CN114836064B - 一种陶瓷微珠凝胶材料及其制备方法 - Google Patents
一种陶瓷微珠凝胶材料及其制备方法 Download PDFInfo
- Publication number
- CN114836064B CN114836064B CN202210514153.2A CN202210514153A CN114836064B CN 114836064 B CN114836064 B CN 114836064B CN 202210514153 A CN202210514153 A CN 202210514153A CN 114836064 B CN114836064 B CN 114836064B
- Authority
- CN
- China
- Prior art keywords
- parts
- solution
- gel
- weight
- silicate solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种陶瓷微珠凝胶材料及其制备方法,其陶瓷微珠凝胶材料包括真空陶瓷微珠,碳化硅纤维,凝胶剂,硅酸锂溶液,硅酸钠溶液,苯‑丙乳液,聚丙烯酰胺,十六烷基三甲基溴化铵,Tween‑80,水和调节剂。本发明的材料采用真空陶瓷微珠作为隔热功能材料,十六烷基三甲基溴化铵作为分散剂,使其它溶质加快溶解,并分散均匀,以耐高温的碳化硅纤维作为增强材料,凝胶剂使得凝胶材料具有高涂抹性和保水性,避免开裂;Tween‑80作为稳定剂,添加的硅酸锂溶液和硅酸钠溶液,使得凝胶导热系数降低,并与真空陶瓷微珠形成更加致密的真空隔热结构,制备而成具有高温隔热功能,且涂抹性能优良,防水性优良的复合涂料。
Description
技术领域
本发明涉及一种陶瓷微珠凝胶材料及制备方法,属于功能材料技术领域。
背景技术
目前用于通用的墙体保温材料有矿岩棉、玻璃棉、泡沫塑料、聚胶脂、硅钙板等,这些保温材料不同程度地存在诸如抗压强度低、耐水性差、不耐高温,使用工艺复杂等缺点,但最大的缺点是造价普遍较高,特别是聚胶脂和硅钙板的价格更高。个别保温材料在制造过程中还产生污染,也有采取聚苯颗粒做墙面保温层的,其工艺是将一定量的聚苯颗粒加水泥加粘结剂加水,搅拌均匀后分两遍抹到墙上,再涂胶粘玻璃纤维网格布增强,然后再抹两遍水泥沙浆。此法虽然单位面积成本有所降低,但仍施工工艺复杂,粘接不牢固,易起层,强度低、保温效果不佳。
发明内容
(一)要解决的技术问题
为了解决现有技术的上述问题,本发明提供一种陶瓷微珠凝胶材料及制备方法。
(二)技术方案
为了达到上述目的,本发明采用的主要技术方案包括:
一种陶瓷微珠凝胶材料,其包括按重量计的真空陶瓷微珠60-80份,碳化硅纤维5~10份,凝胶剂1~2份,硅酸锂溶液15~25份,硅酸钠溶液25~40份,苯-丙乳液0.1~0.8份,聚丙烯酰胺2~6份,十六烷基三甲基溴化铵0.05~1份,Tween-80 0.5~3份,水90~100份和调节剂0.005~3份,调节硅酸锂溶液与硅酸钠溶液混合时,溶液的pH值为9~12;在涂抹真空陶瓷微珠凝胶材料时,用硫酸调节其pH值为6~7时,涂抹操作应在60min内完成。
如上所述的真空陶瓷微珠凝胶材料,优选地,真空陶瓷微珠65~75份,碳化硅纤维7~9份,凝胶剂1.2~1.8份,硅酸锂溶液17~20份,硅酸钠溶液33~35份,苯-丙乳液0.2~0.7份,聚丙烯酰胺2.5~5份,十六烷基三甲基溴化铵0.1~0.5份,Tween-80 1~2份,调节剂0.005~2份。
如上所述的真空陶瓷微珠凝胶材料,优选地,真空陶瓷微珠75份,碳化硅纤维8份,凝胶剂1.3份,硅酸锂溶液18份,硅酸钠溶液32份,苯-丙乳液0.5份,聚丙烯酰胺3份,十六烷基三甲基溴化铵0.3份,Tween-80 1.5份,水95份。
如上所述的真空陶瓷微珠凝胶材料,优选地,所述凝胶剂包括羧甲基纤维素、羟甲基纤维素钠、聚乙烯醇的一种或多种。
如上所述的真空陶瓷微珠凝胶材料,优选地,所述调节剂为氢氧化钠溶液和硫酸溶液,氢氧化钠溶液浓度为0.01~1mol/L,硫酸溶液为5~10%的稀硫酸。
如上所述的真空陶瓷微珠凝胶材料,优选地,所述真空陶瓷微珠的粒径是20~100μm。
如上所述的真空陶瓷微珠凝胶材料,优选地,硅酸锂溶液的模数为2.8~3,固含量为10~25%;硅酸钠溶液的模数3~3.5,固含量31~34%。
一种如上所述真空陶瓷微珠凝胶材料的制备方法,其包括如下步骤:
S1、将十六烷基三甲基溴化溶于部分水量中,搅拌均匀,加入碳化硅纤维、聚丙烯酰胺,苯-丙乳液搅拌混合15~30min,加入Tween-80、真空陶瓷微珠继续搅拌10~20min,
S2、将硅酸锂溶液和硅酸钠溶液混合,搅拌均匀,并用调节剂调节混合液的pH值为9~12;
S3、将凝胶剂用剩余水量溶解,搅拌均匀获得凝胶溶液;
S4、将步骤S1和步骤S2获得的溶液混合,搅拌均匀后,再加入凝胶溶液,搅拌均匀,获得真空陶瓷微珠凝胶材料。
如上所述的制备方法,优选地,在步骤S1中部分水量为总水量的80~90%,搅拌的速率为200~500rpm。
如上所述的制备方法,优选地,在步骤S2中,调节剂为氢氧化钠溶液,调节pH值为10~11。
如上所述的制备方法,优选地,在使用时,用调节剂加入真空陶瓷微珠凝胶材料中调节其pH值为6~7时,可加快凝固,涂抹操作应在60min内完成,形成隔热涂层。
本发明经大量实验研究发现,采用十六烷基三甲基溴化铵作为分散剂,使溶质加快溶解,且不会出现渗液现象,研究发现采用十二烷基硫酸钠作为分散剂时,溶液导致有起泡,出现微孔,导致渗液;采用Tween-80作为稳定剂,使获得的凝胶材料稳定成型,不易结块。采用碳化硅纤维具有良好的相融性,可提高涂料的可涂抹性能,使涂抹更顺滑。
本发明中采用的真空陶瓷微珠,具有真空结构,有极低的导热系数,能有效抑制并屏蔽红外线的辐射热和热量的传导,可抑制高温物体的热辐射和热量的传导,涂料涂抹后真空陶瓷微珠相互挤压填充,可以形成真空墙结构的隔热层,用以阻止热量的传递,空隙率小,提高隔热性能。聚丙烯酰胺,用于粘结粉体颗粒。凝胶剂溶于水中,具有凝胶的特性,同时还能够提高涂抹性,延长可操作时间,其还具有保水性,使涂料不会由于干燥太快而表面开裂,增强涂层硬化后的强度,优选凝胶剂为羟甲基纤维素钠。
本发明的真空陶瓷微珠凝胶材料中添加的硅酸锂溶液和硅酸钠溶液,具有两种硅酸盐的优点,其使的材料整体的导热系数降低,且硅酸锂有助溶的作用,加入苯-丙乳液作为辅助成膜作用,硅酸锂和硅酸钠凝胶成膜后与真空陶瓷微珠形成更加致密的真空隔热结构,Tween-80还能使真空陶瓷微珠有序排列,有利于成膜和隔热保温,同时提高了涂层的防渗透性,具有较好的防水、防腐功能,且具有更好的耐压、耐磨性能;可以缩短涂层固化时间,提高施工效率。优选地硅酸锂溶液的用量为15~25份,硅酸钠溶液的用量为25~40份,如果硅酸钠溶液过量,会导致凝胶材料溶液容易凝胶过快,容易产生沉淀,调节硅酸锂溶液与硅酸钠溶液混合时,要求溶液的pH值在9~12,避免溶液pH值为酸性导致固化,在涂抹真空陶瓷微珠凝胶材料时,用硫酸调节其pH值时,可加快固化,涂抹操作应在60min内完成,形成涂层,超过60min时,固化加剧,容易凝结,不能再使用。
(三)有益效果
本发明的有益效果是:
本发明提供的真空陶瓷微珠凝胶材料,采用真空陶瓷微珠作为隔热功能材料,十六烷基三甲基溴化铵作为分散剂,使其它溶质加快溶解,并分散均匀,以耐高温的碳化硅纤维作为增强材料,凝胶剂使得凝胶材料具有高涂抹性和保水性,避免开裂;Tween-80作为稳定剂,添加的硅酸锂溶液和硅酸钠溶液,使得凝胶导热系数降低,并与真空陶瓷微珠形成更加致密的真空隔热结构,制备而成具有高温隔热功能,且涂抹性能优良,防水性优良的复合涂料。
本发明提供的陶瓷微珠凝胶材料,可用于墙体的保温、隔热,并具有防水、防开裂、抗脱落等优点,材料环保,施工操作方便,环保安全。
具体实施方式
为了更好的解释本发明,以便于理解,下面通过具体实施方式,对本发明作详细描述。
实施例1
一种真空陶瓷微珠凝胶材料的制备方法,其包括如下步骤:
所用的原料按如下重量计进行备料:真空陶瓷微珠75份,碳化硅纤维8份,凝胶剂(羟甲基纤维素钠)1.3份,硅酸锂溶液(模数为2.8,固含量为22.5%)18份,硅酸钠溶液(模数为3.5,固含量32%)32份,苯-丙乳液0.5份,聚丙烯酰胺3份,十六烷基三甲基溴化铵0.3份,Tween-80 1.5份,水95份,氢氧化钠溶液浓度为0.5mol/L,硫酸溶液为5%。
S1、将十六烷基三甲基溴化溶于90%的水量中,搅拌均匀,加入碳化硅纤维、聚丙烯酰胺,苯-丙乳液,在200转/min搅拌混合30min,加入Tween-80和真空陶瓷微珠继续搅拌15min;
S2、将硅酸锂溶液和硅酸钠溶液混合,搅拌均匀,并用调节剂调节混合液的pH值为11~12;
S3、将凝胶剂用剩余10%的水量溶解,搅拌均匀获得凝胶溶液;
S4、将步骤S1和步骤S2获得的溶液混合,搅拌均匀后,再加入凝胶溶液,搅拌均匀,获得真空陶瓷微珠凝胶材料。
实施例2
一种真空陶瓷微珠凝胶材料的制备方法,其包括如下步骤:
所用的原料按如下重量计进行备料:真空陶瓷微珠66份,碳化硅纤维7份,凝胶剂(羧甲基纤维素)1.5份,硅酸锂溶液(模数为2.8,固含量为22.5%)18份,硅酸钠溶液(模数为3.5,固含量32%)35份,苯-丙乳液0.55份,聚丙烯酰胺3份,十六烷基三甲基溴化铵0.4份,Tween-801.2份,水95份,氢氧化钠溶液浓度为0.5mol/L,硫酸溶液为5%。
S1、将十六烷基三甲基溴化溶于85%的水量中,搅拌均匀,加入碳化硅纤维、聚丙烯酰胺,苯-丙乳液,在200转/min搅拌混合30min,加入Tween-80和真空陶瓷微珠继续搅拌15min;
S2、将硅酸锂溶液和硅酸钠溶液混合,搅拌均匀,并用调节剂调节混合液的pH值为11~12;
S3、将凝胶剂用剩余的15%的水量溶解,搅拌均匀获得凝胶溶液;
S4、将步骤S1和步骤S2获得的溶液混合,搅拌均匀后,再加入凝胶溶液,搅拌均匀,获得真空陶瓷微珠凝胶材料。
实施例3
一种真空陶瓷微珠凝胶材料的制备方法,其包括如下步骤:
所用的原料按如下重量计进行备料:真空陶瓷微珠73份,碳化硅纤维8.5份,凝胶剂(聚乙烯醇)1.8份,硅酸锂溶液(模数为2.8,固含量为22.5%)19份,硅酸钠溶液(模数为3.5,固含量32%)35份,苯-丙乳液0.5份,聚丙烯酰胺4.5份,十六烷基三甲基溴化铵0.5份,Tween-802份,水98份,氢氧化钠溶液浓度为0.5mol/L,硫酸溶液为5%。
S1、将十六烷基三甲基溴化溶于90%的水量中,搅拌均匀,加入碳化硅纤维、聚丙烯酰胺,苯-丙乳液,在300转/min搅拌混合30min,加入Tween-80和真空陶瓷微珠继续搅拌15min;
S2、将硅酸锂溶液和硅酸钠溶液混合,搅拌均匀,并用调节剂调节混合液的pH值为11~12;
S3、将凝胶剂用剩余10%的水量溶解,搅拌均匀获得凝胶溶液;
S4、将步骤S1和步骤S2获得的溶液混合,搅拌均匀后,再加入凝胶溶液,搅拌均匀,获得真空陶瓷微珠凝胶材料。
对比例1
在实施例1的基础上,不添加硅酸钠溶液,其它步骤与实施例1相同。
对比例2
在实施例1的基础上,不添加凝胶剂和碳化硅纤维,其它步骤同实施例1。
对比例3
在实施例1的基础上,不添加Tween-80,其它步骤同实施例1。
将本发明实施例和对比例中制备的真空陶瓷微珠凝胶材料,使用时采用5%的硫酸进行调节材料的pH值为6~7,涂抹在基材表面上,涂抹操作在60min内完成,形成涂层。
将上述的凝胶材料进行检测:室温25℃条件下,将凝胶材料涂抹到基材钢板表面形成涂层,基材升温到50℃和100℃,涂层的厚度为4.5mm,测量其凝胶材料涂层表面温度,结果如下表1:
表1
涂层 | 50 | 100 |
实施例1 | 27 | 32 |
实施例2 | 28 | 35 |
实施例3 | 30 | 38 |
对比例1 | 44 | 57 |
对比例2 | 40 | 50 |
对比例3 | 48 | 59 |
将本发明实施例1-3制备的材料和对比例获得材料,分3次涂刷在玻璃板上(玻璃板先打蜡),厚度为1.5mm,静放7天,然后放入烘箱内在50℃烘干24h,取出后放置3h,做不透水实验,不透水性为0.3MPa,保持30分钟后,看看是否有渗漏。结果显示,实施例1-3中的材料无渗漏,对比例1中材料24min时出现渗漏,对比例2中材料15min时出现渗漏,对比例3中材料29min时出现渗漏。
由上可看出,与对比例相比,本发明获得的真空陶瓷微珠凝胶材料,用于制成涂膜使用时,能有效隔热,具有保温隔热功能,涂料均匀,防水性能优良,将本发明制备的涂料涂在墙体表面具有保温、隔热,并具有防水、防开裂、抗脱落等优点,且材料环保。
以上所述,仅是本发明的较佳实施例而已,并非是对本发明做其它形式的限制,任何本领域技术人员可以利用上述公开的技术内容加以变更或改型为等同变化的等效实施例。但是凡是未脱离本发明技术方案内容,依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与改型,仍属于本发明技术方案的保护范围。
Claims (1)
1.一种真空陶瓷微珠凝胶材料,其特征在于,其由按重量计的真空陶瓷微珠75份,碳化硅纤维8份,凝胶剂1.3份,硅酸锂溶液18份,硅酸钠溶液32份,苯-丙乳液0.5份,聚丙烯酰胺3份,十六烷基三甲基溴化铵0.3份,Tween-80 1.5份,水95份和调节剂0.005~3份制备;
所述调节剂为氢氧化钠溶液和硫酸溶液,氢氧化钠溶液浓度为0.5mol/L,硫酸溶液为5%的稀硫酸;
所述真空陶瓷微珠的粒径是20~100μm;
硅酸锂溶液的模数为2.8,固含量为22.5%;
硅酸钠溶液的模数为3.5,固含量为32%;
所述真空陶瓷微珠凝胶材料由如下制备方法获得:
S1、将十六烷基三甲基溴化溶于90%的水量中,搅拌均匀,加入碳化硅纤维、聚丙烯酰胺,苯-丙乳液,在200转/min搅拌混合30min,加入Tween-80和真空陶瓷微珠继续搅拌15min;
S2、将硅酸锂溶液和硅酸钠溶液混合,搅拌均匀,并用调节剂调节混合液的pH值为11~12;
S3、将凝胶剂用剩余10%的水量溶解,搅拌均匀获得凝胶溶液;
S4、将步骤S1和步骤S2获得的溶液混合,搅拌均匀后,再加入凝胶溶液,搅拌均匀,获得真空陶瓷微珠凝胶材料;
在涂抹真空陶瓷微珠凝胶材料时,用硫酸溶液调节其pH值为6~7时,涂抹操作应在60min内完成;
所述凝胶剂为羟甲基纤维素钠。