CN1323180C - 齿科医用钛合金 - Google Patents

齿科医用钛合金 Download PDF

Info

Publication number
CN1323180C
CN1323180C CNB2004100205008A CN200410020500A CN1323180C CN 1323180 C CN1323180 C CN 1323180C CN B2004100205008 A CNB2004100205008 A CN B2004100205008A CN 200410020500 A CN200410020500 A CN 200410020500A CN 1323180 C CN1323180 C CN 1323180C
Authority
CN
China
Prior art keywords
alloy
titanium
present
palladium
zirconium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2004100205008A
Other languages
English (en)
Other versions
CN1570167A (zh
Inventor
蒋志
兰羽
李海涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dalian Sansheng Science & Technology Development Co., Ltd.
Original Assignee
Dalian Sunny Titanium Industry Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dalian Sunny Titanium Industry Co ltd filed Critical Dalian Sunny Titanium Industry Co ltd
Priority to CNB2004100205008A priority Critical patent/CN1323180C/zh
Publication of CN1570167A publication Critical patent/CN1570167A/zh
Application granted granted Critical
Publication of CN1323180C publication Critical patent/CN1323180C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了一种合金，特别是一种齿科用生物医用钛合金，主要用于临床口腔修复、种植、正畸等。其特征在于，它是由钛(Ti)、锆(Zr)、钯(Pd)组成的，各组分所占的重量百分比如下：锆(Zr)：(5～25)%，钯(Pd)：(0.1～0.2)%，钛(Ti)：余量。具有如下优点：1.选择与人体完全相容的Zr、Pd做为合金元素，具有良好的生物相容性。2.弹性模量低(80～90GPa)，比Ti6Al4V低10～20%。3.由于含有阴性活性组元Pd，具有优异的耐腐蚀性能，在生理盐水溶液中，腐蚀速率小于0.0001mm/a。4.更好的工艺成型性，热处理状态的δ：18～25%，φ：45～55%，比Ti6Al4V合金高出50%以上，热加工温度低150～200℃。

Description

齿科医用钛合金
技术领域
本发明涉及一种合金材料，特别是一种齿科用生物医用钛合金，主要用于临床口腔修复、种植、正畸等。
技术背景
随着社会经济的发展，国民生活水平的提高以及社会人口的老龄化，市场对齿科材料需求增长势头明显。临床调查显示钛做为齿科正畸、修复、种植材料的需求以20～30％的速度增长，成为齿科金属材料中一类最有发展和应用前景的新材料，但由于钛工业仅有50多年的发展历史，能为临床提供的齿科用钛合金品种太少，目前使用的主要是商业纯钛和Ti6Al4V合金。纯钛的强度尚显不足，Ti6Al4V合金强度偏高，并存在钒的毒性、工艺性能差、生物相容性不理想等问题。因此研发生物学、工艺性能、综合力学性能更好的齿科医用钛合金已成为世界各国材料科学家追逐的目标。
发明内容
本发明的目的是提供一种生物相容性好，耐蚀性优异，具有600～900Mpa的强度并兼有良好的综合力学性能和工艺成型性能的齿科医用钛合金，以克服现有技术的不足，为临床上提供一种新型换代的齿科材料。
本发明的技术解决方案是：一种齿科医用钛合金，其特征在于，它是由钛(Ti)、锆(Zr)、钯(Pd)组成的，各组分所占的重量百分比如下：锆(Zr)：(5～25)％，钯(Pd)：(0.1～0.2)％，钛(Ti)：余量。
所述的各组分所占的重量百分比可为：锆(Zr)：(13～17)％，钯(Pd)：(0.14～0.16)％，钛(Ti)：余量。
本发明与现有技术相比具有如下优点：
1、选择与人体完全相容的Zr、Pd做为合金元素，具有良好的生物相容性。
2、弹性模量低(80～90Gpa)，比Ti6Al4V低10～20％。
3、由于含有阴性活性组元Pd，具有优异的耐腐蚀性能，在生理盐水溶液中，腐蚀速率小于0.0001mm/a。
4、更好的工艺成型性，热处理状态的δ：18～25％，：45～55％，比Ti6Al4V合金高出50％以上，热加工温度低150～200℃。
5、品种齐全，可以生产板、棒、丝、线、管、锻件、铸件等各种冶金产品。
具体实施方式：
实施例1：
以海绵钛、海绵锆、钯粉为原料配制合金料，各组分的设计质量分别为：钛(Ti)84.8千克，锆(Zr)15千克，钯(Pd)0.15千克。压制电极后进行二次真空电弧自耗熔炼，铸锭900～1050℃开坯，800～900℃加工成合金棒，总变动量控制在65～95％之间。上述加工工艺按现有技术的方法进行即可。
实施例2：
以海绵钛、海绵锆、钯粉为原料配制合金料，各组分的设计质量分别为：钛(Ti)74.8千克，锆(Zr)25千克，钯(Pd)0.2千克。压制电极后进行二次真空电弧自耗熔炼，铸锭900～1050℃开坯，800～900℃加工成合金棒，总变动量控制在65～95％之间。上述加工工艺按现有技术的方法进行即可。
实施例3：
以海绵钛、海绵锆、钯粉为原料配制合金料，各组分的设计质量分别为：钛(Ti)94.85千克，锆(Zr)5千克，钯(Pd)0.15千克。压制电极后进行二次真空电弧自耗熔炼，铸锭900～1050℃开坯，800～900℃加工成合金棒，总变动量控制在65～95％之间。上述加工工艺按现有技术的方法进行即可。
实施例4：
以海绵钛、海绵锆、钯粉为原料配制合金料，各组分的设计质量分别为：钛(Ti)79.9千克，锆(Zr)20千克，钯(Pd)0.1千克。压制电极后进行二次真空电弧自耗熔炼，铸锭900～1050℃开坯，800～900℃加工成合金棒，总变动量控制在65～95％之间。上述加工工艺按现有技术的方法进行即可。
实施例5：
以海绵钛、海绵锆、钯粉为原料配制合金料，各组分的设计质量分别为：钛(Ti)94.9千克，锆(Zr)5千克，钯(Pd)0.1千克。压制电极后进行二次真空电弧自耗熔炼，铸锭900～1050℃开坯，800～900℃加工成合金棒，总变动量控制在65～95％之间。上述加工工艺按现有技术的方法进行即可。
实施例6：
以海绵钛、海绵锆、钯粉为原料配制合金料，各组分的设计质量分别为：钛(Ti)74.83千克，锆(Zr)25千克，钯(Pd)0.17千克。压制电极后进行二次真空电弧自耗熔炼，铸锭900～1050℃开坯，800～900℃加工成合金棒，总变动量控制在65～95％之间。上述加工工艺按现有技术的方法进行即可。
实施例7：
以海绵钛、海绵锆、钯粉为原料配制合金料，各组分的设计质量分别为：钛(Ti)89.8千克，锆(Zr)10千克，钯(Pd)0.2千克。压制电极后进行二次真空电弧自耗熔炼，铸锭900～1050℃开坯，800～900℃加工成合金棒，总变动量控制在65～95％之间。上述加工工艺按现有技术的方法进行即可。
因原料中含有少量杂质，钛的量不能完全确定，故权利要求书中钛的选择为余量。
本发明的合金材料可用作口腔正畸、种植、修复等材料，也可用作外科植入、眼镜架、弹簧、耐腐蚀材料。
本发明的合金材料力学性能见表1，耐蚀性能见表2，同现有医用钛合金性能比较见表3。
                  表1发明合金的力学性能(棒材)
发明合金编号 状态                         力学性能
  σb(Mpa)   σ0.2(Mpa)   δ(％)   (％)   E(Gpa)
  A   退火   600   550   25   55   95
  B   退火   650   600   23   52   93
  C   加工态   900   850   10   /   89
  退火   700   650   21   49   89
  D   退火   750   700   19   46   84
  E   退火   800   750   18   45   80
                     表2发明合金的耐蚀性能
                   37℃模拟人体体液(生理盐水)
            合金   发明合金TZP     Ti6Al4V   Ti
腐蚀特征参量   自腐蚀电位Ecorr(v) -0.190 -0.265 -0.285
  钝化电流密度IO(MA/cm2) 15 268 322
                             表3发明合金与现有同类合金性能比较
合金 状态 σb(Mpa)   σ0.2(Mpa)     δ(％)     (％)     akKJ/m2     E(Gpa) 来源
发明合金TZP 退火 600～800   500～700     18     45     538     80～95     实测
加工态 900 800 10 25 / 80～95 实测
Ti6Al4V 退火 895 825 10 25 392 106 GB13810-97
Ti(TA2) 退火 440 320 18 30 / 112 GB13810-97

Claims (2)

1、一种齿科医用钛合金，其特征在于，它是由钛(Ti)、锆(Zr)、钯(Pd)组成的，各组分配比如下：
名称      重量百分比
锆(Zr)    (5～25)％
钯(Pd)    (0.1～0.2)％
钛(Ti)    余量。
2、根据权利要求1所述的齿科医用钛合金，其特征在于：所述的各组分配比为：
名称      重量百分比
锆(Zr)    (13～17)％
钯(Pd)    (0.14～0.16)％
钛(Ti)    余量。
CNB2004100205008A 2004-04-29 2004-04-29 齿科医用钛合金 Expired - Fee Related CN1323180C (zh)