CN107311588A - A kind of environmentally friendly brushing gypsum and preparation method thereof - Google Patents
A kind of environmentally friendly brushing gypsum and preparation method thereof Download PDFInfo
- Publication number
- CN107311588A CN107311588A CN201710536996.1A CN201710536996A CN107311588A CN 107311588 A CN107311588 A CN 107311588A CN 201710536996 A CN201710536996 A CN 201710536996A CN 107311588 A CN107311588 A CN 107311588A
- Authority
- CN
- China
- Prior art keywords
- parts
- gypsum
- environmentally friendly
- insulation filler
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmentally friendly brushing gypsum and preparation method thereof, it is related to brushing gypsum technical field, includes the raw material of following part meter:45 ~ 75 parts of 55 ~ 60 parts of desulfurated plaster, 35 ~ 37 parts of atoleine, 32 ~ 33 parts of carbide slag, 29 ~ 30 parts of insulation filler, 24 ~ 26 parts of glutinous rice glue, 20 ~ 21 parts of nano whisker exciting agent, 18 ~ 19 parts of auxiliary agent and water.The present invention and the cohesive force of base course wall are strong, with good heat-insulating property.
Description
Technical field
The present invention relates to brushing gypsum technical field, and in particular to a kind of environmentally friendly brushing gypsum and preparation method thereof.
Background technology
China is with a long history using gypsum plaster, but is of limited application, and with the improvement of living standards, people
Construction material is saved, in terms of safety non-toxic evil the reinforcement realized and requirement raising, gypsum material has a series of skills
Art superiority, makes the energy-saving green material for praising highly development in the world.
1h-2h can be carried out surface construction after the completion of brushing gypsum coat of plaster fast solidifying, bottom, greatly shortens and applies
It the work duration, need not be conserved after having constructed, be conducive to the protection of finished product.Crystal water content accounts for whole molecular weight in brushing gypsum
20.9%, when fire occurs for building, as long as moisture contained by gypsum in wall plastering material without discharging and steam completely
Hair, metope temperature would not be more than 40 degrees Celsius.Therefore, wall heating-up time, harm of the control fire to building can be delayed
The extent of damage.But current brushing gypsum caking property and heat-insulating property are poor.
The content of the invention
It is an object of the invention to provide a kind of environmentally friendly brushing gypsum and preparation method thereof, the cohesive force with base course wall is strong,
With good heat-insulating property.
The invention provides following technical scheme:A kind of environmentally friendly brushing gypsum, includes the raw material of following part meter:Desulfurization stone
55 ~ 60 parts of cream, 35 ~ 37 parts of atoleine, 32 ~ 33 parts of carbide slag, 29 ~ 30 parts of insulation filler, 24 ~ 26 parts of glutinous rice glue, receive
45 ~ 75 parts of 20 ~ 21 parts of meter Jing Xu exciting agents, 18 ~ 19 parts of auxiliary agent and water;
The auxiliary agent includes the raw material that following part is counted:It is 5 ~ 6 parts of nano whisker exciting agent, 3 ~ 4 parts of grinding aid, 3 ~ 4 parts of foaming agent, steady
1 ~ 2 part of 2 ~ 3 parts of infusion and retarder.
Wherein, the insulation filler includes the raw material that following part is counted:12 ~ 14 parts of modification infusorial earth, nano barium sulfate 8
2 ~ 3 parts of ~ 9 parts, 6 ~ 7 parts of quartz sand, 5 ~ 6 parts of calx slag and talcum powder.
Wherein, the preparation method of the modification infusorial earth is:Weigh diatomite to be put into the water of 10 ~ 15 times of parts by weight, stir
Mix and uniformly obtain slurry, calgon and sodium hydroxide are added into slurry, under the conditions of 35 ~ 45 DEG C heating water bath 20 ~
Upper strata mud centrifugation is taken after 40min, standing, drying grinds to 400 ~ 500 mesh, obtains the modification infusorial earth.
Wherein, the quartz sand is natural stone diamond stone by broken processing, fine grinding, the exquisiteness that screening fineness is 50 ~ 100 mesh
Quartz sand, the calx slag is boiler of power plant waste residue, carries out magnetic separation through magnetic separator after desulfurization, then be made by fine grinding processing, sieve
It is 45 ~ 95 mesh to select fineness.
Wherein, the preparation method of the glutinous rice glue is:According to 100:200:1 ratio weighs glutinous rice, water and alum, is put into
Boiling is filtered, obtained slurry as glutinous rice glue to pulp in heating kettle.
Wherein, the nano whisker exciting agent is nano zine oxide, nano tin dioxide, nano-zinc stannate, nanometer metastannic acid
One or more mixtures in zinc and nano zinc hydroxyl stannate.
Wherein, the grinding aid is the one or more of triethanolamine, polyalcohol amine, ethylene glycol and diethylene glycol, described
Foam stabilizer is the one or more in silicones polyethers emulsion, polyacrylamide and polyvinyl alcohol, and the foaming agent is dodecane
One or more in base sodium sulphate, neopelex and rosin, the retarder is protein salt retarder, lemon
One or more in lemon acid, sodium citrate and sodium tripolyphosphate.
The present invention provides a kind of preparation method of environmentally friendly brushing gypsum, comprises the following steps:
(1), insulation filler acidification
Insulation filler is weighed, grinds and crosses 80 ~ 90 mesh sieves, be put into rotary kiln and calcine, calcining heat control is 300
~500 DEG C, calcination time control is 2 ~ 3h;
Insulation filler after calcining is put into the dilute sulfuric acid pond that concentration is 90 ~ 95% and carries out acidification, acidificatoin time is
13 ~ 15h, the insulation filler of acidifying is taken out and drained, and is put into rotary dryer and is dried, and is ground and is crossed 100 ~ 120 mesh
Sieve, the insulation filler after being acidified is standby;
(2), prepare plaster of Paris
Desulfurated plaster is weighed, drying baker is put into, 1 ~ 3h is pre-processed under 60 ~ 70 DEG C of hot conditions, then takes out and is put into calcining furnace,
In 120 ~ 160 DEG C of temperature lower calcinations, whole free waters and partially crystallizable water are sloughed, semi-hydrated gypsum is formed and a small amount of II types is anhydrous
Gypsum;Then sintering desulfuration gypsum is placed on room temperature, under unlimited environment after storage 6~8 days, crosses 100 ~ 120 mesh sieves, built
Gypsum is built, it is standby;
(3), prepare modified building gypsum
Weigh step(1)Insulation filler and step after processing(2)Obtained plaster of Paris, adds electricity thereto after mixing
Rock ballast and grinding aid, are put into ball mill and wear into fine powder, cross 150 ~ 180 mesh sieves, are then calcined under 160 ~ 175 DEG C of hot conditions
Modified building gypsum is obtained after 1 ~ 2h, cooling, it is standby;
(4), weigh glutinous rice glue, nano whisker exciting agent and water according to proportioning, add step(3)Obtained modified building gypsum
In, after being uniformly mixed, boiling in steam stove is placed in, temperature control is 90 ~ 160 DEG C, and the time is 1~2h, obtains slurry, standby
With;
(5), weigh surplus stock according to proportioning, add step(4)In obtained slurry, mixed with 300 ~ 400r/min rotating speed
Uniformly, mixed material is obtained, is 6 ~ 10% by the moisture control of mixed material;
(6), by step(5)Obtained mixed material is placed in extruding in double screw extruder, strip of growing up, and is placed in mass fraction
In 0.5 ~ 1mol/L watery hydrochloric acid, to carry out pickling, the spot of strip-like surface is removed, and by after its natural air drying 4~5 days, is obtained
To dry mixed material, dry mixed material is ground into powder by airslide disintegrating mill, the environmental protection is produced and paints stone
Cream.
Beneficial effects of the present invention:Cohesive force with base course wall is strong, specific as follows with good heat-insulating property:
(1), the present invention use desulfurated plaster, by drying and high-temperature process after obtain plaster of Paris, by plaster of Paris and insulation
Thermal insulating filling is mixed, and is modified, and improves cohesive force and heat-insulating property, while its stability is enhanced, obtained environmental protection
Brushing gypsum, it is high and the characteristics of harden fast with intensity, also with good operable time, the cohesive force with base course wall
By force, in construction, only the present invention need to be added water directly to criticize and scraped in the outer surface of construction wall, had good workability, operation letter
It is single;
(2), the environmentally friendly brushing gypsum of the present invention, using quality better, low-cost desulfurated plaster, can substitute completely by natural gypsum system
Into brushing gypsum, while production cost is reduced, substantially increase intensity, improve comprehensive utilization ratio and economic benefit;
(3), the present invention can be deviate from 21% or so the crystallization water by during high temperature action or after meeting fire, and can be formed in surface evaporation
Vapor curtain, can effectively prevent spreading for the intensity of a fire, with good flameproof effect;
(4), the present invention is in the feed using modification infusorial earth, nano barium sulfate, quartz sand, calx slag and talcum powder as filling out
Material so that the present invention has function of heat insulation, the nano barium sulfate used, chemical property is stable, acidproof, alkaline-resisting, Ke Yiti
High-wearing feature, water resistance, heat resistance, case hardness, impact resistance etc.;Modification infusorial earth is added, with preferable suction-operated,
Harmful substance and the peculiar smell such as free formaldehyde, benzene, ammonia in air can be effectively removed, is purified the air of a room;By high temperature and acid
Change the modification infusorial earth of processing, obtained further activation, form loose and porous structure, mitigate weight;
(5), the present invention using nano whisker as exciting agent, can fully improve early hydration speed, effectively improve intensity.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.These embodiments be merely to illustrate the present invention and without
In limitation the scope of the present invention.
Embodiment 1
A kind of environmentally friendly brushing gypsum, includes the raw material of following part meter:55 parts of desulfurated plaster, 35 parts of atoleine, 32 parts of carbide slag,
45 parts of 29 parts of insulation filler, 24 parts of glutinous rice glue, 20 parts of nano whisker exciting agent, 18 parts of auxiliary agent and water;
The auxiliary agent includes the raw material that following part is counted:5 parts of nano whisker exciting agent, 3 parts of grinding aid, 3 parts of foaming agent, foam stabilizer 2
1 part of part and retarder.
Wherein, the insulation filler includes the raw material that following part is counted:12 parts of modification infusorial earth, 8 parts of nano barium sulfate,
2 parts of 6 parts of quartz sand, 5 parts of calx slag and talcum powder.
Wherein, the preparation method of the modification infusorial earth is:Weigh diatomite to be put into the water of 10 times of parts by weight, stirring is equal
It is even to obtain slurry, calgon and sodium hydroxide are added into slurry, under the conditions of 35 DEG C after heating water bath 20min, standing
Upper strata mud centrifugation is taken, drying grinds to 400 mesh, obtains the modification infusorial earth.
Wherein, the quartz sand is natural stone diamond stone by broken processing, fine grinding, the exquisiteness quartz that screening fineness is 50 mesh
Sand, the calx slag is boiler of power plant waste residue, and magnetic separation is carried out through magnetic separator after desulfurization, then is made by fine grinding processing, and screening is thin
Spend for 45 mesh.
Wherein, the preparation method of the glutinous rice glue is:According to 100:200:1 ratio weighs glutinous rice, water and alum, is put into
Boiling is filtered, obtained slurry as glutinous rice glue to pulp in heating kettle.
Wherein, the nano whisker exciting agent is nano zine oxide.
Wherein, the grinding aid is triethanolamine, and the foam stabilizer is silicones polyethers emulsion, and the foaming agent is 12
Sodium alkyl sulfate, the retarder is protein salt retarder.
A kind of preparation method of environmentally friendly brushing gypsum is provided in the present embodiment, comprised the following steps:
(1), insulation filler acidification
Insulation filler is weighed, grinds and crosses 80 mesh sieves, be put into rotary kiln and calcine, calcining heat control is 300 DEG C,
Calcination time control is 2h;
Insulation filler after calcining is put into the dilute sulfuric acid pond that concentration is 90% and carries out acidification, acidificatoin time is
13h, the insulation filler of acidifying is taken out and drained, and is put into rotary dryer and is dried, and is ground and is crossed 100 mesh sieves, obtains
Insulation filler after acidifying, it is standby;
(2), prepare plaster of Paris
Desulfurated plaster is weighed, drying baker is put into, 1h is pre-processed under 60 DEG C of hot conditions, then takes out and be put into calcining furnace, 120
DEG C temperature lower calcination, sloughs whole free waters and partially crystallizable water, forms semi-hydrated gypsum and a small amount of II type anhydrous gypsums;Then
Sintering desulfuration gypsum is placed on room temperature, under unlimited environment after storage 6 days, crosses 100 mesh sieves, obtain plaster of Paris, it is standby;
(3), prepare modified building gypsum
Weigh step(1)Insulation filler and step after processing(2)Obtained plaster of Paris, adds electricity thereto after mixing
Rock ballast and grinding aid, are put into ball mill and wear into fine powder, cross 150 mesh sieves, then calcine 1h under 160 DEG C of hot conditions, cool down
After obtain modified building gypsum, it is standby;
(4), weigh glutinous rice glue, nano whisker exciting agent and water according to proportioning, add step(3)Obtained modified building gypsum
In, after being uniformly mixed, boiling in steam stove is placed in, temperature control is 90 DEG C, and the time is 1h, obtains slurry, standby;
(5), weigh surplus stock according to proportioning, add step(4)It is equal with 300r/min rotating speed mixing in obtained slurry
It is even, mixed material is obtained, is 6% by the moisture control of mixed material;
(6), by step(5)Obtained mixed material is placed in extruding in double screw extruder, strip of growing up, and is placed in mass fraction
In 0.5mol/L watery hydrochloric acid, to carry out pickling, the spot of strip-like surface is removed, and by after its natural air drying 4 days, obtains drying
Mixed material, dry mixed material is ground into powder by airslide disintegrating mill, the environmentally friendly brushing gypsum is produced.
Embodiment 2
A kind of environmentally friendly brushing gypsum, includes the raw material of following part meter:60 parts of desulfurated plaster, 37 parts of atoleine, 33 parts of carbide slag,
75 parts of 30 parts of insulation filler, 26 parts of glutinous rice glue, 21 parts of nano whisker exciting agent, 19 parts of auxiliary agent and water;
The auxiliary agent includes the raw material that following part is counted:6 parts of nano whisker exciting agent, 4 parts of grinding aid, 4 parts of foaming agent, foam stabilizer 3
2 parts of part and retarder.
Wherein, the insulation filler includes the raw material that following part is counted:14 parts of modification infusorial earth, 9 parts of nano barium sulfate,
3 parts of 7 parts of quartz sand, 6 parts of calx slag and talcum powder.
Wherein, the preparation method of the modification infusorial earth is:Weigh diatomite to be put into the water of 15 times of parts by weight, stirring is equal
It is even to obtain slurry, calgon and sodium hydroxide are added into slurry, under the conditions of 45 DEG C after heating water bath 40min, standing
Upper strata mud centrifugation is taken, drying grinds to 500 mesh, obtains the modification infusorial earth.
Wherein, the quartz sand is natural stone diamond stone by broken processing, fine grinding, the exquisite stone that screening fineness is 100 mesh
Sand, the calx slag is boiler of power plant waste residue, carries out magnetic separation through magnetic separator after desulfurization, then be made by fine grinding processing, screening
Fineness is 95 mesh.
Wherein, the preparation method of the glutinous rice glue is:According to 100:200:1 ratio weighs glutinous rice, water and alum, is put into
Boiling is filtered, obtained slurry as glutinous rice glue to pulp in heating kettle.
Wherein, the nano whisker exciting agent is nano tin dioxide.
Wherein, the grinding aid is polyalcohol amine, and the foam stabilizer is polyacrylamide, and the foaming agent is dodecyl
Benzene sulfonic acid sodium salt, the retarder is citric acid.
A kind of preparation method of environmentally friendly brushing gypsum is provided in the present embodiment, comprised the following steps:
(1), insulation filler acidification
Insulation filler is weighed, grinds and crosses 90 mesh sieves, be put into rotary kiln and calcine, calcining heat control is 500 DEG C,
Calcination time control is 3h;
Insulation filler after calcining is put into the dilute sulfuric acid pond that concentration is 95% and carries out acidification, acidificatoin time is 5h,
The insulation filler of acidifying is taken out and drained, is put into rotary dryer and dries, grinds and crosses 120 mesh sieves, be acidified
Insulation filler afterwards, it is standby;
(2), prepare plaster of Paris
Desulfurated plaster is weighed, drying baker is put into, 3h is pre-processed under 70 DEG C of hot conditions, then takes out and be put into calcining furnace, 160
DEG C temperature lower calcination, sloughs whole free waters and partially crystallizable water, forms semi-hydrated gypsum and a small amount of II type anhydrous gypsums;Then
Sintering desulfuration gypsum is placed on room temperature, under unlimited environment after storage 8 days, crosses 120 mesh sieves, obtain plaster of Paris, it is standby;
(3), prepare modified building gypsum
Weigh step(1)Insulation filler and step after processing(2)Obtained plaster of Paris, adds electricity thereto after mixing
Rock ballast and grinding aid, are put into ball mill and wear into fine powder, cross 180 mesh sieves, then calcine 2h under 175 DEG C of hot conditions, cool down
After obtain modified building gypsum, it is standby;
(4), weigh glutinous rice glue, nano whisker exciting agent and water according to proportioning, add step(3)Obtained modified building gypsum
In, after being uniformly mixed, boiling in steam stove is placed in, temperature control is 160 DEG C, and the time is 2h, obtains slurry, standby;
(5), weigh surplus stock according to proportioning, add step(4)It is equal with 400r/min rotating speed mixing in obtained slurry
It is even, mixed material is obtained, is 10% by the moisture control of mixed material;
(6), by step(5)Obtained mixed material is placed in extruding in double screw extruder, strip of growing up, and is placed in mass fraction
In 1mol/L watery hydrochloric acid, to carry out pickling, the spot of strip-like surface is removed, and drying after its natural air drying 5 days, will be obtained
Mixed material, powder is ground into by dry mixed material by airslide disintegrating mill, produces the environmentally friendly brushing gypsum.
Embodiment 3
A kind of environmentally friendly brushing gypsum, includes the raw material of following part meter:57 parts of desulfurated plaster, 36 parts of atoleine, carbide slag 32.5
Part, 29.5 parts of insulation filler, 25 parts of glutinous rice glue, 20.5 parts of nano whisker exciting agent, 18.5 parts of auxiliary agent and 60 parts of water;
The auxiliary agent includes the raw material that following part is counted:It is 5.5 parts of nano whisker exciting agent, 3.5 parts of grinding aid, 3.5 parts of foaming agent, steady
1.5 parts of 2.5 parts of infusion and retarder.
Wherein, the insulation filler includes the raw material that following part is counted:13 parts of modification infusorial earth, nano barium sulfate 8.5
Part, 6.5 parts of quartz sand, 5.5 parts of calx slag and 2.5 parts of talcum powder.
Wherein, the preparation method of the modification infusorial earth is:Weigh diatomite to be put into the water of 12 times of parts by weight, stirring is equal
It is even to obtain slurry, calgon and sodium hydroxide are added into slurry, under the conditions of 40 DEG C after heating water bath 30min, standing
Upper strata mud centrifugation is taken, drying grinds to 450 mesh, obtains the modification infusorial earth.
Wherein, the quartz sand is natural stone diamond stone by broken processing, fine grinding, the exquisiteness quartz that screening fineness is 75 mesh
Sand, the calx slag is boiler of power plant waste residue, and magnetic separation is carried out through magnetic separator after desulfurization, then is made by fine grinding processing, and screening is thin
Spend for 45 ~ 95 mesh.
Wherein, the preparation method of the glutinous rice glue is:According to 100:200:1 ratio weighs glutinous rice, water and alum, is put into
Boiling is filtered, obtained slurry as glutinous rice glue to pulp in heating kettle.
Wherein, the nano whisker exciting agent is nanometer zinc metastannate.
Wherein, the grinding aid is ethylene glycol, and the foam stabilizer is polyvinyl alcohol, and the foaming agent is detergent alkylate sulphur
Sour sodium and rosin, the retarder are sodium citrate and sodium tripolyphosphate.
A kind of preparation method of environmentally friendly brushing gypsum is provided in the present embodiment, comprised the following steps:
(1), insulation filler acidification
Insulation filler is weighed, grinds and crosses 85 mesh sieves, be put into rotary kiln and calcine, calcining heat control is 400 DEG C,
Calcination time control is 2.5h;
Insulation filler after calcining is put into the dilute sulfuric acid pond that concentration is 93% and carries out acidification, acidificatoin time is
14h, the insulation filler of acidifying is taken out and drained, and is put into rotary dryer and is dried, and is ground and is crossed 110 mesh sieves, obtains
Insulation filler after acidifying, it is standby;
(2), prepare plaster of Paris
Desulfurated plaster is weighed, drying baker is put into, 2h is pre-processed under 65 DEG C of hot conditions, then takes out and be put into calcining furnace, 150
DEG C temperature lower calcination, sloughs whole free waters and partially crystallizable water, forms semi-hydrated gypsum and a small amount of II type anhydrous gypsums;Then
Sintering desulfuration gypsum is placed on room temperature, under unlimited environment after storage 7 days, crosses 110 mesh sieves, obtain plaster of Paris, it is standby;
(3), prepare modified building gypsum
Weigh step(1)Insulation filler and step after processing(2)Obtained plaster of Paris, adds electricity thereto after mixing
Rock ballast and grinding aid, are put into ball mill and wear into fine powder, cross 165 mesh sieves, then calcine 1.5h under 165 DEG C of hot conditions, cold
But modified building gypsum is obtained afterwards, it is standby;
(4), weigh glutinous rice glue, nano whisker exciting agent and water according to proportioning, add step(3)Obtained modified building gypsum
In, after being uniformly mixed, boiling in steam stove is placed in, temperature control is 120 DEG C, and the time is 1.5h, obtains slurry, standby;
(5), weigh surplus stock according to proportioning, add step(4)It is equal with 350r/min rotating speed mixing in obtained slurry
It is even, mixed material is obtained, is 8% by the moisture control of mixed material;
(6), by step(5)Obtained mixed material is placed in extruding in double screw extruder, strip of growing up, and is placed in mass fraction
In 0.6mol/L watery hydrochloric acid, to carry out pickling, the spot of strip-like surface is removed, and by after its natural air drying 4 days, obtains drying
Mixed material, dry mixed material is ground into powder by airslide disintegrating mill, the environmentally friendly brushing gypsum is produced.
The present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art, its according to
The technical scheme described in foregoing embodiments can so be modified, or which part technical characteristic is equally replaced
Change.Within the spirit and principles of the invention, any modification, equivalent substitution and improvements made etc., should be included in the present invention
Protection domain within.
Claims (8)
1. a kind of environmentally friendly brushing gypsum, it is characterised in that the raw material counted including following part:55 ~ 60 parts of desulfurated plaster, atoleine
35 ~ 37 parts, 32 ~ 33 parts of carbide slag, 29 ~ 30 parts of insulation filler, 24 ~ 26 parts of glutinous rice glue, nano whisker exciting agent 20 ~ 21
45 ~ 75 parts of part, 18 ~ 19 parts of auxiliary agent and water;
The auxiliary agent includes the raw material that following part is counted:It is 5 ~ 6 parts of nano whisker exciting agent, 3 ~ 4 parts of grinding aid, 3 ~ 4 parts of foaming agent, steady
1 ~ 2 part of 2 ~ 3 parts of infusion and retarder.
2. environmentally friendly brushing gypsum according to claim 1, it is characterised in that the insulation filler is counted including following part
Raw material:12 ~ 14 parts of modification infusorial earth, 8 ~ 9 parts of nano barium sulfate, 6 ~ 7 parts of quartz sand, 5 ~ 6 parts of calx slag and talcum powder 2 ~ 3
Part.
3. environmentally friendly brushing gypsum according to claim 2, it is characterised in that the preparation method of the modification infusorial earth is:
Weigh diatomite to be put into the water of 10 ~ 15 times of parts by weight, be uniformly mixing to obtain slurry, calgon and hydrogen are added into slurry
Sodium oxide molybdena, takes upper strata mud centrifugation under the conditions of 35 ~ 45 DEG C after 20 ~ 40min of heating water bath, standing, drying is ground
To 400 ~ 500 mesh, the modification infusorial earth is obtained.
4. environmentally friendly brushing gypsum according to claim 2, it is characterised in that the quartz sand is natural stone diamond stone by broken
Broken processing, fine grinding, the exquisite quartz sand that screening fineness is 50 ~ 100 mesh, the calx slag is boiler of power plant waste residue, is passed through after desulfurization
Magnetic separator carries out magnetic separation, then is made by fine grinding processing, and screening fineness is 45 ~ 95 mesh.
5. environmentally friendly brushing gypsum according to claim 1, it is characterised in that the preparation method of the glutinous rice glue is:According to
100:200:1 ratio weighs glutinous rice, water and alum, is put into boiling in heating kettle and, to pulp, filters, obtained slurry is i.e.
For glutinous rice glue.
6. environmentally friendly brushing gypsum according to claim 1, it is characterised in that the nano whisker exciting agent is nano oxidized
One or more mixtures in zinc, nano tin dioxide, nano-zinc stannate, nanometer zinc metastannate and nano zinc hydroxyl stannate.
7. environmentally friendly brushing gypsum according to claim 1, it is characterised in that the grinding aid is triethanolamine, polymeric alcohol
The one or more of amine, ethylene glycol and diethylene glycol, the foam stabilizer is silicones polyethers emulsion, polyacrylamide and polyethylene
One or more in alcohol, the foaming agent be lauryl sodium sulfate, neopelex and rosin in one kind or
Several, the retarder is the one or more in protein salt retarder, citric acid, sodium citrate and sodium tripolyphosphate.
8. the preparation method of a kind of environmentally friendly brushing gypsum according to any one of claim 1 ~ 7, it is characterised in that including such as
Lower step:
(1), insulation filler acidification
Insulation filler is weighed, grinds and crosses 80 ~ 90 mesh sieves, be put into rotary kiln and calcine, calcining heat control is 300
~500 DEG C, calcination time control is 2 ~ 3h;
Insulation filler after calcining is put into the dilute sulfuric acid pond that concentration is 90 ~ 95% and carries out acidification, acidificatoin time is
13 ~ 15h, the insulation filler of acidifying is taken out and drained, and is put into rotary dryer and is dried, and is ground and is crossed 100 ~ 120 mesh
Sieve, the insulation filler after being acidified is standby;
(2), prepare plaster of Paris
Desulfurated plaster is weighed, drying baker is put into, 1 ~ 3h is pre-processed under 60 ~ 70 DEG C of hot conditions, then takes out and is put into calcining furnace,
In 120 ~ 160 DEG C of temperature lower calcinations, whole free waters and partially crystallizable water are sloughed, semi-hydrated gypsum is formed and a small amount of II types is anhydrous
Gypsum;Then sintering desulfuration gypsum is placed on room temperature, under unlimited environment after storage 6~8 days, crosses 100 ~ 120 mesh sieves, built
Gypsum is built, it is standby;
(3), prepare modified building gypsum
Weigh step(1)Insulation filler and step after processing(2)Obtained plaster of Paris, adds electricity thereto after mixing
Rock ballast and grinding aid, are put into ball mill and wear into fine powder, cross 150 ~ 180 mesh sieves, are then calcined under 160 ~ 175 DEG C of hot conditions
Modified building gypsum is obtained after 1 ~ 2h, cooling, it is standby;
(4), weigh glutinous rice glue, nano whisker exciting agent and water according to proportioning, add step(3)Obtained modified building gypsum
In, after being uniformly mixed, boiling in steam stove is placed in, temperature control is 90 ~ 160 DEG C, and the time is 1~2h, obtains slurry, standby
With;
(5), weigh surplus stock according to proportioning, add step(4)In obtained slurry, mixed with 300 ~ 400r/min rotating speed
Uniformly, mixed material is obtained, is 6 ~ 10% by the moisture control of mixed material;
(6), by step(5)Obtained mixed material is placed in extruding in double screw extruder, strip of growing up, and is placed in mass fraction
In 0.5 ~ 1mol/L watery hydrochloric acid, to carry out pickling, the spot of strip-like surface is removed, and by after its natural air drying 4~5 days, is obtained
To dry mixed material, dry mixed material is ground into powder by airslide disintegrating mill, the environmental protection is produced and paints stone
Cream.