CN1333041C - M2(1-x)B5O9Cl∶A2x发光薄膜及其制备方法 - Google Patents
M2(1-x)B5O9Cl∶A2x发光薄膜及其制备方法 Download PDFInfo
- Publication number
- CN1333041C CN1333041C CNB2005101220372A CN200510122037A CN1333041C CN 1333041 C CN1333041 C CN 1333041C CN B2005101220372 A CNB2005101220372 A CN B2005101220372A CN 200510122037 A CN200510122037 A CN 200510122037A CN 1333041 C CN1333041 C CN 1333041C
- Authority
- CN
- China
- Prior art keywords
- film
- electron beam
- beam evaporation
- preparation
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种M2(1-x)B5O9Cl∶A2x发光薄膜及其制备方法,其化学表达式为:M2(1-x)B5O9Cl∶A2x,其中,M为Ca,Sr,Ba中的一种元素,A为Pr,Gd,Er,Tm,Ce,Lu中的一种元素,0.001<x≤0.4,其特征在于所说的原料选用纯度为99.99%的BaCl2,CaCl2,SrCl2,H3BO3,Pr2O3,Gd2O3,Er2O3,Tm2O3,Ce2O3,Lu2O3,溶剂为水和乙醇;本发明还提供了该发光薄膜制备方法。本发明制备的发光薄膜表面均匀、致密无开裂;薄膜颗粒大小均匀,而且薄膜的厚度可以控制;薄膜的发光性能优良;本发明的发光薄膜可用于制作场发射显示器的显示屏,该显示屏不但能够克服现有技术的缺点,而且还具有热稳定性高、放气率小、附着力强、表面平整度高等优点。
Description
【技术领域】
本发明涉及发光物理材料与显示技术,特别是一种M2(1-x)B5O9Cl:A2x发光薄膜及其制备方法。
【背景技术】
发光材料制成的显示屏在阴极射线管、电致发光以及场发射显示器件中起着十分重要的作用。目前将发光粉末制成的显示屏应用于场发射显示器存在着诸多障碍。由于颗粒之间的接触电阻,导致屏的电导率不高。此外,颗粒之间以及颗粒与衬底之间的附着力问题,也是难以克服的。同时,这种方法制备的屏表面粗糙,致密及均匀性差,容易造成光的反射且稳定性不好,分辨力也较低。因此,制备性能优良的发光薄膜成为研究的一个重要方向。
【发明内容】
本发明的目的是为了克服现有技术的不足,而提供一种发光性能优良的M2(1-x)B5O9Cl:A2x发光薄膜,以及该发光薄膜的其制备方法。
本发明制备为解决上述问题所采用的技术方案,是提供一种M2(1-x)B5O9Cl:A2x发光薄膜,其特征在于所说的原料选用纯度为99.99%的BaCl2,CaCl2,SrCl2,H3BO3,Pr2O3,Gd2O3,Er2O3,Tm2O3,Ce2O3,Lu2O3,溶剂为水和乙醇;其化学表达式为:
M2(1-x)B5O9Cl:A2x,
其中,M为Ca或Sr,Ba中的一种元素;A为Pr,Gd,Er,Tm,Ce或Lu中的一种元素;0.001<x≤0.4。
本发明还提供了一种M2(1-x)B5O9Cl:A2x发光薄膜制备方法,其特征在于所说的制备过程为:
1)将原料按照化学计量比混合,并加入溶剂充分研磨,采用固态反应,在600-1000℃高温下还原气氛中灼烧2小时,获得靶材料,靶材料经过压制成形,然后经600-800℃还原气氛中烧结2小时,制成直径为3mm的电子束蒸发靶;
2)采用电子束蒸发镀膜***,将衬底表面清洗后经掩模遮盖,装于旋转架上,放入电子束蒸发镀膜***的反应室中,将电子束蒸发靶装入坩埚内;反应室真空度至少抽到10-5Torr,然后加热衬底,使衬底温度为100-400℃,确定真空度、衬底温度,打开电子枪电源,进行蒸发。
3)将电子束蒸发制备的薄膜放入程序升温炉中,以100℃/h的速度加热到500-700℃,并且保留2-3小时。
本发明制备的发光薄膜表面均匀、致密无开裂;薄膜颗粒大小均匀,而且薄膜的厚度可以控制;薄膜的发光性能优良;本发明的发光薄膜可用于制作场发射显示器的显示屏,该显示屏不但能够克服现有技术的缺点,而且还具有热稳定性高、放气率小、附着力强、表面平整度高等优点。
【具体实施方式】
本发明中所使用的原料,选用纯度为99.99%的BaCl2,CaCl2,SrCl2,H3BO3,Pr2O3,Gd2O3,Er2O3,Tm2O3,Ce2O3,Lu2O3,溶剂为水和乙醇。
其化学表达式为:
M2(1-x)B5O9Cl:A2x,
其中,M为Ca,Sr,Ba中的一种元素;A为Pr,Gd,Er,Tm,Ce,Lu中的一种元素;0.001<x≤0.4。
在该薄膜M2(1-x)B5O9Cl:A2x的化学表达式中,x的数值也可以是以下范围:
0.001<x≤0.1。
比较好的发光薄膜可以用以下化学表达式表达为:
(1)Ba1.9B5O9Cl:Tm0.1;
(2)Sr1.94B5O9Cl:Ce0.06。
此外,在发光薄膜的具体实施例还可以按下列表中的数据确定:
M | A | X | |
1 | Ca | Tm | 0.05 |
2 | Sr | Pr | 0.08 |
3 | Ba | Er | 0.06 |
4 | Ba | Pr, | 0.05 |
5 | Ba | Ce | 0.03 |
6 | Ca | Ce | 0.04 |
7 | Ca | Pr | 0.08 |
8 | Ca | Er | 0.06 |
本发明发光薄膜的制备:
以Ba1.9B5O9Cl:Tm0.1为例,按照化学计量比,将BaCl2,H3BO3,Tm2O3,等进行混合,并加入溶剂充分研磨,采用固态反应,在850℃高温下还原气氛中灼烧2小时,获得靶材料,靶材料经过压制成形,然后经700℃还原气氛中烧结2小时,制成直径为3mm的电子束蒸发靶。采用电子束蒸发镀膜***制备,选择ITO玻璃作为衬底,将衬底表面清洗后经掩模遮盖,装于旋转架上,放入电子束蒸发镀膜***的反应室中,将电子束蒸发靶装入坩埚内。反应室真空度抽到10-5Torr,然后加热衬底,使衬底温度为200℃,确定真空度、基底温度保持不变,打开电子枪电源,进行蒸发。生长速度设定为5_/s,薄膜的厚度为200nm。将电子束蒸发制备的薄膜放入程序升温炉中,以100℃/h的速度加热到600℃,并且保留3小时。所得发光薄膜表面均匀、致密无开裂,薄膜颗粒大小均匀。
发光薄膜的衬底材料除采用ITO玻璃外,还可以采用硅、蓝宝石、或玻璃等。
在电子束蒸发制备薄膜时,加热衬底的优选温度为200-300℃。
Claims (6)
1一种M2(1-x)B5O9Cl:A2x发光薄膜,其特征在于其原料选用纯度为99.99%的BaCl2,CaCl2,SrCl2,H3BO3,Pr2O3,Gd2O3,Er2O3,Tm2O3,Ce2O3,Lu2O3,溶剂为水和乙醇;所制备发光薄膜的化学表达式为:
M2(1-x)B5O9Cl:A2x
其中:M为Ca,Sr或Ba中的一种元素;A为Pr,Gd,Er,Tm,Ce或Lu中的一种元素;0.001<x≤0.4。
2按照权利要求1所述的发光薄膜,其特征在于
0.001<x≤0.1。
3按照权利要求1或2所述的发光薄膜,其特征在于所述的发光薄膜的化学表达式为:
Ba1.9B5O9Cl:Tm0.1 。
4按照权利要求1或2所述的发光薄膜,其特征在于所所述的发光薄膜的化学表达式为:
Sr1.94B5O9Cl:Ce0.06。
5一种权利要求1的发光薄膜制备方法,其特征在于所说的制备过程为:
1)将原料按照化学计量比混合,并加入溶剂充分研磨,采用固态反应,在600-1000℃高温下还原气氛中灼烧2小时,获得靶材料,靶材料经过压制成形,然后经600-800℃还原气氛中烧结2小时,制成直径为3mm的电子束蒸发靶;
2)采用电子束蒸发镀膜***,将衬底表面清洗后经掩模遮盖,装于旋转架上,放入电子束蒸发镀膜***的反应室中,将电子束蒸发靶装入坩埚内;反应室真空度至少抽到10-5Torr,然后加热衬底,使衬底温度为100-400℃,确定真空度、衬底温度,打开电子枪电源,进行蒸发。
3)将电子束蒸发制备的薄膜放入程序升温炉中,以100℃/h的速度加热到500-700℃,并且保留2-3小时。
6按照权利要求5所述的制备方法,其特征在于所说的在电子束蒸发制备薄膜时,加热衬底的优选温度为200-300℃。