CN106082979A - A kind of architectural pottery and preparation method thereof - Google Patents
A kind of architectural pottery and preparation method thereof Download PDFInfo
- Publication number
- CN106082979A CN106082979A CN201610413662.0A CN201610413662A CN106082979A CN 106082979 A CN106082979 A CN 106082979A CN 201610413662 A CN201610413662 A CN 201610413662A CN 106082979 A CN106082979 A CN 106082979A
- Authority
- CN
- China
- Prior art keywords
- parts
- glair
- architectural pottery
- anhydrite
- pottery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of architectural pottery and preparation method thereof, including Kaolin 20 35 parts, 20 30 parts of quartz, Anhydrite 15 30 parts, porcelain stone 10 20 parts, 8 15 parts of fiber crops storehouse soil, earthy cobalt 20 35 parts, glair 10 12 parts, sintering aid 5 10 parts.The present invention strengthens that ceramics strength is high, compactness is good, toughness significantly improves, and high temperature resistant and wear-resisting excellence, can be widely used for various the strength of materials being required, high field uses mineral and industrial chemicals, production cost is relatively low, be prone to large-scale production, multiple moulding and texture can be made, save mineral resources;Cheap, production technology is simple, is suitable for large-scale production.
Description
Technical field
The present invention relates to technical field of ceramic preparation, be specifically related to a kind of architectural pottery and preparation method thereof.
Background technology
Existing pottery is mainly fired by china clay and clay and is formed.Due to region and a large amount of exploitation of china clay, its resource is more
Coming the most limited, the problem the most how solving china clay scarcity of resources has become an important subject of the industry.
Pottery is the advanced material of development during human being's production, and it has good chemical stability and sight.Existing
Foundry industry has been carried out substantial amounts of research and experiment on the basis of traditional handicraft to ceramic, wherein with aluminium compound and
Silicon compound is that the ceramic product research of Main Ingredients and Appearance is the most deep, and makes its field studied more concentrate on above-mentioned model
In enclosing, thus limit the development of ceramic product.
Summary of the invention
For solving the problems referred to above, the invention provides a kind of architectural pottery and preparation method thereof.
For achieving the above object, the technical scheme that the present invention takes is:
A kind of architectural pottery and preparation method thereof, is prepared from including by the raw material of following weight portion: Kaolin 20-35 part, stone
English 20-30 part, Anhydrite 15-30 part, porcelain stone 10-20 part, fiber crops storehouse soil 8-15 part, earthy cobalt 20-35 part, glair 10-12 part, sintering
Auxiliary agent 5-10 part.
Further, one or more during described glair is silicon oxide, aluminium oxide, calcium oxide, sodium oxide and potassium oxide.
Further, one or both mixture during described sintering aid is aluminium sesquioxide and magnesium oxide.
Further, the preparation method of a kind of architectural pottery, comprise the steps:
S1, weigh a certain amount of Kaolin 20-35 part, quartz 20-30 part, Anhydrite 15-30 part, porcelain stone 10-20 part, fiber crops storehouse soil 8-
15 parts, add after the mixing of earthy cobalt 20-35 part after pulverizer pulverizes, through 120 mesh sieves, obtain material;
S2, being added water by the material of step S1 gained carries out ball milling, is subsequently adding glair 10-12 part, sintering aid 5-10 part is carried out
Wet ball mill 15-20 minute, after standing 20-30 minute, rewetting ball milling 10-15 minute, obtains ceramic size;
S3, the ceramic size of step S2 gained is carried out slip casting through making mould, make molding, put into kiln and be fired, burn
One-tenth temperature: 1000-1200 DEG C;Obtain pottery first product;
S4, by after ground and roasting for the ceramic first product of step S3 gained water, test package is put in storage.
Further, a kind of architectural pottery, the raw material of following weight portion be prepared from: Kaolin 28 parts, 25 parts of quartz,
Anhydrite 19 parts, porcelain stone 15 parts, 11 parts of fiber crops storehouse soil, earthy cobalt 25 parts, glair 11 parts, sintering aid 7 parts.
The present invention strengthens that ceramics strength is high, compactness is good, toughness significantly improves, and high temperature resistant and wear-resisting excellence, can be extensive
For various, the strength of materials being required, high field uses mineral and industrial chemicals, production cost is relatively low, be prone to large-scale production, can
Make multiple moulding and texture, save mineral resources;Cheap, production technology is simple, is suitable for large-scale production.
Detailed description of the invention
In order to make objects and advantages of the present invention clearer, below in conjunction with embodiment, the present invention is carried out the most in detail
Explanation.Should be appreciated that specific embodiment described herein, only in order to explain the present invention, is not intended to limit the present invention.
The present invention includes being prepared from by the raw material of following weight portion: Kaolin 20-35 part, quartz 20-30 part, Anhydrite
15-30 part, porcelain stone 10-20 part, fiber crops storehouse soil 8-15 part, earthy cobalt 20-35 part, glair 10-12 part, sintering aid 5-10 part.
Described glair is one or more in silicon oxide, aluminium oxide, calcium oxide, sodium oxide and potassium oxide.
Described sintering aid is one or both mixture in aluminium sesquioxide and magnesium oxide.
The preparation method of a kind of architectural pottery, comprises the steps:
S1, weigh a certain amount of Kaolin 20-35 part, quartz 20-30 part, Anhydrite 15-30 part, porcelain stone 10-20 part, fiber crops storehouse soil 8-
15 parts, add after the mixing of earthy cobalt 20-35 part after pulverizer pulverizes, through 120 mesh sieves, obtain material;
S2, being added water by the material of step S1 gained carries out ball milling, is subsequently adding glair 10-12 part, sintering aid 5-10 part is carried out
Wet ball mill 15-20 minute, after standing 20-30 minute, rewetting ball milling 10-15 minute, obtains ceramic size;
S3, the ceramic size of step S2 gained is carried out slip casting through making mould, make molding, put into kiln and be fired, burn
One-tenth temperature: 1000-1200 DEG C;Obtain pottery first product;
S4, by after ground and roasting for the ceramic first product of step S3 gained water, test package is put in storage.
Embodiment 1:
S1, weigh a certain amount of Kaolin 28 parts, quartz 25 parts, Anhydrite 19 parts, porcelain stone 15 parts, fiber crops storehouse soil 11 parts, earthy cobalt 25
After addition pulverizer is pulverized after part mixing, through 120 mesh sieves, obtain material;
S2, being added water by the material of step S1 gained carries out ball milling, is subsequently adding glair 11 parts, sintering aid 7 parts carries out wet ball mill
18 minutes, after standing 25 minutes, rewetting ball milling 13 minutes, obtained ceramic size;
S3, the ceramic size of step S2 gained is carried out slip casting through making mould, make molding, put into kiln and be fired, burn
One-tenth temperature: 1100 DEG C;Obtain pottery first product;
S4, by after ground and roasting for the ceramic first product of step S3 gained water, test package is put in storage.
Embodiment 2:
S1, weigh a certain amount of Kaolin 20 parts, quartz 20 parts, Anhydrite 15 parts, porcelain stone 10 parts, fiber crops storehouse soil 8 parts, earthy cobalt 20 parts
After addition pulverizer is pulverized after mixing, through 120 mesh sieves, obtain material;
S2, being added water by the material of step S1 gained carries out ball milling, is subsequently adding glair 10 parts, sintering aid 5 parts carries out wet ball mill
15 minutes, after standing 20 minutes, rewetting ball milling 10 minutes, obtained ceramic size;
S3, the ceramic size of step S2 gained is carried out slip casting through making mould, make molding, put into kiln and be fired, burn
One-tenth temperature: 1000 DEG C;Obtain pottery first product;
S4, by after ground and roasting for the ceramic first product of step S3 gained water, test package is put in storage.
Embodiment 3:
S1, weigh a certain amount of Kaolin 35 parts, quartz 30 parts, Anhydrite 30 parts, porcelain stone 20 parts, fiber crops storehouse soil 15 parts, earthy cobalt 35
After addition pulverizer is pulverized after part mixing, through 120 mesh sieves, obtain material;
S2, being added water by the material of step S1 gained carries out ball milling, is subsequently adding glair 12 parts, sintering aid 10 parts carries out wet ball mill
20 minutes, after standing 30 minutes, rewetting ball milling 15 minutes, obtained ceramic size;
S3, the ceramic size of step S2 gained is carried out slip casting through making mould, make molding, put into kiln and be fired, burn
One-tenth temperature: 1200 DEG C;Obtain pottery first product;
S4, by after ground and roasting for the ceramic first product of step S3 gained water, test package is put in storage.
The present invention strengthens that ceramics strength is high, compactness is good, toughness significantly improves, and high temperature resistant and wear-resisting excellence, can be extensive
For various, the strength of materials being required, high field uses mineral and industrial chemicals, production cost is relatively low, be prone to large-scale production, can
Make multiple moulding and texture, save mineral resources;Cheap, production technology is simple, is suitable for large-scale production.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (5)
1. an architectural pottery, it is characterised in that include being prepared from by the raw material of following weight portion: Kaolin 20-35 part, stone
English 20-30 part, Anhydrite 15-30 part, porcelain stone 10-20 part, fiber crops storehouse soil 8-15 part, earthy cobalt 20-35 part, glair 10-12 part, sintering
Auxiliary agent 5-10 part.
A kind of architectural pottery the most according to claim 1, it is characterised in that described glair is silicon oxide, aluminium oxide, oxidation
One or more in calcium, sodium oxide and potassium oxide.
A kind of architectural pottery the most according to claim 1, it is characterised in that described sintering aid is aluminium sesquioxide and oxygen
Change one or both mixture in magnesium.
The preparation method of a kind of architectural pottery the most according to claim 1, it is characterised in that comprise the steps:
S1, weigh a certain amount of Kaolin 20-35 part, quartz 20-30 part, Anhydrite 15-30 part, porcelain stone 10-20 part, fiber crops storehouse soil 8-
15 parts, add after the mixing of earthy cobalt 20-35 part after pulverizer pulverizes, through 120 mesh sieves, obtain material;
S2, being added water by the material of step S1 gained carries out ball milling, is subsequently adding glair 10-12 part, sintering aid 5-10 part is carried out
Wet ball mill 15-20 minute, after standing 20-30 minute, rewetting ball milling 10-15 minute, obtains ceramic size;
S3, the ceramic size of step S2 gained is carried out slip casting through making mould, make molding, put into kiln and be fired, burn
One-tenth temperature: 1000-1200 DEG C;Obtain pottery first product;
S4, by after ground and roasting for the ceramic first product of step S3 gained water, test package is put in storage.
A kind of architectural pottery the most according to claim 1, it is characterised in that be prepared from by the raw material of following weight portion:
Kaolin 28 parts, 25 parts of quartz, Anhydrite 19 parts, porcelain stone 15 parts, 11 parts of fiber crops storehouse soil, earthy cobalt 25 parts, glair 11 parts, sintering aid
7 parts.