CN114621620A - Carbon black for antistatic coating - Google Patents
Carbon black for antistatic coating Download PDFInfo
- Publication number
- CN114621620A CN114621620A CN202210434063.2A CN202210434063A CN114621620A CN 114621620 A CN114621620 A CN 114621620A CN 202210434063 A CN202210434063 A CN 202210434063A CN 114621620 A CN114621620 A CN 114621620A
- Authority
- CN
- China
- Prior art keywords
- carbon black
- nano carbon
- antistatic coating
- mass
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides carbon black for an antistatic coating, which greatly increases the specific surface area of the nano carbon black, improves the conductivity of the nano carbon black, effectively reduces the addition amount of the nano carbon black in the antistatic coating and greatly improves the antistatic performance by fully reacting the nano carbon black in a supercritical water system.
Description
Technical Field
The invention relates to the technical field of nano carbon black modification, in particular to carbon black for an antistatic coating.
Background
The nano carbon black has excellent colorability, weather resistance and chemical stability, is rich in source and low in price, and is one of important coloring agents. And because the nano carbon black has conductivity, the nano carbon black has wide application in the field of antistatic coatings.
In the prior art, because the conductivity of the nano carbon black is limited, the addition amount of the nano carbon black in the antistatic coating is generally more than 15%, and the surface resistivity of the nano carbon black is still kept at 107-109Omega, the antistatic performance is not good under dry weather conditions.
Disclosure of Invention
The invention provides carbon black for an antistatic coating, which greatly increases the specific surface area of the nano carbon black, improves the conductivity of the nano carbon black, effectively reduces the addition amount of the nano carbon black in the antistatic coating and greatly improves the antistatic performance by fully reacting the nano carbon black in a supercritical water system.
The preparation process of the carbon black for the antistatic coating comprises the following steps:
(1) dispersing nano carbon black in purified water with the mass multiple of 1-2 times, adding a dispersing agent with the mass of 1-3 per mill of the nano carbon black and polydimethylsiloxane emulsion with the mass of 2-3% of the nano carbon black, and grinding and dispersing to prepare a paste dispersion;
(2) adding the paste dispersion into a supercritical reactor, heating and pressurizing to a supercritical state for 3-5min, then reducing the pressure and evaporating the water to dryness to obtain the carbon black for the antistatic coating.
Further, the particle size of the nano carbon black in the step (1) is 40-100 nm.
Further, the dispersant in the step (1) is one or more of Disper-9076, AKN-2290 and AKN-2300.
Further, the supercritical state control temperature in the step (2) is 374.3 ℃ and the pressure is 22.13 MPa.
Further, graphite powder with the mass of 0.5-1.0% of that of the nano carbon black is added in the step (1).
The invention has the technical effects and advantages that:
1. according to the invention, the nano carbon black reacts with water in a supercritical state, the internal form of the nano carbon black is changed, the specific surface area of the nano carbon black is greatly improved, the conductivity of the nano carbon black is improved, the addition amount of the nano carbon black in the antistatic coating is effectively reduced, and the antistatic performance of the antistatic coating is greatly improved;
2. the conductive performance of the prepared carbon black for the antistatic coating can be further improved by mixing trace graphite powder in the nano carbon black.
Detailed Description
Example 1
The preparation process of the carbon black for the antistatic coating comprises the following steps:
(1) dispersing nano carbon black with the particle size of 40nm in purified water with the mass multiple of 2 times, adding a dispersing agent Disper-9076 with the mass of 3 per mill of the nano carbon black and polydimethylsiloxane emulsion with the mass of 2 percent of the nano carbon black, simultaneously adding graphite powder with the mass of 0.5 percent of the nano carbon black, and grinding and dispersing to prepare a paste-like dispersion;
(2) adding the paste dispersion into a supercritical reactor, heating and pressurizing to a supercritical state for 3min, controlling the temperature of 374.3 ℃ and the pressure of 22.13MPa in the supercritical state, then reducing the pressure and evaporating the water to dryness, thus obtaining the carbon black for the antistatic coating.
Example 2
The preparation process of the carbon black for the antistatic coating comprises the following steps:
(1) dispersing nano carbon black with the particle size of 50nm in purified water with the mass multiple of 1.5 times, adding a dispersing agent AKN-2290 with the mass of 2 thousandth of the nano carbon black and polydimethylsiloxane emulsion with the mass of 2.2 percent of the nano carbon black, simultaneously adding graphite powder with the mass of 1.0 percent of the nano carbon black, and grinding and dispersing to prepare a paste dispersion;
(2) adding the paste dispersion into a supercritical reactor, heating and pressurizing to a supercritical state for 3min, controlling the temperature of 374.3 ℃ and the pressure of 22.13MPa in the supercritical state, then reducing the pressure and evaporating the water to dryness, thus obtaining the carbon black for the antistatic coating.
Example 3
The preparation process of the carbon black for the antistatic coating comprises the following steps:
(1) dispersing nano carbon black with the particle size of 100nm in purified water with the mass multiple of 1, adding AKN-2300 of dispersant with the mass of 1 per mill of the nano carbon black and 3% of polydimethylsiloxane emulsion of the nano carbon black, simultaneously adding graphite powder with the mass of 1.0% of the nano carbon black, and grinding and dispersing to prepare paste dispersion;
(2) adding the paste dispersion into a supercritical reactor, heating and pressurizing to a supercritical state for 5min, controlling the temperature of 374.3 ℃ and the pressure of 22.13MPa in the supercritical state, then reducing the pressure and evaporating the water to dryness, thus obtaining the carbon black for the antistatic coating.
Example 4
The carbon black for the antistatic coating is prepared by the same process as the example 2 except that graphite powder is not added in the step (1).
Comparative example 1
The same lot of the nano carbon black as the nano carbon black in the step (1) of the example 2.
Comparative example 2
Graphite powder was mixed with the same batch of the nano-carbon black as described in the step (1) of example 2 in an amount of 1.0% by mass.
Comparative example 3
The modified nano carbon black has the same process as the example 2 except that no dispersant is added in the step (1).
Comparative example 4
The modified nano carbon black has the same process as the example 2 except that the polydimethylsiloxane emulsion is not added in the step (1).
Comparative example 5
The modified nanometer carbon black has the temperature controlled in the supercritical reactor of step 2 at 372 deg.c and pressure controlled at 22.13MPa, and the other technological steps are the same as those in example 2.
And (3) effect comparison:
epoxy resin E-44 is taken as a curing system, and an organic tin catalyst is added to prepare the thermosetting varnish. Then 10% of the nano carbon black prepared by the processes of the above examples and comparative examples was added to the thermosetting varnish, and sanded by a carbon black rod sander LDM5L to prepare an antistatic coating.
1. Calculating the mass loss of the solid in the supercritical reactor of each embodiment and comparative example process, observing whether the product is agglomerated after water is evaporated, and testing the specific surface area of the nano carbon black by adopting a method of GB/T19587-;
2. the nano carbon black was prepared according to the processes of the above examples and comparative examples, and the time required for sand-milling in the heat-curable varnish was recorded;
3. the antistatic coating was applied to a 20 μm film former and dried, and the surface resistivity (Ω) of the coating was measured according to the measuring method of GB/T1410-2006 test method for volume resistivity and surface resistivity of solid insulating material.
The above examples and comparative examples are only intended to illustrate the technical solution of the present invention and not to limit the same, and although the present invention has been described in detail by the above examples and comparative examples, it will be understood by those skilled in the art that various changes in form and detail may be made therein without departing from the scope of the present invention as defined by the claims.
Claims (5)
1. A carbon black for antistatic coating, characterized in that: the preparation process of the carbon black for the antistatic coating comprises the following steps:
(1) dispersing nano carbon black in purified water with the mass multiple of 1-2 times, adding a dispersing agent with the mass of 1-3 per mill of the nano carbon black and polydimethylsiloxane emulsion with the mass of 2-3% of the nano carbon black, and grinding and dispersing to prepare a paste dispersion;
(2) adding the paste dispersion into a supercritical reactor, heating and pressurizing to a supercritical state for 3-5min, then reducing pressure and evaporating water to dryness to obtain the carbon black for the antistatic coating.
2. The carbon black for antistatic coating according to claim 1, characterized in that: the particle size of the nano carbon black in the step (1) is 40-100 nm.
3. The carbon black for antistatic coating according to claim 1, characterized in that: the dispersant in the step (1) is one or more of Disper-9076, AKN-2290 and AKN-2300.
4. The carbon black for antistatic coating according to claim 1, characterized in that: controlling the temperature of the supercritical state in the step (2) to be 374.3 ℃ and the pressure to be 22.13 MPa.
5. The carbon black for antistatic coating according to claim 1, characterized in that: graphite powder with the mass of 0.5-1.0% of that of the nano carbon black is also added in the step (1).