2/3 · z. The following applies: s = 2.3. Again, deviations of 10% up to 20% are possible. With these proportions can be a particularly low Sintering temperature with relatively good piezoelectric properties achieve the resulting piezoceramic material. But also with the relationship s = w = 0.5, very good results are achieved.

Besonders vorteilhaft ist es, wenn ein Erdalkalimetall AE vorhanden sind, also der Erdalkalianteil c ungleich 0 ist. Die Anwesenheit von Erdalkalimetallen fördert das Kornwachstum des sich bildenden piezokeramischen Werkstoffs. Es werden im Mittel beim Sintern größere Piezokeramik-Körner erhalten. Dadurch können sich die piezokeramischen Eigenschaften verbessern, da das für den piezoelektrischen Effekt notwendige Domänenschalten mit zunehmender Größe der Korner weniger stark beeinträchtigt wird. Der gleiche Effekt lässt sich durch Alkalimetalle AL erzielen. Gemäß einer besonderen Ausgestaltung gilt daher folgender Zusammenhang: 0,005 ≤ c + d ≤ 0,1. Das Erdalkalimetall ist mindestens ein aus der Gruppe Calcium, Strontium und Barium ausgewähltes Metall. Das Alkalimetall ist mindestens ein aus der Gruppe Lithium, Natrium und Kalium ausgewähltes Metall. Dabei kann nur eine Art Erdalkalimetall bzw. Alkalimetall vorhanden sein. Denkbar sind auch mehrere Arten Erdalkalimetalle oder Alkalimetalle, beispielsweise Strontium und Barium oder Natrium und Kalium.It is particularly advantageous if an alkaline earth metal AE are present, that is, the alkaline earth metal component c is not equal to zero. The presence of alkaline earth metals promotes grain growth of the forming piezoceramic material. On average, larger piezoceramic grains are obtained during sintering. As a result, the piezoceramic properties can be improved since the domain switching necessary for the piezoelectric effect is less affected with increasing size of the grains. The same effect can be achieved by alkali metals AL. According to a particular embodiment, therefore, the following relationship applies: 0.005 ≦ c + d ≦ 0.1. The alkaline earth metal is at least one selected from the group calcium, strontium and barium metal. The alkali metal is at least one selected from the group lithium, sodium and potassium metal. It can only one kind Alkaline earth metal or alkali metal may be present. Also conceivable are several types of alkaline earth metals or alkali metals, for example strontium and barium or sodium and potassium.

Im Hinblick auf gute piezokeramische Eigenschaften wird ein geringer Anteil der A-Plätze des piezokeramischen Werkstoffs mit einem oder mehreren Seltenerdmetallen RE besetzt. Der Seltenerdanteil b beträgt unter 15 mol% (b ≤ 0,15). Insbesondere ist b aus dem Bereich von 0,005 bis 0,15 gewählt. Als Seltenerdmetall kann dabei ein beliebiges Element der Lanthaniden- oder Actiniden-Gruppe eingesetzt werden. In einer besonderen Ausgestaltung ist das Seltenerdmetall RE mindestens ein aus der Gruppe Europium, Gadolinium, Lanthan, Neodym, Praseodym, Promethium und Samarium ausgewähltes Metall. Diese Seltenerdmetalle führen mit dem angegebenen geringen Seltenerdmetallanteil c zu einem relativ hohen d33-Koeffizienten im Kleinsignalbereich (bei elektrischen Feldstärken von wenigen V/mm) als auch im Großsignalbereich (bei elektrischen Feldstärken von einigen kV/mm).With regard to good piezoceramic properties, a small proportion of the A sites of the piezoceramic material is occupied by one or more rare earth elements RE. The rare earth ratio b is less than 15 mol% (b ≤ 0.15). In particular, b is selected from the range of 0.005 to 0.15. In this case, any element of the lanthanide or actinide group can be used as the rare earth element. In a particular embodiment, the rare earth element RE is at least one metal selected from the group europium, gadolinium, lanthanum, neodymium, praseodymium, promethium and samarium. These rare earth metals lead to a relatively high d 33 coefficient in the small signal range (with electric field strengths of a few V / mm) and in the large signal range (with electric field strengths of a few kV / mm) with the stated low rare earth metal content c.

Für die komplexe B-Platzdotierung gilt: x + y + z = 1. Als besonders vorteilhaft hat sich herausgestellt, wenn dabei z zwischen 0,001 und 0,5 und insbesondere zwischen 0,001 und 0,05 liegt. Der Scandium-Wolfram-Anteil beträgt unter 5 mol%. Bei höheren Scandium-Wolfram-Anteilen können beim Sinterprozess Schmelzphasen (Glasphasen) aus Bleioxid und Wolframoxid (PbO·WO3) bzw. Scandiumoxid und Wolframoxid (Sc2O3·WO3) zu einem erheblichen Anteil auftreten. Dies führt zu einer Störung eines Gefüges des sich bildenden piezokeramischen Werkstoffs. Es werden die piezoelektrischen Eigenschaftswerte des piezokeramischen Werkstoffs negativ beeinflusst.For the complex B-doping, the following applies: x + y + z = 1. It has turned out to be particularly advantageous if z is between 0.001 and 0.5 and in particular between 0.001 and 0.05. The scandium-tungsten content is less than 5 mol%. At higher scandium-tungsten proportions in the sintering process melt phase (glass phase) of lead oxide and tungsten oxide (WO 3 O 3 Sc 2) to (PbO · WO 3) and tungsten oxide or scandium occur to a considerable extent. This leads to a disturbance of a structure of the forming piezoceramic material. The piezoelectric property values of the piezoceramic material are negatively influenced.

Zum Bereitstellen des Grünkörpers mit der piezokeramischen Zusammensetzung können Vorstufen der Oxide der Metalle, beispielsweise Carbonate oder Oxalate eingesetzt werden. Bevorzugt werden aber direkt Oxide der Metalle verwendet. Beide Arten von Metallverbindungen, also die Vorstufen der Oxide sowie die Oxide selbst, können als oxidische Metallverbindungen bezeichnet werden.To the Providing the green body with the piezoceramic Composition may be precursors of the oxides of the metals, For example, carbonates or oxalates can be used. Prefers but are used directly oxides of metals. Both types of Metal compounds, ie the precursors of the oxides and the oxides themselves, can be referred to as oxidic metal compounds become.

In einer besonderen Ausgestaltung wird zum Bereitstellen des Grünkörpers ein Mischen pulverförmiger, oxidischer Metallverbindungen der für die Zusammensetzung benötigten Metalle durchgeführt. Es werden oxidische Metallverbindungen der Metalle Blei, Seltenenerdmetall RE, Erdalkalimetall AE, Alkalimetall AL, Zirkonium, Titan, Scandium und Wolfram zur piezokeramischen Zusammensetzung vermischt. Zum Herstellen des piezokeramischen Werkstoffs werden die oxidischen Metallverbindungen als Pulver eingesetzt. Die oxidischen Metallverbindungen sind vorzugsweise Bleioxid (PbO), Seltenerdoxide (z. B. La2O3 oder Nd2O3), Erdalkalioxide (z. B. CaO oder SrO), Alkalioxide (z. B. Na2O oder K2O), Zirkoniumdioxid (ZrO2), Titandioxid (TiO2), Scandiumoxid (Sc2O3) und Wolframtrioxid (WO3).In a particular embodiment, to prepare the green body, a mixing of pulverulent, oxidic metal compounds of the metals required for the composition is carried out. Metal oxides of the metals lead, rare earth metal RE, alkaline earth metal AE, alkali metal AL, zirconium, titanium, scandium and tungsten are mixed into the piezoceramic composition. To produce the piezoceramic material, the oxidic metal compounds are used as powder. The oxidic metal compounds are preferably lead oxide (PbO), rare earth oxides (eg La 2 O 3 or Nd 2 O 3 ), alkaline earth oxides (eg CaO or SrO), alkali oxides (eg Na 2 O or K 2 O), zirconia (ZrO 2 ), titania (TiO 2 ), scandium oxide (Sc 2 O 3 ) and tungsten trioxide (WO 3 ).

Die Pulver der oxidischen Metallverbindungen können nach bekannten Verfahren hergestellt werden, beispielsweise über Fällungsreaktionen nach dem Sol-Gel-, dem Citrat-, dem Hydrothermal- oder dem Oxalatverfahren. Dabei können oxidische Metallverbindungen mit nur einer Art Metall hergestellt werden. Denkbar ist insbesondere auch, dass oxidische Metallverbindungen mit mehren Arten von Metallen eingesetzt werden (Mischoxide). Gemäß einer besonderen Ausgestaltung wird daher mindestens ein Mischoxid mit mindestens zwei der Metalle als oxidische Metallverbindung verwendet. Die oxidische Metallverbindung mit mindestens zwei der Metalle ist beispielsweise ein Zirkonattitanat ((Zr, TiO)2) oder ein Wolframat (Metallsalz der Wolframsäure) wie Scandium-Wolframat. Auch hier kann auf die oben erwähnten Fällungreaktionen zurückgegriffen werden. Denkbar ist auch ein Mixed-Oxide-Verfahren. Dabei werden pulverförmige Oxide verschiedener Metalle miteinander vermischt und bei höheren Temperaturen kalziniert. Beim Kalzinieren entstehen die Mischoxide.The powders of the oxidic metal compounds can be prepared by known processes, for example by precipitation reactions according to the sol-gel, citrate, hydrothermal or oxalate processes. In this case, oxidic metal compounds can be produced with only one kind of metal. It is also conceivable, in particular, that oxidic metal compounds are used with a plurality of types of metals (mixed oxides). According to a particular embodiment, therefore, at least one mixed oxide with at least two of the metals is used as the oxidic metal compound. The oxidic metal compound having at least two of the metals is, for example, a zirconium titanate ((Zr, TiO) 2 ) or a tungstate (metal salt of tungstic acid) such as scandium tungstate. Again, the precipitation reactions mentioned above can be used. Also conceivable is a mixed-oxide process. In this case, powdery oxides of various metals are mixed together and calcined at higher temperatures. Calcination results in mixed oxides.

Die Aufarbeitung der Metalloxide mit der Überführung in den piezokeramischen Werkstoff kann auf verschiedenen Weisen erfolgen. Denkbar ist beispielsweise, dass zunächst die Pulver der oxidischen Metallverbindungen homogen vermischt werden. Es entsteht die piezokeramische Zusammensetzung in Form einer homogenen Mischung der Metalloxide. Anschließend wird die piezokeramische Zusammensetzung durch Wärmebehandeln, z. B. durch Kalzinieren, in den piezokeramischen Werkstoff überführt. Der piezokeramische Werkstoff wird zu feinem Piezokeramikpulver zermalen. Anschließend wird aus dem feinen Piezokeramikpulver im Formgebungsprozess ein keramischer Grünkörper mit einem organischen Binder und weiteren organischen Additiven hergestellt. Dieser keramische Grünkörper wird entbindert und gesintert. Dabei bildet sich das piezokeramische Bauteil mit dem piezokeramische Werkstoff.The Workup of the metal oxides with the transfer in the piezoceramic material can be in different ways respectively. It is conceivable, for example, that the first Powder of the oxidic metal compounds are homogeneously mixed. The result is the piezoceramic composition in the form of a homogeneous Mixture of metal oxides. Subsequently, the piezoceramic composition by heat treatment, for. B. by calcination, in the piezoceramic Material transferred. The piezoceramic material will crunch to fine piezoceramic powder. Subsequently is made from the fine piezoceramic powder in the molding process ceramic green body with an organic binder and other organic additives. This ceramic green body is debinded and sintered. The piezoceramic forms Component with the piezoceramic material.

Alternativ zum beschriebenen Vorgehen können die Pulver der oxidischen Metallverbindungen homogen vermischt und im Formgebungsprozess zum keramischen Grünkörper mit organischem Binder verarbeitet werden. Auch dieser Grünkörper weist bereits die piezokeramische Zusammensetzung auf. Nachfolgendes Sintern führt zum piezokeramischen Bauteil mit dem piezokeramischen Werkstoff.alternative For the procedure described, the powders of the oxidic Metal compounds homogeneously mixed and used in the shaping process ceramic green body with organic binder are processed. Also this green body points already on the piezoceramic composition. Subsequent sintering leads to the piezoceramic component with the piezoceramic material.

Gemäß einer besonderen Ausgestaltung wird ein piezokeramischer Bauteil mit mindestens einem Piezoelement hergestellt, das eine Elektrodenschicht mit Elektrodenmaterial, mindestens eine weitere Elektrodenschicht mit einem weiteren Elektrodenmaterial und mindestens eine zwischen den Elektrodenschichten angeordnete Piezokeramikschicht mit dem piezokeramischen Werkstoff aufweist. Ein einziges Piezoelement stellt die kleinste Einheit des piezokeramischen Bauteils dar. Zum Herstellen des Piezoelements wird beispielsweise eine keramische Grünfolie mit der piezokeramischen Zusammensetzung beidseitig mit den Elektrodenmaterialien bedruckt. Die Elektrodenmaterialien können dabei gleich oder unterschiedlich sein. Durch nachfolgendes Entbindern und Sintern resultiert das Piezoelement.According to a particular embodiment, a piezoceramic component with at least ei A piezoelectric element has been produced, which has an electrode layer with electrode material, at least one further electrode layer with a further electrode material and at least one piezoceramic layer arranged between the electrode layers with the piezoceramic material. A single piezoelectric element represents the smallest unit of the piezoceramic component. To produce the piezoelectric element, for example, a ceramic green sheet with the piezoceramic composition is printed on both sides with the electrode materials. The electrode materials may be the same or different. Subsequent debindering and sintering results in the piezoelectric element.

Die piezokeramische Zusammensetzung verdichtet bei relativ niedrigen Sintertemperaturen. Somit ist es möglich, elementare Metalle als Elektrodenmaterial einzusetzen, die relativ niedrige Schmelztemperaturen aufweisen. Gemäß einer besonderen Ausgestaltung wird daher ein Piezoelement verwendet, bei dem das Elektrodenmaterial und/oder das weitere Elektrodenmaterial mindestens ein aus der Gruppe Silber, Kupfer und Palladium ausgewähltes elementares Metall aufweisen. Der piezokeramische Werkstoff bzw. das Piezoelement wird insbesondere durch ein gemeinsames Sintern der piezokeramischen Zusammensetzung und der Elektrodenmaterials hergestellt (Cofiring). Das Elektrodenmaterial kann dabei aus den reinen Metallen bestehen, beispielsweise nur aus Silber (Schmelztemperatur ca. 960°C) oder nur aus Kupfer (Schmelztemperatur ca. 1080°C). Eine Legierung der genannten Metalle ist ebenfalls möglich, beispielsweise eine Legierung aus Silber und Palladium. Insbesondere weisen das Elektrodenmaterial und/oder das weitere Elektrodenmaterial einen Palladiumanteil auf, der aus dem Bereich von einschließlich 0 Gew.-% bis einschließlich 30 Gew.-% ausgewählt wird. Vorzugsweise beträgt der Palladiumanteil maximal 20 Gew.-%. Dabei bedeuten 0 Gew.-%, dass nahezu kein Palladium vorhanden ist. Geringe Palladiumanteile von bis zu 0,5 Gew.-% sind allerdings möglich. Durch die Verringerung des Palladiumanteils erniedrigt sich die Schmelztemperatur der Silber-Palladium-Legierung. Beispielsweise beträgt die Schmelztemperatur der Legierung bei einem Palladiumanteil von 20 Gew.-% etwa 1100°C. Vorzugsweise beträgt der Palladiumanteil maximal 5 Gew.-% (Schmelztemperatur etwa 1000°C). Durch den geringen Palladiumanteil werden die Kosten für die Herstellung derartiger Bauteile ebenfalls deutlich reduziert. Gleichzeitig ist aber durch das Verdichten bei niedrigen Temperaturen ein piezokeramischer Werkstoff mit guten piezoelektrischen Eigenschaften zugänglich.The Piezoceramic composition compacts at relatively low Sintering temperatures. Thus, it is possible elemental metals to use as electrode material, the relatively low melting temperatures exhibit. According to a particular embodiment Therefore, a piezoelectric element is used, in which the electrode material and / or the further electrode material at least one of the group silver, Having copper and palladium selected elemental metal. The piezoceramic material or the piezoelectric element is in particular by a common sintering of the piezoceramic composition and the electrode material produced (cofiring). The electrode material can consist of the pure metals, for example only made of silver (melting temperature about 960 ° C) or only of copper (Melting temperature about 1080 ° C). An alloy of said Metals are also possible, for example an alloy of silver and palladium. In particular, the electrode material and / or the further electrode material has a palladium content, from the range of from 0 wt% up to and including 30 wt .-% is selected. Preferably the palladium content is at most 20% by weight. Where 0% by weight means that almost no palladium is present. Low palladium content of up to 0.5 wt .-% are possible. By the Reduction of the palladium content lowers the melting temperature the silver-palladium alloy. For example, is the melting temperature of the alloy at a palladium content of 20 wt .-% about 1100 ° C. Preferably, the Palladium content maximum 5 wt .-% (melting temperature about 1000 ° C). Due to the low palladium content, the costs for the production of such components also significantly reduced. At the same time, however, is by compacting at low temperatures a piezoceramic material with good piezoelectric properties accessible.

Das Sintern zum piezokeramischen Werkstoff kann sowohl in reduzierender oder oxidierender Sinteratmosphäre durchgeführt werden. In einer reduzierenden Sinteratmosphäre ist nahezu kein Sauerstoff vorhanden. Ein Sauerstoffpartialdruck beträgt weniger als 1·10–2 mbar und vorzugsweise weniger als 1·10–3 mbar. Durch Sintern in einer reduzierenden Sinteratmosphäre ist kostengünstiges Kupfer als Elektrodenmaterial möglich.The sintering to the piezoceramic material can be carried out both in a reducing or oxidizing sintering atmosphere. In a reducing sintering atmosphere, almost no oxygen is present. An oxygen partial pressure is less than 1 x 10 -2 mbar, and preferably less than 1 x 10 -3 mbar. By sintering in a reducing sintering atmosphere inexpensive copper is possible as an electrode material.

Prinzipiell kann mit Hilfe der piezokeramischen Zusammensetzung jedes beliebige piezokeramische Bauteil hergestellt werden. Das piezokeramische Bauteil weist vornehmlich mindestens ein oben beschriebenes Piezoelement auf. Vorzugsweise wird das piezokeramische Bauteil mit dem Piezoelement aus der Gruppe piezokeramischer Biegewandler, piezokeramischer Vielschichtaktor, piezokeramischer Transformator, piezokeramischer Motor und piezokeramischer Ultraschallwandler ausgewählt. Das Piezoelement ist beispielsweise Bestandteil eines piezoelektrischen Biegewandlers. Durch Übereinanderstapeln einer Vielzahl von einseitig oder beidseitig mit Elektrodenmaterial bedruckten Grünfolien, nachfolgendes Entbindern und Sintern entsteht ein monolithischer Stapel aus Piezoelementen. Bei geeigneter Dimensionierung und Form resultiert ein monolithischer piezokeramischer Vielschichtaktor. Dieser piezokeramische Vielschichtaktor wird vorzugsweise zur Ansteuerung eines Kraftstoffeinspritzventils einer Brennkraftmaschine eingesetzt. Durch die stapelförmige Anordnung der Piezoelemente ist auch, bei geeigneter Dimensionierung und Form, ein piezokeramischer Ultraschallwandler zugänglich. Der Ultraschallwandler wird beispielsweise in der Medizintechnik oder zur Materialprüfung eingesetzt.in principle can with the help of piezoceramic composition any piezoceramic component are produced. The piezoceramic Component has primarily at least one piezoelectric element described above on. Preferably, the piezoceramic component with the piezoelectric element is made the group piezoceramic bending transducer, piezoceramic multilayer actuator, piezoceramic transformer, piezoceramic motor and piezoceramic Ultrasonic transducer selected. The piezo element is for example Component of a piezoelectric bending transducer. By stacking a variety of single-sided or double-sided with electrode material printed green sheets, subsequent binder removal and sintering creates a monolithic stack of piezo elements. With suitable dimensioning and form results in a monolithic piezoceramic multilayer actuator. This piezoceramic multilayer actuator is preferably used for driving a fuel injection valve of an internal combustion engine used. By the stack-shaped arrangement of the piezo elements is also, with suitable dimensioning and shape, a piezoceramic Ultrasonic transducer accessible. The ultrasonic transducer is For example, in medical technology or for material testing used.

Zusammenfassend ergeben sich mit der Erfindung folgende Vorteile:

  • – Durch die komplexe B-Platzdotierung mit Scandium und Wolfram verdichtet die piezokeramische Zusammensetzung bereits unter 1000°C.
  • – Aufgrund des bei tieferen Temperaturen stattfindenden Verdichtens sind relativ niedrige Sintertemperaturen zugänglich.
  • – Die niedrigen Sintertemperaturen eröffnen die Möglichkeit, bei niedrigerer Temperatur schmelzende Metalle oder Legierungen als Elektrodenmaterial im Herstellungsprozess piezokeramischer Bauteile zu verwenden. Im Vergleich zum Stand der Technik werden Kosten gespart.
  • – Durch die A-Platzdotierung mit den Seltenerdmetallen werden gute piezoelektrische Eigenschaften des resultierenden piezokeramischen Werkstoffs erzielt.
  • – Durch Erdalkalimetall-Ionen und/oder Alkalimetall-Ionen, die vornehmlich die A-Plätze des piezokeramischen Werkstoffs besetzen, können die guten piezoelektrischen Eigenschaften zusätzlich verbessert werden.
In summary, the invention provides the following advantages:
  • - Due to the complex B-site doping with scandium and tungsten, the piezoceramic composition already densifies below 1000 ° C.
  • - Due to the taking place at lower temperatures compaction relatively low sintering temperatures are accessible.
  • The low sintering temperatures open up the possibility of using metals or alloys melting at lower temperatures as electrode material in the production process of piezoceramic components. Costs are saved compared to the prior art.
  • - The A-doping with the rare earth metals good piezoelectric properties of the resulting piezoceramic material can be achieved.
  • By alkaline earth metal ions and / or alkali metal ions, which occupy primarily the A-sites of the piezoceramic material, the good piezoelectric properties can be further improved.

Anhand mehrerer Beispiele und der dazugehörigen Figuren wird die Erfindung im Folgenden näher beschrieben. Die Figuren sind schematisch und stellen keine maßstabsgetreuen Abbildungen dar.On the basis of several examples and the associated figures, the invention is nä in the following described here. The figures are schematic and do not represent true to scale figures.

1 zeigt ein keramisches Piezoelement mit einem piezokeramischen Werkstoff in einem seitlichen Querschnitt. 1 shows a ceramic piezoelectric element with a piezoceramic material in a lateral cross-section.

2 zeigt ein piezokeramisches Bauteil mit einer Vielzahl von Piezoelementen in einem seitlichen Querschnitt. 2 shows a piezoceramic component with a plurality of piezo elements in a lateral cross-section.

3 zeigt das Schwindungsverhalten beim Sintern einer der piezokeramischen Zusammensetzungen. 3 shows the shrinkage behavior during sintering of one of the piezoceramic compositions.

Folgende Zusammensetzungen wurden basierend auf der Erfindung zusammengestellt:
I : Pb1,00Nd0,02[Zr0,515Ti0,485)0,95(Sc0,5W0,5)0,05]O3
II : Pb1,00Gd0,01[Zr0,525Ti0,475)0,98(Sc0,75W0,25)0,02]O3 The following compositions were compiled based on the invention:
I: Pb 1.00 Nd 0.02 [Zr 0.515 Ti 0.485] 0.95 (Sc 0.5 W 0.5 ) 0.05 ] O 3
II: Pb 1.00 Gd 0.01 [Zr 0.525 Ti 0.475 ] 0.98 (Sc 0.75 W 0.25 ) 0.02 ] O 3

Das Schwindungsverhalten der Zusammensetzungen I ist der 3 zu entnehmen. Aufgetragen ist eine dilatometrisch gemessene Längenänderung dl (in %) gegen die Temperatur T (in °C). Bei einer Temperatur von unter 1000°C findet ein merkliches Verdichten statt.The shrinkage behavior of the compositions I is the 3 refer to. Plotted is a dilatometrically measured change in length dl (in%) against the temperature T (in ° C). At a temperature of less than 1000 ° C a significant compression takes place.

Zum Herstellen der piezokeramischen Zusammensetzungen I und II werden entsprechende Anteile an pulverförmigem PbO, Nd2O3, Gd2O3, ZrO2, TiO2, Sc2O3 und WO3 homogen miteinander vermischt und kalziniert bzw. gesintert. PbO wird jeweils mit einem Überschuss von 3 mol% eingesetzt. Beim Sintern entweicht der überschüssige Anteil an Bleioxid.For the production of the piezoceramic compositions I and II, corresponding proportions of powdered PbO, Nd 2 O 3 , Gd 2 O 3 , ZrO 2 , TiO 2 , Sc 2 O 3 and WO 3 are homogeneously mixed with one another and calcined or sintered. PbO is used in each case with an excess of 3 mol%. During sintering, the excess amount of lead oxide escapes.

Durch das Sintern entsteht aus den piezokeramischen Zusammensetzungen jeweils ein piezokeramischer Werkstoff, dessen piezoelektrische Eigenschaften der Tabelle 1 zu entnehmen sind. Aufgelistet sind in der Tabelle 1 jeweils neben den d33-Werten (Großsignal-d33 bei einem elektrischen Feld von 2 kV/mm und Großsignal-d33 bei einem elektrischen Feld von 1 kV/mm), die mittlere Korngröße (mittlerer Durchmesser der Piezokeramik-Körner), der Kp-Wert (planarer Kopplungsfaktor), die relative Permittivität εr (nach der Polung des piezokeramischen Werkstoffs) und die Curie-Temperatur Tc. Die Sinterdauer betrug jeweils zwei Stunden. Gesintert wurde in oxidierender Sinteratmosphäre bei jeweils 1100°C. Tabelle 1: I II εr (nach der Polung) 1753 1471 Großsignal-d33 bei 2 kV/mm [pm/V] 728 723 Großsignal-d33 bei 1 kV/mm [pm/V] 734 720 Kp [%] 0,63 0,62 Korngröße [μm] > 2 >2 TCurie [°C] 298 342 By sintering, a piezoceramic material is produced from the piezoceramic compositions, the piezoelectric properties of which are shown in Table 1. Listed in Table 1 in each case in addition to the d 33 values (large signal d 33 at an electric field of 2 kV / mm and large signal d 33 at an electric field of 1 kV / mm), the average particle size (mean diameter of Piezoceramic grains), the Kp value (planar coupling factor), the relative permittivity ε r (after the polarity of the piezoceramic material) and the Curie temperature T c . The sintering time was two hours each. Sintering was carried out in an oxidizing sintering atmosphere at 1100 ° C. Table 1: I II ε r (after polarity) 1753 1471 Large signal d 33 at 2 kV / mm [pm / V] 728 723 Large signal d 33 at 1 kV / mm [pm / V] 734 720 Kp [%] 0.63 0.62 Grain size [μm] > 2 > 2 T Curie [° C] 298 342

Die piezokeramischen Zusammensetzungen werden zum Herstellen eines piezokeramischen Bauteils 1 verwendet. Das piezokeramische Bauteil 1 ist gemäß einer ersten Ausführungsform ein Piezoaktor 1 in monolithischer Vielschichtbauweise (2). Der Piezoaktor 1 besteht aus einer Vielzahl von übereinander zu einem Stapel angeordneten Piezoelementen 10. Jedes der Piezoelemente 10 weist eine Elektrodenschicht 11, eine weitere Elektrodenschicht 12 und eine zwischen den Elektrodenschichten 11 und 12 angeordnete Piezokeramikschicht 13 auf (1). Die im Stapel benachbarten Piezoelemente 10 weisen jeweils eine gemeinsame Elektrodenschicht auf. Die Elektrodenschichten 11 und 12 weisen ein Elektrodenmaterial aus einer Silber-Palladium-Legierung auf, bei der Palladium zu einem Anteil von 5 Gew.-% enthalten ist. In einer alternativen Ausführungsform bestehen die Elektrodenschichten aus (annähernd) reinem Silber. Gemäß einer weiteren Alternative ist das Elektrodenmaterial Kupfer.The piezoceramic compositions are used to produce a piezoceramic component 1 used. The piezoceramic component 1 is a piezoelectric actuator according to a first embodiment 1 in monolithic multilayer construction ( 2 ). The piezo actuator 1 consists of a plurality of piezo elements arranged one above the other to form a stack 10 , Each of the piezo elements 10 has an electrode layer 11 , another electrode layer 12 and one between the electrode layers 11 and 12 arranged piezoceramic layer 13 on ( 1 ). The piezo elements adjacent in the stack 10 each have a common electrode layer. The electrode layers 11 and 12 have an electrode material of a silver-palladium alloy, in which palladium is contained in a proportion of 5 wt .-%. In an alternative embodiment, the electrode layers consist of (approximately) pure silver. According to another alternative, the electrode material is copper.

Zum Herstellen des Piezoaktors 1 werden Grünkörper in Form von Grünfolien mit der piezokeramischen Zusammensetzung bereitgestellt. Dazu wird ein Pulver mit der jeweiligen piezokeramischen Zusammensetzung mit einem organischen Binder und weiteren organischen Additiven vermischt. Aus dem auf diese Weise erhaltenen Schlicker werden die keramischen Grünfolien gegossen. Die Grünfolien werden getrocknet, mit einer Paste mit dem Elektrodenmaterial bedruckt, übereinander gestapelt, laminiert, entbindert und zum Piezoaktor 1 unter oxidierender Sinteratmosphäre (Silber oder Silber-Palladium-Legierung als Elektrodenmaterial) oder reduzierender Sinteratmosphäre (Kupfer als Elektrodenmaterial) gesintert.For manufacturing the piezoelectric actuator 1 Green bodies are provided in the form of green sheets with the piezoceramic composition. For this purpose, a powder with the respective piezoceramic composition is mixed with an organic binder and further organic additives. From the slip obtained in this way, the ceramic green sheets are cast. The green sheets are dried, printed with a paste with the electrode material, stacked on top of one another, laminated, debinded and transferred to the piezoactuator 1 sintered under oxidizing sintering atmosphere (silver or silver-palladium alloy as electrode material) or reducing sintering atmosphere (copper as electrode material).

Der resultierende monolithische piezokeramische Vielschichtaktor wird zum Betätigen eines Kraftstoffeinspritzventils einer Brennkraftmaschine eines Kraftfahrzeugs eingesetzt.Of the resulting monolithic piezoceramic multilayer actuator is for actuating a fuel injection valve of an internal combustion engine Motor vehicle used.

Weitere, nicht dargestellte Ausführungsformen wie piezokeramischer Biegewandler, piezokeramischer Transformator oder piezokeramischer Ultraschallwandler sind mit Hilfe der piezokeramischen Zusammensetzungen ebenfalls zugänglich.Further, not shown embodiments such as piezoceramic Bending transducer, piezoceramic transformer or piezoceramic Ultrasonic transducers are using the piezoceramic compositions also accessible.

ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list The documents listed by the applicant have been automated generated and is solely for better information recorded by the reader. The list is not part of the German Patent or utility model application. The DPMA takes over no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • - EP 0894341 B1 [0003] - EP 0894341 B1 [0003]

Claims (18)

Piezokeramische Zusammensetzung mit einer nominalen Summenformel Pb1-aREbAEcALd[ZrxTiy(ScsW)z]O3, wobei – RE ein Seltenerdmetall mit einem Seltenerdmetallanteil b ist, – AE ein Erdalkalimetall mit einem Erdalkalimetallanteil c ist, AL ein Alkalimetall mit einem Alkalimetallanteil d ist, – Scandium mit einem Scandiumanteil s·z vorhanden ist, – Wolfram mit einem Wolframanteil w·z vorhanden ist, und folgende Zusammenhänge gelten: a < 1 0 ≤ b ≤ 0,4 0 ≤ c ≤ 0,5 0 ≤ d ≤ 0,5 s > 0 w > 0 0,1 ≤ s/w ≤ 5 x > 0 y > 0 z > 0 x + y + z = 1Piezoceramic composition having a nominal empirical formula Pb 1-a RE b AE c AL d [Zr x Ti y (Sc s W) z ] O 3 , wherein - RE is a rare earth metal having a rare earth metal content b, - AE is an alkaline earth metal having an alkaline earth metal content c Al is an alkali metal with an alkali metal content d, scandium with a scandium content s z, tungsten with a tungsten content w z, and the following relationships apply: a <1 0 ≦ b ≦ 0.4 0 ≦ c ≤ 0.5 0 ≤ d ≤ 0.5 s> 0 w> 0 0.1 ≤ s / w ≤ 5 x> 0 y> 0 z> 0 x + y + z = 1 Piezokeramische Zusammensetzung nach Anspruch 1, wobei gilt: 0,5 ≤ s/w ≤ 3Piezoceramic composition according to claim 1, where: 0.5 ≤ s / w ≤ 3 Piezokeramische Zusammensetzung nach Anspruch 1 oder 2, wobei gilt: s/w = 2.Piezoceramic composition according to claim 1 or 2, where: s / w = 2. Piezokeramische Zusammensetzung nach Anspruch 3, wobei gilt: s = 2/3.Piezoceramic composition according to claim 3, where: s = 2/3. Piezokeramische Zusammensetzung nach einem der Ansprüche 1 bis 4, wobei gilt: 0,005 ≤ c ≤ 0,1.Piezoceramic composition according to one of the claims 1 to 4, where: 0.005 ≦ c ≦ 0.1. Piezokeramische Zusammensetzung nach einem der Ansprüche 1 bis 5, wobei gilt: 0,005 ≤ b ≤ 0,15.Piezoceramic composition according to one of the claims 1 to 5, where: 0.005 ≦ b ≦ 0.15. Piezokeramische Zusammensetzung nach einem der Ansprüche 1 bis 6, wobei gilt: 0,001 ≤ z ≤ 0,5.Piezoceramic composition according to one of the claims 1 to 6, where: 0.001 ≦ z ≦ 0.5. Piezokeramische Zusammensetzung nach Anspruch 7, wobei gilt: 0,001 ≤ z ≤ 0,05.Piezoceramic composition according to claim 7, where: 0.001 ≤ z ≤ 0.05. Piezokeramische Zusammensetzung nach einem der Ansprüche 1 bis 8, wobei das Seltenerdmetall RE mindestens ein aus der Gruppe Europium, Gadolinium, Lanthan, Neodym, Praseodym, Promethium und Samarium ausgewähltes Metall ist.Piezoceramic composition according to one of the claims 1 to 8, wherein the rare earth element RE at least one of the group Europium, gadolinium, lanthanum, neodymium, praseodymium, promethium and Samarium is selected metal. Verfahren zum Herstellen eines piezokeramischen Bauteils (1) mit einem piezokeramischen Werkstoff unter Verwendung der piezokeramischen Zusammensetzung nach einem der Ansprüche 1 bis 9 mit folgenden Verfahrensschritten: a) Bereitstellen eines Grünkörpers mit der piezokeramischen Zusammensetzung und b) Wärmebehandeln des Grünkörpers, wobei aus der piezokeramischen Zusammensetzung der piezokeramische Werkstoff des Bauteils (1) entsteht.Method for producing a piezoceramic component ( 1 ) with a piezoceramic material using the piezoceramic composition according to one of claims 1 to 9 with the following method steps: a) providing a green body with the piezoceramic composition and b) heat treating the green body, wherein from the piezoceramic composition of the piezoceramic material of the component ( 1 ) arises. Verfahren nach Anspruch 10, wobei zum Bereitstellen des Grünkörpers ein Mischen pulverförmiger, oxidischer Metallverbindungen der für die Zusammensetzung benötigten Metalle durchgeführt wird.The method of claim 10, wherein providing of the green body mixing powdered, oxide metal compounds of the composition required metals is performed. Verfahren nach Anspruch 11, wobei mindestens ein Mischoxid mit mindestens zwei der Metalle als oxidische Metallverbindung verwendet wird.The method of claim 11, wherein at least one Mixed oxide with at least two of the metals as oxidic metal compound is used. Verfahren nach einem der Ansprüche 10 bis 12, wobei ein piezokeramisches Bauteil (1) mit mindestens einem Piezoelement (10) hergestellt wird, das eine Elektrodenschicht (11) mit Elektrodenmaterial, mindestens eine weitere Elektrodenschicht (12) mit einem weiteren Elektrodenmaterial und mindestens eine zwischen den Elektrodenschichten (11, 12) angeordnete Piezokeramikschicht (13) mit dem piezokeramischen Werkstoff aufweist.Method according to one of claims 10 to 12, wherein a piezoceramic component ( 1 ) with at least one piezo element ( 10 ), which has an electrode layer ( 11 ) with electrode material, at least one further electrode layer ( 12 ) with a further electrode material and at least one between the electrode layers ( 11 . 12 ) arranged piezoceramic layer ( 13 Having) with the piezoceramic material. Verfahren nach einem der Ansprüche 14, wobei ein Piezoelement (10) verwendet wird, bei dem das Elektrodenmaterial und/oder das weitere Elektrodenmaterial mindestens ein aus der Gruppe Silber, Kupfer und Palladium ausgewähltes elementares Metall aufweisen.Method according to one of claims 14, wherein a piezoelement ( 10 ), in which the electrode material and / or the further electrode material have at least one selected from the group consisting of silver, copper and palladium elemental metal. Verfahren nach Anspruch 15, wobei ein Piezoelement (10) verwendet wird, bei dem das Elektrodenmaterial und/oder das weitere Elektrodenmaterial einen Palladium-Anteil aufweisen, der aus dem Bereich von einschließlich 0 Gew.-% bis einschließlich 30 Gew.-% und insbesondere aus dem Bereich von einschließlich 0 Gew.-% bis einschließlich 20 Gew.-% ausgewählt wird.Method according to claim 15, wherein a piezoelement ( 10 ), in which the electrode material and / or the further electrode material have a palladium content which ranges from 0% by weight to 30% by weight and in particular from the range of 0% by weight. is selected up to and including 20 wt .-%. Verfahren nach einem der Ansprüche 16, wobei ein Palladium-Anteil von maximal 5 Gew.-% verwendet wird.Method according to one of Claims 16, wherein a palladium content of at most 5 wt .-% is used. Verfahren nach einem der Ansprüche 11 bis 17, wobei das piezokeramische Bauteil (1) mit dem Piezoelement (10) aus der Gruppe piezokeramischer Biegewandler, piezokeramischer Vielschichtaktor, piezokeramischer Transformator, piezokeramischer Motor und piezokeramischer Ultraschallwandler ausgewählt wird.Method according to one of claims 11 to 17, wherein the piezoceramic component ( 1 ) with the piezo element ( 10 ) is selected from the group piezoceramic bending transducer, piezoceramic multilayer actuator, piezoceramic transformer, piezoceramic motor and piezoceramic ultrasonic transducer. Verwendung eines nach dem Verfahren nach Anspruch 18 hergestellten piezokeramischen Vielschichtaktors zur Ansteuerung eines Kraftstoffeinspritzventils einer Brennkraftmaschine.Use of a method according to the claim 18 produced piezoceramic multilayer actuator for driving a fuel injection valve of an internal combustion engine.
DE102007029600A 2007-06-27 2007-06-27 Novel piezoceramic composition is prepared by utilizing piezoceramic material, and green body is supplied with piezoceramic composition Withdrawn DE102007029600A1 (en)