CN107814556A - A kind of wine heater and preparation method thereof - Google Patents
A kind of wine heater and preparation method thereof Download PDFInfo
- Publication number
- CN107814556A CN107814556A CN201711099423.3A CN201711099423A CN107814556A CN 107814556 A CN107814556 A CN 107814556A CN 201711099423 A CN201711099423 A CN 201711099423A CN 107814556 A CN107814556 A CN 107814556A
- Authority
- CN
- China
- Prior art keywords
- mud
- base
- upper step
- walk
- base substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of wine heater, the raw material of its following weight percentage is prepared：Blue or green cash, clinker, anthracite, clay, feldspar, Li Jiangshi, medical stone.Its preparation process：Dispensing：Blue or green cash, clinker, anthracite, clay, feldspar, vertical boundary stone and medical stone are weighed by proportioning, and is well mixed；Grinding：Dispensing in upper step is put into ball mill be ground to 200 mesh go out mill, by the fine powder after grinding and water on demand soft durometer requirement matched；Clear mud：Mud is separated by the mud mixed in upper step in clear mud with water, base mud is made；Dry：Base mud in upper step is placed and dried in the cool, the water content for making base mud is 70%；Rub mud：The base mud dried in upper step is kneaded into walk repeatedly, walk requires pore-free, free from admixture, and shale is uniform；Shaping：The walk made in upper step is placed on throwing on mud platform required base substrate is made, and carry out shape and moulding and the modification of color；Drying：The base substrate made in upper step is dried at a temperature of 50 60 DEG C；Fire：The base substrate that upper step makes is placed in kiln, is fired 24 hours at a temperature of 1,250 1300 DEG C, naturally cools to kiln discharge after normal temperature.
Description
Technical field
The invention belongs to sand device manufacture technology field, and in particular to a kind of wine heater and preparation method thereof.
Background technology
At present, sand device kettle has the manufacturing history of more than 2,000 years in China, because it is chiltern vessel, so with preferably thoroughly
Gas and adsorptivity, by people extensively with as the vessel for holding food, because its used cost of material is low, and do not contain
Any noxious material, environmentally-friendly sanitary, thus be widely adopted, still, existing sand device kettle because raw material and raw material proportioning are unreasonable,
Tea set made of causing has that physical property is poor and easily fried, easily splits, using it is dangerous the problems such as.
The content of the invention
It is an object of the invention to provide a kind of wine heater and preparation method thereof.Wine heater environmental protection, tea made of the present invention
Device is safe to use, and reasonable raw material proportioning.
The technical solution adopted by the present invention：A kind of wine heater, the raw material of its following weight percentage are prepared：
The feldspar 10% of 10% anthracite of blue or green 50% clinker of cash, 5% clay 10% founds the medical stone 5% of boundary stone 10%.
A kind of preparation method of wine heater, it comprises the following steps：
（1）Dispensing：Blue or green cash, clinker, anthracite, clay, feldspar, vertical boundary stone and medical stone are weighed by proportioning, and is well mixed；
（2）Grinding：Dispensing in upper step is put into ball mill and is ground to 200 mesh and goes out mill, by the fine powder after grinding and water on demand
The soft durometer requirement wanted is matched；
（3）Clear mud：By step（2）In the mud that mixes mud is separated with water in clear mud, base mud is made；
（4）Dry：By step（3）In base mud place dry in the cool, make base mud water content be 70%；
（5）Rub mud：By step（4）In the base mud that has dried be kneaded into walk repeatedly, walk requires pore-free, free from admixture, and shale
Uniformly；
（6）Shaping：By step（5）In the walk that makes be placed on throwing on mud platform required base substrate be made, and carry out shape and make
The modification of type and color；
（7）Drying：By step（6）In the base substrate that makes dried at a temperature of 50-60 DEG C；
（8）Fire：By step（7）The base substrate made is placed in kiln, is fired 24 hours at a temperature of 1250-1300 DEG C,
Naturally cool to kiln discharge after normal temperature.
Its advantage is the present invention compared with prior art：Manufacture craft of the present invention is simple, high yield rate, and color is pure
Just, it is smooth to the touch, service life length, and tea set health environment-friendly is pollution-free, has very big market application foreground.
Embodiment
A kind of wine heater, the raw material of its following weight percentage are prepared：
The feldspar 10% of 10% anthracite of blue or green 50% clinker of cash, 5% clay 10% founds the medical stone 5% of boundary stone 10%.
A kind of preparation method of wine heater, it comprises the following steps：
（1）Dispensing：Blue or green cash, clinker, anthracite, clay, feldspar, vertical boundary stone and medical stone are weighed by proportioning, and is well mixed；
（2）Grinding：Dispensing in upper step is put into ball mill and is ground to 200 mesh and goes out mill, by the fine powder after grinding and water on demand
The soft durometer requirement wanted is matched；
（3）Clear mud：By step（2）In the mud that mixes mud is separated with water in clear mud, base mud is made；
（4）Dry：By step（3）In base mud place dry in the cool, make base mud water content be 70%；
（5）Rub mud：By step（4）In the base mud that has dried be kneaded into walk repeatedly, walk requires pore-free, free from admixture, and shale
Uniformly；
（6）Shaping：By step（5）In the walk that makes be placed on throwing on mud platform required base substrate be made, and carry out shape and make
The modification of type and color；
（7）Drying：By step（6）In the base substrate that makes dried at a temperature of 50-60 DEG C；
（8）Fire：By step（7）The base substrate made is placed in kiln, is fired 24 hours at a temperature of 1250-1300 DEG C,
Naturally cool to kiln discharge after normal temperature.
Claims (2)
1. a kind of wine heater, it is characterised in that the raw material of its following weight percentage is prepared：
The feldspar 10% of 10% anthracite of blue or green 50% clinker of cash, 5% clay 10% founds the medical stone 5% of boundary stone 10%.
2. a kind of preparation method of wine heater as claimed in claim 1, it is characterised in that comprise the following steps：
（1）Dispensing：Blue or green cash, clinker, anthracite, clay, feldspar, vertical boundary stone and medical stone are weighed by proportioning, and is well mixed；
（2）Grinding：Dispensing in upper step is put into ball mill and is ground to 200 mesh and goes out mill, by the fine powder after grinding and water on demand
The soft durometer requirement wanted is matched；
（3）Clear mud：By step（2）In the mud that mixes mud is separated with water in clear mud, base mud is made；
（4）Dry：By step（3）In base mud place dry in the cool, make base mud water content be 70%；
（5）Rub mud：By step（4）In the base mud that has dried be kneaded into walk repeatedly, walk requires pore-free, free from admixture, and shale
Uniformly；
（6）Shaping：By step（5）In the walk that makes be placed on throwing on mud platform required base substrate be made, and carry out shape and make
The modification of type and color；
（7）Drying：By step（6）In the base substrate that makes dried at a temperature of 50-60 DEG C；
（8）Fire：By step（7）The base substrate made is placed in kiln, is fired 24 hours at a temperature of 1250-1300 DEG C,
Naturally cool to kiln discharge after normal temperature.