CN111139539A - Method for preparing antibacterial and antiallergic cotton balls - Google Patents

Abstract

The invention discloses a method for manufacturing an antibacterial and antiallergic cotton ball, which comprises the following steps: cutting silkworm cocoons by a cocoon cutting machine, separating silkworm chrysalis to obtain cut cocoons and silkworm chrysalis, putting the cut cocoons into water added with 0.2% edible alkali and 0.4% edible salt to soften and degum the open cocoons, repeatedly rinsing by clear water at the temperature of 58 ℃ to remove colloid, edible alkali and edible salt to obtain degummed open cocoons, cutting the open cocoons into silk floss pieces, putting the prepared silk floss pieces into clear water at the temperature of 58 ℃ to be cleaned by a water washing machine, drying the dried silk floss pieces by a drying machine, preparing silk floss into 0.9 kg of mulberry floss balls, loosening the prepared balls by the cocoon cutting machine to form cotton belts, cutting the loosened cotton belts into about 11cm short cotton balls by the cotton cutting machine, putting the cotton floss balls on a circular machine to be short cotton floss pieces, manually removing impurities of the cotton floss pieces, and preparing about 150 g of cotton balls on an extension machine, thus obtaining the antibacterial and antiallergic cotton balls.

Description

Method for preparing antibacterial and antiallergic cotton balls

Technical Field

The invention relates to the field of home textiles, in particular to a method for manufacturing an antibacterial and antiallergic cotton ball.

Background

Silk is the lightest, softest and finest natural fiber in nature, and cellulose has the reputation of 'second skin of human body'. The silk can be recovered after the external force is removed, the inner tube does not cake, is not stuffy, does not shrink, is uniform and soft, and is called as 'fiber queen'. Because the silk has the advantages of sweat absorption, heat preservation, antibacterial property and the like, the silk quilt made of the silk is fluffy and soft and can be used for skin care next to the skin, and sanitary cleaning products such as cosmetic cotton and wet tissues made of the silk mulberry cotton balls have good skin affinity and soft hand feeling and are popular with consumers.

Disclosure of Invention

The invention provides a method for preparing an antibacterial and antiallergic cotton ball.

The technical scheme adopted by the invention for realizing the technical effects is as follows:

a method for preparing an antibacterial and antiallergic sponge ball comprises the following steps:

s1, selecting cocoons, and classifying the mulberry silkworm cocoons according to different colors for later use;

s2, cutting cocoons, namely cutting mulberry silkworm cocoons by using a cocoon cutting machine, and separating silkworm chrysalis to obtain cut cocoons and silkworm chrysalis;

s3, boiling the cocoons, namely putting the cut cocoons into water added with 0.2% of edible alkali and 0.4% of edible salt, controlling the temperature of the water to be 65-70 ℃, boiling for 130-140 minutes to soften and degum the open cocoons;

s4, cleaning, namely repeatedly rinsing with clear water at the temperature of 55-60 ℃, and removing colloid, edible alkali and edible salt to obtain degummed open cocoons;

s5, opening the cocoon into a silk floss sheet;

s6, cleaning again, namely, putting the prepared silk floss piece into clean water at the temperature of 55-60 ℃ and cleaning with a water washing machine;

s7, dehydrating, and drying the cleaned silk floss piece by a dehydrator;

s8, drying, namely drying the dried silk floss piece by using a dryer;

s9, preparing balls, namely preparing silk floss balls with the weight of 0.9 kg each;

s10, opening the cocoons, and opening the matched balls by using a cocoon opener to form a cotton belt;

s11, cutting cotton, namely cutting the loosened cotton belt into short cotton with the length of about 11cm by using a cotton cutting machine;

s12, carding cotton, namely, carding the short cotton on a circular carding machine to form a cotton sheet;

s13, removing impurities, and manually removing impurities from the cotton piece;

s14, preparing balls, and preparing the balls with the weight of about 150 g on a spreading machine to obtain the antibacterial and antiallergic cotton balls.

The invention has the beneficial effects that: the antibacterial and antiallergic cotton balls prepared by the preparation method have good skin-friendly property, do not contain allergic components, and do not cause environmental pollution in the processing process. The product has the characteristics of good skin-friendly property and soft hand feeling, has the antibacterial and antiallergic effects, can prevent skin diseases such as pruritus and the like, and is very beneficial to skin health.

Detailed Description

The present invention will now be described in detail with reference to specific embodiments for better understanding of the technical features, objects and effects of the present invention.

A method for preparing an antibacterial and antiallergic sponge ball comprises the following steps:

s1, selecting cocoons, and classifying the mulberry silkworm cocoons according to different colors for later use;

s2, cutting cocoons, namely cutting mulberry silkworm cocoons by using a cocoon cutting machine, and separating silkworm chrysalis to obtain cut cocoons and silkworm chrysalis;

s3, boiling the cocoons, namely putting the cut cocoons into water added with 0.2% of edible alkali and 0.4% of edible salt, controlling the temperature of the water to be 65-70 ℃, boiling for 130-140 minutes to soften and degum the open cocoons;

s4, cleaning, namely repeatedly rinsing with clear water at the temperature of 55-60 ℃, and removing colloid, edible alkali and edible salt to obtain degummed open cocoons;

s5, opening the cocoon into a silk floss sheet;

s6, cleaning again, namely, putting the prepared silk floss piece into clean water at the temperature of 55-60 ℃ and cleaning with a water washing machine;

s7, dehydrating, and drying the cleaned silk floss piece by a dehydrator;

s8, drying, namely drying the dried silk floss piece by using a dryer;

s9, preparing balls, namely preparing silk floss balls with the weight of 0.9 kg each;

s10, opening the cocoons, and opening the matched balls by using a cocoon opener to form a cotton belt;

s11, cutting cotton, namely cutting the loosened cotton belt into short cotton with the length of about 11cm by using a cotton cutting machine;

s12, carding cotton, namely, carding the short cotton on a circular carding machine to form a cotton sheet;

s13, removing impurities, and manually removing impurities from the cotton piece;

s14, preparing balls, and preparing the balls with the weight of about 150 g on a spreading machine to obtain the antibacterial and antiallergic cotton balls.

The antibacterial and antiallergic sponge ball prepared by the preparation method has good skin-friendly property, does not contain allergic components, and does not cause environmental pollution in the processing process. The product has the characteristics of good skin-friendly property and soft and smooth hand feeling, has the antibacterial and antiallergic effects, can prevent skin diseases such as pruritus and the like, and is very beneficial to skin health.

The foregoing shows and describes the general principles, essential features, and advantages of the invention. It will be understood by those skilled in the art that the present invention is not limited to the embodiments described above, which are merely illustrative of the principles of the invention, but that various changes and modifications may be made without departing from the spirit and scope of the invention, which is defined by the appended claims and their equivalents.

Claims (1)

1. A method for manufacturing an antibacterial and antiallergic sponge ball is characterized by comprising the following steps:

s1, selecting cocoons, and classifying the mulberry silkworm cocoons according to different colors for later use;

s2, cutting cocoons, namely cutting mulberry silkworm cocoons by using a cocoon cutting machine, and separating silkworm chrysalis to obtain cut cocoons and silkworm chrysalis;

s3, boiling the cocoons, namely putting the cut cocoons into water added with 0.2% of edible alkali and 0.4% of edible salt, controlling the temperature of the water to be 65-70 ℃, boiling for 130-140 minutes to soften and degum the open cocoons;

s4, cleaning, namely repeatedly rinsing with clear water at the temperature of 55-60 ℃, and removing colloid, edible alkali and edible salt to obtain degummed open cocoons;

s5, opening the cocoon into a silk floss sheet;

s6, cleaning again, namely, putting the prepared silk floss piece into clean water at the temperature of 55-60 ℃ and cleaning with a water washing machine;

s7, dehydrating, and drying the cleaned silk floss piece by a dehydrator;

s8, drying, namely drying the dried silk floss piece by using a dryer;

s9, preparing balls, namely preparing silk floss balls with the weight of 0.9 kg each;

s10, opening the cocoons, and opening the matched balls by using a cocoon opener to form a cotton belt;

s11, cutting cotton, namely cutting the loosened cotton belt into short cotton with the length of about 11cm by using a cotton cutting machine;

s12, carding cotton, namely, carding the short cotton on a circular carding machine to form a cotton sheet;

s13, removing impurities, and manually removing impurities from the cotton piece;

s14, preparing balls, and preparing the balls with the weight of about 150 g on a spreading machine to obtain the antibacterial and antiallergic cotton balls.