CN115477325B - 一种铋系负极材料的制备方法及其应用 - Google Patents
一种铋系负极材料的制备方法及其应用 Download PDFInfo
- Publication number
- CN115477325B CN115477325B CN202211121072.2A CN202211121072A CN115477325B CN 115477325 B CN115477325 B CN 115477325B CN 202211121072 A CN202211121072 A CN 202211121072A CN 115477325 B CN115477325 B CN 115477325B
- Authority
- CN
- China
- Prior art keywords
- bismuth
- negative electrode
- electrode material
- based negative
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种铋系负极材料的制备方法及其应用,属于无机材料制备和纳米能源技术领域。本发明提供的铋系负极材料的制备方法,包括在配置含铋酸盐的水溶液,并将其pH调整至11~13后,进行水热反应。上述制备方法制得的铋系负极材料能够有效提高所得铋系负极材料的电化学性能。本发明还提供了上述制备方法制得的铋系负极材料以及对应铋系负极材料的应用。
Description
技术领域
本发明涉及无机材料制备和纳米能源技术领域,尤其是涉及一种铋系负极材料的制备方法及其应用。
背景技术
为了满足新能源汽车和便携式电子产品不断增长的需求,开发具有高功率密度和能量密度的储能设备是目前研发的重点方向之一。
氧化铋(Bi2O3)是一种重要的功能材料,由于其独特的特性(半导体带隙、高折射率、高介电常数、高氧导电性、电阻率、光电导率和光致发光等)而被深入研究,并被广泛应用于光电转换材料、高温超导材料、电子陶瓷材料、防火材料、核工程玻璃制造和核反应堆燃料等技术领域。由于氧化铋具有优异的电化学稳定性、较好的氧化还原可逆性,所以,氧化铋还被认为是一种潜在的二次电池电极材料。但当用于二次电池电极材料时,无论是单质铋还是Bi2O3的比容量都相对较低。
因此,有必要开发一种铋氧化物材料的制备方法,以通过简单、温和的制备条件,获取比容量大的铋系电极材料。
发明内容
本发明旨在至少解决现有技术中存在的技术问题之一。为此,本发明提出一种铋系负极材料的制备方法,能够有效提高所得铋系负极材料的容量。
本发明还提供上述制备方法制得的铋系负极材料及其应用。
根据本发明的第一方面实施例,提出了一种铋系负极材料的制备方法,所述制备方法包括:
配置含铋酸盐的水溶液,并将其pH调整至11~13后,进行水热反应。
所述制备方法的机理如下:
铋酸盐在碱性条件下水热反应,过程中发生了结晶化,具体的,铋酸盐的阳离子脱出,剩余的BiO2 -转为BiO2-x,得到的铋系负极材料表面具有大量缺陷(氧空位)。
根据本发明实施例的制备方法,至少具有如下有益效果:
(1)具有缺陷的BiO2-x是由六边形组装的典型分层结构,它是一种高价含铋化合物,具有较窄的带隙(1.67eV),对整个光谱的具有良好的响应;而且,其具有优异的光催化活性(光电化学性质)和较好的稳定性,且还具有绿色环保、低毒、成本低且光催化性能高等优点。但是具有缺陷的BiO2-x鲜有被用作锂离子电池负极材料。
与Bi2O3相比,BiO2-x拥有氧空位,这些氧空位使其用于二次电池负极材料时,具有有更高的能量密度、较大的化学扩散系数、较高的安全系数。
(2)本发明研究发现,BiO2-x的结晶程度、粒径和氧空位与水热反应体系的pH相关,且影响其作为负极材料时的储锂能力。
(3)本发明提供的制备方法工艺简单,利用水热法一步得出BiO2-x,操作简便,条件温和,可重复性好,且原材料绿色环保,低毒,成本低。
本发明通过控制pH为11~13,显著提升了所得产物的结晶程度,并提升了其储锂能力。
根据本发明的一些实施例,所述铋酸盐包括铋酸钠。与其他种类的铋酸盐相比,铋酸钠更有利于在碱性条件下生成缺氧的氧化铋,由此降低了所述制备方法进行的难度。
根据本发明的一些实施例,所述水溶液的配制方法包括将所述铋酸盐和水混合后进行加热搅拌。
根据本发明的一些实施例,所述加热搅拌的温度为60-80℃。
根据本发明的一些优选的实施例,所述加热搅拌的温度约为70℃。
根据本发明的一些实施例,所述加热搅拌的转速为200-800rpm。
根据本发明的一些优选的实施例,所述加热搅拌的转速约为400rpm。
根据本发明的一些实施例,所述加热搅拌的时长为30~50min。
根据本发明的一些优选的实施例,所述加热搅拌的时长约为30min。
根据本发明的一些实施例,所述加热搅拌所用的仪器包括磁力搅拌器和机械搅拌器(机械驱动浆叶)中的至少一种。
根据本发明的一些实施例,所述水溶液中铋酸盐的浓度约为0.1~0.2mol/L。
根据本发明的一些实施例,所述pH的调整试剂包括氢氧化钠水溶液和氢氧化钾水溶液中的至少一种。
优选地,所述pH的调整试剂选自氢氧化钠水溶液。
根据本发明的一些实施例,所述调整试剂的浓度约为3mol/L。由此,调整试剂的浓度较高,在调节pH的过程中不会严重影响所述铋酸盐的水溶液的浓度,进而不会影响所得铋系负极材料的性能。
根据本发明的一些实施例,所述调整试剂的配置方法包括:将所述氢氧化钠或氢氧化钾中的至少一种,与水混合后搅拌。
根据本发明的一些实施例,所述搅拌的转速为200-800rpm。
根据本发明的一些优选的实施例,所述搅拌的转速约为400rpm。
根据本发明的一些实施例,所述搅拌的时长为30-50min。
根据本发明的一些优选的实施例,所述搅拌的时长约为30min。
在上述搅拌的转速、时长以及温度条件下,所述水溶液和所述调整试剂中的溶质均可充分溶解,并生成质地均匀的分散体系,为后续水热反应生成质地、粒度均匀的铋系负极材料提供了基础。
但是上述搅拌方法、搅拌速度并不是唯一的方法,只要能将溶质充分溶解的方法均可。
根据本发明的一些实施例,所述pH的调整方法,包括将所述调整试剂和水溶液搅拌混合。
根据本发明的一些实施例,所述搅拌混合的转速为200~500rpm。
根据本发明的一些实施例,所述搅拌混合的时长≥30min。由此增加了传质速度,间接增加了所述水热反应的速度和均匀程度。
根据本发明的一些优选的实施例,调整后,所述水溶液的pH约为12。
根据本发明的一些实施例,所述水热反应的温度为180~200℃。
在上述温度范围内,有利于铋系负极材料的临界成核,并有助于提升其生长速率,还有助于提升其结晶程度和粒径均匀度。
根据本发明的一些实施例,所述水热反应的时长为4~12h。
根据本发明的一些实施例,所述水热反应的容器材质包括聚四氟乙烯。由此可避免容器对反应体系的污染,同时避免反应体系对容器的侵蚀。
根据本发明的一些实施例,所述制备方法还包括在所述水热反应后进行固液分离,并洗涤、干燥所得固体。
根据本发明的一些实施例,所述固液分离之前还包括将所述水热反应后的体系进行冷却。
根据本发明的一些实施例,所述冷却后的温度为室温(10~50℃)。由此,可避免在后续固液分离等操作中的损伤。
根据本发明的一些实施例,所述固液分离的方法包括离心、静置沉降和过滤中的至少一种。
根据本发明的一些实施例,所述洗涤包括水洗、无水乙醇洗和丙酮洗涤中的至少一种。
根据本发明的一些实施例,所述洗涤包括依次进行的水洗、无水乙醇洗和丙酮洗涤。由此,水洗和去除未反应完全的无机水溶物,无水乙醇洗和丙酮洗涤可去除固体中残留的水分,并利用其蒸发快的优点,提升后续干燥的速度,并避免干燥后固体产物的板结。
根据本发明的一些实施例,所述干燥的温度为60~90℃。
根据本发明的一些实施例,所述干燥的方法为负压干燥。
根据本发明的第二方面实施例,提供了一种所述制备方法制得的铋系负极材料,所述铋系负极材料的化学式为BiO2-x,其中0<x<2。
根据本发明实施例的铋系负极材料,至少具有如下有益效果:
根据化学式可知,本发明提供的铋系负极材料具有一定量的氧空位,即同时具备较窄的带隙和更高的活性,在充放电时,能储存锂离子的数量更多,容量得到很大的提升。即与传统的以Bi或Bi2O3做负极材料时相比,提升了容量。
根据本发明的一些实施例,所述铋系负极材料继承了铋酸盐,特别是铋酸钠的特殊结构,具体的拥有独特的层状结构和[Bi-O]单元,由此更有利于锂离子的嵌入和脱出,以使所得产物更适合用于铋系负极材料。
根据本发明的一些实施例,所述铋系负极材料的克比容量≥1000mAh/g。
根据本发明的一些优选的实施例,所述铋系负极材料的克比容量≥1112mAh/g。
所述克比容量的测试电流≤100mA/g,测试电压为0.01-3V(Vs Li/Li+)。
根据本发明的一些实施例,所述铋系负极材料具有片状结构。
根据本发明的一些实施例,所述片状结构的片径为200~1000nm。
根据本发明的一些实施例,所述铋系负极材料中存在氧缺陷。
根据本发明的一些实施例,所述铋系负极材料中铋的价态包括+3价和+5价。
根据本发明的第三方面实施例,提出了一种负极极片,所述负极极片的制备原料包括所述铋系负极材料。
根据本发明的一些实施例,所述负极极片的制备原料还包括导电剂、粘结剂和溶剂。
根据本发明的一些实施例,所述导电剂包括炭黑、石墨烯和乙炔黑中的至少一种。
根据本发明的一些实施例,所述粘结剂包括PVDF(聚偏氟乙烯)。
根据本发明的一些实施例,所述溶剂包括NMP(N-甲基吡咯烷酮)。
根据本发明的一些实施例,按重量份计,所述铋系负极材料、导电剂和粘结剂的比例为70~96:1.5~15:1.5~15。
根据本发明的一些优选的实施例,按重量份计,所述铋系负极材料、导电剂和粘结剂的比例约为75:15:10。
根据本发明的第四方面实施例,提供了一种二次电池,所述二次电池包括所述的铋系负极材料。
由于所述二次电池均引用了前述实施例提到的铋系负极材料,因此所述二次电池具有所述铋系负极材料所有的有益效果。
根据本发明的一些实施例,所述二次电池包括锂离子电池、锂金属电池、钠离子电池和钠金属电池中的至少一种。
根据本发明的一些实施例,所述二次电池可用作动力电池、储能电池和3C电池(家用小电子)中的至少一个领域。
若无特殊说明,本发明中的“约”表示误差范围在±2%之间,例如约100表示的实际含义是100±2%×100。
本发明的其它特征和优点将在随后的说明书中阐述,并且,部分地从说明书中变得显而易见,或者通过实施本发明而了解。
附图说明
本发明的上述和/或附加的方面和优点从结合下面附图对实施例的描述中将变得明显和容易理解,其中:
图1是本发明实施例1所得铋系负极材料的XRD图谱;
图2为本发明实施例1所得铋系负极材料的SEM图;
图3为本发明实施例1所得铋系负极材料的SEM图;
图4为本发明实施例1所得铋系负极材料的TEM图;
图5为本发明实施例1所得铋系负极材料的HR-TEM图;
图6为本发明对比例1所得铋系负极材料的SEM图;
图7为本发明对比例1所得铋系负极材料的SEM图;
图8为本发明对比例1所得铋系负极材料的SEM图;
图9为本发明实施例1所得铋系负极材料的充放电曲线图;
图10为本发明实施例1所得铋系负极材料的循环伏安曲线图;
图11为本发明对比例1所得铋系负极材料的充放电曲线图;
图12为本发明对比例1所得铋系负极材料的循环伏安曲线图;
具体实施方式
以下将结合实施例对本发明的构思及产生的技术效果进行清楚、完整地描述,以充分地理解本发明的目的、特征和效果。显然,所描述的实施例只是本发明的一部分实施例,而不是全部实施例,基于本发明的实施例,本领域的技术人员在不付出创造性劳动的前提下所获得的其他实施例,均属于本发明保护的范围。
在本发明的描述中,若干的含义是一个以上,多个的含义是两个以上,大于、小于、超过等理解为不包括本数,以上、以下、以内等理解为包括本数。如果有描述到第一、第二只是用于区分技术特征为目的,而不能理解为指示或暗示相对重要性或者隐含指明所指示的技术特征的数量或者隐含指明所指示的技术特征的先后关系。
实施例1
本实施例制备了一种铋系负极材料,具体步骤为:
S1.首先称取2mmol NaBiO3与20ml去离子水混合,之后放置于磁力搅拌器上加热至70℃,并以400rpm的转速搅拌30min,得铋酸盐的水溶液;
称取2.4g的NaOH溶于20ml去离子水混合后于400rpm的转速搅拌30min,得pH的调整试剂。
S2.调整试剂倒入处于70℃的铋酸盐的水溶液中,以400rpm的转速搅拌30min后,测试pH值为12;
S3.将步骤S2所得混合物倒入容量为100ml的聚四氟乙烯反应釜中,密封后,在180℃烘箱内水热反应6h(烘箱的恒温时长)。
S4.待反应釜冷却至室温后(50℃以下,以不烫手为宜),将所得混合物进行离心,收集固体成分;
对固体成分进行洗涤:先用去离子水洗涤3次,再用无水乙醇洗涤3次;其中,每次洗涤结束后,采用离心的方法将洗涤试剂和固体分离,然后将所得固体进行下一步的洗涤;
最终,将所得固体在80℃干燥24h(真空烘箱),得到BiO2-x。
对比例1
本对比例制备了一种铋系负极材料,具体和实施例1的区别在于:
(1)步骤S1中,调整试剂的配制方法为:称取3.2g的NaOH溶于20ml去离子水混合后于400rpm的转速搅拌30min;
(2)步骤S2所得混合物的pH为14。
应用例1
本应用例制备了一种负极极片,具体步骤为:
以实施例1和对比例1所得铋系负极材料为活性材料,将活性材料与导电炭黑和粘结剂(PVDF)按质量比为7.5:1.5:1质量比研磨均匀后,加3mL NMP(N-甲基吡咯烷酮)调制成浆状,然后均匀涂在铜箔上,并置于80℃鼓风干燥箱中干燥过夜,得负极极片。
应用例2
本应用例以应用例1所得负极极片为原料,制备了用于测试的扣式电池,具体步骤为:
在无水无氧的手套箱中(水、氧含量<0.01PPm),将扣式电池正极壳开口朝上,平放于垫板上,应用例1所得负极极片放入正极壳的正中;然后用胶头滴管滴加2~3滴(每滴的量约为0.05ml)电解液,浸润负极极片表面,并夹取隔膜(celgard 2400film),覆盖负极极片;再次滴加2~3滴电解液,润湿隔膜表面;然后夹取金属锂片置于隔膜正中,盖上负极壳后密封,即得扣式电池,扣式电池以制备铋系负极材料的具体实施方式进行命名。
测试例
本测试例的第一方面,表征了实施例1所得铋系负极材料的物相,具体表征方法为XRD测试。
结果显示,实施例1所得铋系负极材料在2θ位于28.2°,32.6°,46.9°,55.6°,58.3°,68.5°,75.6°和77.9°均有比较明显的特征峰,且完全与BiO2-x标准卡片(JCPDSNo.47-1057)一致。上述衍射峰分别对应于BiO2-x的(111)、(200)、(220)、(311)、(222)、(400)、(331)和(420)的衍射晶面;XRD图谱中没有其他的杂峰出现,各衍射峰强度高(半峰宽较小),表明所合成的样品为纯相BiO2-x且具有良好的结晶性。具体图谱如图1所示。
本测试例的第二方面,表征了实施例1和对比例1所得铋系负极材料的形貌,具体表征方法有扫描电镜(SEM)、普通透射电镜(TEM)和高分辨率透射电镜(HR-TEM),结果显示:
实施例1所得铋系负极材料具有片状结构,片径主要分布在200~1000nm,同时在HR-TEM中,还显示出清晰、等间距的晶格条纹,这进一步佐证了本发明所得铋系负极材料的结晶性能良好,这与XRD图谱相一致。具体形貌图片如图2~5所示。
对比例1所得铋系负极材料的形貌显示:部分片层结构结晶性不好,猜测有原子脱落的可能,因此其电化学性能可能劣于实施例1所得铋系负极材料。具体测试图谱如图6~8所示。
本测试例的第三方面,测试了应用例2所得扣式电池,以此表征实施例1和对比例1所得铋系负极材料的电化学性能,具体测试了前5周的充放电曲线以及前3周循环伏安曲线(CV图),结果显示:
当循环电压为0.01~3.0V,充放电电流密度为100mA g-1时,实施例1所得铋系负极材料的放电克比容量高达1112mAh/g,可以预期的是,若对电池的结构、配比进行优化,本发明提供的铋系负极材料的克比容量会高于1112mAh/g,具体测试图谱如图9所示。同等条件下,对比例1所得铋系负极材料的克比容量发挥约为960mAh/g,显著低于实施例1所得铋系负极材料,这进一步佐证,参与水热反应时,混合体系的pH对所得铋系负极材料的电化学性能有明显影响,具体是通过影响结晶性能,进而影响电化学性能。具体测试图谱如图11所示。
实施例1所得铋系负极材料在0.01-3V电压窗口(Vs Li/Li+)下测试的CV测试结果显示,在电压值为1.0V、1.7V和2.4V时出现了明显的氧化峰,而在电压值为0.5V、1.15V、1.35V和1.8V处出现了还原峰。这些氧化还原反应对应于锂离子的脱嵌,其反应机理如下:
BiO2-x+(5-2x)Li++(5-2x)e-→LiBi+(5-2x)Li2O;
LiBi+Li++e-→Li2Bi;
Li2Bi+Li++e-→Li3Bi;
Li2Bi+3Li++3e-→Li5Bi;
由上述机理可知,本发明提供的铋系负极材料BiO2-x的电化学储能行为与单质Bi类似,即在首圈放电过程中BiO2-x还原成Bi伴随着锂离子的逐步***,随后在充电时又逐步脱出锂离子,与Bi2O3相比,能储存锂离子的数量更多,容量得到很大的提升。实施例1所得CV图谱如图10所示。
对比例1所得铋系负极材料的CV测试结果显示:在电压值为0.97V、1.8V和2.35V时出现了明显的氧化峰,而在电压值为0.18V、0.92V、1.16V和1.6V处出现了还原峰;由此可知,对比例所得铋系负极材料在充放电过程中出现了不可逆相变,因此作为负极材料的电化学性能较差。具体测试图谱如图12所示。
综上,本发明提供的制备方法可制得结晶性能良好的片状材料,该材料用作二次电池负极活性材料后,可发挥优异的电化学性能。可以预期的是,本发明所得的铋系负极材料有望在动力电池、储能电池和3C电池领域具有广阔的应用前景。
上面结合附图对本发明实施例作了详细说明,但是本发明不限于上述实施例,在所属技术领域普通技术人员所具备的知识范围内,还可以在不脱离本发明宗旨的前提下作出各种变化。此外,在不冲突的情况下,本发明的实施例及实施例中的特征可以相互组合。
Claims (5)
1.一种铋系负极材料的制备方法在制备负极极片中的应用,其特征在于,所述制备方法包括:
配置含铋酸钠的水溶液,并将其pH调整至11~13后,进行水热反应;所述pH的调整试剂包括氢氧化钠水溶液和氢氧化钾水溶液中的至少一种;所述水热反应的温度为180~200℃;
所述制备方法制得的铋系负极材料的化学式为BiO2-x,其中0<x<2。
2.根据权利要求1所述的应用,其特征在于,所述水热反应的时长为4~12h。
3.根据权利要求1所述的应用,其特征在于,所述水溶液中铋酸钠的浓度为0.1~0.2mol/L。
4.根据权利要求1~3任一项所述的应用,其特征在于,所述制备方法还包括在所述水热反应后进行固液分离,并洗涤、干燥所得固体。
5.根据权利要求1~3任一项所述的应用,其特征在于,所述负极极片用于制备二次电池。