CN1332752C - 一种合成甲基异丙基酮和二乙酮的催化剂及制法和应用 - Google Patents
一种合成甲基异丙基酮和二乙酮的催化剂及制法和应用 Download PDFInfo
- Publication number
- CN1332752C CN1332752C CNB2004100580319A CN200410058031A CN1332752C CN 1332752 C CN1332752 C CN 1332752C CN B2004100580319 A CNB2004100580319 A CN B2004100580319A CN 200410058031 A CN200410058031 A CN 200410058031A CN 1332752 C CN1332752 C CN 1332752C
- Authority
- CN
- China
- Prior art keywords
- catalyst
- salt
- mixed oxide
- alkali metal
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供一种从甲乙酮和甲醇合成甲基异丙基酮和二乙酮的高活性新催化剂以及该催化剂的制备方法和该催化剂在制备酮反应时的应用。本发明催化剂由Zr、Mn、Zn和碱金属的混合氧化物担载少量的Pd组成。使用这种新的高活性催化剂,反应可以在低得多的温度下进行,不易结焦,产品的原料消耗低;生产效率高;过程对设备的要求低,运转费用省的优点。
Description
技术领域
本发明涉及一种合成甲基异丙基酮和二乙酮的催化剂。
本发明还涉及上述催化剂的制备方法。
本发明还涉及上述催化剂应用合成酮,特别是合成甲基异丙基酮和二乙酮的过程。
技术背景
甲基异丙基酮(MIPK)和二乙酮(DEK)是高级溶剂和重要的有机合成中间体,被广泛用于农业、医药、香料、染料、金属加工及食品等领域。甲基异丙基酮是生产重要的阳离子活性染料桃红FG,艳红5GN及光敏变色物质的原料。二乙酮是生产二甲乐茂的关键中间体。甲基异丙基酮和二乙基酮是合成维生素E的重要中间体和溶剂。
现有的甲基异丙基酮的工业生产方法:
(1)DE 2758113报道了由异丁酸与乙酸在水存在下催化热分解,生成甲基异丙基酮产品,同时生成丙酮和二异丙基酮等副产品,并放出等克分子的CO2和水,反应温度430~450℃。异丁酸的转化率约88.5mol%,乙酸的转化率约77.5mol%。按异丁酸计的MIPK的选择性为74.6mol%,按乙酸计的MIPK选择性为58.1mol%。反应式如下:
主反应:
CH3CH(CH3)COOH+CH3COOH→CH3CH(CH3)COCH3+CO2+H2O
副反应:
2 CH3CH(CH3)COOH→CH3CH(CH3)COCH(CH3)CH3+CO2+H2O
2 CH3COOH→CH3COCH3+CO2+H2O
这一过程的缺点是原料单耗高,反应温度高,能耗较大。
(2)EP 0224218发明专利描述,甲基乙基酮和甲醇在Ce、Cr、Fe、Mg或Mn的氧化物催化剂和水的存在下,于0.1~2.0MPa压力反应合成甲基异丙基酮和二乙酮的方法。最好的实施例:72克甲基乙基酮、32克甲醇和18克水的混合物在汽化器中于550℃持续加热并汽化1小时,然后通入500℃和装有350毫升MgO催化剂的反应器中。反应产物经冷凝收集和气相色谱分析。在甲基乙基酮转化率为52mol%时,生成的甲基异丙基酮为21.3mol%,二乙酮为19.2mol%。这一过程的优点是生成的两种酮产物都是重要的酮产品,不生成如CO2和水那样无用的副产物,产品的原料单耗较低,经济效益有所提高。但也存在反应温度过高,催化剂表面容易结焦和操作不够方便等缺点。因此,有必要研究开发新的更实用的催化剂和新的制备过程,使过程能在较低的反应温度和更有效地进行,从而改进这一过程的经济效益。
发明内容
本发明的目的是提供一种合成甲基异丙基酮和二乙酮的高活性高选择性的催化剂。
本发明的另一目的是提供上述催化剂的制备方法。
本发明催化剂的优点是活性高,生产效率高;反应温度低,催化剂不易结焦,产品的原料单耗低,催化剂寿命长;过程对设备的要求低,运行费用省。
为实现上述目的,本发明提供的催化剂由Zr、Mn、Zn和碱金属的混合氧化物负载少量的Pd组成;混合氧化物中ZrO2的重量含量为10~70%,最好是20~50%。MnO2的重量含量为2~40%,最好是10~30%。ZnO的重量含量为10~70%,最好是10~30%。碱金属可以是Li、Na、K和Cs,最好是Na和K。它们的重量含量为0.01~7.0%,最好是0.05~5%。Pd的载量为上述金属氧化物总重量的0.01~2.0%,最好为0.1~1%。
上述催化剂的制备步骤如下:
①Zr-Mn-Zn混合氧化物的制备:由Zr-Mn-Zn的前体,如硝酸盐、氯化物、氯氧化物按比例混合配制成混合的水溶液,用碱金属和铵的氢氧化物、碳酸盐或碳酸氢盐作沉淀剂,用共沉淀法制备。共沉淀终点的PH值控制在8~10。沉淀物经通常共沉淀法制备金属氧化物的步骤,即陈化、过滤、洗涤、干燥、焙烧后即得到Zr-Mn-Zn的混合氧化物。焙烧温度为300~500℃,最好为350~450℃。焙烧时间1~10小时,最好是2~6小时。
②含碱金属的混合金属氧化物的制备:用一定浓度的碱金属的水溶液浸渍由步骤①制得的混合金属氧化物。浸渍后经干燥、焙烧后得含碱金属的Zr-Mn-Zn混合氧化物。焙烧温度为300~500℃,最好是350~450℃。焙烧时间1~10小时,最好是1~6小时。
③在步骤②制得的混合金属氧化物上负载上少量的Pd。Pd的前体可以是PdCl2,Pd(NO3)2,Pd(CH3COO)或Pd的氨络合物。浸渍Pd盐后的催化剂前躯体经干燥或和焙烧后便得到备用的催化剂。干燥的温度和时间无严格的限制,一般在100~120℃干燥2~20小时,当选择再焙烧过程时,可在250~450℃焙烧1~6小时。
进行合成反应前,把备用的催化剂置于固定床反应器中,用H2或含H2的气体于250~450℃,最好350~450℃还原1~10小时,最好是1~6小时,然后切换成N2或Ar等惰性气体,调节到预定的反应温度和压力,注入甲乙酮、甲醇和水的混合液进行反应。
本发明提供的催化剂从甲乙酮和甲醇制备甲基异丙基酮的合适反应条件是:
①原料甲乙酮对甲醇的摩尔比是1∶(1~3),最好是1∶(1~1.5);甲乙酮对水的摩尔比是1∶(0.5~3),最好是1∶(1.0~2.0)。
②原料(甲乙酮、甲醇和水的混合物)的液相空速为0.5~3小时-1,最好是1.0~2.0小时-1。
③反应温度为300~450℃,更好的为330~380℃。
④反应压力为:常压~3.0MPa,更好的是:常压~2.0MPa。
具体实施方式
下面是本发明的一些具体的例子,但本发明并不限于下列的例子:
实施例1
50克Zr(NO3)4.5H2O,41.6克含Mn(NO3)2 50%的水溶液,17.3克Zn(NO3)26H2O用290毫升去离子水配制成混合的水溶液(Zr/Mn/Zn原子比=2∶2∶1),用0.3摩尔浓度的NaOH溶液并流法共沉淀,控制最终PH值等于9。在75~90℃搅拌下陈化4小时,将沉淀过滤,并用去离子水反复洗涤至几近中性。在110℃干燥16小时后,在450℃焙烧4小时制得Zr-Mn-Zn的混合氧化物。用合适浓度的NaOH溶液浸渍混合氧化物,使加入的Na量为混合氧化物重量的0.24wt%。在110℃干燥后,于400℃焙烧3小时,得Zr-Mn-Zn的混合氧化物。用合适浓度的Pd(NO3)2溶液浸渍混合氧化物,使Pd的负载量为混合氧化物的0.25wt%。在110℃干燥16小时后,在400℃焙烧2小时,制得备用的催化剂。
实施例2
用0.3摩尔浓度的KOH溶液代替NaOH溶液并流法共沉淀,控制最终PH值等于9和加入的钾量为混合氧化物的0.5wt%。其余同实施例1所述。
实施例3
用合适浓度的Pd(NO3)2溶液浸渍Zr-Mn-Zn-Na的混合氧化物,使Pd的负载量为混合氧化物的0.5wt%。其余同实施例1所述。
实施例4
50克Zr(NO3)4.5H2O,20.8克含Mn(NO3)2 50%的水溶液,17.3克Zn(NO3)26H2O用290毫升去离子水配制成混合的水溶液(Zr/Mn/Zn原子比=2∶1∶1),用0.3摩尔浓度的NaOH溶液并流法共沉淀,控制最终PH值等于9。其余同实施例1所述。
实施例5
50克Zr(NO3)4.5H2O,10.4克含Mn(NO3)2 50%的水溶液,17.3克Zn(NO3)26H2O用290毫升去离子水配制成混合的水溶液(Zr/Mn/Zn原子比=2∶0.5∶1),用0.3摩尔浓度的NaOH溶液并流法共沉淀,控制最终PH值等于9。其余同实施例1所述。
实施例6
50克Zr(NO3)4.5H2O,41.6克含Mn(NO3)2 50%的水溶液,4.3克Zn(NO3)26H2O用290毫升去离子水配制成混合的水溶液(Zr/Mn/Zn原子比=2∶2∶0.25),用0.3摩尔浓度的NaOH溶液并流法共沉淀,控制最终PH值等于9。其余同实施例1所述。
实施例7
50克Zr(NO3)4.5H2O,41.6克含Mn(NO3)2 50%的水溶液,8.7克Zn(NO3)26H2O用290毫升去离子水配制成混合的水溶液(Zr/Mn/Zn原子比=2∶2∶0.5),用0.3摩尔浓度的NaOH溶液并流法共沉淀,控制最终PH值等于9。其余同实施例1所述。
实施例8
50克Zr(NO3)4.5H2O,41.6克含Mn(NO3)2 50%的水溶液,17.3克Zn(NO3)26H2O用290毫升去离子水配制成混合的水溶液(Zr/Mn/Zn原子比=2∶2∶1),用0.3摩尔浓度的Na2CO3溶液并流法共沉淀,控制最终PH值等于9。其余同实施例1所述。
实施例9
38.5克ZrOCl2.xH2O,41.6克含Mn(NO3)2 50%的水溶液,17.3克Zn(NO3)26H2O用290毫升去离子水配制成混合的水溶液(Zr/Mn/Zn原子比=2∶2∶1),用0.3摩尔浓度的NaOH溶液并流法共沉淀,控制最终PH值等于9。在75~90℃搅拌下陈化4小时,将沉淀过滤,并用去离子水反复洗涤至几近中性。在110℃干燥16小时后,在450℃焙烧4小时制得Zr-Mn-Zn的混合氧化物。用合适浓度的NaOH溶液浸渍混合氧化物,使加入的Na量为混合氧化物重量的0.24wt%。在110℃干燥后,于400℃焙烧3小时,得Zr-Mn-Zn的混合氧化物。用合适浓度的Pd(NO3)2溶液浸渍混合氧化物,使Pd的负载量为混合氧化物的0.25wt%。在110℃干燥16小时后,在400℃焙烧2小时,制得备用的催化剂。
实施例10
用合适浓度的PdCl2溶液浸渍Zr-Mn-Zn-Na的混合氧化物,使Pd的负载量为混合氧化物的0.25wt%。其余同实施例1所述。
由实施例1至10制得的备用催化剂,在反应前置于反应器中用纯H2于420℃和常压下还原2小时,切换成N2,降至370℃,泵入甲乙酮/甲醇/水摩尔比等于1∶1∶1的原料,在常压和液体空速1小时-1下反应4小时。反应产物经冷凝收集,用气相色谱分析。结果见表1。
实施例11
用实施例3制得的催化剂,在反应前置于反应器中用纯H2在420℃和常压下还原2小时,切换成N2,降至370℃,通入甲乙酮/甲醇/水摩尔比等于1∶1∶1的原料,在压力1.0MPa和液体空速1小时-1下反应4小时。反应产物经冷凝收集,用气相色谱分析。结果见表1。结果表明,通过反应压力的升高能提高原料甲乙酮的转化率,同时表明反应产物的分布与所用的反应条件有关。
比较例1
50克Zr(NO3)4.5H2O,用290毫升去离子水配制成水溶液(Zr/Mn/Zn原子比=2∶0∶0),用0.3摩尔浓度的NaOH溶液并流法共沉淀,控制最终PH值等于9。经洗涤和在1 10℃干燥16小时后,在450℃焙烧4小时制得Zr-Mn-Zn的混合氧化物作为备用的催化剂。其余同实施例1所述。
比较例2
41.6克含Mn(NO3)250%的水溶液,用290毫升去离子水配制成水溶液(Zr/Mn/Zn原子比=0∶2∶0),用0.3摩尔浓度的NaOH溶液并流法共沉淀,控制最终PH值等于9。在110℃干燥16小时后,在450℃焙烧4小时制得Mn的氧化物作为备用催化剂。其余同实施例1所述。
比较例3
17.3克Zn(NO3)26H2O用290毫升去离子水配制成水溶液(Zr/Mn/Zn原子比=0∶0∶1),用0.3摩尔浓度的NaOH溶液并流法共沉淀,控制最终PH值等于9。经洗涤和在110℃干燥16小时后,在450℃焙烧4小时制得Zn的氧化物,用作备用的催化剂。其余同实施例1所述。
比较例4
50克Zr(NO3)4.5H2O,用290毫升去离子水配制成水溶液(Zr/Mn/Zn原子比=2∶0∶0),用0.3摩尔浓度的NaOH溶液并流法共沉淀,控制最终PH值等于9。经洗涤和在110℃干燥16小时后,在450℃焙烧4小时制得Zr的氧化物。用合适浓度的Pd(NO3)2溶液浸渍Zr的氧化物,使Pd的负载量为氧化物的0.25wt%。在110℃干燥16小时后,在400℃焙烧2小时,制得备用的催化剂。其余同实施例1所述。
比较例5
41.6克含Mn(NO3)250%的水溶液,用290毫升去离子水配制成水溶液(Zr/Mn/Zn原子比=0∶2∶0),用0.3摩尔浓度的NaOH溶液并流法共沉淀,控制最终PH值等于9。经洗涤和在110℃干燥16小时后,在450℃焙烧4小时制得Mn的氧化物。用合适浓度的Pd(NO3)2溶液浸渍Mn的氧化物,使Pd的负载量为氧化物的0.25wt%。在110℃干燥16小时后,在400℃焙烧2小时,制得备用的催化剂。其余同实施例1所述。
比较例6
1 7.3克Zn(NO3)26H2O用290毫升去离子水配制成水溶液(Zr/Mn/Zn原子比=0∶0∶1),用0.3摩尔浓度的NaOH溶液并流法共沉淀,控制最终PH值等于9。经洗涤和在110℃干燥16小时后,在450℃焙烧4小时制得Zn的氧化物。用合适浓度的Pd(NO3)2溶液浸渍Zn的氧化物,使Pd的负载量为氧化物的0.25wt%。在110℃干燥16小时后,在400℃焙烧2小时,制得备用的催化剂。其余同实施例1所述。
比较例1至6所述的备用催化剂,在反应前置于反应器中用纯H2于420℃和常压下还原2小时,切换成N2,升至500℃,泵入甲乙酮/甲醇/水摩尔比等于1∶1∶1的原料,在常压和液体空速1小时-1下反应4小时。反应产物经冷凝收集,用气相色谱分析。结果见表1。
表1实施例催化剂的反应评价结果
实施例 | Zr/Mn/ZnMol比 | 加碱金属wt% | Pdwt% | MEK转化率 | 选择性mol% | |||
MIPK | DEK | EIPK | S-BuOH | |||||
1 | 2∶2∶1 | Na,0.24 | 0.25 | 38.1 | 42.6 | 39.6 | 15.0 | 2.8 |
2 | 2∶2∶1 | K,0.5 | 0.25 | 36.6 | 43.0 | 38.8 | 14.9 | 3.2 |
3 | 2∶2∶1 | Na,0.24 | 0.5 | 36.1 | 40.7 | 40.5 | 14.5 | 4.3 |
4 | 2∶1∶1 | Na,0.24 | 0.25 | 30.2 | 42.9 | 39.5 | 12.1 | 5.5 |
5 | 2∶0.5∶1 | Na,0.24 | 0.25 | 29.9 | 46.2 | 34.6 | 12.6 | 6.5 |
6 | 2∶2∶0.25 | Na,0.24 | 0.25 | 35.0 | 38.0 | 43.8 | 14.6 | 3.6 |
7 | 2∶2∶0.5 | Na,0.24 | 0.25 | 31.7 | 45.2 | 34.3 | 13.9 | 6.6 |
8 | 2∶2∶1 | Na,1.0 | 0.25 | 35.8 | 40.2 | 38.7 | 14.1 | 5.8 |
9 | 2∶2∶1 | Na,0.24 | 0.25 | 37.8 | 42.1 | 38.4 | 14.8 | 2.9 |
10 | 2∶2∶1 | Na,0.24 | 0.25 | 37.4 | 41.6 | 39.5 | 14.2 | 4.3 |
11* | 2∶2∶1 | K,1.0 | 0.5 | 44.4 | 41.7 | 35.7 | 14.9 | 7.6 |
比较例 | ||||||||
1 | 2∶0∶0 | - | - | 30.3 | 12.2 | 43.1 | 11.2 | 33.4 |
2 | 0∶2∶0 | - | - | 14.1 | 28.7 | 47.1 | 17.9 | 6.9 |
3 | 0∶0∶0 | - | - | 14.5 | 32.0 | 51.7 | 8.4 | 7.9 |
4 | 2∶0∶0 | - | 0.25 | 27.2 | 25.5 | 60.9 | 10.7 | 2.85 |
5 | 0∶2∶0 | - | 0.25 | 14.2 | 31.7 | 36.7 | 23.1 | 8.4 |
6 | 0∶0∶2 | - | 0.25 | 15.3 | 34.2 | 49.5 | 10.1 | 6.3 |
注:实施例1至8的反应条件:催化剂装量2克,原料组成:甲乙酮/甲醇/水(摩尔比)=1∶1∶1,液相空速:1h-1,温度:370℃,压力:常压。
*实施例9的反应条件:压力:1.0MPa,其余同实施例1-8
比较例1至6的反应条件:温度500℃,其余同实施例1-8。
MIPK:甲基异丙基酮,DEK:二乙酮,EIPK:乙基异丙基酮。
从表1实施例的反应结果可以看到,随催化剂及反应条件的不同,目的产物甲基异丙基酮和二乙酮的选择性可达79~83摩尔%,伴随有12~15摩尔%的乙基异丙基酮和2~7摩尔%的仲丁醇生成。乙基异丙基酮可回收作为溶剂出售,少量的仲丁醇可随未反应的甲乙酮循环反应利用,原料具有较高的利用率。反应产物的分布与所用的反应条件有关,可通过改变反应条件调整目的产物的构成。使用本发明的催化剂时,反应温度明显地比现有的过程低,这既便利操作,又可降低过程对设备条件的要求和能耗。因此,具有较好的应用前景。
Claims (8)
1.一种合成甲基异丙基酮和二乙酮的催化剂,由Zr、Mn、Zn和碱金属的混合氧化物担载Pd组成;混合氧化物中ZrO2的重量含量为10~70%,MnO2的重量含量为2~40%,ZnO的重量含量为10~70%,碱金属的重量含量为0.05~8.0%,Pd的载量为上述金属氧化物总重量的0.01~2.0%;
所述碱金属为Li、Na、K或Cs。
2.权利要求1的催化剂,其特征在于,所述碱金属是Na或K。
3.一种制备权利要求1所述催化剂的方法,主要步骤为:
a)Zr-Mn-Zn混合氧化物的制备:配制Zr、Mn和Zn可溶性盐的混合水溶液,用碱性化合物水溶液为沉淀剂共沉淀,控制终点pH值大于7,在搅拌下经过陈化、过滤,沉淀物用去离子水洗涤至中性,在干燥后于300~500℃焙烧1~10小时,得到Zr-Mn-Zn混合氧化物;
b)含碱金属的Zr-Mn-Zn混合氧化物的制备:用碱金属氢氧化物或盐的水溶液浸渍步骤a得到的Zr-Mn-Zn混合氧化物,于80~120℃干燥后在300~500℃焙烧1~10小时,得到含碱金属的Zr-Mn-Zn混合氧化物;
c)在含碱金属的Zr-Mn-Zn混合氧化物上负载金属Pd:用Pd盐溶液浸渍含碱金属的Zr-Mn-Zn混合氧化物,在80~120℃干燥4~20小时和300~500℃焙烧1~10小时,得到备用的催化剂;
所述沉淀剂为碱金属或铵的氢氧化物、碳酸盐或碳酸氢盐。
所述碱金属氢氧化物或盐为碱金属的氢氧化物、碳酸盐、碳酸氢盐、甲酸盐或醋酸盐。
4.权利要求3的制备方法,其特征在于,其中Zr盐是Zr(NO3)4、ZrO(NO3)2或ZrOCl2可溶性锆盐;Mn盐是Mn(NO3)2或MnCl2可溶性锰盐;Zn盐是Zn(NO3)2可溶性锌盐;Pd盐是Pd(NO3)2、PdCl2或Pd(CH3COO)2可溶性钯盐。
5.权利要求4的制备方法,其特征在于,Zr的盐是Zr(NO3)4或ZrO(NO3)2;Mn的盐是Mn(NO3)2;Zn的盐是Zn(NO3)2。
6.权利要求3的制备方法,其特征在于,得到的催化剂用打片、挤条或滚球方法制成需要的粒度和形状,该形状为片状、条状、球状或圆柱状。
7.权利要求3的制备方法,其特征在于,得到的催化剂使用前置于反应器中,用氢气或含氢的气体于300~500℃原位还原1~10小时,然后切换成惰性气体,调节到所需的温度和压力,泵入原料进行反应。
8.权利要求1所述催化剂的应用,其特征在于,应用在从甲乙酮、甲醇和水的混合液合成甲基异丙基酮和二乙酮的合成过程中,其反应条件是:甲乙酮/甲醇的摩尔比是1.0∶1.0~3.0,甲乙酮/水的摩尔比是1.0∶2.0至2.0∶1.0,原料甲基乙基酮-甲醇-水混合物的液相空速为0.5~3.0h-1,反应温度300~400℃,反应压力为常压至3.0MPa。