CN107902893A - A kind of refrigerator shelf prepared using discarded glass - Google Patents
A kind of refrigerator shelf prepared using discarded glass Download PDFInfo
- Publication number
- CN107902893A CN107902893A CN201711059713.5A CN201711059713A CN107902893A CN 107902893 A CN107902893 A CN 107902893A CN 201711059713 A CN201711059713 A CN 201711059713A CN 107902893 A CN107902893 A CN 107902893A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass
- discarded glass
- refrigerator shelf
- discarded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of refrigerator shelf prepared using discarded glass, is made of the component of following weight：80 100 parts of discarded glass, 10 20 parts of α amyl groups cinnamic aldehyde, 5 10 parts of Tissuemat E, 36 parts of carborundum, 20 30 parts of calcined diatomite, 25 parts of rosin, 25 parts of barium carbonate, 10 15 parts of calcium carbonate, 48 parts of quartz sand, 36 parts of calcium silicide, 5 10 parts of ooze, 25 parts of silicon nitride, 15 18 parts of industrial soda, 58 parts of sepiolite cashmere, 35 parts of phosphotungstic acid potassium, 57 parts of cornstarch, 10 15 parts of additive.The present invention is slided by the formulated to raw material, the glass partition mass color of preparation, and beautiful in colour, intensity is good, solves the Utilizing question of discarded glass；Compared with traditional handicraft, short the time required to the present invention, energy consumption is low, and product texture is good, nonhazardous material residual, has very high economic benefit and social benefit.
Description
Technical field
The present invention relates to glass technical field of regeneration, and in particular to a kind of refrigerator shelf prepared using discarded glass.
Background technology
The departments such as glass is widely built because of its unique performance, chemical industry, equipment, daily life use, with
The development of construction industry and the development of other industry, building, door/window glass of automobile, glass container, electrical type glass and vial
Largely widely used etc. various glass in national economy so that scrap glass rolls up.On the other hand, in Chinese large-sized base
Infrastructure scale is unprecedented, and natural aggregate is increasingly in short supply, therefore under discarded glass discharge capacity again increasingly increased situation, research will
Scrap glass substitutes the thought that natural aggregate carrys out concrete batching, meets the macro-economic strategy of sustainable development.
The content of the invention
The technical problems to be solved by the invention are to provide that a kind of technique is relatively simple, and the high utilization of final product quality is waste and old
The refrigerator shelf of glass preparation.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of refrigerator shelf prepared using discarded glass, is made of the component of following weight：80-100 parts of discarded glass,
10-20 parts of α amyl cinnamic aldehyde, 5-10 parts of Tissuemat E, 3-6 parts of carborundum, 20-30 parts of calcined diatomite, 2-5 parts of rosin, carbonic acid
2-5 parts of barium, 10-15 parts of calcium carbonate, 4-8 parts of quartz sand, 3-6 parts of calcium silicide, 5-10 parts of ooze, 2-5 parts of silicon nitride, industrial soda
15-18 parts, 5-8 parts of sepiolite cashmere, 3-5 parts of phosphotungstic acid potassium, 5-7 parts of cornstarch, 10-15 parts of additive.
Further, the above-mentioned refrigerator shelf prepared using discarded glass, the component of preferably following weight are made：Waste and old glass
90 parts of glass, 15 parts of α amyl cinnamic aldehyde, 8 parts of Tissuemat E, 5 parts of carborundum, 25 parts of calcined diatomite, 4 parts of rosin, 4 parts of barium carbonate,
13 parts of calcium carbonate, 6 parts of quartz sand, 5 parts of calcium silicide, 8 parts of ooze, 4 parts of silicon nitride, 17 parts of industrial soda, 7 parts of sepiolite cashmere, phosphorus tungsten
Sour 4 parts of potassium, 6 parts of cornstarch, 13 parts of additive.
Above-mentioned additive is made of following raw material according to parts by weight：5-8 parts of mica, 3-6 parts of lanolin, 5-10 parts of bamboo charcoal,
4-6 parts of activated carbon, 1-3 parts of titanium dioxide, 0.8-1.5 parts of quaternary ammonium salt, 5-8 parts of bloom wax.
The preferably following raw material of above-mentioned additive is formed according to parts by weight：6 parts of mica, 5 parts of lanolin, 8 parts of bamboo charcoal, activated carbon
5 parts, 2 parts of titanium dioxide, 1.2 parts of quaternary ammonium salt, 6 parts of bloom wax.
The preparation process of above-mentioned refrigerator shelf is as follows：
(1) discarded glass is collected, is classified according to different colours and quality, it is waste and old to same class using water spray mode
Glass carries out cleaning showers, washes away surface blot；Then discarded glass is ground into graininess again, is sent into cold wind drying equipment,
Cold air drying 30-35 minutes, makes glass particle dry tack free no moisture at 50-55 DEG C of temperature；Water after spray is wadded a quilt with cotton through precipitation
Solidifying Posterior circle uses；
(2) glass particle after cold air drying is sent into vacuum tumbler and carries out tumbling processing, every 5-8 minutes during tumbling
Vacuumize once, exhaust tumbling 5-10 minutes after vacuum every time, then vacuum pumping, so circulation 2-4 times, make the miscellaneous of glass surface
Matter starts to decompose；
(3) glass particle after tumbling is taken out, when immersion 1.5-2 is small into the water, then is pulled out and drained the water with strainer, soaked
It is soaked to return to first of spray process use；Due to have passed through tumbling processing, the debris and oil stain on glass particle surface are easy to
Fill and wash off；
(4) glass particle after spray is drained away the water, is sent into drying equipment and carries out drying and processing, drying temperature control
At 55-60 DEG C, to glass particle surface no moisture；
(5) glass particle after drying is put into nylon ball grinder, adds α amyl cinnamic aldehyde, Tissuemat E, carbonization
Silicon, calcined diatomite, rosin, barium carbonate, calcium carbonate, quartz sand, calcium silicide, ooze, silicon nitride, industrial soda, sepiolite cashmere, phosphorus
Potassium tungstate, cornstarch, when continuous ball milling 4-6 is small, take out, add additive, be then fed into smelting furnace, make material melting, obtain
Mother liquor；
(6) mother liquor is sent into forming machine, refrigerator shelf is made.
The beneficial effects of the invention are as follows：The present invention is slided by the formulated to raw material, the cup mass color of preparation, and color is gorgeous
Beautiful, spottiness, intensity is good, solves the Utilizing question of discarded glass；Compared with traditional handicraft, short, energy the time required to the present invention
Consume low, product texture is good, nonhazardous material residual, has very high economic benefit and social benefit.
Embodiment
In order to make the technical means, the creative features, the aims and the efficiencies achieved by the present invention easy to understand, tie below
Specific embodiment is closed, the present invention is further explained.
Embodiment 1
A kind of refrigerator shelf prepared using discarded glass, is made of the component of following weight：80 parts of discarded glass, α-penta
10 parts of base cinnamic aldehyde, 5 parts of Tissuemat E, 3 parts of carborundum, 20 parts of calcined diatomite, 2 parts of rosin, 2 parts of barium carbonate, 10 parts of calcium carbonate,
4 parts of quartz sand, 3 parts of calcium silicide, 5 parts of ooze, 2 parts of silicon nitride, 15 parts of industrial soda, 5 parts of sepiolite cashmere, 3 parts of phosphotungstic acid potassium, corn
5 parts of starch, 10 parts of additive.
Above-mentioned additive is made of following raw material according to parts by weight：5 parts of mica, 3 parts of lanolin, 5 parts of bamboo charcoal, activated carbon 4
Part, 1 part of titanium dioxide, 0.8 part of quaternary ammonium salt, 5 parts of bloom wax.
The preparation process of above-mentioned refrigerator shelf is as follows：
(1) discarded glass is collected, is classified according to different colours and quality, it is waste and old to same class using water spray mode
Glass carries out cleaning showers, washes away surface blot；Then discarded glass is ground into graininess again, is sent into cold wind drying equipment,
Cold air drying 30 minutes under temperature 50 C, make glass particle dry tack free no moisture；Water after spray follows after precipitation is flocculated
Ring uses；
(2) glass particle after cold air drying is sent into vacuum tumbler and carries out tumbling processing, when tumbling took out every 5 minutes
Vacuum once, exhausts tumbling 5 minutes after vacuum, then vacuum pumping every time, so circulation 2 times, starts the impurity of glass surface
Decompose；
(3) glass particle after tumbling is taken out, when immersion 1.5 is small into the water, then is pulled out and drained the water with strainer, soaked
Water returns to first of spray process and uses；Due to have passed through tumbling processing, the debris and oil stain on glass particle surface are easy to fill
Wash off；
(4) glass particle after spray is drained away the water, is sent into drying equipment and carries out drying and processing, drying temperature control
At 55-60 DEG C, to glass particle surface no moisture；
(5) glass particle after drying is put into nylon ball grinder, adds α amyl cinnamic aldehyde, Tissuemat E, carbonization
Silicon, calcined diatomite, rosin, barium carbonate, calcium carbonate, quartz sand, calcium silicide, ooze, silicon nitride, industrial soda, sepiolite cashmere, phosphorus
Potassium tungstate, cornstarch, when continuous ball milling 4 is small, take out, add additive, be then fed into smelting furnace, make material melting, obtain mother
Liquid；
(6) mother liquor is sent into forming machine, refrigerator shelf is made.
Embodiment 2
A kind of refrigerator shelf prepared using discarded glass, is made of the component of following weight：100 parts of discarded glass, α-
20 parts of amyl group cinnamic aldehyde, 10 parts of Tissuemat E, 6 parts of carborundum, 30 parts of calcined diatomite, 5 parts of rosin, 5 parts of barium carbonate, calcium carbonate 15
Part, 8 parts of quartz sand, 6 parts of calcium silicide, 10 parts of ooze, 5 parts of silicon nitride, 18 parts of industrial soda, 8 parts of sepiolite cashmere, 5 parts of phosphotungstic acid potassium,
7 parts of cornstarch, 15 parts of additive.
Above-mentioned additive is made of following raw material according to parts by weight：8 parts of mica, 6 parts of lanolin, 10 parts of bamboo charcoal, activated carbon 6
Part, 3 parts of titanium dioxide, 1.5 parts of quaternary ammonium salt, 8 parts of bloom wax.
The preparation process of above-mentioned refrigerator shelf is as follows：
(1) discarded glass is collected, is classified according to different colours and quality, it is waste and old to same class using water spray mode
Glass carries out cleaning showers, washes away surface blot；Then discarded glass is ground into graininess again, is sent into cold wind drying equipment,
Cold air drying 35 minutes, makes glass particle dry tack free no moisture at 55 DEG C of temperature；Water after spray follows after precipitation is flocculated
Ring uses；
(2) glass particle after cold air drying is sent into vacuum tumbler and carries out tumbling processing, when tumbling took out every 8 minutes
Vacuum once, exhausts tumbling 10 minutes after vacuum, then vacuum pumping every time, so circulation 4 times, starts the impurity of glass surface
Decompose；
(3) glass particle after tumbling is taken out, when immersion 2 is small into the water, then is pulled out and drained the water with strainer, soaking water
First of spray process is returned to use；Due to have passed through tumbling processing, the debris and oil stain on glass particle surface, which are easy to fill, to be washed
Fall；
(4) glass particle after spray is drained away the water, is sent into drying equipment and carries out drying and processing, drying temperature control
At 60 DEG C, to glass particle surface no moisture；
(5) glass particle after drying is put into nylon ball grinder, adds α amyl cinnamic aldehyde, Tissuemat E, carbonization
Silicon, calcined diatomite, rosin, barium carbonate, calcium carbonate, quartz sand, calcium silicide, ooze, silicon nitride, industrial soda, sepiolite cashmere, phosphorus
Potassium tungstate, cornstarch, when continuous ball milling 6 is small, take out, add additive, be then fed into smelting furnace, make material melting, obtain mother
Liquid；
(6) mother liquor is sent into forming machine, refrigerator shelf is made.
Embodiment 3
A kind of refrigerator shelf prepared using discarded glass, is made of the component of following weight：90 parts of discarded glass, α-penta
15 parts of base cinnamic aldehyde, 8 parts of Tissuemat E, 5 parts of carborundum, 25 parts of calcined diatomite, 4 parts of rosin, 4 parts of barium carbonate, 13 parts of calcium carbonate,
6 parts of quartz sand, 5 parts of calcium silicide, 8 parts of ooze, 4 parts of silicon nitride, 17 parts of industrial soda, 7 parts of sepiolite cashmere, 4 parts of phosphotungstic acid potassium, corn
6 parts of starch, 13 parts of additive.
Above-mentioned additive is made of following raw material according to parts by weight：6 parts of mica, 5 parts of lanolin, 8 parts of bamboo charcoal, activated carbon 5
Part, 2 parts of titanium dioxide, 1.2 parts of quaternary ammonium salt, 6 parts of bloom wax.
The preparation process of above-mentioned refrigerator shelf is as follows：
(1) discarded glass is collected, is classified according to different colours and quality, it is waste and old to same class using water spray mode
Glass carries out cleaning showers, washes away surface blot；Then discarded glass is ground into graininess again, is sent into cold wind drying equipment,
Cold air drying 33 minutes, makes glass particle dry tack free no moisture at 53 DEG C of temperature；Water after spray follows after precipitation is flocculated
Ring uses；
(2) glass particle after cold air drying is sent into vacuum tumbler and carries out tumbling processing, when tumbling took out every 6 minutes
Vacuum once, exhausts tumbling 8 minutes after vacuum, then vacuum pumping every time, so circulation 3 times, starts the impurity of glass surface
Decompose；
(3) glass particle after tumbling is taken out, when immersion 1.8 is small into the water, then is pulled out and drained the water with strainer, soaked
Water returns to first of spray process and uses；Due to have passed through tumbling processing, the debris and oil stain on glass particle surface are easy to fill
Wash off；
(4) glass particle after spray is drained away the water, is sent into drying equipment and carries out drying and processing, drying temperature control
At 58 DEG C, to glass particle surface no moisture；
(5) glass particle after drying is put into nylon ball grinder, adds α amyl cinnamic aldehyde, Tissuemat E, carbonization
Silicon, calcined diatomite, rosin, barium carbonate, calcium carbonate, quartz sand, calcium silicide, ooze, silicon nitride, industrial soda, sepiolite cashmere, phosphorus
Potassium tungstate, cornstarch, when continuous ball milling 5 is small, take out, add additive, be then fed into smelting furnace, make material melting, obtain mother
Liquid；
(6) mother liquor is sent into forming machine, is blow molded into glass tube, you can be used to prepare glass shell.
The basic principles, main features and the advantages of the invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (5)
1. a kind of refrigerator shelf prepared using discarded glass, it is characterised in that be made of the component of following weight：Discarded glass
80-100 parts, 10-20 parts of α amyl cinnamic aldehyde, 5-10 parts of Tissuemat E, 3-6 parts of carborundum, 20-30 parts of calcined diatomite, rosin
2-5 parts, 2-5 parts of barium carbonate, 10-15 parts of calcium carbonate, 4-8 parts of quartz sand, 3-6 parts of calcium silicide, 5-10 parts of ooze, silicon nitride 2-5
Part, 15-18 parts of industrial soda, 5-8 parts of sepiolite cashmere, 3-5 parts of phosphotungstic acid potassium, 5-7 parts of cornstarch, 10-15 parts of additive.
2. the refrigerator shelf according to claim 1 prepared using discarded glass, it is characterised in that preferred following weight
Component is made：90 parts of discarded glass, 15 parts of α amyl cinnamic aldehyde, 8 parts of Tissuemat E, 5 parts of carborundum, 25 parts of calcined diatomite, pine
Fragrant 4 parts, 4 parts of barium carbonate, 13 parts of calcium carbonate, 6 parts of quartz sand, 5 parts of calcium silicide, 8 parts of ooze, 4 parts of silicon nitride, 17 parts of industrial soda,
7 parts of sepiolite cashmere, 4 parts of phosphotungstic acid potassium, 6 parts of cornstarch, 13 parts of additive.
3. a kind of refrigerator shelf prepared using discarded glass, it is characterised in that above-mentioned additive is by following raw material according to weight
Part composition：5-8 parts of mica, 3-6 parts of lanolin, 5-10 parts of bamboo charcoal, 4-6 parts of activated carbon, 1-3 parts of titanium dioxide, quaternary ammonium salt 0.8-1.5
Part, 5-8 parts of bloom wax.
4. a kind of refrigerator shelf prepared using discarded glass, it is characterised in that the preferably following raw material of above-mentioned additive is according to weight
Measure part composition：6 parts of mica, 5 parts of lanolin, 8 parts of bamboo charcoal, 5 parts of activated carbon, 2 parts of titanium dioxide, 1.2 parts of quaternary ammonium salt, 6 parts of bloom wax.
5. a kind of technique for preparing refrigerator shelf described in claim 1, it is characterised in that step is as follows：
(1) discarded glass is collected, is classified according to different colours and quality, using water spray mode to same class discarded glass
Cleaning showers are carried out, wash away surface blot；Then discarded glass is ground into graininess again, cold wind drying equipment is sent into, in temperature
Cold air drying 30-35 minutes, makes glass particle dry tack free no moisture at 50-55 DEG C of degree；Water after spray is after precipitation is flocculated
Recycle；
(2) glass particle after cold air drying is sent into vacuum tumbler and carries out tumbling processing, when tumbling took out very every 5-8 minute
It is empty once, exhaust tumbling 5-10 minute after vacuum every time, then vacuum pumping, so circulates 2-4 times, open the impurity of glass surface
Begin to decompose；
(3) glass particle after tumbling is taken out, when immersion 1.5-2 is small into the water, then is pulled out and drained the water with strainer, soaking water
First of spray process is returned to use；Due to have passed through tumbling processing, the debris and oil stain on glass particle surface, which are easy to fill, to be washed
Fall；
(4) glass particle after spray is drained away the water, is sent into drying equipment and carries out drying and processing, drying temperature control exists
55-60 DEG C, to glass particle surface no moisture；
(5) glass particle after drying is put into nylon ball grinder, adds α amyl cinnamic aldehyde, Tissuemat E, carborundum, forges
Burn diatomite, rosin, barium carbonate, calcium carbonate, quartz sand, calcium silicide, ooze, silicon nitride, industrial soda, sepiolite cashmere, phosphotungstic acid
Potassium, cornstarch, when continuous ball milling 4-6 is small, take out, add additive, be then fed into smelting furnace, make material melting, obtain mother liquor；
(6) mother liquor is sent into forming machine, refrigerator shelf is made.