CN1176227C - 一种提高合金结构钢硬度的热处理方法 - Google Patents
一种提高合金结构钢硬度的热处理方法 Download PDFInfo
- Publication number
- CN1176227C CN1176227C CNB001107690A CN00110769A CN1176227C CN 1176227 C CN1176227 C CN 1176227C CN B001107690 A CNB001107690 A CN B001107690A CN 00110769 A CN00110769 A CN 00110769A CN 1176227 C CN1176227 C CN 1176227C
- Authority
- CN
- China
- Prior art keywords
- hardness
- steel
- steel parts
- steel part
- room temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种提高合金结构钢硬度的热处理方法，首先对钢件作好调质处理前的所有预处理，其特征在于：经预处理后的钢件在单向近静高压下进行调质热处理，压力范围为1.5～6.0GPa，即钢件在上述高压下加热至正常淬火温度，按正常时间保温，然后水淬至室温；钢件随后在上述高压下加热至正常回火温度，按正常时间保温，然后空冷至室温。本发明可以大幅度地提高合金结构钢件的硬度。
Description
本发明涉及金属材料的热处理制度，特别提供了一种提高合金结构钢硬度的热处理方法。
钢的热处理是利用钢在高温区发生的固态相变而改变钢的显微组织结构，从而达到改变钢的力学性能的高温处理过程。钢的调质处理是一种常用的热处理方法，它由淬火和回火两种处理方式组成，可以得到回火马氏体(低温回火)或回火索氏体组织(高温回火)，目的是使钢获得较好的强韧性水平。为使钢获得更好的性能水平，在常规热处理方法的基础上，人们还发展了许多特殊的热处理工艺。如化学热处理：工件在特定的化学环境中进行热处理，以形成特殊的表面处理层，达到耐腐蚀、耐磨损的目的。机械热处理：在热处理过程中对工件同时施加塑性变形(几十到几百NPa数量级的外力)，以达到改善钢的显微组织，进一步提高强度的目的。磁场热处理：在热处理过程中对工件同时施加一定强度的磁场，以达到改善钢的显微组织，进一步提高强度的目的。
本发明的目的在于提供一种提高合金结构钢硬度的热处理方法，其可以大幅度地提高合金结构钢件的硬度。
本发明提供了一种提高合金结构钢硬度的热处理方法，首先对钢件作好调质处理前的所有预处理，其特征在于：
经预处理后的钢件在单向近静高压下进行调质热处理，压力范围为1.5～6.0GPa，即钢件在上述高压下加热至正常淬火温度，按正常时间保温，然后水淬至室温；钢件随后在上述高压下加热至正常回火温度，按正常时间保温，然后空冷至室温。
经过上述超高压热处理的合金结构钢件的硬度可大幅度提高。下面通过实施例详述本发明。
附图1为压力与硬度的关系曲线
实施例
1、材料：30CrMo
2、热处理工艺：870℃(加压)/空冷
3、性能见附图及下表
超高压热处理中压力对硬度的影响
| 压力(Gpa) | 0 | 2.8 | 3.8 | 4.8 | 5.8 |
| Hv100 | 330 | 413 | 442 | 471 | 485 |
Claims (1)
1、一种提高合金结构钢硬度的热处理方法，首先对钢件作好调质处理前的所有预处理，其特征在于：
经预处理后的钢件在单向近静高压下进行调质热处理，压力范围为1.5～6.0GPa，即钢件在上述高压下加热至正常淬火温度，按正常时间保温，然后水淬至室温；钢件随后在上述高压下加热至正常回火温度，按正常时间保温，然后空冷至室温。