CN1914341A - 抗hic性优良的管线钢及用该钢材制造出的管线管 - Google Patents
抗hic性优良的管线钢及用该钢材制造出的管线管 Download PDFInfo
- Publication number
- CN1914341A CN1914341A CNA2004800413583A CN200480041358A CN1914341A CN 1914341 A CN1914341 A CN 1914341A CN A2004800413583 A CNA2004800413583 A CN A2004800413583A CN 200480041358 A CN200480041358 A CN 200480041358A CN 1914341 A CN1914341 A CN 1914341A
- Authority
- CN
- China
- Prior art keywords
- steel
- tin
- hic
- present
- line pipe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
钢 | 成份(其余为Fe和杂质单位为质量百分比 | 制造条件 | |||||||||||
C | Si | Mn | P | S | Al | Ca | Ti | N | O | Ca添加量(kg/ton) | 熔渣成份(CaO/Al2O3) | 冷却速度(℃/min) | |
X1 | 0.06 | 0.19 | 1.06 | 0.006 | 0.0019 | 0.041 | 0.006 | 0.015 | 0.0041 | 0.0036 | 0.24 | 0.9 | 200 |
X2 | 0.05 | 0.24 | 1.25 | 0.008 | 0.0034 | 0.015 | 0.016 | 0.016 | 0.0034 | 0.0042 | 0.35 | 1.4 | 240 |
X3 | 0.04 | 0.17 | 1.25 | 0.008 | 0.0026 | 0.021 | 0.003 | 0.016 | 0.0036 | 0.0043 | 0.21 | 1.3 | 250 |
X4 | 0.06 | 0.19 | 1.09 | 0.009 | 0.0031 | 0.048 | 0.008 | 0.015 | 0.0034 | 0.0041 | 0.22 | 1.3 | 50 |
成份(其余为Fe杂质单位为质量百分比) | 制造案件 | TiN(μm) | YS(MPa) | CAR(%) | |||||||||||||||||||
C | Si | Mn | P | S | Al | Ca | Ti | N | O | Cr | Mo | Nb | V | B | Cu | Ni | Ca添加量(kg/ton) | 熔渣成份(CaO/Al2O3) | 冷却速度(℃/min) | ||||
本发明钢 | |||||||||||||||||||||||
1 | 0.05 | 0.18 | 1.23 | 0.007 | 0.0031 | 0.022 | 0.002 | 0.015 | 0.0041 | 0.0040 | 0.11 | 1.2 | 450 | 25 | 453 | 2.0 | |||||||
2 | 0.04 | 0.20 | 1.12 | 0.008 | 0.0029 | 0.051 | 0.007 | 0.014 | 0.0043 | 0.0043 | 0.21 | 1.4 | 250 | 11 | 468 | 0.6 | |||||||
3 | 0.06 | 0.22 | 1.67 | 0.006 | 0.0034 | 0.026 | 0.005 | 0.015 | 0.0044 | 0.0041 | 0.22 | 1.3 | 250 | 12 | 470 | 0.6 | |||||||
4 | 0.08 | 0.19 | 1.78 | 0.005 | 0.0021 | 0.031 | 0.004 | 0.013 | 0.0034 | 0.0033 | 0.20 | 1.4 | 250 | 11 | 460 | 0.5 | |||||||
5 | 0.05 | 0.17 | 1.41 | 0.007 | 0.0021 | 0.015 | 0.004 | 0.016 | 0.0033 | 0.0034 | 0.53 | 0.13 | 1.3 | 50 | 10 | 556 | 0.5 | ||||||
6 | 0.04 | 0.25 | 1.45 | 0.002 | 0.0028 | 0.021 | 0.005 | 0.017 | 0.0028 | 0.0046 | 0.31 | 0.15 | 1.3 | 50 | 15 | 544 | 0.0 | ||||||
7 | 0.05 | 0.15 | 1.28 | 0.005 | 0.0011 | 0.014 | 0.005 | 0.013 | 0.0045 | 0.0031 | 0.023 | 0.16 | 1.3 | 150 | 15 | 523 | 0.8 | ||||||
8 | 0.04 | 0.24 | 1.33 | 0.007 | 0.0009 | 0.022 | 0.004 | 0.015 | 0.0049 | 0.0038 | 0.041 | 0.13 | 1.3 | 50 | 12 | 560 | 0.0 | ||||||
9 | 0.06 | 0.27 | 1.16 | 0.008 | 0.0024 | 0.022 | 0.005 | 0.015 | 0.0035 | 0.0035 | 0.0003 | 0.14 | 1.3 | 450 | 18 | 559 | 0.5 | ||||||
10 | 0.04 | 0.16 | 1.39 | 0.006 | 0.0031 | 0.023 | 0.005 | 0.015 | 0.0039 | 0.0043 | 0.61 | 0.28 | 0.0002 | 0.15 | 1.4 | 50 | 15 | 601 | 0.0 | ||||
11 | 0.05 | 0.23 | 1.34 | 0.005 | 0.0038 | 0.024 | 0.003 | 0.017 | 0.0042 | 0.0041 | 0.19 | 0.13 | 1.3 | 100 | 12 | 454 | 0.6 | ||||||
12 | 0.04 | 0.22 | 1.35 | 0.004 | 0.0022 | 0.025 | 0.004 | 0.015 | 0.0041 | 0.0046 | 0.3 | 0.14 | 1.3 | 100 | 18 | 447 | 0.7 | ||||||
13 | 0.06 | 0.18 | 1.28 | 0.006 | 0.0026 | 0.019 | 0.005 | 0.013 | 0.0035 | 0.0048 | 0.33 | 0.21 | 0.15 | 1.3 | 200 | 15 | 456 | 0.3 | |||||
14 | 0.06 | 0.19 | 1.44 | 0.008 | 0.0024 | 0.018 | 0.006 | 0.014 | 0.0036 | 0.0031 | 0.51 | 0.33 | 0.31 | 0.21 | 0.17 | 1.4 | 150 | 17 | 560 | 0.9 | |||
比较钢 | |||||||||||||||||||||||
A | 0.04 | 0.18 | 1.03 | 0.005 | 0.0018 | 0.004 | 0.005 | 0.013 | 0.0039 | 0.0034 | 0.14 | 1.3 | 1000* | 48 | 469 | 15.3 | |||||||
B | 0.06 | 0.23 | 1.24 | 0.007 | 0.0330 | 0.013 | 0.013 | 0.015 | 0.0036 | 0.0041 | 0.28 | 1.6* | 250 | 36 | 456 | 7.5 | |||||||
C | 0.03 | 0.25 | 1.34 | 0.007 | 0.0041 | 0.009 | 0.019 | 0.015 | 0.0041 | 0.0038 | 0.45* | 1.7* | 250 | 42 | 475 | 11.0 | |||||||
D | 0.05 | 0.20 | 1.32 | 0.005 | 0.0034 | 0.034 | 0.004 | 0.014 | 0.0034 | 0.0035 | 0.09* | 1.3 | 150 | 37 | 455 | 4.8 | |||||||
E | 0.05 | 0.22 | 1.28 | 0.006 | 0.0008 | 0.034 | 0.005 | 0.014 | 0.0031 | 0.0036 | 0.13 | 1.3 | 700* | 32 | 463 | 3.4 | |||||||
F | 0.05 | 0.24 | 1.24 | 0.007 | 0.0007 | 0.041 | 0.004 | 0.016 | 0.0038 | 0.0041 | 0.12 | 1.1* | 150 | 44 | 449 | 10.5 |
成份(其余为Fe杂质单位为质量百分比) | 制造案件 | TiN(μm) | YS(MPa) | CAR(%) | |||||||||||||||||||
C | Si | Mn | P | S | Al | Ca | Ti | N | O | Cr | Mo | Nb | V | B | Cu | Ni | Ca添加量(kg/ton) | 熔渣成份(CaO/Al2O3) | 冷却速度(℃/min) | ||||
本发明钢 | |||||||||||||||||||||||
15 | 0.05 | 0.17 | 1.01 | 0.008 | 0.0034 | 0.091 | 0.005 | 0.014 | 0.0061 | 0.0034 | 0.15 | 1.4 | 450 | 27 | 456 | 2.5 | |||||||
16 | 0.07 | 0.14 | 0.99 | 0.007 | 0.0031 | 0.075 | 0.005 | 0.015 | 0.0062 | 0.0041 | 0.20 | 1.5 | 150 | 18 | 450 | 0.2 | |||||||
17 | 0.08 | 0.22 | 0.98 | 0.009 | 0.0029 | 0.061 | 0.003 | 0.016 | 0.0059 | 0.0045 | 0.13 | 1.2 | 100 | 12 | 457 | 0.6 | |||||||
18 | 0.09 | 0.17 | 1.12 | 0.007 | 0.0031 | 0.042 | 0.005 | 0.015 | 0.0040 | 0.0038 | 0.14 | 1.5 | 250 | 10 | 457 | 0.0 | |||||||
19 | 0.07 | 0.16 | 1.43 | 0.007 | 0.0021 | 0.031 | 0.003 | 0.017 | 0.0059 | 0.0049 | 0.11 | 1.2 | 250 | 15 | 456 | 0.0 | |||||||
20 | 0.08 | 0.21 | 1.69 | 0.006 | 0.0035 | 0.026 | 0.004 | 0.014 | 0.0043 | 0.0034 | 0.13 | 1.3 | 250 | 11 | 461 | 0.2 | |||||||
21 | 0.07 | 0.22 | 1.79 | 0.005 | 0.0034 | 0.033 | 0.005 | 0.013 | 0.0051 | 0.0035 | 0.11 | 1.4 | 250 | 12 | 468 | 0.3 | |||||||
22 | 0.05 | 0.15 | 1.41 | 0.009 | 0.0019 | 0.026 | 0.002 | 0.020 | 0.0041 | 0.0043 | 0.41 | 0.12 | 1.2 | 100 | 12 | 543 | 0.0 | ||||||
23 | 0.06 | 0.18 | 1.44 | 0.007 | 0.0024 | 0.024 | 0.002 | 0.016 | 0.0038 | 0.0038 | 0.28 | 0.11 | 1.2 | 220 | 13 | 546 | 0.0 | ||||||
24 | 0.04 | 0.19 | 1.31 | 0.011 | 0.0023 | 0.023 | 0.003 | 0.011 | 0.0043 | 0.0041 | 0.025 | 0.12 | 1.2 | 220 | 17 | 522 | 0.3 | ||||||
25 | 0.07 | 0.16 | 1.32 | 0.007 | 0.0011 | 0.022 | 0.002 | 0.014 | 0.0044 | 0.0038 | 0.06 | 0.13 | 1.2 | 240 | 15 | 556 | 0.3 | ||||||
26 | 0.04 | 0.18 | 1.30 | 0.012 | 0.0022 | 0.034 | 0.003 | 0.015 | 0.0046 | 0.0045 | 0.0003 | 0.16 | 1.3 | 340 | 19 | 565 | 0.5 | ||||||
27 | 0.09 | 0.11 | 1.29 | 0.006 | 0.0023 | 0.026 | 0.002 | 0.013 | 0.0039 | 0.0044 | 0.48 | 0.31 | 0.021 | 0.038 | 0.0002 | 0.14 | 1.2 | 120 | 16 | 580 | 0.4 | ||
28 | 0.05 | 0.20 | 1.33 | 0.008 | 0.0015 | 0.039 | 0.002 | 0.015 | 0.0064 | 0.0046 | 0.31 | 0.13 | 1.2 | 120 | 12 | 455 | 0.2 | ||||||
29 | 0.08 | 0.19 | 1.42 | 0.005 | 0.0024 | 0.025 | 0.003 | 0.016 | 0.0051 | 0.0039 | 0.21 | 0.15 | 1.3 | 340 | 18 | 449 | 0.6 | ||||||
30 | 0.07 | 0.18 | 1.34 | 0.007 | 0.0029 | 0.024 | 0.003 | 0.017 | 0.0062 | 0.0034 | 0.28 | 0.22 | 0.14 | 1.2 | 150 | 14 | 455 | 0.4 | |||||
31 | 0.04 | 0.23 | 1.35 | 0.009 | 0.0018 | 0.023 | 0.003 | 0.018 | 0.0062 | 0.0036 | 0.51 | 0.34 | 0.021 | 0.041 | 0.31 | 0.21 | 0.15 | 1.3 | 200 | 13 | 586 | 0.3 | |
比较钢 | |||||||||||||||||||||||
G | 0.08 | 0.16 | 0.97 | 0.011 | 0.0029 | 0.055 | 0.011 | 0.015 | 0.0041 | 0.0042 | 0.27 | 1.6* | 250 | 38 | 450 | 4.8 | |||||||
H | 0.09 | 0.22 | 0.97 | 0.008 | 0.0036 | 0.044 | 0.012 | 0.014 | 0.0051 | 0.0043 | 0.45* | 1.4 | 200 | 45 | 456 | 8.0 | |||||||
I | 0.08 | 0.17 | 0.99 | 0.007 | 0.0011 | 0.061 | 0.002 | 0.013 | 0.0055 | 0.0041 | 0.12 | 1.0* | 250 | 43 | 455 | 5.1 | |||||||
J | 0.07 | 0.23 | 1.02 | 0.008 | 0.0014 | 0.043 | 0.002 | 0.015 | 0.0046 | 0.0039 | 0.05* | 1.3 | 150 | 38 | 456 | 3.5 |
Claims (4)