CN114230285A - 一种装配式绿色建筑保温墙体结构及其装配方法 - Google Patents
一种装配式绿色建筑保温墙体结构及其装配方法 Download PDFInfo
- Publication number
- CN114230285A CN114230285A CN202111640843.4A CN202111640843A CN114230285A CN 114230285 A CN114230285 A CN 114230285A CN 202111640843 A CN202111640843 A CN 202111640843A CN 114230285 A CN114230285 A CN 114230285A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- formaldehyde resin
- melamine formaldehyde
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种装配式绿色建筑保温墙体结构及其装配方法,先以三聚氰胺甲醛树脂和改性纳米二氧化硅为原料,纺丝制成三聚氰胺甲醛树脂纤维;再将硅藻土、膨胀珍珠岩混合研磨得到混合粉,造粒成球,煅烧,得到预制颗粒;然后将三聚氰胺甲醛树脂纤维、预制颗粒加入二氧化硅溶胶中,凝胶化,得到凝胶材料;最后将硅酸盐水泥、聚氨酯类发泡剂、凝胶材料混合均匀,加入水,搅拌混匀,养护,即得。该保温墙体结构强度高,保温效果好,适用于装配式绿色建筑。
Description
技术领域
本发明涉及一种保温墙体结构,具体涉及一种装配式绿色建筑保温墙体结构及其装配方法。属于绿色建筑技术领域。
背景技术
装配式建筑大大节省了人力资源和建筑材料,减少了现场抹灰、砌墙等操作,受天气影响较小,大大提高了施工进度,减少建筑垃圾以及有害气体排放,故装配式绿色建筑符合当前的绿色环保理念,颇受人们的青睐。而墙体保温又是影响建筑节能的重要因素,因此保温墙体结构是装配式绿色建筑的核心所在。
为了实现墙体保温,现有技术中多采用多孔结构阻断热量传递,如此一来大部分保温墙体的强度相对较差。而且,多孔结构对养护条件要求较为苛刻,难以控制均匀,严重影响了保温墙体的使用寿命。
另外,现有的保温墙体结构复杂,内部各墙体,模块连接稳定性差,使用寿命短,且使用过程中存在脱落风险。故保温墙体结构的具体装配方法也非常重要。
发明内容
本发明的目的是为克服上述现有技术的不足,提供一种装配式绿色建筑保温墙体结构及其装配方法。
为实现上述目的,本发明采用下述技术方案:
一种装配式绿色建筑保温墙体结构的制备方法,具体步骤如下:
(1)先以三聚氰胺甲醛树脂和改性纳米二氧化硅为原料,纺丝制成三聚氰胺甲醛树脂纤维;
(2)再将硅藻土、膨胀珍珠岩混合研磨得到混合粉,造粒成球,煅烧,得到预制颗粒;
(3)然后将三聚氰胺甲醛树脂纤维、预制颗粒加入二氧化硅溶胶中,凝胶化,得到凝胶材料;
(4)最后将硅酸盐水泥、聚氨酯类发泡剂、凝胶材料混合均匀,加入水,搅拌混匀,养护,即得所述的保温墙体结构。
优选的,步骤(1)中,以重量份计,所述改性纳米二氧化硅的制备方法如下:先将3~ 5份γ-氨丙基三乙氧基硅烷加入55~60份无水乙醇中,搅拌混匀,接着加入15~20份纳米二氧化硅,300~500W超声波振荡处理30~40分钟,离心取沉淀,得到氨基改性纳米二氧化硅;然后将氨基改性纳米二氧化硅超声波分散于55~60份无水乙醇中,接着加入4~6 份双丙酮丙烯酰胺,35~45℃搅拌反应8~10小时,离心取沉淀,即得改性纳米二氧化硅。
优选的,以重量份计,步骤(1)的具体方法如下:先将70~80份三聚氰胺甲醛树脂、5~6份改性纳米二氧化硅、5~7份十二烷基苯磺酸钠、75~85份水混合均匀,接着在60~65℃条件下,500~600W超声波振荡处理5~7小时,得到纺丝原液,最后将纺丝原液通过喷丝孔进行喷丝,空气中冷却,即得三聚氰胺甲醛树脂纤维。
进一步优选的,喷丝孔直径为0.4~0.6mm。
优选的,以重量份计,步骤(2)的具体方法为:先将20~25份硅藻土、55~60份膨胀珍珠岩混合研磨得到粒径5~10μm的混合粉,接着将混合粉加水造粒成球,球体直径为 0.5~1mm,烘干,转移至回转窑中煅烧,即得预制颗粒。
进一步优选的,煅烧的工艺条件为:1200~1300℃煅烧45~50分钟。
优选的,以重量份计,步骤(3)的具体方法为:先将5~7份三聚氰胺甲醛树脂纤维、8~10份预制颗粒加入120~130份二氧化硅溶胶中,搅拌直至变为凝胶,然后将凝胶依次在蒸馏水、体积浓度50%乙醇溶液、无水乙醇中分别浸泡24小时,干燥,即得凝胶材料。
优选的,步骤(3)中,二氧化硅溶胶的制备方法如下:先将1份正硅酸乙酯和1.1份无水乙醇加入20~30份水中,接着利用质量浓度20~30%硫酸溶液调节pH=2.5,300~500r/min搅拌25~30小时,再利用质量浓度20~22%氨水溶液调节pH=6,即得所述的二氧化硅溶胶。
优选的,步骤(4)中,硅酸盐水泥、聚氨酯类发泡剂、凝胶材料、水的质量比为10:0.8~1:1~2:28~30。
优选的,步骤(4)中,养护条件为:1.5~2MPa蒸压反应釜中养护6~8小时。
利用上述制备方法得到的一种装配式绿色建筑保温墙体结构。
上述一种装配式绿色建筑保温墙体结构的装配方法,具体步骤如下:先将上述保温墙体进行切割,并在建筑物外部墙体上设置龙骨安装架,龙骨穿过龙骨安装架,以实现保温墙体和建筑物外部墙体的连接,然后将保温墙体通过预混砂浆粘结在龙骨上,接着利用塑料铆栓固定,即可完成保温墙体结构的装配;其中,预混砂浆是由以下重量份的组分混合制成的:普通硅酸盐水泥50~60份,石英砂30~40份,聚合物树脂胶粉3~5份,预制颗粒5~8份,水60~65份。
优选的,保温墙体的外侧面设置2~3层燕尾槽结构,且燕尾槽结构的燕尾部分与保温墙体外侧面之间的夹角为40~50°。
优选的,以重量份计,预制颗粒是通过以下方法制备得到的:先将20~25份硅藻土、 55~60份膨胀珍珠岩混合研磨得到粒径5~10μm的混合粉,接着将混合粉加水造粒成球,球体直径为0.5~1mm,烘干,转移至回转窑中煅烧,即得预制颗粒。
进一步优选的,煅烧的工艺条件为:1200~1300℃煅烧45~50分钟。
本发明的有益效果:
本发明先以三聚氰胺甲醛树脂和改性纳米二氧化硅为原料,纺丝制成三聚氰胺甲醛树脂纤维;再将硅藻土、膨胀珍珠岩混合研磨得到混合粉,造粒成球,煅烧,得到预制颗粒;然后将三聚氰胺甲醛树脂纤维、预制颗粒加入二氧化硅溶胶中,凝胶化,得到凝胶材料;最后将硅酸盐水泥、聚氨酯类发泡剂、凝胶材料混合均匀,加入水,搅拌混匀,养护,即得保温墙体结构。该保温墙体结构强度高,保温效果好,适用于装配式绿色建筑。
该保温墙体结构的装配方法简单,先将上述保温墙体进行切割,并在建筑物外部墙体上设置龙骨安装架,龙骨穿过龙骨安装架,以实现保温墙体和建筑物外部墙体的连接,然后将保温墙体通过预混砂浆粘结在龙骨上,接着利用塑料铆栓固定,即可完成保温墙体结构的装配;其中,预混砂浆是由普通硅酸盐水泥、石英砂、聚合物树脂胶粉和预制颗粒混合制成的,预制砂浆的使用可以保证保温墙体结构的装配效果,以发挥其强度和保温效果。
本发明先将纳米二氧化硅利用γ-氨丙基三乙氧基硅烷进行改性处理得到氨基改性纳米二氧化硅,然后将氨基改性纳米二氧化硅与双丙酮丙烯酰胺反应得到改性纳米二氧化硅。改性纳米二氧化硅与三聚氰胺甲醛树脂具有良好的相容性,制成纤维,起到增强作用,提高保温墙体的强度。硅藻土、膨胀珍珠岩制成的预制颗粒孔隙丰富,起到增强作用的同时,与二氧化硅凝胶协同改善产品的保温效果。
具体实施方式
下面结合实施例对本发明进行进一步的阐述,应该说明的是,下述说明仅是为了解释本发明,并不对其内容进行限定。
实施例1
一种装配式绿色建筑保温墙体结构的制备方法,具体步骤如下:
(1)先以三聚氰胺甲醛树脂和改性纳米二氧化硅为原料,纺丝制成三聚氰胺甲醛树脂纤维;
(2)再将硅藻土、膨胀珍珠岩混合研磨得到混合粉,造粒成球,煅烧,得到预制颗粒;
(3)然后将三聚氰胺甲醛树脂纤维、预制颗粒加入二氧化硅溶胶中,凝胶化,得到凝胶材料;
(4)最后将硅酸盐水泥、聚氨酯类发泡剂、凝胶材料混合均匀,加入水,搅拌混匀,养护,即得所述的保温墙体结构。
步骤(1)中,改性纳米二氧化硅的制备方法如下:先将3kgγ-氨丙基三乙氧基硅烷加入60kg无水乙醇中,搅拌混匀,接着加入15kg纳米二氧化硅,500W超声波振荡处理30 分钟,离心取沉淀,得到氨基改性纳米二氧化硅;然后将氨基改性纳米二氧化硅超声波分散于60kg无水乙醇中,接着加入4kg双丙酮丙烯酰胺,45℃搅拌反应8小时,离心取沉淀,即得改性纳米二氧化硅。
步骤(1)的具体方法如下:先将80kg三聚氰胺甲醛树脂、5kg改性纳米二氧化硅、7kg 十二烷基苯磺酸钠、75kg水混合均匀,接着在65℃条件下,500W超声波振荡处理7小时,得到纺丝原液,最后将纺丝原液通过喷丝孔进行喷丝,空气中冷却,即得三聚氰胺甲醛树脂纤维。喷丝孔直径为0.4mm。
步骤(2)的具体方法为:先将25kg硅藻土、55kg膨胀珍珠岩混合研磨得到粒径10μm的混合粉,接着将混合粉加水造粒成球,球体直径为0.5mm,烘干,转移至回转窑中煅烧,即得预制颗粒。
煅烧的工艺条件为:1300℃煅烧45分钟。
步骤(3)的具体方法为:先将7kg三聚氰胺甲醛树脂纤维、8kg预制颗粒加入130kg二氧化硅溶胶中,搅拌直至变为凝胶,然后将凝胶依次在蒸馏水、体积浓度50%乙醇溶液、无水乙醇中分别浸泡24小时,干燥,即得凝胶材料。
步骤(3)中,二氧化硅溶胶的制备方法如下:先将1kg正硅酸乙酯和1.1kg无水乙醇加入20kg水中,接着利用质量浓度30%硫酸溶液调节pH=2.5,300r/min搅拌30小时,再利用质量浓度20%氨水溶液调节pH=6,即得所述的二氧化硅溶胶。
步骤(4)中,硅酸盐水泥、聚氨酯类发泡剂、凝胶材料、水的质量比为10:1:1:30。
步骤(4)中,养护条件为:1.5MPa蒸压反应釜中养护8小时。
一种装配式绿色建筑保温墙体结构的装配方法,具体步骤如下:先将上述保温墙体进行切割,并在建筑物外部墙体上设置龙骨安装架,龙骨穿过龙骨安装架,以实现保温墙体和建筑物外部墙体的连接,然后将保温墙体通过预混砂浆粘结在龙骨上,接着利用塑料铆栓固定,即可完成保温墙体结构的装配;其中,预混砂浆是由以下组分混合制成的:普通硅酸盐水泥50kg,石英砂40kg,聚合物树脂胶粉3kg,预制颗粒8kg,水60kg。
保温墙体的外侧面设置2层燕尾槽结构,且燕尾槽结构的燕尾部分与保温墙体外侧面之间的夹角为50°。
预制颗粒的制备方法如下:先将20kg硅藻土、60kg膨胀珍珠岩混合研磨得到粒径5μ m的混合粉,接着将混合粉加水造粒成球,球体直径为1mm,烘干,转移至回转窑中煅烧,即得预制颗粒。
煅烧的工艺条件为:1200℃煅烧50分钟。
实施例2
一种装配式绿色建筑保温墙体结构的制备方法,具体步骤如下:
(1)先以三聚氰胺甲醛树脂和改性纳米二氧化硅为原料,纺丝制成三聚氰胺甲醛树脂纤维;
(2)再将硅藻土、膨胀珍珠岩混合研磨得到混合粉,造粒成球,煅烧,得到预制颗粒;
(3)然后将三聚氰胺甲醛树脂纤维、预制颗粒加入二氧化硅溶胶中,凝胶化,得到凝胶材料;
(4)最后将硅酸盐水泥、聚氨酯类发泡剂、凝胶材料混合均匀,加入水,搅拌混匀,养护,即得所述的保温墙体结构。
步骤(1)中,改性纳米二氧化硅的制备方法如下:先将5kgγ-氨丙基三乙氧基硅烷加入55kg无水乙醇中,搅拌混匀,接着加入20kg纳米二氧化硅,300W超声波振荡处理40 分钟,离心取沉淀,得到氨基改性纳米二氧化硅;然后将氨基改性纳米二氧化硅超声波分散于55kg无水乙醇中,接着加入6kg双丙酮丙烯酰胺,35℃搅拌反应10小时,离心取沉淀,即得改性纳米二氧化硅。
步骤(1)的具体方法如下:先将70kg三聚氰胺甲醛树脂、6kg改性纳米二氧化硅、5kg 十二烷基苯磺酸钠、85kg水混合均匀,接着在60℃条件下,600W超声波振荡处理5小时,得到纺丝原液,最后将纺丝原液通过喷丝孔进行喷丝,空气中冷却,即得三聚氰胺甲醛树脂纤维。喷丝孔直径为0.6mm。
步骤(2)的具体方法为:先将20kg硅藻土、60kg膨胀珍珠岩混合研磨得到粒径5μm的混合粉,接着将混合粉加水造粒成球,球体直径为1mm,烘干,转移至回转窑中煅烧,即得预制颗粒。
煅烧的工艺条件为:1200℃煅烧50分钟。
步骤(3)的具体方法为:先将5kg三聚氰胺甲醛树脂纤维、10kg预制颗粒加入120kg二氧化硅溶胶中,搅拌直至变为凝胶,然后将凝胶依次在蒸馏水、体积浓度50%乙醇溶液、无水乙醇中分别浸泡24小时,干燥,即得凝胶材料。
步骤(3)中,二氧化硅溶胶的制备方法如下:先将1kg正硅酸乙酯和1.1kg无水乙醇加入30kg水中,接着利用质量浓度20%硫酸溶液调节pH=2.5,500r/min搅拌25小时,再利用质量浓度22%氨水溶液调节pH=6,即得所述的二氧化硅溶胶。
步骤(4)中,硅酸盐水泥、聚氨酯类发泡剂、凝胶材料、水的质量比为10:0.8:2:28。
步骤(4)中,养护条件为:2MPa蒸压反应釜中养护6小时。
一种装配式绿色建筑保温墙体结构的装配方法,具体步骤如下:先将上述保温墙体进行切割,并在建筑物外部墙体上设置龙骨安装架,龙骨穿过龙骨安装架,以实现保温墙体和建筑物外部墙体的连接,然后将保温墙体通过预混砂浆粘结在龙骨上,接着利用塑料铆栓固定,即可完成保温墙体结构的装配;其中,预混砂浆是由以下组分混合制成的:普通硅酸盐水泥60kg,石英砂30kg,聚合物树脂胶粉5kg,预制颗粒5kg,水65kg。
保温墙体的外侧面设置3层燕尾槽结构,且燕尾槽结构的燕尾部分与保温墙体外侧面之间的夹角为40°。
预制颗粒的制备方法如下:先将20kg硅藻土、60kg膨胀珍珠岩混合研磨得到粒径5μ m的混合粉,接着将混合粉加水造粒成球,球体直径为1mm,烘干,转移至回转窑中煅烧,即得预制颗粒。
煅烧的工艺条件为:1200℃煅烧50分钟。
实施例3
一种装配式绿色建筑保温墙体结构的制备方法,具体步骤如下:
(1)先以三聚氰胺甲醛树脂和改性纳米二氧化硅为原料,纺丝制成三聚氰胺甲醛树脂纤维;
(2)再将硅藻土、膨胀珍珠岩混合研磨得到混合粉,造粒成球,煅烧,得到预制颗粒;
(3)然后将三聚氰胺甲醛树脂纤维、预制颗粒加入二氧化硅溶胶中,凝胶化,得到凝胶材料;
(4)最后将硅酸盐水泥、聚氨酯类发泡剂、凝胶材料混合均匀,加入水,搅拌混匀,养护,即得所述的保温墙体结构。
步骤(1)中,改性纳米二氧化硅的制备方法如下:先将4kgγ-氨丙基三乙氧基硅烷加入58kg无水乙醇中,搅拌混匀,接着加入18kg纳米二氧化硅,400W超声波振荡处理35 分钟,离心取沉淀,得到氨基改性纳米二氧化硅;然后将氨基改性纳米二氧化硅超声波分散于58kg无水乙醇中,接着加入5kg双丙酮丙烯酰胺,40℃搅拌反应9小时,离心取沉淀,即得改性纳米二氧化硅。
步骤(1)的具体方法如下:先将75kg三聚氰胺甲醛树脂、5.5kg改性纳米二氧化硅、6kg十二烷基苯磺酸钠、80kg水混合均匀,接着在63℃条件下,600W超声波振荡处理6 小时,得到纺丝原液,最后将纺丝原液通过喷丝孔进行喷丝,空气中冷却,即得三聚氰胺甲醛树脂纤维。喷丝孔直径为0.5mm。
步骤(2)的具体方法为:先将22kg硅藻土、58kg膨胀珍珠岩混合研磨得到粒径8μm的混合粉,接着将混合粉加水造粒成球,球体直径为0.8mm,烘干,转移至回转窑中煅烧,即得预制颗粒。
煅烧的工艺条件为:1250℃煅烧48分钟。
步骤(3)的具体方法为:先将6kg三聚氰胺甲醛树脂纤维、9kg预制颗粒加入125kg二氧化硅溶胶中,搅拌直至变为凝胶,然后将凝胶依次在蒸馏水、体积浓度50%乙醇溶液、无水乙醇中分别浸泡24小时,干燥,即得凝胶材料。
步骤(3)中,二氧化硅溶胶的制备方法如下:先将1kg正硅酸乙酯和1.1kg无水乙醇加入25kg水中,接着利用质量浓度25%硫酸溶液调节pH=2.5,400r/min搅拌28小时,再利用质量浓度21%氨水溶液调节pH=6,即得所述的二氧化硅溶胶。
步骤(4)中,硅酸盐水泥、聚氨酯类发泡剂、凝胶材料、水的质量比为10:0.9:1.5:29。
步骤(4)中,养护条件为:2MPa蒸压反应釜中养护7小时。
一种装配式绿色建筑保温墙体结构的装配方法,具体步骤如下:先将上述保温墙体进行切割,并在建筑物外部墙体上设置龙骨安装架,龙骨穿过龙骨安装架,以实现保温墙体和建筑物外部墙体的连接,然后将保温墙体通过预混砂浆粘结在龙骨上,接着利用塑料铆栓固定,即可完成保温墙体结构的装配;其中,预混砂浆是由以下组分混合制成的:普通硅酸盐水泥55kg,石英砂35kg,聚合物树脂胶粉4kg,预制颗粒7kg,水62kg。
保温墙体的外侧面设置3层燕尾槽结构,且燕尾槽结构的燕尾部分与保温墙体外侧面之间的夹角为45°。
预制颗粒的制备方法如下:先将22kg硅藻土、58kg膨胀珍珠岩混合研磨得到粒径8μ m的混合粉,接着将混合粉加水造粒成球,球体直径为0.8mm,烘干,转移至回转窑中煅烧,即得预制颗粒。
煅烧的工艺条件为:1250℃煅烧48分钟。
对比例1
一种装配式绿色建筑保温墙体结构的制备方法,具体步骤如下:
(1)先以三聚氰胺甲醛树脂和纳米二氧化硅为原料,纺丝制成三聚氰胺甲醛树脂纤维;
(2)再将硅藻土、膨胀珍珠岩混合研磨得到混合粉,造粒成球,煅烧,得到预制颗粒;
(3)然后将三聚氰胺甲醛树脂纤维、预制颗粒加入二氧化硅溶胶中,凝胶化,得到凝胶材料;
(4)最后将硅酸盐水泥、聚氨酯类发泡剂、凝胶材料混合均匀,加入水,搅拌混匀,养护,即得所述的保温墙体结构。
步骤(1)的具体方法如下:先将80kg三聚氰胺甲醛树脂、5kg纳米二氧化硅、7kg十二烷基苯磺酸钠、75kg水混合均匀,接着在65℃条件下,500W超声波振荡处理7小时,得到纺丝原液,最后将纺丝原液通过喷丝孔进行喷丝,空气中冷却,即得三聚氰胺甲醛树脂纤维。喷丝孔直径为0.4mm。
步骤(2)的具体方法为:先将25kg硅藻土、55kg膨胀珍珠岩混合研磨得到粒径10μm的混合粉,接着将混合粉加水造粒成球,球体直径为0.5mm,烘干,转移至回转窑中煅烧,即得预制颗粒。
煅烧的工艺条件为:1300℃煅烧45分钟。
步骤(3)的具体方法为:先将7kg三聚氰胺甲醛树脂纤维、8kg预制颗粒加入130kg二氧化硅溶胶中,搅拌直至变为凝胶,然后将凝胶依次在蒸馏水、体积浓度50%乙醇溶液、无水乙醇中分别浸泡24小时,干燥,即得凝胶材料。
步骤(3)中,二氧化硅溶胶的制备方法如下:先将1kg正硅酸乙酯和1.1kg无水乙醇加入20kg水中,接着利用质量浓度30%硫酸溶液调节pH=2.5,300r/min搅拌30小时,再利用质量浓度20%氨水溶液调节pH=6,即得所述的二氧化硅溶胶。
步骤(4)中,硅酸盐水泥、聚氨酯类发泡剂、凝胶材料、水的质量比为10:1:1:30。
步骤(4)中,养护条件为:1.5MPa蒸压反应釜中养护8小时。
一种装配式绿色建筑保温墙体结构的装配方法,具体步骤如下:先将上述保温墙体进行切割,并在建筑物外部墙体上设置龙骨安装架,龙骨穿过龙骨安装架,以实现保温墙体和建筑物外部墙体的连接,然后将保温墙体通过预混砂浆粘结在龙骨上,接着利用塑料铆栓固定,即可完成保温墙体结构的装配;其中,预混砂浆是由以下组分混合制成的:普通硅酸盐水泥50kg,石英砂40kg,聚合物树脂胶粉3kg,预制颗粒8kg,水60kg。
保温墙体的外侧面设置2层燕尾槽结构,且燕尾槽结构的燕尾部分与保温墙体外侧面之间的夹角为50°。
预制颗粒的制备方法如下:先将20kg硅藻土、60kg膨胀珍珠岩混合研磨得到粒径5μ m的混合粉,接着将混合粉加水造粒成球,球体直径为1mm,烘干,转移至回转窑中煅烧,即得预制颗粒。
煅烧的工艺条件为:1200℃煅烧50分钟。
对比例2
一种装配式绿色建筑保温墙体结构的制备方法,具体步骤如下:
(1)先以三聚氰胺甲醛树脂和改性纳米二氧化硅为原料,纺丝制成三聚氰胺甲醛树脂纤维;
(2)然后将三聚氰胺甲醛树脂纤维加入二氧化硅溶胶中,凝胶化,得到凝胶材料;
(3)最后将硅酸盐水泥、聚氨酯类发泡剂、凝胶材料混合均匀,加入水,搅拌混匀,养护,即得所述的保温墙体结构。
步骤(1)中,改性纳米二氧化硅的制备方法如下:先将3kgγ-氨丙基三乙氧基硅烷加入60kg无水乙醇中,搅拌混匀,接着加入15kg纳米二氧化硅,500W超声波振荡处理30 分钟,离心取沉淀,得到氨基改性纳米二氧化硅;然后将氨基改性纳米二氧化硅超声波分散于60kg无水乙醇中,接着加入4kg双丙酮丙烯酰胺,45℃搅拌反应8小时,离心取沉淀,即得改性纳米二氧化硅。
步骤(1)的具体方法如下:先将80kg三聚氰胺甲醛树脂、5kg改性纳米二氧化硅、7kg 十二烷基苯磺酸钠、75kg水混合均匀,接着在65℃条件下,500W超声波振荡处理7小时,得到纺丝原液,最后将纺丝原液通过喷丝孔进行喷丝,空气中冷却,即得三聚氰胺甲醛树脂纤维。喷丝孔直径为0.4mm。
步骤(2)的具体方法为:先将7kg三聚氰胺甲醛树脂纤维加入130kg二氧化硅溶胶中,搅拌直至变为凝胶,然后将凝胶依次在蒸馏水、体积浓度50%乙醇溶液、无水乙醇中分别浸泡24小时,干燥,即得凝胶材料。
步骤(2)中,二氧化硅溶胶的制备方法如下:先将1kg正硅酸乙酯和1.1kg无水乙醇加入20kg水中,接着利用质量浓度30%硫酸溶液调节pH=2.5,300r/min搅拌30小时,再利用质量浓度20%氨水溶液调节pH=6,即得所述的二氧化硅溶胶。
步骤(3)中,硅酸盐水泥、聚氨酯类发泡剂、凝胶材料、水的质量比为10:1:1:30。
步骤(3)中,养护条件为:1.5MPa蒸压反应釜中养护8小时。
一种装配式绿色建筑保温墙体结构的装配方法,具体步骤如下:先将上述保温墙体进行切割,并在建筑物外部墙体上设置龙骨安装架,龙骨穿过龙骨安装架,以实现保温墙体和建筑物外部墙体的连接,然后将保温墙体通过预混砂浆粘结在龙骨上,接着利用塑料铆栓固定,即可完成保温墙体结构的装配;其中,预混砂浆是由以下组分混合制成的:普通硅酸盐水泥50kg,石英砂40kg,聚合物树脂胶粉3kg,水60kg。
保温墙体的外侧面设置2层燕尾槽结构,且燕尾槽结构的燕尾部分与保温墙体外侧面之间的夹角为50°。
试验例
对实施例1~3和对比例1、2所得保温墙体结构进行性能测试,结果见表1。
其中,保温性能参考GB/T 10294-2008,强度测定参考GB/T 50081-2019。
表1.性能测试结果
导热系数(W/(m·K)) | 抗压强度(MPa) | |
实施例1 | 0.011 | 8.3 |
实施例2 | 0.012 | 8.4 |
实施例3 | 0.009 | 8.6 |
对比例1 | 0.011 | 7.4 |
对比例2 | 0.158 | 6.3 |
由表1可知,实施例1~3所得保温墙体结构的导热系数低,抗压强度高,说明强度高,保温效果好。
对比例1用纳米二氧化硅替换改性纳米二氧化硅,对比例2略去预制颗粒,所得保温墙体结构的强度均明显变差,对比例2的保温效果变差,说明改性纳米二氧化硅在三聚氰胺甲醛树脂纤维中的加入与预制颗粒协同作用,改善产品的强度,预制颗粒与二氧化硅凝胶协同改善产品的保温效果。
上述虽然对本发明的具体实施方式进行了描述,但并非对本发明保护范围的限制,在本发明的技术方案的基础上,本领域技术人员不需要付出创造性劳动即可做出的各种修改或变形仍在本发明的保护范围以内。
Claims (10)
1.一种装配式绿色建筑保温墙体结构的制备方法,其特征在于,具体步骤如下:
(1)先以三聚氰胺甲醛树脂和改性纳米二氧化硅为原料,纺丝制成三聚氰胺甲醛树脂纤维;
(2)再将硅藻土、膨胀珍珠岩混合研磨得到混合粉,造粒成球,煅烧,得到预制颗粒;
(3)然后将三聚氰胺甲醛树脂纤维、预制颗粒加入二氧化硅溶胶中,凝胶化,得到凝胶材料;
(4)最后将硅酸盐水泥、聚氨酯类发泡剂、凝胶材料混合均匀,加入水,搅拌混匀,养护,即得所述的保温墙体结构。
2.根据权利要求1所述的制备方法,其特征在于,步骤(1)中,以重量份计,所述改性纳米二氧化硅的制备方法如下:先将3~5份γ-氨丙基三乙氧基硅烷加入55~60份无水乙醇中,搅拌混匀,接着加入15~20份纳米二氧化硅,300~500W超声波振荡处理30~40分钟,离心取沉淀,得到氨基改性纳米二氧化硅;然后将氨基改性纳米二氧化硅超声波分散于55~60份无水乙醇中,接着加入4~6份双丙酮丙烯酰胺,35~45℃搅拌反应8~10小时,离心取沉淀,即得改性纳米二氧化硅。
3.根据权利要求1所述的制备方法,其特征在于,以重量份计,步骤(1)的具体方法如下:先将70~80份三聚氰胺甲醛树脂、5~6份改性纳米二氧化硅、5~7份十二烷基苯磺酸钠、75~85份水混合均匀,接着在60~65℃条件下,500~600W超声波振荡处理5~7小时,得到纺丝原液,最后将纺丝原液通过喷丝孔进行喷丝,空气中冷却,即得三聚氰胺甲醛树脂纤维。
4.根据权利要求1所述的制备方法,其特征在于,以重量份计,步骤(2)的具体方法为:先将20~25份硅藻土、55~60份膨胀珍珠岩混合研磨得到粒径5~10μm的混合粉,接着将混合粉加水造粒成球,球体直径为0.5~1mm,烘干,转移至回转窑中煅烧,即得预制颗粒。
5.根据权利要求1所述的制备方法,其特征在于,以重量份计,步骤(3)的具体方法为:先将5~7份三聚氰胺甲醛树脂纤维、8~10份预制颗粒加入120~130份二氧化硅溶胶中,搅拌直至变为凝胶,然后将凝胶依次在蒸馏水、体积浓度50%乙醇溶液、无水乙醇中分别浸泡24小时,干燥,即得凝胶材料。
6.根据权利要求1所述的制备方法,其特征在于,步骤(3)中,二氧化硅溶胶的制备方法如下:先将1份正硅酸乙酯和1.1份无水乙醇加入20~30份水中,接着利用质量浓度20~30%硫酸溶液调节pH=2.5,300~500r/min搅拌25~30小时,再利用质量浓度20~22%氨水溶液调节pH=6,即得所述的二氧化硅溶胶。
7.根据权利要求1所述的制备方法,其特征在于,步骤(4)中,硅酸盐水泥、聚氨酯类发泡剂、凝胶材料、水的质量比为10:0.8~1:1~2:28~30。
8.根据权利要求1所述的制备方法,其特征在于,步骤(4)中,养护条件为:1.5~2MPa蒸压反应釜中养护6~8小时。
9.利用权利要求1~8中任一项所述制备方法得到的一种装配式绿色建筑保温墙体结构。
10.权利要求9所述一种装配式绿色建筑保温墙体结构的装配方法,其特征在于,具体步骤如下:先将上述保温墙体进行切割,并在建筑物外部墙体上设置龙骨安装架,龙骨穿过龙骨安装架,以实现保温墙体和建筑物外部墙体的连接,然后将保温墙体通过预混砂浆粘结在龙骨上,接着利用塑料铆栓固定,即可完成保温墙体结构的装配;其中,预混砂浆是由以下重量份的组分混合制成的:普通硅酸盐水泥50~60份,石英砂30~40份,聚合物树脂胶粉3~5份,预制颗粒5~8份,水60~65份。