CN108134046A - 一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法 - Google Patents
一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法 Download PDFInfo
- Publication number
- CN108134046A CN108134046A CN201810020192.0A CN201810020192A CN108134046A CN 108134046 A CN108134046 A CN 108134046A CN 201810020192 A CN201810020192 A CN 201810020192A CN 108134046 A CN108134046 A CN 108134046A
- Authority
- CN
- China
- Prior art keywords
- coprecipitation
- positive electrode
- carbonate precursor
- mentioned steps
- reaction kettle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法,主要包括以下步骤:1)分别配置金属盐溶液、碱溶液和络合剂溶液并加入到主反应釜,一定条件下进行共沉淀反应;2)将主反应釜的固体沉淀产物进行脱水、洗涤及干燥处理后制得碳酸盐前驱体;3)将主反应釜的上清液和离心脱水后的废水汇集并采用RO膜进行分离,其纯水循环用作洗涤用水,浓水进入二次反应釜;4)加碱溶液调配浓水组分进行二次共沉淀反应,其固体沉淀产物循环至主反应釜;5)将二次反应釜的上清液进行高效蒸发结晶,制得硫酸钠副产物。本发明整个生产过程做到清洁生产,其中金属盐完全沉淀、产品产率高,无需添加其他药剂,同时废水零排放,无重金属污染问题。
Description
技术领域
本发明涉及一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法。
背景技术
锂离子电池作为二次电池,已广泛商业化应用于3C、电工工具、电动自行车等领域中,并且在混合电动车、纯电动车及储能领域也有着良好的应用前景。锂离子电池主要有正极、负极、电解液和隔膜等组成,而正极成品材料又主要通过正极材料前驱体和锂盐进行混合煅烧后制得。
目前共沉淀法生产锂离子电池正极材料前驱体主要有氢氧化物、碳酸盐和氧化物三种类型。现有比较成熟的技术主要是氢氧化物和碳酸盐前驱体,两者生产废水均含有镍钴锰金属离子、氨氮、硫酸根和钠离子等,前者需要在氮气气氛的保护下进行共沉淀反应,反应条件严格,反应体系pH值高,生产废水的大量排放不仅对水体环境造成严重的破坏,也降低了生产过程的经济性。
现有技术CN106957124A公开了一种三元正极材料生产废水的处理方法及处理***,针对pH值为10~14的生产废水,该方法采用了膜分离技术,以硫酸为吸收液进行脱氨处理,同时采用硫酸进行固体沉淀物的酸溶处理,操作过程多次需要用到硫酸,工艺流程复杂,操作危险。现有技术CN106430783A公开了一种三元前驱体废水处理***及处理方法,该处理***和处理方法采用了电解、脱氨、精馏、中和、蒸发-结晶、浓缩等化工操作单元,其工艺流程复杂,废水处理成本高。现有技术CN101624248A公开了一种镍钴锰酸锂生产废水的处理方法,该处理方法需要设置多个pH值调节池及沉淀池,其占地面积大,需另外投加处理药剂,并且同样需要进行脱氨处理。
发明内容
本发明针对以上所述现有技术存在的技术缺陷,提供了一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法,通过设置RO膜和二次反应釜,使整个生产过程做到清洁生产,其中金属盐完全沉淀、产品产率高,无需添加其他药剂,同时实现废水零排放,无重金属污染问题。
为实现上述目的,本发明采用如下技术方案,具体包括以下步骤:
1)采用去离子水分别配置一定摩尔浓度的金属盐溶液、碱溶液和络合剂溶液,按一定速率加入到主反应釜,将所述主反应釜控制在一定的pH值范围内,恒温搅拌进行共沉淀反应;
2)将上述步骤1)中主反应釜的固体沉淀产物进行多次离心脱水和加水洗涤,最后完成干燥处理后即可制得正极材料碳酸盐前驱体;
3)将上述步骤1)中主反应釜的上清液和上述步骤2)中离心脱水后的废水进行汇集并采用多级RO膜进行分离,分离后的纯水循环用作上述步骤2)中的洗涤用水,浓水进入到二次反应釜;
4)根据上述步骤3)中二次反应釜浓水所含金属盐溶液和络合剂含量进行组分调配,添加上述步骤1)中的碱溶液,将所述二次反应釜同样控制在一定的pH值范围内,恒温搅拌进行二次共沉淀反应,其固体沉淀产物循环至上述步骤1)中的主反应釜,整个生产过程中的金属盐完全沉淀,无重金属废水外排,同时络合剂得到循环使用;
5)将上述步骤4)中二次反应釜的上清液进行高效蒸发结晶,制得硫酸钠副产物。
优选地,所述步骤1)或步骤4)中反应釜内的pH值为7-9。
优选地,所述步骤1)中的碱溶液为碳酸钠溶液,其摩尔浓度为1-3mol/L。
优选地,所述步骤1)中盐溶液为硫酸镍、硫酸钴和硫酸锰的混合盐溶液,其摩尔浓度为1-3mol/L。
优选地,所述步骤1)中络合剂溶液为氨水,其摩尔浓度为0.2-0.6mol/L。
优选地,所述步骤2)中多次离心脱水和加水洗涤,其次数为1-5次,洗涤后离心脱水的废水硫酸钠含量小于500ppm。
优选地,所述步骤3)中RO膜回收率为30%-60%。
本发明的有益效果:
1、通过RO膜分离和二次反应釜的设置进行纯水循环回用,实现废水零排放,浓水进行二次共沉淀反应,使金属盐得到完全沉淀,提高了碳酸盐前驱体的产品产率,无重金属污染问题。
2、整个生产过程无需额外添加任何药剂进行废水处理,占地面积小。
3、废水处理过程中无需进行脱氨操作,整个生产工艺流程简单,操作简便。
附图说明
图1是本发明一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法的工艺流程图。
具体实施方式
以下通过具体实施例结合附图对本发明作进一步说明。
实施例1
如图1所示,一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法,包括以下步骤:
1)采用去离子水分别配置1mol/L的硫酸镍、硫酸钴和硫酸锰混合盐溶液、1mol/L的碳酸钠溶液和和0.25mol/L的氨水溶液,按一定速率加入到主反应釜,将所述主反应釜的pH值控制在7.8左右,60℃恒温水浴搅拌进行共沉淀反应;
2)将上述步骤1)中主反应釜的固体沉淀产物进行3次离心脱水和2次加水洗涤后,废水硫酸钠含量为320ppm,接着进行干燥处理,即可制得正极材料碳酸盐前驱体;
3)将上述步骤1)中主反应釜的上清液和上述步骤2)中离心脱水后的废水进行汇集并采用多级RO膜进行分离,RO膜回收率为35%,分离后的纯水循环用作上述步骤2)中的洗涤用水,浓水进入到二次反应釜;
4)根据上述步骤3)中二次反应釜浓水所含硫酸镍、硫酸钴和硫酸锰混合盐溶液和氨氮含量进行组分调配,添加上述步骤1)中的碳酸钠溶液,将所述二次反应釜pH值同样控制7.8左右,60℃恒温水浴搅拌进行二次共沉淀反应,其固体沉淀产物循环至上述步骤1)中的主反应釜,整个生产过程中的金属盐完全沉淀,无重金属废水外排,同时络合剂氨水得到循环使用;
5)将上述步骤4)中二次反应釜的上清液进行高效蒸发结晶,制得硫酸钠副产物。
实施例2
一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法,包括以下步骤:
1)采用去离子水分别配置2.5mol/L的硫酸镍、硫酸钴和硫酸锰混合盐溶液、2.5mol/L的碳酸钠溶液和和0.45mol/L的氨水溶液,按一定速率加入到主反应釜,将所述主反应釜的pH值控制在8.4左右,60℃恒温水浴搅拌进行共沉淀反应;
2)将上述步骤1)中主反应釜的固体沉淀产物进行5次离心脱水和4次加水洗涤后,废水硫酸钠含量为480ppm,接着进行干燥处理,即可制得正极材料碳酸盐前驱体;
3)将上述步骤1)中主反应釜的上清液和上述步骤2)中离心脱水后的废水进行汇集并采用多级RO膜进行分离,RO膜回收率为55%,分离后的纯水循环用作上述步骤2)中的洗涤用水,浓水进入到二次反应釜;
4)根据上述步骤3)中二次反应釜浓水所含硫酸镍、硫酸钴和硫酸锰混合盐溶液和氨氮含量进行组分调配,添加上述步骤1)中的碳酸钠溶液,将所述二次反应釜pH值同样控制8.4左右,60℃恒温水浴搅拌进行二次共沉淀反应,其固体沉淀产物循环至上述步骤1)中的主反应釜,整个生产过程中的金属盐完全沉淀,无重金属废水外排,同时络合剂氨水得到循环使用;
5)将上述步骤4)中二次反应釜的上清液进行高效蒸发结晶,制得硫酸钠副产物。
以上内容仅仅是对本发明结构所作的举例和说明,所属本技术领域的技术人员对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代,只要不偏离发明的结构或者超越本权利要求书所定义的范围,均应属于本发明的保护范围。
Claims (7)
1.一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法,其特征在于:包括以下步骤:
1)采用去离子水分别配置一定摩尔浓度的金属盐溶液、碱溶液和络合剂溶液,按一定速率加入到主反应釜中,将所述主反应釜控制在一定的pH值范围内,恒温搅拌进行共沉淀反应;
2)将上述步骤1)中主反应釜的固体沉淀产物进行多次离心脱水和加水洗涤,最后完成干燥处理后即可制得正极材料碳酸盐前驱体;
3)将上述步骤1)中主反应釜的上清液和上述步骤2)中离心脱水后的废水进行汇集并采用多级RO膜进行分离,分离后的纯水循环用作上述步骤2)中的洗涤用水,浓水进入到二次反应釜;
4)根据上述步骤3)中二次反应釜浓水所含金属盐溶液和络合剂含量进行组分调配,添加上述步骤1)中的碱溶液,将所述二次反应釜同样控制在一定的pH值范围内,恒温搅拌进行二次共沉淀反应,其固体沉淀产物循环至上述步骤1)中的主反应釜,整个生产过程中的金属盐完全沉淀,无重金属废水外排,同时络合剂得到循环使用;
5)将上述步骤4)中二次反应釜的上清液进行高效蒸发结晶,制得硫酸钠副产物。
2.根据权利要求1所述的一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法,其特征在于:所述步骤1)或步骤4)中反应釜内的pH值为7-9。
3.根据权利要求1所述的一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法,其特征在于:所述步骤1)中的碱溶液为碳酸钠溶液,其摩尔浓度为1-3mol/L。
4.根据权利要求1所述的一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法,其特征在于:所述步骤1)中盐溶液为硫酸镍、硫酸钴和硫酸锰的混合盐溶液,其摩尔浓度为1-3mol/L。
5.根据权利要求1所述的一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法,其特征在于:所述步骤1)中络合剂为氨水,其摩尔浓度为0.2-0.6mol/L。
6.根据权利要求1所述的一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法,其特征在于:所述步骤2)中多次离心脱水和加水洗涤,其次数为1-5次,洗涤后离心脱水的废水硫酸钠含量小于500ppm。
7.根据权利要求1所述的一种共沉淀法正极材料碳酸盐前驱体的清洁生产方法,其特征在于:所述步骤3)中RO膜回收率为30%-60%。