CN110357428A - A kind of preparation method and Ceramic Tiles of the controllable Ceramic Tiles of glaze glossiness - Google Patents
A kind of preparation method and Ceramic Tiles of the controllable Ceramic Tiles of glaze glossiness Download PDFInfo
- Publication number
- CN110357428A CN110357428A CN201910736568.2A CN201910736568A CN110357428A CN 110357428 A CN110357428 A CN 110357428A CN 201910736568 A CN201910736568 A CN 201910736568A CN 110357428 A CN110357428 A CN 110357428A
- Authority
- CN
- China
- Prior art keywords
- glaze
- ceramic tiles
- glossiness
- controllable
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses the preparation method and Ceramic Tiles of a kind of controllable Ceramic Tiles of glaze glossiness, which comprises A, blank compression moulding is placed in roller kilns is dried, obtain Ceramic Tiles green body；B, apply ground coat enamel on Ceramic Tiles green body, obtain ground glaze layer；Step C, the inkjet printing decorative pattern on ground glaze layer, obtains pattern decorative layer；D, apply the mixing bright glaze that glossiness is controllable after being burnt on pattern decorative layer, obtain mixing gloss glaze layer.By applying ground coat enamel, and then background color entrained by Ceramic Tiles green body is covered, has promoted the color colouring effect of pattern decorative ink；Bright glaze is mixed by glossiness after applying firing, the glossiness for realizing Ceramic Tiles after control is burnt into, simplifies Ceramic Tiles preparation method, realizes the unification of formula, the preparation efficiency for promoting Ceramic Tiles, reduces the otherness with a batch of Ceramic Tiles product surface texture and glossiness.
Description
Technical field
The present invention relates to architectural pottery production field more particularly to a kind of preparation methods of the controllable Ceramic Tiles of glaze glossiness
And Ceramic Tiles.
Background technique
It is not required to polishing glazed ceramic brick in existing building Ceramic Tiles, packet is distinguished according to the power of lustrous surface intensity
It includes: mat glaze Ceramic Tiles, matting glaze Ceramic Tiles, satin glaze Ceramic Tiles, sheen glaze Ceramic Tiles and light glaze Ceramic Tiles etc.；These are not
The texture on surface and gloss are all had any different between same Ceramic Tiles.
Currently, the glazed tile for surface without polishing treatment, prepares often through different glaze formulas；So
And different prescription systems is intended to different control standards, this is resulted in when identical production interchange to other areas
Production line production when, to obtain the original luster effect of ceramic brick product, usually also need to adjust the formula of the product, this makes
Obtaining production process becomes complicated, and process recipe is difficult to unification, increases the workload of technical staff and reduces work effect
Rate, while also increasing the uncontrollability of product duplication of production, causes the batch that identical product is different, product texture, gloss,
Color number difference is larger.
Therefore, how the preparation method and Ceramic Tiles of a kind of controllable Ceramic Tiles of glaze glossiness are provided, brief solution is become
The problem of.
Summary of the invention
In view of above-mentioned deficiencies of the prior art, the purpose of the present invention is to provide a kind of controllable Ceramic Tiles of glaze glossiness
Preparation method and Ceramic Tiles, it is intended to solve the problems, such as that the glaze glossiness of existing Ceramic Tiles is uncontrollable.
The present invention is in order to solve the above technical problems, the technical solution provided is as follows: a kind of controllable Ceramic Tiles of glaze glossiness
Preparation method comprising:
A, blank compression moulding is placed in roller kilns and is dried, obtain Ceramic Tiles green body；
B, apply ground coat enamel on the Ceramic Tiles green body, obtain ground glaze layer；
C, the inkjet printing decorative pattern on the ground glaze layer, obtains pattern decorative layer；
D, apply the mixing bright glaze that glossiness is controllable after being burnt on the pattern decorative layer, obtain mixing bright glaze
Layer.
Further, the sequencing of the step C and step D can be replaced mutually.
Further, the chemical composition of the ground coat enamel is by percentage to the quality, comprising:
SiO250~55%, Al2O325~30%, F2O30~0.17%, CaO 0~2%, MgO 3~6%, K2O 0
~5%, Na2O 0~5%, ZrO26~10%.
Further, the chemical composition of the ground coat enamel by percentage to the quality, specifically includes:
SiO253.37%, Al2O326.53%, F2O30.17%, CaO 1.38%, MgO 3.98%, K2O
2.67%, Na2O 3.04%, ZrO28.86%.
Further, the mixing bright glaze includes matting glaze and/or bloom glaze；
The sum of matting glaze and bloom glaze component are 100% in the mixing bright glaze.
Further, the chemical composition of the matting glaze is by percentage to the quality, comprising:
SiO248~53%, Al2O314~18%, CaO 6~11%, MgO 0~3%, K2O 0~5%, Na2O 0~
5%, ZnO 0~5%, BaO 6~12%.
Further, the chemical composition of the bloom glaze is by percentage to the quality, comprising:
SiO250~60%, Al2O315~18%, CaO 9~15%, MgO 0~3%, K2O 0~5%, Na2O 0~
5%, ZnO 0~5%, BaO 0~5%.
The sum of matting glaze and bloom glaze component are 100% in the mixing bright glaze.
The present invention is in order to solve the above technical problems, the another technical solution provided is as follows: a kind of glaze glossiness is controllably made pottery
Ceramic tile, wherein the controllable Ceramic Tiles of glaze glossiness by upper described in any item controllable Ceramic Tiles of glaze glossiness preparation
Method preparation.
Further, the controllable Ceramic Tiles of glaze glossiness successively include: from the bottom to top Ceramic Tiles green body, ground glaze layer,
Pattern decorative layer and mixing glaze layer.
Further, the controllable Ceramic Tiles of glaze glossiness successively include: from the bottom to top Ceramic Tiles green body, ground glaze layer,
Mix glaze layer and pattern decorative layer.
The utility model has the advantages that the present invention provides the preparation method and Ceramic Tiles of a kind of controllable Ceramic Tiles of glaze glossiness, it is described
Preparation method includes: A, blank compression moulding is placed in roller kilns is dried, and obtains Ceramic Tiles green body；B, in the pottery
Apply ground coat enamel on ceramic tile blank, obtains ground glaze layer；Step C, the inkjet printing decorative pattern on the ground glaze layer obtains pattern dress
Adorn layer；D, apply the mixing bright glaze that glossiness is controllable after being burnt on the pattern decorative layer, obtain mixing gloss glaze layer.It can
To understand, background color entrained by Ceramic Tiles green body has been covered by applying ground coat enamel on the Ceramic Tiles green body, and then effectively,
Also the color colouring effect of pattern decorative ink is effectively promoted；Pass through glossiness after the application firing on the pattern decorative layer
Bright glaze is mixed, and then controls the glossiness of Ceramic Tiles after firing by controlling the mixing bright glaze, effectively simplifies pottery
Ceramic tile preparation method realizes the unification of formula, greatly promotes the preparation efficiency of Ceramic Tiles, gloss when ensure that ceramic tile production
The controllability of degree greatly reduces the otherness with a batch of Ceramic Tiles product surface texture and glossiness.
Detailed description of the invention
Fig. 1 is a kind of preparation method flow diagram of the controllable Ceramic Tiles of glaze glossiness in the present invention；
Fig. 2 is a kind of preparation method process deformation schematic diagram of the controllable Ceramic Tiles of glaze glossiness in the present invention；
Fig. 3 is the firing temperature curve graph in the present invention in a kind of preparation method of the controllable Ceramic Tiles of glaze glossiness；
Fig. 4 is a kind of schematic perspective view of the controllable Ceramic Tiles of glaze glossiness in the present invention；
Fig. 5 is a kind of stereochemical structure deformation schematic diagram of the controllable Ceramic Tiles of glaze glossiness in the present invention.
Description of symbols:
11, Ceramic Tiles green body；12, ground glaze layer；13, pattern decorative layer；14, glaze layer is mixed.
Specific embodiment
The present invention provides the preparation method and Ceramic Tiles of a kind of controllable Ceramic Tiles of glaze glossiness, to make mesh of the invention
, technical solution and effect it is clearer, clear, the present invention is described in more detail below.It should be appreciated that described herein
Specific embodiment be only used to explain the present invention, be not intended to limit the present invention.
Referring to Fig. 1, the embodiment of the invention provides a kind of preparation method of controllable Ceramic Tiles of glaze glossiness, packet
It includes:
Blank compression moulding is placed in roller kilns and is dried by step 11, obtains Ceramic Tiles green body；
Step 12 applies ground coat enamel on the Ceramic Tiles green body, obtains ground glaze layer；
Step 13, the inkjet printing decorative pattern on the ground glaze layer, obtain pattern decorative layer；
Step 14 applies the mixing bright glaze that glossiness is controllable after being burnt on the pattern decorative layer, obtains mixed light
Damp glaze layer；
Step 15, kiln-firing molding, obtain the controllable Ceramic Tiles of glaze glossiness.
It should be noted that by high-pressure press by blank compression moulding in the step 11, and in the roller kilns
It is dried, and then obtains Ceramic Tiles green body；Meanwhile by applying ground coat enamel on the Ceramic Tiles green body, so it is effective
Background color entrained by Ceramic Tiles green body has been covered, the color colouring effect of pattern decorative ink is also effectively promoted；By institute
State glossiness mixing bright glaze after applying firing on pattern decorative layer, and then after being burnt by controlling mixing bright glaze control
The glossiness of Ceramic Tiles effectively simplifies Ceramic Tiles preparation method, realizes the unification of formula, greatly promotes the system of Ceramic Tiles
Standby efficiency, the controllability of glossiness when ensure that ceramic tile production are greatly reduced with a batch of Ceramic Tiles product surface matter
The otherness of sense and glossiness.
Referring to Fig. 2, in some embodiments, the sequencing of the step 13 and step 14 can be replaced mutually；
That is, in these embodiments, the preparation method of the controllable Ceramic Tiles of glaze glossiness includes:
Blank compression moulding is placed in roller kilns and is dried by step 11, obtains Ceramic Tiles green body；
Step 12 applies ground coat enamel on the Ceramic Tiles green body, obtains ground glaze layer；
Step 13`, apply the mixing bright glaze that glossiness is controllable after being burnt on the ground glaze layer, obtain mixing bright glaze
Layer；
Step 14`, the inkjet printing decorative pattern in the mixing gloss glaze layer, obtains pattern decorative layer；
Step 15, kiln-firing molding, obtain the controllable Ceramic Tiles of glaze glossiness.
In some embodiments, the chemical composition of the ground coat enamel is by percentage to the quality, comprising:
SiO250~55%, Al2O325~30%, F2O30~0.17%, CaO 0~2%, MgO 3~6%, K2O 0
~5%, Na2O 0~5%, ZrO26~10%.
It should be noted that the sum of the above components are 100%, the ground coat enamel can be by using glaze spraying or the work of leaching glaze
Ground coat enamel is applied to Ceramic Tiles billet surface, and then effectively covers in itself background color of Ceramic Tiles green body, while significant by process
Promotion ink colors colour generation.
In some embodiments, the chemical composition of the ground coat enamel by percentage to the quality, specifically includes:
SiO253.37%, Al2O326.53%, F2O30.17%, CaO 1.38%, MgO 3.98%, K2O
2.67%, Na2O 3.04%, ZrO28.86%.
In some embodiments, the mixing bright glaze includes matting glaze and/or bloom glaze；
Matting glaze in the mixing bright glaze: bloom glaze=0~1.
It should be noted that the component of matting glaze and bloom glaze is later 100% in the mixing bright glaze；That is mixed light
Matting glaze in damp glaze: bloom glaze=100%:0%~0%:100%；Glossiness after the matting glaze firing is 15~25 degree,
Glossiness after the bloom glaze firing is 90~100 degree；It is appreciated that by controlling the matting glaze in the mixing bright glaze
With the ratio of bloom glaze, and then realize control firing after Ceramic Tiles surface gloss；Specifically, passing through glaze in the present invention
The surface gloss for the Ceramic Tiles that the preparation method of the controllable Ceramic Tiles of face glossiness obtains is 15~100 degree.
In some embodiments, the chemical composition of the matting glaze is by percentage to the quality, comprising:
SiO248~53%, Al2O314~18%, CaO 6~11%, MgO 0~3%, K2O 0~5%, Na2O 0~
5%, ZnO 0~5%, BaO 6~12%；It should be noted that the sum of the above components are 100%.
In some embodiments, the chemical composition of the bloom glaze is by percentage to the quality, comprising:
SiO250~60%, Al2O315~18%, CaO 9~15%, MgO 0~3%, K2O 0~5%, Na2O 0~
5%, ZnO 0~5%, BaO 0~5%；It should be noted that the sum of the above components are 100%.
Referring to Fig. 3, in some embodiments, the kiln in the step 15 is roller kilns, and the length of the roller-way is
220m, firing temperature are up to 1223 DEG C, firing time 46-50min.
It should be noted that being set as oxidizing atmosphere in the roller kilns, i.e., sufficient air is provided in the described roller-way, into
And sufficient oxygen is provided for fuel；The roller kilns need preheating 16-20min in advance, and kiln burning can be just entered after the completion of preheating
System；Meanwhile the firing temperature includes upper mild lower temperature；The upper temperature is the temperature in Ceramic Tiles opposite upper parts region, setting
It is 725~1207 DEG C；The lower temperature is the temperature in Ceramic Tiles opposing lower portions region, is set as 765~1223 DEG C；The firing
Temperature is preferably 48min.
Referring to Fig. 4, the present invention also provides a kind of controllable Ceramic Tiles of glaze glossiness, wherein the glaze glossiness can
Ceramic Tiles are controlled to be prepared by the preparation method of the above-mentioned controllable Ceramic Tiles of glaze glossiness.It is appreciated that by the Ceramic Tiles
Apply ground glaze layer on green body, and then effectively covered background color entrained by Ceramic Tiles green body, also effectively promotes pattern decorative
The color colouring effect of ink；Gloss glaze layer, Jin Ertong are mixed by glossiness after applying firing on the pattern decorative layer
The glossiness for crossing Ceramic Tiles after controlling the mixing bright glaze control firing, effectively simplifies Ceramic Tiles preparation method, realizes
The unification of formula, greatly promotes the preparation efficiency of Ceramic Tiles, the controllability of glossiness, drops significantly when ensure that ceramic tile production
The low otherness with a batch of Ceramic Tiles product surface texture and glossiness.
In some embodiments, the controllable Ceramic Tiles of glaze glossiness, successively include: ceramic adobe from the bottom to top
Body 11, ground glaze layer 12, pattern decorative layer 13 and mixing glaze layer 14.
Referring to Fig. 5, in some embodiments, the controllable Ceramic Tiles of glaze glossiness successively include: from the bottom to top
Ceramic Tiles green body 11, ground glaze layer 12, mixing glaze layer 14 and pattern decorative layer 13.
The present invention is further described in detail below by specific embodiment.
Embodiment one:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness comprising:
Blank compression moulding is placed in roller kilns and is dried by step 11, obtains Ceramic Tiles green body；
Step 12 applies ground coat enamel on the Ceramic Tiles green body, obtains ground glaze layer；
Step 13, the inkjet printing decorative pattern on the ground glaze layer, obtain pattern decorative layer；
Step 14 applies the mixing bright glaze that glossiness is controllable after being burnt on the pattern decorative layer, obtains mixed light
Damp glaze layer；
Step 15, kiln-firing molding, obtain the controllable Ceramic Tiles of glaze glossiness.
Further, the chemical composition of the ground coat enamel is by percentage to the quality, comprising:
SiO250~55%, Al2O325~30%, F2O30~0.17%, CaO 0~2%, MgO 3~6%, K2O 0
~5%, Na2O 0~5%, ZrO26~10%.
Further, the mixing bright glaze includes matting glaze and/or bloom glaze；
The sum of component of matting glaze and bloom glaze is 100% in the mixing bright glaze.
Further, the chemical composition of the matting glaze is by percentage to the quality, comprising:
SiO248~53%, Al2O314~18%, CaO 6~11%, MgO 0~3%, K2O 0~5%, Na2O 0~
5%, ZnO 0~5%, BaO 6~12%.
Further, the chemical composition of the bloom glaze is by percentage to the quality, comprising:
SiO250~60%, Al2O315~18%, CaO 9~15%, MgO 0~3%, K2O 0~5%, Na2O 0~
5%, ZnO 0~5%, BaO 0~5%.
Further, the kiln in the step 15 is roller kilns, and the length of the roller-way is 220m, and firing temperature is up to
1223 DEG C, firing time 46-50min.
It is appreciated that by applying ground coat enamel on the Ceramic Tiles green body, and then effectively covered Ceramic Tiles green body institute
The background color of carrying also effectively promotes the color colouring effect of pattern decorative ink；By applying on the pattern decorative layer
Glossiness mixes bright glaze after firing, and then the glossiness of Ceramic Tiles after firing is controlled by controlling the mixing bright glaze, has
Effect simplifies Ceramic Tiles preparation method, realizes the unification of formula, greatly promotes the preparation efficiency of Ceramic Tiles, ensure that ceramics
The controllability of glossiness, greatly reduces the difference with a batch of Ceramic Tiles product surface texture and glossiness when brick produces
Property.
Meanwhile the ratio by controlling matting glaze and bloom glaze in the mixing bright glaze, and then realize control firing
The surface gloss of Ceramic Tiles afterwards；Specifically, the preparation method by the controllable Ceramic Tiles of glaze glossiness in the present invention obtains
The surface gloss of the Ceramic Tiles obtained is 15~100 degree.
Embodiment two:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness comprising:
Blank compression moulding is placed in roller kilns and is dried by step 11, obtains Ceramic Tiles green body；
Step 12 applies ground coat enamel on the Ceramic Tiles green body, obtains ground glaze layer；
Step 13`, apply the mixing bright glaze that glossiness is controllable after being burnt on the ground glaze layer, obtain mixing bright glaze
Layer；
Step 14`, the inkjet printing decorative pattern in the mixing gloss glaze layer, obtains pattern decorative layer；
Step 15, kiln-firing molding, obtain the controllable Ceramic Tiles of glaze glossiness.
Further, the chemical composition of the ground coat enamel is by percentage to the quality, comprising:
SiO250~55%, Al2O325~30%, F2O30~0.17%, CaO 0~2%, MgO 3~6%, K2O 0
~5%, Na2O 0~5%, ZrO26~10%.
Further, the mixing bright glaze includes matting glaze and/or bloom glaze；
Matting glaze and bloom glaze component are later 100% in the mixing bright glaze.
Further, the chemical composition of the matting glaze is by percentage to the quality, comprising:
SiO248~53%, Al2O314~18%, CaO 6~11%, MgO 0~3%, K2O 0~5%, Na2O 0~
5%, ZnO 0~5%, BaO 6~12%.
Further, the chemical composition of the bloom glaze is by percentage to the quality, comprising:
SiO250~60%, Al2O315~18%, CaO 9~15%, MgO 0~3%, K2O 0~5%, Na2O 0~
5%, ZnO 0~5%, BaO 0~5%.
Further, the kiln in the step 15 is roller kilns, and the length of the roller-way is 220m, and firing temperature is up to
1223 DEG C, firing time 46-50min.
It is appreciated that by applying ground coat enamel on the Ceramic Tiles green body, and then effectively covered Ceramic Tiles green body institute
The background color of carrying also effectively promotes the color colouring effect of pattern decorative ink；By applying firing on the ground glaze layer
Glossiness mixes bright glaze afterwards, and then realizes through the glossiness of Ceramic Tiles after the control mixing bright glaze control firing, has
Effect simplifies Ceramic Tiles preparation method, realizes the unification of formula, greatly promotes the preparation efficiency of Ceramic Tiles, ensure that ceramics
The controllability of glossiness, greatly reduces the difference with a batch of Ceramic Tiles product surface texture and glossiness when brick produces
Property.Meanwhile the ratio by controlling matting glaze and bloom glaze in the mixing bright glaze, and then realize the pottery after control firing
The surface gloss of ceramic tile；Specifically, the pottery that the preparation method by the controllable Ceramic Tiles of glaze glossiness in the present invention obtains
The surface gloss of ceramic tile is 15~100 degree.
Embodiment three:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness, above-described embodiment one or embodiment
Two the difference lies in that the chemical composition of the ground coat enamel by percentage to the quality, specifically includes:
SiO253.37%, Al2O326.53%, F2O30.17%, CaO 1.38%, MgO 3.98%, K2O
2.67%, Na2O 3.04%, ZrO28.86%.
Example IV:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness, above-described embodiment one or embodiment
Two the difference lies in that being provided with matting glaze 100% in the mixing bright glaze；That is, the mixing bright glaze setting
For matting glaze；The gloss on the surface of the Ceramic Tiles prepared in the present embodiment by the preparation method of the controllable Ceramic Tiles of glaze glossiness
Degree is 15~25 degree；Preferably, the glossiness of the controllable Ceramic Tiles of glaze glossiness obtained in the present embodiment is 21.
Embodiment five:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness, above-described embodiment one or embodiment
Two the difference lies in that the mixing bright glaze is provided with matting glaze 90%, bloom glaze 10%；Pass through glaze light in the present embodiment
The glossiness on the surface of the Ceramic Tiles of the preparation method preparation of the damp controllable Ceramic Tiles of degree is 23~28 degree；Preferably, the present embodiment
The glossiness of the controllable Ceramic Tiles of glaze glossiness of middle acquisition is 26.
Embodiment six:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness, above-described embodiment one or embodiment
Two the difference lies in that matting glaze 80%, bloom glaze 20% in the mixing bright glaze；Pass through glaze glossiness in the present embodiment
The glossiness on the surface of the Ceramic Tiles of the preparation method preparation of controllable Ceramic Tiles is 26~30 degree；Preferably, it is obtained in the present embodiment
The glossiness of the controllable Ceramic Tiles of glaze glossiness obtained is 28.
Embodiment seven:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness, above-described embodiment one or embodiment
Two the difference lies in that matting glaze 70% in the mixing bright glaze, bloom glaze 30% is that is, pass through glaze in the present embodiment
The glossiness on the surface of the Ceramic Tiles of the preparation method preparation of the controllable Ceramic Tiles of face glossiness is 32~38 degree；Preferably, this reality
The glossiness for applying the controllable Ceramic Tiles of glaze glossiness obtained in example is 35.
Embodiment eight:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness, above-described embodiment one or embodiment
Two the difference lies in that matting glaze 60%, bloom glaze 40% in the mixing bright glaze；Pass through glaze glossiness in the present embodiment
The glossiness on the surface of the Ceramic Tiles of the preparation method preparation of controllable Ceramic Tiles is 38~42 degree；Preferably, it is obtained in the present embodiment
The glossiness of the controllable Ceramic Tiles of glaze glossiness obtained is 40.
Embodiment nine:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness, above-described embodiment one or embodiment
Two the difference lies in that matting glaze 50%, bloom glaze 50% in the mixing bright glaze；Pass through glaze glossiness in the present embodiment
The glossiness on the surface of the Ceramic Tiles of the preparation method preparation of controllable Ceramic Tiles is 58~63 degree；Preferably, it is obtained in the present embodiment
The glossiness of the controllable Ceramic Tiles of glaze glossiness obtained is 60.
Embodiment ten:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness, above-described embodiment one or embodiment
Two the difference lies in that matting glaze 40%, bloom glaze 60% in the mixing bright glaze；Pass through glaze glossiness in the present embodiment
The glossiness on the surface of the Ceramic Tiles of the preparation method preparation of controllable Ceramic Tiles is 82~88 degree；Preferably, it is obtained in the present embodiment
The glossiness of the controllable Ceramic Tiles of glaze glossiness obtained is 85.
Embodiment 11:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness, above-described embodiment one or embodiment
Two the difference lies in that matting glaze 30%, bloom glaze 70% in the mixing bright glaze；Pass through glaze glossiness in the present embodiment
The glossiness on the surface of the Ceramic Tiles of the preparation method preparation of controllable Ceramic Tiles is 85~89 degree；Preferably, it is obtained in the present embodiment
The glossiness of the controllable Ceramic Tiles of glaze glossiness obtained is 87.
Embodiment 12:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness, above-described embodiment one or embodiment
Two the difference lies in that matting glaze 20%, bloom glaze 80% in the mixing bright glaze；Pass through glaze glossiness in the present embodiment
The glossiness on the surface of the Ceramic Tiles of the preparation method preparation of controllable Ceramic Tiles is 97~99 degree；Preferably, it is obtained in the present embodiment
The glossiness of the controllable Ceramic Tiles of glaze glossiness obtained is 98.
Embodiment 13:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness, above-described embodiment one or embodiment
Two the difference lies in that matting glaze 10%, bloom glaze 90% in the mixing bright glaze；Pass through glaze glossiness in the present embodiment
The glossiness on the surface of the Ceramic Tiles of the preparation method preparation of controllable Ceramic Tiles is 98~100 degree；Preferably, it is obtained in the present embodiment
The glossiness of the controllable Ceramic Tiles of glaze glossiness obtained is 99.
Embodiment 14:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness, above-described embodiment one or embodiment
Two the difference lies in that bloom glaze 100% in the mixing bright glaze；Pass through the controllable Ceramic Tiles of glaze glossiness in the present embodiment
Preparation method preparation Ceramic Tiles surface glossiness be 98~100 degree；Preferably, the glaze light obtained in the present embodiment
The glossiness of the damp controllable Ceramic Tiles of degree is 99.
Embodiment 15:
Present embodiments provide a kind of preparation method of controllable Ceramic Tiles of glaze glossiness, above-described embodiment one or embodiment
Two the difference lies in that kiln in the step 15 is roller kilns, the length of the roller-way is 220m, and firing temperature is up to
1223 DEG C, firing time 48min.
Embodiment 16:
The present invention also provides a kind of controllable Ceramic Tiles of glaze glossiness, wherein the controllable Ceramic Tiles of glaze glossiness by
It is prepared by the preparation method of the above-mentioned controllable Ceramic Tiles of glaze glossiness.
Embodiment 17:
The present invention also provides a kind of controllable Ceramic Tiles of glaze glossiness, the difference of above-described embodiment 16 is:
The controllable Ceramic Tiles of glaze glossiness, successively include: Ceramic Tiles green body, ground glaze layer, pattern decorative from the bottom to top
Layer and mixing glaze layer.
Embodiment 18:
The present invention also provides a kind of controllable Ceramic Tiles of glaze glossiness, the difference of above-described embodiment 16 is:
The controllable Ceramic Tiles of glaze glossiness successively include: Ceramic Tiles green body, ground glaze layer, mixing glaze layer from the bottom to top
And pattern decorative layer.
In conclusion the preparation method and Ceramic Tiles of a kind of controllable Ceramic Tiles of glaze glossiness provided by the invention, described
Preparation method includes: A, blank compression moulding is placed in roller kilns is dried, and obtains Ceramic Tiles green body；B, in the pottery
Apply ground coat enamel on ceramic tile blank, obtains ground glaze layer；Step C, the inkjet printing decorative pattern on the ground glaze layer obtains pattern dress
Adorn layer；D, apply the mixing bright glaze that glossiness is controllable after being burnt on the pattern decorative layer, obtain mixing gloss glaze layer.It can
To understand, background color entrained by Ceramic Tiles green body has been covered by applying ground coat enamel on the Ceramic Tiles green body, and then effectively,
Also the color colouring effect of pattern decorative ink is effectively promoted；Pass through glossiness after the application firing on the pattern decorative layer
Bright glaze is mixed, and then controls the glossiness of Ceramic Tiles after firing by controlling the mixing bright glaze, effectively simplifies pottery
Ceramic tile preparation method realizes the unification of formula, greatly promotes the preparation efficiency of Ceramic Tiles, gloss when ensure that ceramic tile production
The controllability of degree greatly reduces the otherness with a batch of Ceramic Tiles product surface texture and glossiness.
It should be understood that the application of the present invention is not limited to the above for those of ordinary skills can
With improvement or transformation based on the above description, all these modifications and variations all should belong to the guarantor of appended claims of the present invention
Protect range.
Claims (10)
1. a kind of preparation method of the controllable Ceramic Tiles of glaze glossiness characterized by comprising
A, blank compression moulding is placed in roller kilns and is dried, obtain Ceramic Tiles green body；
B, apply ground coat enamel on the Ceramic Tiles green body, obtain ground glaze layer；
C, the inkjet printing decorative pattern on the ground glaze layer, obtains pattern decorative layer；
D, apply the mixing bright glaze that glossiness is controllable after being burnt on the pattern decorative layer, obtain mixing gloss glaze layer.
2. the preparation method of the controllable Ceramic Tiles of glaze glossiness according to claim 1, which is characterized in that the step C
It can be replaced mutually with the sequencing of step D.
3. the preparation method of the controllable Ceramic Tiles of glaze glossiness according to claim 1, which is characterized in that the ground coat enamel
Chemical composition is by percentage to the quality, comprising:
SiO250~55%, Al2O325~30%, F2O30~0.17%, CaO 0~2%, MgO 3~6%, K2O 0~
5%, Na2O 0~5%, ZrO26~10%.
4. the preparation method of the controllable Ceramic Tiles of glaze glossiness according to claim 1, which is characterized in that the ground coat enamel
Chemical composition by percentage to the quality, specifically includes:
SiO253.37%, Al2O326.53%, F2O30.17%, CaO 1.38%, MgO 3.98%, K2O 2.67%, Na2O
3.04%, ZrO28.86%.
5. the preparation method of the controllable Ceramic Tiles of glaze glossiness according to claim 1, which is characterized in that
The mixing bright glaze includes matting glaze and/or bloom glaze；
The sum of matting glaze and bloom glaze component are 100% in the mixing bright glaze.
6. the preparation method of the controllable Ceramic Tiles of glaze glossiness according to claim 5, which is characterized in that
The chemical composition of the matting glaze is by percentage to the quality, comprising:
SiO248~53%, Al2O314~18%, CaO 6~11%, MgO 0~3%, K2O 0~5%, Na2O 0~5%,
ZnO 0~5%, BaO 6~12%.
7. the preparation method of the controllable Ceramic Tiles of glaze glossiness according to claim 5, which is characterized in that
The chemical composition of the bloom glaze is by percentage to the quality, comprising:
SiO250~60%, Al2O315~18%, CaO 9~15%, MgO 0~3%, K2O 0~5%, Na2O 0~5%,
ZnO 0~5%, BaO 0~5%.
8. a kind of controllable Ceramic Tiles of glaze glossiness, which is characterized in that
The controllable Ceramic Tiles of glaze glossiness are controllably ceramic by the described in any item glaze glossiness of the claims 1~8
It is prepared by the preparation method of brick.
9. the controllable Ceramic Tiles of glaze glossiness according to claim 8, which is characterized in that
The controllable Ceramic Tiles of glaze glossiness successively include: Ceramic Tiles green body, ground glaze layer, pattern decorative layer and mix from the bottom to top
Close glaze layer.
10. the controllable Ceramic Tiles of glaze glossiness according to claim 8, which is characterized in that
The controllable Ceramic Tiles of glaze glossiness successively include: Ceramic Tiles green body, ground glaze layer, mixing glaze layer and pattern from the bottom to top
Decorative layer.