CN111139584A - Method for making silk balls - Google Patents

Abstract

The invention discloses a method for manufacturing silk balls, which comprises the following steps: cutting mulberry silkworm cocoons by a cocoon cutting machine, separating silkworm chrysalis to obtain cut cocoons and silkworm chrysalis, putting the cut cocoons into water added with 1-1.3% of edible alkali and 2-2.5% of edible salt to soften the cut cocoons, degumming, repeatedly rinsing by using clean water at the temperature of 62 ℃, removing colloid, edible alkali and edible salt to obtain degummed open cocoons, cutting the open cocoons into silk floss pieces, putting the prepared silk floss pieces into clean water at the temperature of 62 ℃, cleaning the cleaned silk floss pieces by using a dehydrator, spin-drying the spin-dried silk floss pieces by using a dryer, preparing 0.8 kg of mulberry cotton balls from the silk floss by using the cocoon cutting machine, opening the prepared balls into cotton belts, cutting the opened cotton belts into about 10cm short cotton by using the cotton cutting machine, putting the short cotton balls on a circular carding machine into cotton floss pieces, removing impurities of the cotton floss pieces by using an artificial cotton floss machine, and preparing the cotton balls with the weight of about 140 g cotton floss balls on the cotton floss carding machine, thus obtaining the silk ball.

Description

Method for making silk balls

Technical Field

The invention relates to the field of home textiles, in particular to a method for manufacturing a silk ball.

Background

Silk is the lightest, softest and finest natural fiber in nature, and cellulose has the reputation of 'second skin of human body'. The silk can be recovered after the external force is removed, the inner tube does not cake, is not stuffy, does not shrink, is uniform and soft, and is called as 'fiber queen'. Because the silk has the advantages of sweat absorption, heat preservation, antibacterial property and the like, the silk quilt made of the silk is fluffy and soft and can be used for skin care next to the skin, and sanitary cleaning products such as cosmetic cotton and wet tissues made of the silk mulberry cotton balls have good skin affinity and soft hand feeling and are popular with consumers.

Disclosure of Invention

The invention provides a method for manufacturing silk balls.

The technical scheme adopted by the invention for realizing the technical effects is as follows:

a method for manufacturing a silk ball, the method comprising the steps of:

s1, selecting cocoons, and classifying the mulberry silkworm cocoons according to different colors for later use;

s2, cutting cocoons, namely cutting mulberry silkworm cocoons by using a cocoon cutting machine, and separating silkworm chrysalis to obtain cut cocoons and silkworm chrysalis;

s3, boiling the cocoons, namely putting the cut cocoons into water added with 1-1.3% of edible alkali and 2-2.5% of edible salt, controlling the temperature of the water at 70-80 ℃, boiling for 110-120 minutes to soften and degum the open cocoons;

s4, cleaning, namely repeatedly rinsing with clear water at the temperature of 60-65 ℃, and removing colloid, edible alkali and edible salt to obtain degummed open cocoons;

s5, opening the cocoon into a silk floss sheet;

s6, cleaning again, namely, putting the prepared silk floss sheet into clean water at the temperature of 60-65 ℃ and cleaning with a water washing machine;

s7, dehydrating, and drying the cleaned silk floss piece by a dehydrator;

s8, drying, namely drying the dried silk floss piece by using a dryer;

s9, preparing balls, namely preparing silk floss balls with the weight of 0.8 kg each;

s10, opening the cocoons, and opening the matched balls by using a cocoon opener to form a cotton belt;

s11, cutting cotton, namely cutting the loosened cotton belt into short cotton of about 10cm by using a cotton cutting machine;

s12, carding cotton, namely, carding the short cotton on a circular carding machine to form a cotton sheet;

s13, removing impurities, and manually removing impurities from the cotton piece;

and S14, preparing balls, and preparing the balls with the weight of about 140 grams on a spreading machine to obtain silk balls.

The invention has the beneficial effects that: the silk ball prepared by the preparation method has good skin-friendly property, does not contain allergic components, and does not cause environmental pollution in the processing process. The product has the characteristics of good skin-friendly property and soft hand feeling, has the antibacterial and antiallergic effects, can prevent skin diseases such as pruritus and the like, and is very beneficial to skin health.

Detailed Description

The present invention will now be described in detail with reference to specific embodiments for better understanding of the technical features, objects and effects of the present invention.

A method for manufacturing a silk ball, the method comprising the steps of:

s1, selecting cocoons, and classifying the mulberry silkworm cocoons according to different colors for later use;

s2, cutting cocoons, namely cutting mulberry silkworm cocoons by using a cocoon cutting machine, and separating silkworm chrysalis to obtain cut cocoons and silkworm chrysalis;

s3, boiling the cocoons, namely putting the cut cocoons into water added with 1-1.3% of edible alkali and 2-2.5% of edible salt, controlling the temperature of the water at 70-80 ℃, boiling for 110-120 minutes to soften and degum the open cocoons;

s4, cleaning, namely repeatedly rinsing with clear water at the temperature of 60-65 ℃, and removing colloid, edible alkali and edible salt to obtain degummed open cocoons;

s5, opening the cocoon into a silk floss sheet;

s6, cleaning again, namely, putting the prepared silk floss sheet into clean water at the temperature of 60-65 ℃ and cleaning with a water washing machine;

s7, dehydrating, and drying the cleaned silk floss piece by a dehydrator;

s8, drying, namely drying the dried silk floss piece by using a dryer;

s9, preparing balls, namely preparing silk floss balls with the weight of 0.8 kg each;

s10, opening the cocoons, and opening the matched balls by using a cocoon opener to form a cotton belt;

s11, cutting cotton, namely cutting the loosened cotton belt into short cotton of about 10cm by using a cotton cutting machine;

s12, carding cotton, namely, carding the short cotton on a circular carding machine to form a cotton sheet;

s13, removing impurities, and manually removing impurities from the cotton piece;

and S14, preparing balls, and preparing the balls with the weight of about 140 grams on a spreading machine to obtain silk balls.

The silk ball prepared by the preparation method has good skin-friendly property, does not contain allergic components, and does not cause environmental pollution in the processing process. The product has the characteristics of good skin-friendly property and soft and smooth hand feeling, has the antibacterial and antiallergic effects, can prevent skin diseases such as pruritus and the like, and is very beneficial to skin health.

The foregoing shows and describes the general principles, essential features, and advantages of the invention. It will be understood by those skilled in the art that the present invention is not limited to the embodiments described above, which are merely illustrative of the principles of the invention, but that various changes and modifications may be made without departing from the spirit and scope of the invention, which is defined by the appended claims and their equivalents.

Claims (1)

1. A manufacturing method of a silk ball is characterized by comprising the following steps:

s1, selecting cocoons, and classifying the mulberry silkworm cocoons according to different colors for later use;

s2, cutting cocoons, namely cutting mulberry silkworm cocoons by using a cocoon cutting machine, and separating silkworm chrysalis to obtain cut cocoons and silkworm chrysalis;

s3, boiling the cocoons, namely putting the cut cocoons into water added with 1-1.3% of edible alkali and 2-2.5% of edible salt, controlling the temperature of the water at 70-80 ℃, boiling for 110-120 minutes to soften and degum the open cocoons;

s4, cleaning, namely repeatedly rinsing with clear water at the temperature of 60-65 ℃, and removing colloid, edible alkali and edible salt to obtain degummed open cocoons;

s5, opening the cocoon into a silk floss sheet;

s6, cleaning again, namely, putting the prepared silk floss sheet into clean water at the temperature of 60-65 ℃ and cleaning with a water washing machine;

s7, dehydrating, and drying the cleaned silk floss piece by a dehydrator;

s8, drying, namely drying the dried silk floss piece by using a dryer;

s9, preparing balls, namely preparing silk floss balls with the weight of 0.8 kg each;

s10, opening the cocoons, and opening the matched balls by using a cocoon opener to form a cotton belt;

s11, cutting cotton, namely cutting the loosened cotton belt into short cotton of about 10cm by using a cotton cutting machine;

s12, carding cotton, namely, carding the short cotton on a circular carding machine to form a cotton sheet;

s13, removing impurities, and manually removing impurities from the cotton piece;

and S14, preparing balls, and preparing the balls with the weight of about 140 grams on a spreading machine to obtain silk balls.