CN108796813A - The manufacture craft of non-woven silk mask base fabric - Google Patents
The manufacture craft of non-woven silk mask base fabric Download PDFInfo
- Publication number
- CN108796813A CN108796813A CN201810618830.9A CN201810618830A CN108796813A CN 108796813 A CN108796813 A CN 108796813A CN 201810618830 A CN201810618830 A CN 201810618830A CN 108796813 A CN108796813 A CN 108796813A
- Authority
- CN
- China
- Prior art keywords
- silk
- cocoon
- base fabric
- mask base
- silkworm
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of manufacture crafts of non-woven silk mask base fabric; specific the step of describing work; in the technique of the present invention; due to without strong degumming process; entire process conditions are milder; without mechanical treatment, therefore the insoluble mistake of sericin can be preferably protected, these sericins on silk mask with having natural cosmetic result.
Description
Technical field
The present invention relates to a kind of manufacture crafts of non-woven silk mask base fabric.
Background technology
Silk is as the industry for having developed thousands of years, and in beauty industry foreground, for another example this is wide, and why it is as silk
The research of mask substrate is but so few, and in fact, real silk mask base fabric has very unlike " silk technique " facial mask
Good tensile property, it may be said that " silk technique " oneself through having surmounted the appearance of real silk mask completely.Why real silkworm
Silk can not produce such mask substrate, most important the reason is that silk water-retaining property itself is bad, and nothing after base fabric is made
Method retain Essence, it is even more impossible to skin attachement.If not solving this technical barrier, can not only it hinder silk in beauty industry
Using, and want to be extended to other application field to be also extremely difficult.This is also the weight that silk industry is gone no further always
Want reason.
In addition, the cost of silk raw material is too high, there is the trend being good in recent years.Under the premise of technical maturity, one is made
100% silk mask base fabric of money, the price evaluation of monolithic base fabric is also at 1 yuan or so.
Finally, processing technology is difficult point.Technical limitation is not so that real silk mask is consumed also on the market
Person is widely used.Present silk mask base fabric mostly uses greatly spun lacing and is processed without spinning process, not due to silk fiber electric conductivity
It is good, the phenomenon that electrostatic is easy tod produce in carding process, and generated electrostatic can be kept for a long time, cause curling round the roll, lead to water
Carding process before thorn is unable to complete successfully.
Invention content
The purpose of the present invention is to provide a kind of manufacture crafts of non-woven silk mask base fabric, to solve above-mentioned background skill
The problem of being proposed in art.
To achieve the above object, the present invention provides the following technical solutions：
The manufacture craft of non-woven silk mask base fabric, steps are as follows,
S1, decatize:First by silk cocoon at NaHC03 containing 0.3g/L, 0.5g/L penetrating agent JFCs, the pre- place that temperature is 40 DEG C
Reason liquid in impregnate 0.5h, then the wet process 2h in the soda ash steam of 2g/L, is pulled open after washing lye in cold water, it is upper bow at
Type；
S2, shell cocoon networking:Silk cocoon after decatize is cleaned with cold water, to remove the alkaline agent on silk cocoon.It is subsequently placed in room temperature water,
Cocoon layer is gently torn with hand, backhand is sleeved on the finger closed up, picks up silkworm chrysalis and other sundries, forms the silk as hat-shaped
Obtained silkworm cap after so repeating 4-5 silk cocoon, then is directly put on the arch of similar parabola line by the string bag, referred to as silkworm cap
The continuous pocket of certain size is made in mold；
S3, water conservation processing：Bath raio is set as 20：1, sour bubble is carried out in a concentration of 0. 3% HaS04 aqueous solutions, makes silk fibroin
Dimension fully swelling, taken amount lOg/L, pH 3, temperature is impregnates 60min in 60 DEG C of warm polyether modified silicon oil, using brine
It washes, room temperature washing 5min, neutralization, which is placed in 105-110 DEG C of baking oven, dries；
S4, it is fixed-type：The continuous pocket made is impregnated into 15min in the aqueous solution that content is 12% sericin powder, is used again after drying is dry
Vapour iron is pressed the silk mask base fabric after being shaped.
Compared with prior art, the beneficial effects of the invention are as follows：In the technique of the present invention, at without strong degumming
Reason, entire process conditions are milder, no mechanical treatment, therefore can preferably protect the insoluble mistake of sericin, these silk gum eggs
In vain with having natural cosmetic result on silk mask.
Specific implementation mode
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
The every other embodiment that art personnel are obtained without making creative work belongs to the model that the present invention protects
It encloses.
The manufacture craft of non-woven silk mask base fabric, steps are as follows,
S1, decatize:First by silk cocoon at NaHC03 containing 0.3g/L, 0.5g/L penetrating agent JFCs, the pre- place that temperature is 40 DEG C
Reason liquid in impregnate 0.5h, then the wet process 2h in the soda ash steam of 2g/L, is pulled open after washing lye in cold water, it is upper bow at
Type；
S2, shell cocoon networking:Silk cocoon after decatize is cleaned with cold water, to remove the alkaline agent on silk cocoon.It is subsequently placed in room temperature water,
Cocoon layer is gently torn with hand, backhand is sleeved on the finger closed up, picks up silkworm chrysalis and other sundries, forms the silk as hat-shaped
Obtained silkworm cap after so repeating 4-5 silk cocoon, then is directly put on the arch of similar parabola line by the string bag, referred to as silkworm cap
The continuous pocket of certain size is made in mold；
S3, water conservation processing：Bath raio is set as 20：1, sour bubble is carried out in a concentration of 0. 3% HaS04 aqueous solutions, makes silk fibroin
Dimension fully swelling, taken amount lOg/L, pH 3, temperature is impregnates 60min in 60 DEG C of warm polyether modified silicon oil, using brine
It washes, room temperature washing 5min, neutralization, which is placed in 105-110 DEG C of baking oven, dries；
S4, it is fixed-type：The continuous pocket made is impregnated into 15min in the aqueous solution that content is 12% sericin powder, is used again after drying is dry
Vapour iron is pressed the silk mask base fabric after being shaped.
Then it is tested, is compared in the silk cocoon of prior art and the mask substrate of present invention process making by LC-MS/MS
Sericin Sui condition, it has been found that:151 kinds of albumen are extracted in the silk cocoon of present invention process, are carried after mask substrate is made
122 kinds of albumen are taken out, illustrate that present invention process can be very good to retain sericin.The former material that one side present invention process uses
Material is silk cocoon, and prior art（Spun lacing method and paper process）In raw material be part degumming, silk cocoon itself has more
Sericin, even if also a large amount of sericins residual if postorder has partial loss in decatize, on the other hand, the present invention
Technique wants milder with respect to spun lacing method and paper process, and in addition to decatize, the complete alkali-free of other flows can be very good without high temperature
Retain sericin.
In the albumen detected in mask substrate, Seroinl is the small molecular weight protein one by one identified in silk, this
A albumen is multifunctional protein, has antimicrobial antiviral activity, it is also possible to take part in the assembling of fibroin.Silk gum 1 is sericin
One kind, belong to internal layer silk gum, play a part of protection and gluing fibroin in fibroin periphery, meanwhile, silk gum 1 have very strong suction
It is moist, good performance of keeping humidity can be provided for skin.Protease inhibitors can inhibit the proteinase activity of fungus secretion, can
To ensure the integrality of silk cocoon silk, to protect the safety of pupa in silk cocoon.These albumen are retained in silk mask base fabric, will be assigned
Its natural moisturizing antibiotic effect is given, achievees the effect that beauty.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (1)
1. the manufacture craft of non-woven silk mask base fabric, it is characterized in that：Steps are as follows,
S1, decatize:First by silk cocoon at NaHC03 containing 0.3g/L, 0.5g/L penetrating agent JFCs, the pre- place that temperature is 40 DEG C
Reason liquid in impregnate 0.5h, then the wet process 2h in the soda ash steam of 2g/L, is pulled open after washing lye in cold water, it is upper bow at
Type；
S2, shell cocoon networking:Silk cocoon after decatize is cleaned with cold water, to remove the alkaline agent on silk cocoon；It is subsequently placed in room temperature water,
Cocoon layer is gently torn with hand, backhand is sleeved on the finger closed up, picks up silkworm chrysalis and other sundries, forms the silk as hat-shaped
Obtained silkworm cap after so repeating 4-5 silk cocoon, then is directly put on the arch of similar parabola line by the string bag, referred to as silkworm cap
The continuous pocket of certain size is made in mold；
S3, water conservation processing：Bath raio is set as 20：1, sour bubble is carried out in a concentration of 0. 3% HaS04 aqueous solutions, makes silk fibroin
Dimension fully swelling, taken amount lOg/L, pH 3, temperature is impregnates 60min in 60 DEG C of warm polyether modified silicon oil, using brine
It washes, room temperature washing 5min, neutralization, which is placed in 105-110 DEG C of baking oven, dries；
S4, it is fixed-type：The continuous pocket made is impregnated into 15min in the aqueous solution that content is 12% sericin powder, is used again after drying is dry
Vapour iron is pressed the silk mask base fabric after being shaped.