CN108976502A - A kind of environment friendly bacteriostatic latex bed mattress - Google Patents
A kind of environment friendly bacteriostatic latex bed mattress Download PDFInfo
- Publication number
- CN108976502A CN108976502A CN201810888739.9A CN201810888739A CN108976502A CN 108976502 A CN108976502 A CN 108976502A CN 201810888739 A CN201810888739 A CN 201810888739A CN 108976502 A CN108976502 A CN 108976502A
- Authority
- CN
- China
- Prior art keywords
- parts
- bed mattress
- environment friendly
- latex bed
- friendly bacteriostatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of environment friendly bacteriostatic latex bed mattress, it is related to latex bed mattress technical field, it is made of following component: the modified hydrogel of natural emulsion, chitosan, sulphur, 2,4- dichlorobenzoperoxide, literary bamboo leaf powder, white carbon black, activating agent, deep grass meal, nano-titanium dioxide；A kind of environment friendly bacteriostatic latex bed mattress prepared by the present invention has good mechanical strength and resilience performance, while having good antimildew and antibacterial effect, and permeability is good, and working life is longer, and preparation method is simple, easy to industrialized production.
Description
Technical field
The invention belongs to latex bed mattress technical fields, and in particular to a kind of environment friendly bacteriostatic latex bed mattress.
Background technique
Mattress is the regular supplies of people's home life, plays the role of very important, city at present to daily life
Mattress on field mainly has cotton pad, sponge matress, latex bed mattress, sping mattress, palm mattress etc., due to cotton pad resilience not
It is good, and it is easy hardened, the gas permeability of sping mattress is preferable, but spring bed core must be with soft stuffing materials such as sponge, latexes
Disperse human bady gravitational for matting layer, the fiber of monofilament pad is easy aging and becomes fragile to fracture, and buckle resistance can be bad, and palm silk
Deng the case of manufacture filling mattress material, but this filling mattress material generally requires the plant fiber using adhesive by dispersion
Bonding is got up, and therefore, the product that developed contains the noxious materials such as formaldehyde, is unfavorable for human health.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of environment friendly bacteriostatic latex bed mattress is provided.
The present invention is achieved by the following technical solutions:
A kind of environment friendly bacteriostatic latex bed mattress, is made of following component by weight: 90 parts of natural emulsion, 3-5 parts of chitosan, sulphur
1.4 parts of sulphur, 2,4- dichlorobenzoperoxide are modified hydrogel 8-10 parts, literary 3.6 parts of bamboo leaf powder, 2.2 parts of white carbon black, activating agent
1.5 parts, 1.5 parts of deep grass meal, 1.6 parts of nano-titanium dioxide.
Further, 2, the 4- dichlorobenzoperoxide modified water gel process for preparing are as follows:
Polyvinyl alcohol, hyaluronic acid are put into distilled water solution, is stirred at 85 DEG C, is formed uniform solution, then adjust the temperature to
50 DEG C, then add the sodium metasilicate of polyvinyl alcohol quality 10% and continue to stir 30min, then add the 2,4- of polyvinyl alcohol quality 0.35%
Dichlorobenzoperoxide is heated to 68 DEG C under inert gas protection, reacts 2 hours, then discharges, dry to containing
Water rate to 15% to get.
Further, the polyvinyl alcohol, hyaluronic acid, distilled water mixing mass ratio are 10:3:15.
Further, the inert gas is neon.
Further, the asparagus fern leaf powder, preparation method thereof are as follows: use mass fraction to soak for 5% sodium chloride solution on asparagus fern leaf
Steep 30min, be then dried again to constant weight, crush, cross 200 meshes to get.
Further, the activating agent is iso-cyanuric acid triallyl ester.
Further, the lopseed powder, preparation method thereof are as follows:
It uses mass fraction to impregnate 20min for 5.5% sodium chloride solution lopseed, is then dried to constant weight, crushes again,
Cross 250 meshes to get.
The present invention has the advantage that a kind of environment friendly bacteriostatic latex bed mattress prepared by the present invention compared with prior art, has
Good mechanical strength and resilience performance, while there is good antimildew and antibacterial effect, permeability is good, and working life is longer,
And preparation method is simple, easy to industrialized production.
Specific embodiment
Embodiment 1
A kind of environment friendly bacteriostatic latex bed mattress, is made of following component by weight: 90 parts of natural emulsion, 3 parts of chitosan, sulphur
1.4 parts, modified 8 parts of the hydrogel of 2,4- dichlorobenzoperoxide, literary 3.6 parts of bamboo leaf powder, 2.2 parts of white carbon black, activating agent 1.5
Part, 1.5 parts of deep grass meal, 1.6 parts of nano-titanium dioxide.
Further, 2, the 4- dichlorobenzoperoxide modified water gel process for preparing are as follows:
Polyvinyl alcohol, hyaluronic acid are put into distilled water solution, is stirred at 85 DEG C, is formed uniform solution, then adjust the temperature to
50 DEG C, then add the sodium metasilicate of polyvinyl alcohol quality 10% and continue to stir 30min, then add the 2,4- of polyvinyl alcohol quality 0.35%
Dichlorobenzoperoxide is heated to 68 DEG C under inert gas protection, reacts 2 hours, then discharges, dry to containing
Water rate to 15% to get.
Further, the polyvinyl alcohol, hyaluronic acid, distilled water mixing mass ratio are 10:3:15.
Further, the inert gas is neon.
Further, the asparagus fern leaf powder, preparation method thereof are as follows: use mass fraction to soak for 5% sodium chloride solution on asparagus fern leaf
Steep 30min, be then dried again to constant weight, crush, cross 200 meshes to get.
Further, the activating agent is iso-cyanuric acid triallyl ester.
Further, the lopseed powder, preparation method thereof are as follows:
It uses mass fraction to impregnate 20min for 5.5% sodium chloride solution lopseed, is then dried to constant weight, crushes again,
Cross 250 meshes to get.
Embodiment 2
A kind of environment friendly bacteriostatic latex bed mattress, is made of following component by weight: 90 parts of natural emulsion, 5 parts of chitosan, sulphur
1.4 parts, modified 10 parts of the hydrogel of 2,4- dichlorobenzoperoxide, literary 3.6 parts of bamboo leaf powder, 2.2 parts of white carbon black, activating agent 1.5
Part, 1.5 parts of deep grass meal, 1.6 parts of nano-titanium dioxide.
Further, 2, the 4- dichlorobenzoperoxide modified water gel process for preparing are as follows:
Polyvinyl alcohol, hyaluronic acid are put into distilled water solution, is stirred at 85 DEG C, is formed uniform solution, then adjust the temperature to
50 DEG C, then add the sodium metasilicate of polyvinyl alcohol quality 10% and continue to stir 30min, then add the 2,4- of polyvinyl alcohol quality 0.35%
Dichlorobenzoperoxide is heated to 68 DEG C under inert gas protection, reacts 2 hours, then discharges, dry to containing
Water rate to 15% to get.
Further, the polyvinyl alcohol, hyaluronic acid, distilled water mixing mass ratio are 10:3:15.
Further, the inert gas is neon.
Further, the asparagus fern leaf powder, preparation method thereof are as follows: use mass fraction to soak for 5% sodium chloride solution on asparagus fern leaf
Steep 30min, be then dried again to constant weight, crush, cross 200 meshes to get.
Further, the activating agent is iso-cyanuric acid triallyl ester.
Further, the lopseed powder, preparation method thereof are as follows:
It uses mass fraction to impregnate 20min for 5.5% sodium chloride solution lopseed, is then dried to constant weight, crushes again,
Cross 250 meshes to get.
Embodiment 3
A kind of environment friendly bacteriostatic latex bed mattress, is made of following component by weight: 90 parts of natural emulsion, 4 parts of chitosan, sulphur
1.4 parts, modified 9 parts of the hydrogel of 2,4- dichlorobenzoperoxide, literary 3.6 parts of bamboo leaf powder, 2.2 parts of white carbon black, activating agent 1.5
Part, 1.5 parts of deep grass meal, 1.6 parts of nano-titanium dioxide.
Further, 2, the 4- dichlorobenzoperoxide modified water gel process for preparing are as follows:
Polyvinyl alcohol, hyaluronic acid are put into distilled water solution, is stirred at 85 DEG C, is formed uniform solution, then adjust the temperature to
50 DEG C, then add the sodium metasilicate of polyvinyl alcohol quality 10% and continue to stir 30min, then add the 2,4- of polyvinyl alcohol quality 0.35%
Dichlorobenzoperoxide is heated to 68 DEG C under inert gas protection, reacts 2 hours, then discharges, dry to containing
Water rate to 15% to get.
Further, the polyvinyl alcohol, hyaluronic acid, distilled water mixing mass ratio are 10:3:15.
Further, the inert gas is neon.
Further, the asparagus fern leaf powder, preparation method thereof are as follows: use mass fraction to soak for 5% sodium chloride solution on asparagus fern leaf
Steep 30min, be then dried again to constant weight, crush, cross 200 meshes to get.
Further, the activating agent is iso-cyanuric acid triallyl ester.
Further, the lopseed powder, preparation method thereof are as follows:
It uses mass fraction to impregnate 20min for 5.5% sodium chloride solution lopseed, is then dried to constant weight, crushes again,
Cross 250 meshes to get.
Environment friendly bacteriostatic latex bed mattress prepared by the present invention is up to 99% to Escherichia coli sterilizing rate.
Claims (7)
1. a kind of environment friendly bacteriostatic latex bed mattress, which is characterized in that be made by weight of following component: 90 parts of natural emulsion,
3-5 parts of chitosan, 1.4 parts of sulphur, 2,4- dichlorobenzoperoxide are modified hydrogel 8-10 parts, literary 3.6 parts of bamboo leaf powder, hard charcoal
Black 2.2 parts, 1.5 parts of activating agent, 1.5 parts of deep grass meal, 1.6 parts of nano-titanium dioxide.
2. a kind of environment friendly bacteriostatic latex bed mattress according to claim 1, which is characterized in that 2, the 4- dichloro benzoyl peroxide
Formyl modified water gel process for preparing are as follows:
Polyvinyl alcohol, hyaluronic acid are put into distilled water solution, is stirred at 85 DEG C, is formed uniform solution, then adjust the temperature to
50 DEG C, then add the sodium metasilicate of polyvinyl alcohol quality 10% and continue to stir 30min, then add the 2,4- of polyvinyl alcohol quality 0.35%
Dichlorobenzoperoxide is heated to 68 DEG C under inert gas protection, reacts 2 hours, then discharges, dry to containing
Water rate to 15% to get.
3. a kind of environment friendly bacteriostatic latex bed mattress according to claim 2, which is characterized in that the polyvinyl alcohol, hyalomitome
Acid, distilled water mixing mass ratio are 10:3:15.
4. a kind of environment friendly bacteriostatic latex bed mattress according to claim 2, which is characterized in that the inert gas is neon.
5. a kind of environment friendly bacteriostatic latex bed mattress according to claim 1, which is characterized in that the asparagus fern leaf powder, preparation method thereof
Are as follows: it uses mass fraction to impregnate 30min for 5% sodium chloride solution on asparagus fern leaf, is then dried to constant weight, crushes, mistake again
200 meshes to get.
6. a kind of environment friendly bacteriostatic latex bed mattress according to claim 1, which is characterized in that the activating agent is triallyl
Fulminuric acid ester.
7. a kind of environment friendly bacteriostatic latex bed mattress according to claim 1, which is characterized in that the lopseed powder, preparation method thereof
Are as follows:
It uses mass fraction to impregnate 20min for 5.5% sodium chloride solution lopseed, is then dried to constant weight, crushes again,
Cross 250 meshes to get.