CN106242515A - A kind of marmite and preparation method thereof - Google Patents

A kind of marmite and preparation method thereof Download PDF

Info

Publication number
CN106242515A
CN106242515A CN201610644879.2A CN201610644879A CN106242515A CN 106242515 A CN106242515 A CN 106242515A CN 201610644879 A CN201610644879 A CN 201610644879A CN 106242515 A CN106242515 A CN 106242515A
Authority
CN
China
Prior art keywords
parts
mud
marmite
base substrate
soil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610644879.2A
Other languages
Chinese (zh)
Inventor
高秋祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
PINGDING YINGYU PORCELAIN Co Ltd
Original Assignee
PINGDING YINGYU PORCELAIN Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by PINGDING YINGYU PORCELAIN Co Ltd filed Critical PINGDING YINGYU PORCELAIN Co Ltd
Priority to CN201610644879.2A priority Critical patent/CN106242515A/en
Publication of CN106242515A publication Critical patent/CN106242515A/en
Pending legal-status Critical Current

Abstract

The invention belongs to sand container and preparation method thereof, be specifically related to a kind of marmite and preparation method thereof.Without heavy metals such as any lead, cadmiums in the dispensing of the present invention；By experiment, determining that moil fineness is moderate, keep certain porosity, good heat conduction effect, heat conduction is uniform, the advantage maintaining tradition marmite；Only at the external surface glazing of base substrate, inner surface not glazing, environmentally-friendly sanitary, it is easy to cleaning；In this formula chemical composition silicon, aluminum, magnesium during high-temperature firing can generating portion cordierite phase, sintered bauxite is introduced primarily into aggregate simultaneously, and both can effectively reduce thermal coefficient of expansion, and heat stability is more preferable, and the scope of application is wider；By technological transformation, can use multiple molding mode, production difficulty reduces, and cost reduces, and is suitable for batch production and the market demand.

Description

A kind of marmite and preparation method thereof
Technical field
The invention belongs to sand container and preparation method thereof, be specifically related to a kind of marmite and preparation method thereof.
Background technology
Tradition marmite is by the raw material that culm clay (rock of quartz, Anhydrite, clay mixing) is master, through high-temperature firing The ceramic become, has aeration, adsorptivity, the features such as heat transfer is uniform, and heat radiation is slow.Due to processing technology and raw material problem, Existing marmite exist heat stability the best, not environmentally, production method is single and high in cost of production technical problem.
Modern lithium marmite is to be raw material by quartz, Anhydrite, clay and spodumene, through the ceramic of high-temperature firing The features such as product, have Heat stability is good, and glaze is smooth easy to clean, resistance to rapid heat cycle, high insulating effect.But due to porcelain effect Good, porcelain is fine and smooth, and existing marmite breathability is the best, causes food taste not as tradition marmite.
Summary of the invention
Present invention aim to address that existing marmite exists the technical problem that breathability can not have concurrently with heat stability, it is provided that A kind of Heat stability is good preserves marmite of fine air permeability of tradition marmite and preparation method thereof the most simultaneously.
For solving above-mentioned technical problem, the technical solution used in the present invention is:
A kind of marmite, it is to be prepared from the following raw materials in parts by weight blank: ubac soil 10-20 part, blue or green cash 25-35 part, Anhydrite 5-10 part, quartz 15-20 part, Talcum 5-10 part, Huiyuan soil 2-5 part, cast alumin(i)um Alumina 6-8 part, sintered bauxite 15-25 part and Useless sagger powder 5-10 part.
A kind of method making described marmite, comprises the following steps:
1) dispensing: weigh ubac soil 10-20 part, blue or green cash 25-35 part, Anhydrite 5-10 part, quartz 15-20 part, Talcum 5-10 Part, Huiyuan soil 2-5 part, cast alumin(i)um Alumina 6-8 part, sintered bauxite 15-25 part and useless sagger powder 5-10 part, and mix homogeneously；
2) mud processed: by step 1) dispensing put in ball mill, the water adding 80 parts grinds to form mud；
3) filter mud device is used by step 2) moisture content in the mud prepared leaches, and makes mud by vacuum pugging device Section, and seal with plastic sheeting, old 4-7 days, then make molding standby mud section by vacuum pugging device；
4) use molding rolling device that standby for molding mud section is made the base substrate of required form, and by body drying to aqueous Divide 5%；
5) base substrate oral area is sealed, and at the external surface glazing of base substrate, open sealing, by the body drying of first-class glaze to containing Moisture less than 3%；
6) fire: by step 5) base substrate after glazing is positioned in kiln, is warming up to the programming rate of 4 DEG C/min 1250-1270 DEG C, and at a temperature of 1250-1270 DEG C, it is incubated 80min, naturally cool to room temperature, kiln discharge.
The present invention uses above technical scheme, without heavy metals such as any lead, cadmiums in dispensing；By experiment, determine mud Fineness is moderate, keeps certain porosity, good heat conduction effect, and heat conduction is uniform, the advantage maintaining tradition marmite；Only outside base substrate Surface glazing, inner surface not glazing, environmentally-friendly sanitary, it is easy to cleaning；In this formula chemical composition, silicon, aluminum, magnesium are in high-temperature firing mistake In journey can generating portion cordierite phase, sintered bauxite is introduced primarily into aggregate simultaneously, and both can effectively reduce thermal coefficient of expansion, heat Stability is more preferable, and the scope of application is wider；By technological transformation, can use multiple molding mode, production difficulty reduces, and cost drops Low, it is suitable for batch production and the market demand.
Detailed description of the invention
Embodiment 1
A kind of marmite, it is to be prepared from the following raw materials in parts by weight blank: 10 parts of ubac soil, blue or green cash 26 parts, Anhydrite 8 Part, 15 parts of quartz, 8 parts of Talcum, 2 parts of Huiyuan soil, 6 parts of cast alumin(i)um Alumina, sintered bauxite 20 parts and useless sagger powder 5 parts.
A kind of method making marmite described in the present embodiment, comprises the following steps:
1) dispensing: weigh 10 parts of ubac soil, blue or green cash 26 parts, Anhydrite 8 parts, 15 parts of quartz, 8 parts of Talcum, 2 parts of Huiyuan soil, life Bauxite 6 parts, sintered bauxite 20 parts and useless sagger powder 5 parts, and mix homogeneously；
2) mud processed: by step 1) dispensing put in ball mill, the water adding 80 parts grinds to form mud；
3) filter mud device is used by step 2) moisture content in the mud prepared leaches, and makes mud by vacuum pugging device Section, and seal with plastic sheeting, old 4 days, then make molding standby mud section by vacuum pugging device；
4) use molding rolling device that standby for molding mud section is made the base substrate of required form, and by body drying to aqueous Divide 5%；
5) base substrate oral area is sealed, and at the external surface glazing of base substrate, open sealing, by the body drying of first-class glaze to containing Moisture less than 3%；
6) fire: by step 5) base substrate after glazing is positioned in kiln, is warming up to 1250 with the programming rate of 4 DEG C/min DEG C, and at a temperature of 1250 DEG C, it is incubated 80min, naturally cool to room temperature, kiln discharge.
Embodiment 2
A kind of marmite, it is to be prepared from the following raw materials in parts by weight blank: 15 parts of ubac soil, blue or green cash 25 parts, Anhydrite 5 Part, 16 parts of quartz, 6 parts of Talcum, 3 parts of Huiyuan soil, 6 parts of cast alumin(i)um Alumina, sintered bauxite 17 parts and useless sagger powder 7 parts.
A kind of method making marmite described in the present embodiment, comprises the following steps:
1) dispensing: 15 parts of ubac soil, blue or green cash 25 parts, Anhydrite 5 parts, 16 parts of quartz, 6 parts of Talcum, Huiyuan soil 3 parts, cast alumin(i)um vitriol 6 parts of soil, sintered bauxite 17 parts and useless sagger powder 7 parts, and mix homogeneously；
2) mud processed: by step 1) dispensing put in ball mill, the water adding 80 parts grinds to form mud；
3) filter mud device is used by step 2) moisture content in the mud prepared leaches, and makes mud by vacuum pugging device Section, and seal with plastic sheeting, old 7 days, then make molding standby mud section by vacuum pugging device；
4) use molding rolling device that standby for molding mud section is made the base substrate of required form, and by body drying to aqueous Divide 5%；
5) base substrate oral area is sealed, and at the external surface glazing of base substrate, open sealing, by the body drying of first-class glaze to containing Moisture less than 3%；
6) fire: by step 5) base substrate after glazing is positioned in kiln, is warming up to 1270 with the programming rate of 4 DEG C/min DEG C, and at a temperature of 1270 DEG C, it is incubated 80min, naturally cool to room temperature, kiln discharge.
Embodiment 3
A kind of marmite, it is to be prepared from the following raw materials in parts by weight blank: 18 parts of ubac soil, blue or green cash 28 parts, Anhydrite 5 Part, 15 parts of quartz, 5 parts of Talcum, 2 parts of Huiyuan soil, 7 parts of cast alumin(i)um Alumina, sintered bauxite 15 parts and useless sagger powder 5 parts.
A kind of method making marmite described in the present embodiment, comprises the following steps:
1) dispensing: weigh 18 parts of ubac soil, blue or green cash 28 parts, Anhydrite 5 parts, 15 parts of quartz, 5 parts of Talcum, 2 parts of Huiyuan soil, life Bauxite 7 parts, sintered bauxite 15 parts and useless sagger powder 5 parts, and mix homogeneously；
2) mud processed: by step 1) dispensing put in ball mill, the water adding 80 parts grinds to form mud；
3) filter mud device is used by step 2) moisture content in the mud prepared leaches, and makes mud by vacuum pugging device Section, and seal with plastic sheeting, old 6 days, then make molding standby mud section by vacuum pugging device；
4) use molding rolling device that standby for molding mud section is made the base substrate of required form, and by body drying to aqueous Divide 5%；
5) base substrate oral area is sealed, and at the external surface glazing of base substrate, open sealing, by the body drying of first-class glaze to containing Moisture less than 3%；
6) fire: by step 5) base substrate after glazing is positioned in kiln, is warming up to 1260 with the programming rate of 4 DEG C/min DEG C, and at a temperature of 1260 DEG C, it is incubated 80min, naturally cool to room temperature, kiln discharge.
Embodiment 4
A kind of marmite, it is to be prepared from the following raw materials in parts by weight blank: 20 parts of ubac soil, blue or green cash 35 parts, Anhydrite 10 Part, 20 parts of quartz, 10 parts of Talcum, 5 parts of Huiyuan soil, 8 parts of cast alumin(i)um Alumina, sintered bauxite 25 parts and useless sagger powder 10 parts.
A kind of method making described marmite, comprises the following steps:
1) dispensing: weigh 20 parts of ubac soil, blue or green cash 35 parts, Anhydrite 10 parts, 20 parts of quartz, 10 parts of Talcum, 5 parts of Huiyuan soil, 8 parts of cast alumin(i)um Alumina, sintered bauxite 25 parts and useless sagger powder 10 parts, and mix homogeneously；
2) mud processed: by step 1) dispensing put in ball mill, the water adding 80 parts grinds to form mud；
3) filter mud device is used by step 2) moisture content in the mud prepared leaches, and makes mud by vacuum pugging device Section, and seal with plastic sheeting, old 5 days, then make molding standby mud section by vacuum pugging device；
4) use molding rolling device that standby for molding mud section is made the base substrate of required form, and by body drying to aqueous Divide 5%；
5) base substrate oral area is sealed, and at the external surface glazing of base substrate, open sealing, by the body drying of first-class glaze to containing Moisture less than 3%；
6) fire: by step 5) base substrate after glazing is positioned in kiln, is warming up to 1250 with the programming rate of 4 DEG C/min DEG C, and at a temperature of 1250 DEG C, it is incubated 80min, naturally cool to room temperature, kiln discharge.

Claims (2)

1. a marmite, it is characterised in that: it is to be prepared from the following raw materials in parts by weight blank: ubac soil 10-20 part, blue or green cash 25-35 part, Anhydrite 5-10 part, quartz 15-20 part, Talcum 5-10 part, Huiyuan soil 2-5 part, cast alumin(i)um Alumina 6-8 part, sintered bauxite 15-25 part and useless sagger powder 5-10 part.
2. the manufacture method of marmite described in a claim 1, it is characterised in that: comprise the following steps:
1) dispensing: weigh ubac soil 10-20 part, blue or green cash 25-35 part, Anhydrite 5-10 part, quartz 15-20 part, Talcum 5-10 part, muddy Source soil 2-5 part, cast alumin(i)um Alumina 6-8 part, sintered bauxite 15-25 part and useless sagger powder 5-10 part, and mix homogeneously；
2) mud processed: by step 1) dispensing put in ball mill, the water adding 80 parts grinds to form mud；
3) filter mud device is used by step 2) moisture content in the mud prepared leaches, and makes mud section by vacuum pugging device, and Seal with plastic sheeting, old 4-7 days, then make molding standby mud section by vacuum pugging device；
4) use molding rolling device that standby for molding mud section is made the base substrate of required form, and by body drying to moisture content 5%；
5) base substrate oral area is sealed, and at the external surface glazing of base substrate, open sealing, by the body drying of first-class glaze to moisture content Less than 3%；
6) fire: by step 5) base substrate after glazing is positioned in kiln, is warming up to 1250-with the programming rate of 4 DEG C/min 1270 DEG C, and at a temperature of 1250-1270 DEG C, it is incubated 80min, naturally cool to room temperature, kiln discharge.
CN201610644879.2A 2016-08-08 2016-08-08 A kind of marmite and preparation method thereof Pending CN106242515A (en)