CN106045468A - Imitated Song-Dynasty Ge-kiln crackle-glaze celadon and manufacturing technique thereof - Google Patents
Imitated Song-Dynasty Ge-kiln crackle-glaze celadon and manufacturing technique thereof Download PDFInfo
- Publication number
- CN106045468A CN106045468A CN201610355276.0A CN201610355276A CN106045468A CN 106045468 A CN106045468 A CN 106045468A CN 201610355276 A CN201610355276 A CN 201610355276A CN 106045468 A CN106045468 A CN 106045468A
- Authority
- CN
- China
- Prior art keywords
- glaze
- kiln
- parts
- glazing
- celadon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of porcelain, and particularly relates to an imitated Song-Dynasty Ge-kiln crackle-glaze celadon and a manufacturing technique thereof. The imitated Song-Dynasty Ge-kiln crackle-glaze celadon comprises a body material and a glaze material. The body material is mainly prepared from the following raw materials in parts by weight: 80-90 parts of Zijin clay, 10-20 parts of Xiyuan porcelain clay and 10-20 parts of Huangtan porcelain clay. The glaze material is mainly prepared from the following raw materials in parts by weight: 32-35 parts of Linggen glaze clay, 20-24 parts of quicklime, 3-5 parts of quartz, 3-5 parts of pyrite, 11-13 parts of Dayao Zijin clay and 22-25 parts of yellow fluorite. By using the characteristic that iron oxide appears blue in a high-temperature reduction atmosphere, multiple porcelain clay minerals are used as raw materials to imitate the Southern-Song-Dynasty black body Ge-kiln crackle-glaze celadon in the high-temperature reduction atmosphere; and the imitated finished product has very similar appearance to the Southern-Song-Dynasty black body Ge-kiln crackle-glaze celadon.
Description
Technical field
The invention belongs to porcelain field, hack celadon formula and manufacturing process particularly to a kind of imitation Song-Dynasty-style typeface for brother's kiln.
Background technology
The tire color of brother's kiln porcelain has the multiple color and lusters such as dark-grey, light gray, grey black and the colour of loess, and glaze colours more has pale blue, bluish white, oily
Ash, the difference of bluish yellow, and based on putty.It is mainly characterized by glaze and is covered with the stricture of vagina sheet of be full of cracks, normally referred to as " hacking "
.This sheet stricture of vagina formed by fine cracks, size is different, the depth of crackle color also differs.
Imitation Song-Dynasty-style typeface brother's kiln crack glaze has stronger vitality as the decoration of a kind of art pottery.Due to of the remote past, brother
Kiln porcelain formula and manufacturing process are the most lost, for meeting the consumer demand day by day increased, have tried in recent years recover
Brother's kiln porcelain formula and manufacturing process, but effect is not fully up to expectations.
Summary of the invention
The present invention provides a kind of imitation Song-Dynasty-style typeface to hack celadon formula for brother's kiln, and the prepared product image Southern Song Dynasty's black tire brother's kiln hacks
Celadon, and the glaze of the good cream-coloured glaze of glossiness can be realized.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of imitation Song-Dynasty-style typeface hacks celadon formula for brother's kiln, including tire material and glaze, wherein: described tire material is mainly by following weight portion
Raw material is made: Zijin soil 80-90 part, western source china clay 10-20 part, yellow altar china clay 10-20 part；Described glaze is mainly by following
The raw material of weight portion is made: ridge root glaze soil 32-35 part, quick lime 20-24 part, quartz 3-5 part, troilite 3-5 part and Dayao
Zijin soil 11-13 part and yellow fluorite 22-25 part.The present invention, under high temperature reducing atmospheres, utilizes ferrum oxide at high temperature reduction
Presenting cyan under atmosphere is feature, with multiple china clay mineral as raw material, has copied the Southern Song Dynasty's black tire brother's kiln and has hacked celadon, imitated finished product
Outward appearance is with the Southern Song Dynasty's black tire brother's kiln celadon pole seemingly.The fluorite added not only makes the celadon glaze prepared shinny penetrating, and and sulfur ferrum
Ore deposit makes glaze present the color and luster of cream colour glaze together.
A kind of described imitation Song-Dynasty-style typeface hacks celadon formula taxi driver brother's kiln for brother's kiln and hacks celadon manufacturing process, comprises the following steps:
A, fire biscuit: add water mix homogeneously by all raw materials of described tire material, makes base mud, by described base mud shaping and drying
After, kiln-firing, make biscuit；
B, preparation ceramic glaze: the raw material in described glaze is mixed according to proportioning, after pulverizing, adds water for ball milling, after sieving i.e.
Obtain ceramic glaze；
C, glazing: described ceramic glaze is imposed on described biscuit, dried formation glaze layer in uniform thickness, obtain base substrate, base
Second time glazing is carried out after body cooling；
D, fire: after the glaze layer on base substrate parches naturally, kiln-firing, fire rear kiln discharge and get product；Wherein sintering procedure
Sequentially pass through following several stage: the stage that is rapidly heated, slow temperature rise period and natural cooling.
As preferably, firing middle start-stop temperature and be room temperature, the programming rate in the stage that is rapidly heated is 2-3 DEG C/min, slow
The programming rate of slow temperature rise period is 0.3-0.5 DEG C/min.
As preferably, before glazing, first base substrate is put into biscuiting in kiln and, to 800 DEG C, carries out after its cooling and dedusting for the first time
Leaching glaze, the leaching glaze time is between 10s-15s；Afterwards, put into roasting in kilns to 500 DEG C, after its cooling and dedusting, carry out second time
Glazing.
As preferably, glazing for the second time uses spray glazing, is positioned on rotating disk by biscuit and slowly rotates, and uses compression pump pair
It carries out glazing, stops glazing when glazed thickness is 1.3:1 with carcass thickness ratio.
The invention has the beneficial effects as follows: the present invention uses rational raw ore raw material to test out tire, glaze formula, and at high temperature also
Burning out the thick glaze celadon glaze that glaze layer is abundant, show the cream-coloured glaze whitened in Huang in Primordial Qi atmosphere, such glaze colours can be by ferrum tire
Black quality be covered with comprehensively, it is beautiful that glaze color and luster presents exquisite in texture, gentle class under the setting off of black tire, and glossiness is more preferably.
Accompanying drawing explanation
Fig. 1 is the process chart of the present invention；
Fig. 2 be the present invention burn till heating curve.
Detailed description of the invention
Below by specific embodiment, technical scheme is described in further detail.Should be appreciated that this
Bright enforcement is not limited to the following examples, and any pro forma accommodation and/or the change of being made the present invention all will fall
Enter scope.
In the present invention, if not refering in particular to, all of part, percentage ratio are unit of weight, the equipment used and raw material etc.
All it is commercially available or commonly used in the art.Method in following embodiment, if no special instructions, is the normal of this area
Rule method.
Embodiment 1:
A kind of imitation Song-Dynasty-style typeface hacks celadon formula for brother's kiln, including tire material and glaze, wherein: described tire material is former by following weight portion
Material is made: 80 parts of Zijin soil, western source china clay 18 parts, yellow altar china clay 15 parts；Described glaze is by the raw material system of following weight portion
Become: 32 parts of ridge root glaze soil, quick lime 24 parts, 5 parts of quartz, 5 parts of troilite, Dayao Zijin soil 13 parts, 22 parts of yellow fluorite.
A kind of brother's kiln hacks celadon manufacturing process, and flow process is as it is shown in figure 1, comprise the following steps:
A, fire biscuit: add water mix homogeneously by all raw materials of described tire material, makes base mud, by described base mud shaping and drying
After, kiln-firing, make biscuit；
B, preparation ceramic glaze: the raw material in described glaze is mixed according to proportioning, after pulverizing, adds water for ball milling, after sieving i.e.
Obtain ceramic glaze；
C, glazing: described ceramic glaze is imposed on described biscuit, dried formation glaze layer in uniform thickness, obtain base substrate, base
Second time glazing is carried out after body cooling；
D, fire: after the glaze layer on base substrate parches naturally, kiln-firing, fire rear kiln discharge and get product；Wherein sintering procedure
Sequentially pass through following several stage: the stage that is rapidly heated, slow temperature rise period and natural cooling.
Wherein, glazing process: the Southern Song Dynasty's black tire brother's kiln hacks celadon, and it is mainly characterized in that thin tire thickness glaze, and glaze is thicker than tire, therefore,
Glazing process is particularly critical.The present embodiment mainly uses repeatedly glazing method, and this glazing method is divided into leaching glaze and glaze spraying two parts.Glazing
Before, first base substrate to be put in kiln biscuiting to about 800 DEG C, after its cooling and dedusting, carry out soaking for the first time glaze, the leaching glaze time is
Between 10s 15s.Afterwards, put into roasting in kilns to 500 DEG C, after its cooling and dedusting, carry out second time glazing.Glazing for the second time
Use spray glazing, biscuit is positioned on rotating disk and slowly rotates, use compression pump that it is carried out glazing, treat glazed thickness and carcass
Glazing is stopped when thickness ratio is about 1.3:1.
Firing process: in order to ensure products appearance effect and improve yield rate, the present embodiment uses shuttle kiln slowly to burn till,
Enter the strong reductive firing stages in 1080 DEG C, and transfer in 1200 DEG C and weak be reduced to 1320 DEG C of only fire, total time-consuming nearly 18h.It burns
Become curve as shown in Figure 2.Firing middle start-stop temperature and be room temperature, the programming rate in the stage that is rapidly heated is 2-3 DEG C/min, slow
The programming rate of slow temperature rise period is 0.3-0.5 DEG C/min.
Embodiment 2:
A kind of imitation Song-Dynasty-style typeface hacks celadon formula for brother's kiln, including tire material and glaze, wherein: described tire material is former by following weight portion
Material is made: 90 parts of Zijin soil, western source china clay 15 parts, yellow altar china clay 20 parts；Described glaze is by the raw material system of following weight portion
Become: 35 parts of ridge root glaze soil, quick lime 20 parts, 3 parts of quartz, 3 parts of troilite, Dayao Zijin soil 11 parts, 25 parts of yellow fluorite.
Brother's kiln hacks celadon manufacturing process with embodiment 1.
Embodiment 3:
A kind of imitation Song-Dynasty-style typeface hacks celadon formula for brother's kiln, including tire material and glaze, wherein: described tire material is former by following weight portion
Material is made: 85 parts of Zijin soil, western source china clay 16 parts, yellow altar china clay 18 parts；Described glaze is by the raw material system of following weight portion
Become: 34 parts of ridge root glaze soil, quick lime 22 parts, 3 parts of quartz, 5 parts of troilite, Dayao Zijin soil 12 parts, 24 parts of yellow fluorite.Brother
Kiln hacks celadon manufacturing process with embodiment 1.
The present invention has made black tire brother's kiln by many experiments and has hacked celadon tire material, and such tire material has preferable mouldability
Can, present black when burning till for 1300 DEG C 1320 DEG C.Celadon glaze outward appearance effect is hacked for burning out tire brother's kiln black with the Southern Song Dynasty
Celadon as fruit, by many experiments, obtains rational formula, finally burns out glaze exquisite in texture, gentle class is beautiful, victory is beautiful refined
Causing, glaze colours is simple and elegant, the cream-coloured glaze of whiting in Huang.
Embodiment described above is the one preferably scheme of the present invention, not makees the present invention any pro forma
Limit, on the premise of without departing from the technical scheme described in claim, also have other variant and remodeling.
Claims (5)
1. an imitation Song-Dynasty-style typeface hacks celadon formula for brother's kiln, it is characterised in that: include tire material and glaze, wherein: described tire material is main
It is made up of the raw material of following weight portion: Zijin soil 80-90 part, western source china clay 10-20 part, yellow altar china clay 10-20 part；Described
Glaze is mainly made up of the raw material of following weight portion: ridge root glaze soil 32-35 part, quick lime 20-24 part, quartz 3-5 part, sulfur ferrum
Ore deposit 3-5 part, Dayao Zijin soil 11-13 part and yellow fluorite 22-25 part.
2. imitation Song-Dynasty-style typeface hacks celadon formula taxi driver brother's kiln for brother's kiln and hacks a celadon manufacturing process according to claim 1, and it is special
Levy and be, comprise the following steps:
A, fire biscuit: add water mix homogeneously by all raw materials of described tire material, makes base mud, by described base mud shaping and drying
After, kiln-firing, make biscuit；
B, preparation ceramic glaze: the raw material in described glaze is mixed according to proportioning, after pulverizing, adds water for ball milling, after sieving i.e.
Obtain ceramic glaze；
C, glazing: described ceramic glaze is imposed on described biscuit, dried formation glaze layer in uniform thickness, obtain base substrate, base
Second time glazing is carried out after body cooling；
D, fire: after the glaze layer on base substrate parches naturally, kiln-firing, fire rear kiln discharge and get product；Wherein sintering procedure
Sequentially pass through following several stage: the stage that is rapidly heated, slow temperature rise period and natural cooling.
Manufacturing process the most according to claim 2, it is characterised in that: fire middle start-stop temperature and be room temperature, be rapidly heated
The programming rate in stage is 2-3 DEG C/min, and the programming rate of slow temperature rise period is 0.3-0.5 DEG C/min.
Manufacturing process the most according to claim 2, it is characterised in that: before glazing, first base substrate is put in kiln biscuiting to 800
DEG C, after its cooling and dedusting, carrying out soaking for the first time glaze, the leaching glaze time is between 10s-15s；Afterwards, roasting in kilns is put into 500
DEG C, after its cooling and dedusting, carry out second time glazing.
Manufacturing process the most according to claim 2, it is characterised in that: glazing for the second time uses spray glazing, is placed by biscuit
Slowly rotate on rotating disk, use compression pump that it is carried out glazing, stop when glazed thickness is 1.3:1 with carcass thickness ratio
Glazing.