CN1171818C - 高级日用瓷无铅熔块釉 - Google Patents
高级日用瓷无铅熔块釉 Download PDFInfo
- Publication number
- CN1171818C CN1171818C CNB991204050A CN99120405A CN1171818C CN 1171818 C CN1171818 C CN 1171818C CN B991204050 A CNB991204050 A CN B991204050A CN 99120405 A CN99120405 A CN 99120405A CN 1171818 C CN1171818 C CN 1171818C
- Authority
- CN
- China
- Prior art keywords
- lead
- glaze
- porcelain
- frit
- grade
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供一种高级日用瓷无铅熔块釉,采用了烧成范围宽、光泽度好的锆、锂熔块釉,组成中加入了较大量的硼砂,不含有毒铅丹组分。本发明高级日用瓷无铅熔块釉,组成科学合理,易于实施,坯釉适应好,适应于多种高级日用瓷坯体,能够满足高级日用瓷的要求。釉面细腻光滑,光亮度高,弹性好,机械强度大,热震稳定性好,铅溶出量为0.00ppm,彻底免除了瓷器中铅釉对人体的毒害问题。
Description
本发明涉及一种用于高级日用瓷上的无铅熔块釉。
目前,高级日用瓷用熔块釉均为铅熔块釉,由铅丹和硼砂、硅酸盐矿物、其它碱金属氧化物制成低温熔块,由于铅成分的独特特性,使得铅熔块釉具有易熔性、光亮度高、弹性好、机械强度大、热震稳定性好等特点,因此,多少年来,铅熔块釉一直被广泛沿用着。
随着社会的不断发展,人民生活水平的不断提高,铅对人体的危害已引起了人们的高度重视。铅成分持续或经常地侵入人体,会引起多发性神经炎、中毒性脑病等。GB12651-90标准中规定,与食物接触的陶瓷制品的铅、镉溶出量需小于7ppm。因此,开发一种能够满足高级日用瓷要求的无铅熔块釉,是人们迫切需要解决的重大难题,是时代的要求。
本发明的目的在于提供一种高级日用瓷无铅熔块釉,该釉组成科学合理,易于实施,能够满足高级日用瓷的要求,彻底免除了瓷器中铅釉对人体的毒害问题。
本发明所述的高级日用瓷无铅熔块釉,含有SiO2、Al2O3,其其化学组成的重量百分比为:
SiO2 50~70
Al2O3 9~14
B2O3 1~7
CaO 1~9
MgO 0~4
SrO 0~6
ZnO 0~5
K2O 0~3
Na2O 0~3
Li2O 1~3
P2O5 0~6
ZrO2 1~4
上述组成的高级日用瓷无铅熔块釉,主要由熔块和粘土配制而成,其中,熔块的配料重量百分组成如下,釉中不足组分由相应的原料调整,如SiO2的量由石英调整等:
石英25.00~30.00 长石12.00~17.00 锆英石5.00~7.00 硼砂13.00~17.00 粘土12.00~16.00 碳酸钙0~8.00 白云石2.00~3.00硼酸0.5~1 碳酸锶7.00~8.00 碳酸锂2.00~4.00 骨灰3.00~5.00氧化锌4.00~6.00。
熔块的最佳配料重量百分组成为:
石英26.00 长石15.00 锆英石6.00 硼砂13.34 龙岩土13.00碳酸钙7.00 白云石3.00 硼酸0.66 碳酸锶7.00 碳酸锂2.00 骨灰3.00 氧化锌4.00。
所述的高级日用瓷无铅熔块釉,其釉料的重量配料比为:熔块80~90% 石英0~10% 粘土4~10% 瓷粉0~16% 白云石0~4% 碳酸锂0~2%硼酸钙0~6%。
本发明无铅熔块釉采用了烧成范围宽、光泽度好的锆、锂熔块釉,组成中加入了较大量的硼砂,为了改善釉面光泽和高温流动性,外加了少量的强助熔剂。
釉料制备需首先制作熔块,然后再制备釉料。原料的选择、使用与通常的相同,本发明所用原料的组成见表1。
第一步:将熔块原料按要求配比配料,按熔块常规制备工艺制备熔块,熔融温度1200~1300℃。熔块粉碎后备用。
第二步:将熔块粉料和其余生粉料混合,配合减水剂等制备釉料,可以直接在球磨机中粉碎制成备用釉浆,釉浆细度控制在万孔筛余为0.02~0.05%。
本发明釉料按常规的高级日用瓷生产工艺要求和规程使用即可,进行常规的施釉、烧成,得成品。该无铅釉的适宜烧成温度为1160~1200℃。
本发明高级日用瓷无铅熔块釉,组成科学合理,易于实施,坯釉适应好,适应于多种高级日用瓷坯体,如高石英瓷、高长石瓷、骨灰瓷、滑石瓷等等,能够满足高级日用瓷的要求。釉面细腻光滑,光亮度高,透明度好,弹性好,机械强度大,热震稳定性好,铅溶出量为0.00ppm,彻底免除了瓷器中铅釉对人体的毒害问题。
下面结合实施例对本发明作进一步的说明。
实施例用熔块的配料重量百分组成为:
石英26.00 长石15.00 锆英石6.00 硼砂13.34 龙岩土13.00碳酸钙7.00 白云石3.00 硼酸0.66 碳酸锶7.00 碳酸锂2.00 骨灰3.00 氧化锌4.00。
按常规的熔块熔制法用坩埚熔制成熔块,熔融温度1200~1300℃,将熔块粉碎后备用。
实施例1:
釉料重量配比:熔块80% 瓷粉16% 龙岩土4%
将釉料在球磨机中湿磨制成万孔筛余为0.02~0.05%的釉浆备用;
在高级骨灰瓷坯(重量百分组成为:SiO2 40.32 Al2O3 14.65 Fe2O3 0.21CaO 20.64 MgO 0.94 K2O 1.35 Na2O 0.06 P2O5 18.2 TiO2 0.05 余量为常规杂质)上施釉后,在1160~1200℃的温度下烧成,得高级日用骨灰细瓷。产品釉面细腻光亮,经检测,光泽度>115,白度>77,硬度>660Kgf/mm2,铅溶出量为0.00ppm。
实施例2:
釉料重量配比:熔块84% 石英4% 苏州土5% 白云石2% 碳酸锂1% 硼酸钙4%
将釉料在球磨机中湿磨制成万孔筛余为0.02~0.05%的釉浆备用;
在高长石瓷坯(重量百分组成为 SiO2 59.33 Al2O3 28.40 Fe2O3 0.35CaO 0.55 MgO 0.85 K2O 3.72 Na2O 5.52 余量为常规杂质)上施釉后,在1160~1200℃的温度下烧成,得高级日用长石质细瓷。产品釉面光润,经检测,光泽度>115,硬度>660Kgf/mm2,铅溶出量为0.00ppm。
实施例的化学组成见表2。
表1:原料化学组成表(重量百分组成)
表2、实施例的化学组成表(重量百分组成)
Claims (4)
1、一种高级日用瓷无铅熔块釉,含有SiO2、Al2O3,其特征在于其化学组成的重量百分比为:
SiO2 50~70
Al2O3 9~14
B2O3 1~7
CaO 1~9
MgO 0~4
SrO 0~6
ZnO 0~5
K2O 0~3
Na2O 0~3
Li2O 1~3
P2O5 0~6
ZrO2 1~4
2、根据权利要求1所述的高级日用瓷无铅熔块釉,其特征在于主要由熔块和粘土配制而成,其中,熔块的配料重量百分组成如下,釉中不足组分由相应的原料调整:
石英25.00~30.00 长石12.00~17.00 锆英石5.00~7.00 硼砂13.00~17.00 粘土12.00~16.00 碳酸钙0~8.00 白云石2.00~3.00 硼酸0.5~1碳酸锶7.00~8.00 碳酸锂2.00~4.00 骨灰3.00~5.00 氧化锌4.00~6.00。
3、根据权利要求2所述的高级日用瓷无铅熔块釉,其特征在于熔块的配料重量百分组成为:
石英26.00 长石15.00 锆英石6.00 硼砂13.34 龙岩土13.00 碳酸钙7.00 白云石3.00 硼酸0.66 碳酸锶7.00 碳酸锂2.00 骨灰3.00 氧化锌4.00。
4、根据权利要求2或3所述的高级日用瓷无铅熔块釉,其特征在于釉料的重量配料比为:熔块80~90% 石英0~10% 粘土4~10% 瓷粉0~16% 白云石0~4%碳酸锂0~2% 硼酸钙0~6%。