CN113135558A - Photothermal material based on porous carbon spheres and preparation method thereof - Google Patents

Photothermal material based on porous carbon spheres and preparation method thereof Download PDF

Info

Publication number
CN113135558A
CN113135558A CN202110419575.7A CN202110419575A CN113135558A CN 113135558 A CN113135558 A CN 113135558A CN 202110419575 A CN202110419575 A CN 202110419575A CN 113135558 A CN113135558 A CN 113135558A
Authority
CN
China
Prior art keywords
porous carbon
carbon sphere
metal
photo
sphere
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN202110419575.7A
Other languages
Chinese (zh)
Other versions
CN113135558B (en
Inventor
庞靖怡
刘心娟
张希龙
黎晋良
潘丽坤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Jiliang University
Original Assignee
China Jiliang University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China Jiliang University filed Critical China Jiliang University
Priority to CN202110419575.7A priority Critical patent/CN113135558B/en
Publication of CN113135558A publication Critical patent/CN113135558A/en
Application granted granted Critical
Publication of CN113135558B publication Critical patent/CN113135558B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a porous carbon sphere-based photo-thermal material and a preparation method thereof, wherein the material is in a micron-sized porous carbon sphere structure, and the structure is assembled by carbon nano-particles; the diameter of the carbon sphere is 2-5 mu m, and the diameter of the carbon nano-particle is 100-200 nm. In addition, the porous carbon spheres may also be non-metal (e.g., N/S) or metal (e.g., Au/Ag/Cu/Al) or metal-non-metal co-doped porous carbon spheres. The preparation method comprises the steps of preparing a carbon sphere photo-thermal material precursor by using a carbon source, a template material and concentrated hydrochloric acid as raw materials, and performing heat treatment and template removal to obtain the carbon sphere photo-thermal material precursor. The porous carbon spheres have excellent photo-thermal conversion efficiency, and can be used in the fields of seawater desalination, sewage purification, heavy metal recovery, sterilization and the like. The preparation method is simple, mild in condition, simple to operate, low in cost and suitable for large-scale production.

Description

Photothermal material based on porous carbon spheres and preparation method thereof
Technical Field
The invention belongs to the field of photo-thermal materials, and particularly relates to a photo-thermal material based on porous carbon spheres and a preparation method thereof.
Background
Water is one of the basic substances which depend on the survival and development of human society, and is a source of all lives and civilization. However, as the world economy is continuously developed, the population is continuously increased, the environment is continuously deteriorated, and the situation of water resources, particularly fresh water resources, is increasingly severe, which seriously affects the life of human beings. The desalination and purification of seawater can effectively increase desalination resources, is one of effective methods for solving the shortage and pollution of fresh water resources, and draws wide attention.
Solar energy is an important renewable energy source, and has the advantages of cleanness, no pollution, no damage to earth heat balance, abundant resources and the like. Therefore, solar energy is a new energy source, and a technology for desalinating seawater by using the solar energy is developed and receives close attention from various fields. The efficiency of the traditional solar-driven seawater evaporation technology is usually 30-45%. But the solar interface photo-thermal evaporation effect can reach more than 90 percent at most. The photo-thermal conversion efficiency of the solar photo-thermal system is determined by the solar photo-thermal material, the hydrophilic porous material for transporting moisture and the thermal insulation material for blocking heat transfer. Therefore, designing a photothermal conversion material with high efficiency solar energy utilization and moisture evaporation interface properties is the key in this field.
Commonly used light absorbing materials are carbon materials, noble metal nanoparticles, semiconductor structures, etc. Although some progress has been made in the field of solar seawater desalination, the problems of poor hydrophilicity of photo-thermal materials, low photo-thermal conversion efficiency, expensive raw materials, complex preparation method, high cost and the like still exist at present, and the practical application of the technology is limited. The photo-thermal material with high efficiency, simple preparation and low cost is still a very urgent problem.
The porous carbon sphere material obtained by the invention can be used as a potential photothermal material due to the characteristics of unique pore structure, adjustable pore diameter, better thermal conductivity and light absorption performance, high stability and the like. The synergistic effect among the multiple materials can show the performance superior to that of a single component, and further the photo-thermal conversion efficiency is improved. The nonmetal, metal or nonmetal and metal codoping effectively inhibits the compounding of charges due to the rapid transfer of electrons, and meanwhile, the plasma metal has a strong light absorption enhancement effect due to the local surface plasmon resonance characteristic, so that the photo-thermal conversion efficiency of the porous carbon ball can be greatly improved. Therefore, the invention provides a high-efficiency photo-thermal material based on porous carbon spheres or metal and nonmetal co-doped porous carbon spheres. And provides a simple method for preparing the porous carbon spheres, which is beneficial to the deep research, popularization and application of the porous carbon spheres.
Disclosure of Invention
In order to solve the problems, the invention provides a porous carbon sphere-based photo-thermal material and a preparation method thereof. The porous carbon sphere material has good photo-thermal conversion efficiency, and can be used in the fields of seawater desalination, sewage treatment, sterilization and the like. The preparation method adopted by the invention has the advantages of simple preparation process, convenient operation, low cost and the like, and is suitable for industrial production.
In order to achieve the technical purpose, the invention adopts the technical scheme that the photothermal material is based on porous carbon spheres, the material is a micron-sized porous carbon sphere structure, and the structure is formed by assembling carbon nano particles.
Furthermore, the diameter of the carbon sphere is 2-5 μm, and the diameter of the carbon nano-particle is 100-200 nm.
Further, the photo-thermal material is a doped carbon sphere structure, the doping is non-metal doping, metal doping or metal-non-metal co-doping, and the metal refers to metal with a plasma effect.
Further, the nonmetal comprises N or S, and the metal comprises Au, Ag, Cu or Al.
The invention also discloses a preparation method of the photo-thermal material based on the carbon spheres, which comprises the following steps:
firstly, dispersing a carbon source, a template material and concentrated hydrochloric acid (usually 37 mass percent) in deionized water, performing ultrasonic treatment and stirring at normal temperature to obtain a uniform mixed solution; transferring the mixed solution into a hydrothermal reaction kettle, reacting for 6-12 h at the constant temperature of 120-180 ℃, centrifuging, cleaning, and freeze-drying for 30-50 h at the temperature of-30 to-60 ℃ to obtain a carbon sphere photo-thermal material precursor;
secondly, placing the carbon sphere photo-thermal material precursor into a tube furnace, annealing for 2-4 hours at 400-800 ℃ under the argon atmosphere, wherein the heating rate is 2-5 ℃/min; then annealing at 200-400 ℃ for 2-4 hours in air atmosphere, wherein the heating rate is 2-5 ℃/min; obtaining carbon spheres with templates;
and thirdly, removing the template from the obtained carbon spheres with the template, cleaning and drying to obtain the photo-thermal material based on the carbon spheres.
Further, a metal precursor is added into the mixed solution in the first step, and a metal-doped carbon sphere photo-thermal material precursor is obtained after the first-step hydrothermal reaction, wherein the metal precursor is chloroauric acid, silver nitrate, copper nitrate or aluminum nitrate, and the mass ratio of metal in the precursor is 5% -10%.
And further, in the second step, the argon atmosphere is replaced by ammonia gas atmosphere for treatment, and the other treatment steps are not changed, so that the N-doped carbon spheres with the templates are obtained.
And further, after the third step is finished, mixing the obtained photo-thermal material based on the carbon spheres with sulfur, putting the mixture into a tubular furnace, and carrying out annealing treatment to obtain the S-doped carbon sphere photo-thermal material.
Further, in the first step, the template material is Na2MoO3·2H2O, the template in the carbon ball with the template is MoO3(ii) a The carbon source is at least one of sucrose, glucose and oatmeal.
Furthermore, in the mixed solution in the first step, the concentration of the template material is 0.002-0.004 mol/L, the concentration of the carbon source is 0.02-0.05 mol/L, and the volume ratio of hydrochloric acid is 0.03-0.08.
The porous carbon sphere photothermal material provided by the invention has high-efficiency light evaporation efficiency and photothermal conversion efficiency, shows excellent photothermal performance in seawater desalination, sewage treatment and solution purification, and is a potential photothermal material.
Specifically, the preparation method of the porous carbon sphere-based photothermal material of the invention can adopt the following steps:
in the first step, 0.72g of Na is added2MoO4And 5.89g of glucose are dispersed in 57.5ml of deionized water, and are subjected to ultrasonic dispersion and magnetic stirring at normal temperature to obtain a uniform solution A; dripping 2.5ml of concentrated hydrochloric acid into the solution A, and magnetically stirring at normal temperature to obtain a uniform solution B; and then transferring the mixed solution B into a hydrothermal reaction kettle, reacting for 6h at the constant temperature of 180 ℃, cleaning, and freeze-drying for 35h at the temperature of 50 ℃ below zero to obtain the carbon sphere photo-thermal material precursor.
Secondly, placing the obtained carbon sphere photo-thermal material precursor into a tube furnace, and annealing at 800 ℃ for 2 hours under the argon atmosphere at the heating rate of 5 ℃/min; then annealing for 2 hours at 300 ℃ in air atmosphere, wherein the heating rate is 1 ℃/min; to obtain a band MoO3The porous carbon spheres of (1);
thirdly, the obtained belt is carried with MoO3The porous carbon spheres are dispersed in ammonia solution, magnetically stirred for 12 hours, and etched to remove MoO3And cleaning and drying to obtain the porous carbon sphere photo-thermal material.
Or, in the first step, chloroauric acid, silver nitrate, copper nitrate or aluminum nitrate are dispersed in the mixed solution B, and after hydrothermal reaction, MoO is removed by heat treatment and etching3And obtaining the plasma metal Au/Ag/Cu/Al doped porous carbon sphere photo-thermal material.
Or in the second step, the obtained carbon sphere photo-thermal material precursor is placed into a tube furnace, and MoO is removed through heat treatment and etching in the ammonia atmosphere3And obtaining the N-doped porous carbon spheres.
Or, in the third step, mixing the obtained porous carbon sphere photo-thermal material with sulfur, placing the mixture into a tubular furnace, and annealing to obtain the S-doped porous carbon sphere photo-thermal material.
The preparation method of the invention can prepare various products in one method by adjusting template materials (such as Na)2MoO4) Use ofThe porous shape of the product is controlled by the amount to obtain porous carbon spheres or doped porous carbon spheres so as to meet different requirements. The preparation method is simple, the conditions are mild, the operation is convenient, the cost is low, and the prepared material has high-efficiency light evaporation efficiency and light-heat conversion efficiency and is suitable for industrial production and popularization.
Drawings
FIG. 1 is a scanning electron micrograph of porous carbon spheres synthesized in example 1(a) and example 2(b) of the present invention.
FIG. 2 is an X-ray diffraction pattern of the porous carbon spheres synthesized in example 1 of the present invention.
Fig. 3 is a graph showing the change in the quality of water under solar irradiation of the porous carbon spheres synthesized in examples 1 to 5 of the present invention.
FIG. 4 is a graph showing the evaporation rate of the porous carbon spheres synthesized in examples 1 to 5 of the present invention under solar irradiation.
Fig. 5 is a graph showing cycle performance of the porous carbon spheres synthesized in example 2 of the present invention.
FIG. 6 is a scanning electron micrograph (a) of a product made without the addition of a template material and its photothermal properties (b) with a variety of different carbon materials.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention more apparent, the technical solutions of the present invention are further described below with reference to specific embodiments. It should be understood that these examples are for illustrative purposes only and are not intended to limit the scope of the present invention. Furthermore, it should be understood that various changes or modifications can be made by those skilled in the art after reading the disclosure of the present invention, and such equivalents also fall within the scope of the invention.
Example 1
0.54g of Na2MoO4And 5.89g of glucose are dispersed in 57.5ml of deionized water, and are subjected to ultrasonic dispersion and magnetic stirring at normal temperature to obtain a uniform solution A; dripping 2.5ml of concentrated hydrochloric acid into the solution A, and magnetically stirring at normal temperature to obtain a uniform solution B; and then transferring the mixed solution B into a hydrothermal reaction kettle, reacting for 6h at the constant temperature of 180 ℃, cleaning, and freeze-drying for 35h at the temperature of 50 ℃ below zero to obtain the carbon sphere photo-thermal material precursor.
Putting the obtained carbon sphere photo-thermal material precursor into a tube furnace, annealing for 2 hours at 800 ℃ under the argon atmosphere, wherein the heating rate is 5 ℃/min; then annealing for 2 hours at 300 ℃ in air atmosphere, wherein the heating rate is 1 ℃/min; to obtain a band MoO3The porous carbon spheres of (1); subsequently, the resulting tape was MoO3The porous carbon spheres are dispersed in ammonia solution, magnetically stirred for 12 hours, and etched to remove MoO3And cleaning and drying to obtain the porous carbon sphere photo-thermal material.
The test method is as follows: and dispersing the prepared porous carbon spheres in water, and preparing the porous carbon sphere-PVDF film by adopting a vacuum filtration method. The film is placed on a polytetrafluoroethylene bottle mouth foam substrate filled with 50ml of water, the thickness of the foam is 1cm, the foam is parallel to the bottle mouth, a xenon lamp is used for simulating the irradiation of 1 piece of sunlight, the mass change of the water is accurately observed through a precise electronic balance, and the mass change is recorded by a related instrument.
Example 2
0.72g of Na2MoO4And 5.89g of glucose are dispersed in 57.5ml of deionized water, and are subjected to ultrasonic dispersion and magnetic stirring at normal temperature to obtain a uniform solution A; dripping 2.5ml of concentrated hydrochloric acid into the solution A, and magnetically stirring at normal temperature to obtain a uniform solution B; and then transferring the mixed solution B into a hydrothermal reaction kettle, reacting for 6h at the constant temperature of 180 ℃, cleaning, and freeze-drying for 35h at the temperature of 50 ℃ below zero to obtain the carbon sphere photo-thermal material precursor.
Putting the obtained carbon sphere photo-thermal material precursor into a tube furnace, annealing for 2 hours at 800 ℃ under the argon atmosphere, wherein the heating rate is 5 ℃/min; then annealing for 2 hours at 300 ℃ in air atmosphere, wherein the heating rate is 1 ℃/min; to obtain a band MoO3The porous carbon spheres of (1); subsequently, the resulting tape was MoO3The porous carbon spheres are dispersed in ammonia solution, magnetically stirred for 12 hours, and etched to remove MoO3And cleaning and drying to obtain the porous carbon sphere photo-thermal material.
The porous carbon spheres prepared in this example were tested for evaporation efficiency of pure water and seawater using the test method described in example 1.
Example 3
0.54g of Na2MoO4And 5.89Dispersing glucose in 57.5ml of deionized water, performing ultrasonic dispersion, and magnetically stirring at normal temperature to obtain a uniform solution A; dripping 2.5ml of concentrated hydrochloric acid into the solution A, and magnetically stirring at normal temperature to obtain a uniform solution B; and then transferring the mixed solution B into a hydrothermal reaction kettle, reacting for 6h at the constant temperature of 180 ℃, cleaning, and freeze-drying for 35h at the temperature of 50 ℃ below zero to obtain the carbon sphere photo-thermal material precursor.
Putting the obtained carbon sphere photo-thermal material precursor into a tube furnace, annealing for 2 hours at 800 ℃ in an ammonia atmosphere, wherein the heating rate is 5 ℃/min; then annealing for 2 hours at 300 ℃ in air atmosphere, wherein the heating rate is 1 ℃/min; to obtain a band MoO3The N-doped porous carbon spheres of (1); subsequently, the resulting tape was MoO3Dispersing the N-doped porous carbon spheres in an ammonia solution, magnetically stirring for 12 hours, and etching to remove MoO3And cleaning and drying to obtain the N-doped porous carbon sphere photo-thermal material.
The porous carbon spheres prepared in this example were tested for evaporation efficiency of pure water and seawater using the test method described in example 1.
Example 4
0.54g of Na2MoO45.89g glucose and 20mg Cu (NO)3)2Dispersing in 57.5ml deionized water, performing ultrasonic dispersion, and magnetically stirring at normal temperature to obtain a uniform solution A; dripping 2.5ml of concentrated hydrochloric acid into the solution A, and magnetically stirring at normal temperature to obtain a uniform solution B; and then transferring the mixed solution B into a hydrothermal reaction kettle, reacting for 6h at a constant temperature of 180 ℃, cleaning, and freeze-drying for 35h at a temperature of-50 ℃ to obtain the Cu-doped carbon sphere photo-thermal material precursor.
Putting the obtained Cu-doped carbon sphere photo-thermal material precursor into a tube furnace, and annealing at 800 ℃ for 2 hours in an ammonia atmosphere at the heating rate of 5 ℃/min; then annealing for 2 hours at 300 ℃ in air atmosphere, wherein the heating rate is 1 ℃/min; to obtain a band MoO3The N/Cu co-doped porous carbon spheres; subsequently, the resulting tape was MoO3Dispersing the N/Cu doped porous carbon spheres in an ammonia solution, magnetically stirring for 12 hours, and etching to remove MoO3And cleaning and drying to obtain the N/Cu doped porous carbon sphere photo-thermal material.
The porous carbon spheres prepared in this example were tested for evaporation efficiency of pure water and seawater using the test method described in example 1.
Fig. 1(a) is a scanning electron micrograph of the porous carbon sphere synthesized in example 1. As can be seen from the figure, the sample has a spherical porous carbon structure, relatively uniform surface roughness and particle size distribution, and an average diameter of about 3 μm. The porous carbon spheres are assembled by carbon nano-particles, and the diameter of the carbon nano-particles is about 100 nm.
FIG. 1(b) is a scanning electron micrograph of the porous carbon sphere synthesized in example 2. As can be seen from the figure, the sample has a spherical porous carbon structure, a rough surface, a relatively uniform particle size distribution and an average diameter of about 4 μm. The porous carbon sphere is assembled by carbon nano-particles, and the diameter of the carbon nano-particles is about 200 nm. The surface roughness was increased and the diameter was enlarged as compared with the porous carbon spheres obtained in example 1.
Fig. 2 is an X-ray diffraction pattern of the porous carbon sphere synthesized in example 1. Different Na2MoO4The X-ray diffraction patterns of the content-synthesized porous carbon spheres are similar, so that the X-ray patterns of other porous carbon spheres are not given here. In an X-ray diffraction pattern, two broadened diffraction peaks of about 22 ° and 43 ° correspond to (002) and (100) planes of a graphite-based structure, respectively, and are characteristic of a typical disordered carbon material.
FIG. 3 is a graph showing the change in water quality under solar irradiation with the luminescent material of the present invention. Wherein a, b, c and d represent the samples synthesized in example 1, example 2, example 3 and example 4, respectively. As can be seen from the figure, the non-metal N-doped porous carbon spheres exhibited superior photothermal conversion efficiency than the porous carbon spheres under solar irradiation. Meanwhile, the N and Cu co-doped porous carbon spheres exhibit more excellent photo-thermal conversion efficiency than pure porous carbon spheres.
FIG. 4 is a graph showing the water evaporation rate under solar irradiation using the luminescent material of the present invention. Under 1 sun irradiation, the evaporation rate of the N and Cu co-doped porous carbon spheres reaches 1.33kg m-2h-1And the evaporation efficiency reaches 91.6%, excellent photo-thermal conversion performance is shown, a high-efficiency photo-thermal conversion effect is achieved, and photo-evaporation water is realized.
Fig. 5 shows the cyclicity of photothermal evaporation of water under solar irradiation for the porous carbon sphere photothermal material synthesized in example 2. As can be seen from the figure, the evaporation efficiency of the prepared porous carbon sphere photo-thermal material is basically not changed in the 5-cycle application process, which shows that the prepared porous carbon sphere photo-thermal material has good cycle stability.
The values of the surface temperature, evaporation rate and evaporation efficiency of the sample film under 1 sun exposure for the samples synthesized in examples 1 to 4 are given in tables 1 and 2. As can be seen from the table, the N and Cu co-doped porous carbon spheres show excellent photo-thermal conversion performance, achieve high-efficiency photo-thermal conversion effect, and can realize photo-evaporation of water.
In addition, for comparison, no Na was added2MoO4Then, the carbon spheres were prepared by the preparation method of example 1 of the present invention, and the photothermal properties of the carbon spheres were tested by the test method described in example 1. In addition, the photo-thermal properties of other carbon materials such as carbon tubes, graphene, graphite, and the like were also compared, see fig. 6. As can be seen from FIG. 6(a), Na was not added2MoO4In the process, the synthesized sample is of a spherical carbon structure, the surface is smooth, the particle size distribution is relatively uniform, and the average diameter is about 4-5 microns. However, in the presence of Na2MoO4Thereafter, the carbon spheres become rough surfaces, forming porous carbon spheres, thereby changing the light absorption properties of the carbon spheres. According to the experimental results of evaporation of pure water by different carbon materials, the porous carbon spheres prepared by the method have excellent photo-thermal evaporation performance.
Therefore, the porous carbon spheres and the doped porous carbon spheres of the invention are used as a photo-thermal material, show excellent photo-evaporation efficiency and photo-thermal conversion efficiency, and can be used in the fields of seawater desalination, sewage treatment, sterilization and the like. The preparation method of the invention has the advantages of easiness, mild reaction conditions, convenient operation and low cost, and is suitable for large-scale production.
The invention can be implemented in other ways than the embodiments described above, and any obvious alternatives are within the scope of the invention without departing from the invention.
TABLE 1 surface temperature of photothermal materials under solar radiation and Total enthalpy during evaporation
Figure BDA0003027370630000111
TABLE 2 Evaporation Rate and Evaporation efficiency of photothermal Material under solar radiation
Figure BDA0003027370630000112

Claims (9)

1. The porous carbon sphere-based photo-thermal material is characterized in that the material is a micron-sized porous carbon sphere structure, and the structure is formed by assembling carbon nano-particles; the diameter of the carbon sphere is 2-5 mu m, and the diameter of the carbon nano-particle is 100-200 nm.
2. The porous carbon sphere based photothermal material of claim 1 wherein the photothermal material is a doped carbon sphere structure, the doping is non-metal doping, metal doping or metal-non-metal co-doping, and the metal is a metal with a plasma effect.
3. The porous carbon sphere-based photothermal material of claim 1 wherein said nonmetal comprises N or S and said metal comprises Au, Ag, Cu or Al.
4. The method for preparing a porous carbon sphere-based photothermal material of claim 1, comprising the steps of:
dispersing a carbon source, a template material and concentrated hydrochloric acid in deionized water, performing ultrasonic treatment and stirring at normal temperature to obtain a uniform mixed solution; transferring the mixed solution into a hydrothermal reaction kettle, reacting for 6-12 h at the constant temperature of 120-180 ℃, centrifuging, cleaning, and freeze-drying for 30-50 h at the temperature of-30 to-60 ℃ to obtain a carbon sphere photo-thermal material precursor;
secondly, placing the carbon sphere photo-thermal material precursor into a tube furnace, annealing for 2-4 hours at 400-800 ℃ under the argon atmosphere, wherein the heating rate is 2-5 ℃/min; then annealing at 200-400 ℃ for 2-4 hours in air atmosphere, wherein the heating rate is 2-5 ℃/min; obtaining carbon spheres with templates;
and thirdly, removing the template from the obtained carbon spheres with the template, cleaning and drying to obtain the porous carbon sphere-based photo-thermal material.
5. The method for preparing the porous carbon sphere-based photothermal material according to claim 4, wherein a metal precursor is added to the mixed solution in the first step, and the metal-doped carbon sphere photothermal material precursor is obtained through the hydrothermal reaction in the first step, wherein the metal precursor is chloroauric acid, silver nitrate, copper nitrate or aluminum nitrate, and the mass ratio of the metal in the precursor is 5% to 10%.
6. The method for preparing a porous carbon sphere-based photothermal material according to claim 4, wherein in the second step, the argon atmosphere is replaced by ammonia gas atmosphere, and the other atmosphere is not changed, so that the template-attached N-doped carbon sphere is obtained after the second step.
7. The method for preparing a porous carbon sphere-based photothermal material according to claim 4, wherein after the third step is completed, the obtained carbon sphere-based photothermal material is mixed with sulfur, placed in a tube furnace, and annealed to obtain an S-doped carbon sphere photothermal material.
8. The method for preparing a porous carbon sphere-based photothermal material according to claim 4, wherein the template material is Na2MoO3·2H2O, the template in the carbon ball with the template is MoO3(ii) a The carbon source is at least one of sucrose, glucose and oatmeal.
9. The method for preparing a porous carbon sphere-based photothermal material according to claim 4, wherein the concentration of the template material in the mixed solution of the first step is 0.002-0.004 mol/L, the concentration of the carbon source is 0.02-0.05 mol/L, and the volume ratio of the hydrochloric acid is 0.03-0.08.
CN202110419575.7A 2021-04-19 2021-04-19 Photothermal material based on porous carbon spheres and preparation method thereof Active CN113135558B (en)