CN107468567B - 远红外离子水 - Google Patents
远红外离子水 Download PDFInfo
- Publication number
- CN107468567B CN107468567B CN201710722203.5A CN201710722203A CN107468567B CN 107468567 B CN107468567 B CN 107468567B CN 201710722203 A CN201710722203 A CN 201710722203A CN 107468567 B CN107468567 B CN 107468567B
- Authority
- CN
- China
- Prior art keywords
- water
- rose
- parts
- far infrared
- nano powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于化妆品技术领域，涉及一种远红外离子水。本发明包括负离子水和玫瑰花水，制备方法是：按质量份数取99份负离子材料和1份乳化剂，加入800份蒸馏水，在40‑50℃，2000‑2500rpm下恒温搅拌90min，得到负离子水混合液，按质量份数取100份玫瑰花水，加入到上述混合液中，在常温下搅拌10‑15min，使混合物充分融合，静置24小时以上，过滤除渣后得到远红外离子水。本发明具有抗氧化、保湿、抑菌及释放负离子等效果。
Description
技术领域
本发明属于化妆品技术领域，涉及一种远红外离子水。
背景技术
目前市场上的保湿、护肤的化妆水很多，也有一些采用天然物质调配的产品。但现在市场上的各类化妆水存在很多的问题。首先，在化妆水中添加各类人造成分或化学合成成分，导致产品对皮肤产生刺激；其次，效果欠佳，市场上很多化妆水功能较为单一，在宣传上有很多的功能，但实际只有补水保湿功能，且保湿时间并不持久；再次，化妆水市场混乱，各类产品宣传过于夸大，造成消费者无法分辨优劣，往往会有很高的价格买到低效的产品，达不到消费者预期的效果。
发明内容
本发明的目的是针对上述问题，提供一种远红外离子水。
为达到上述目的，本发明采用了下列技术方案：
一种远红外离子水，本远红外离子水包括负离子水和玫瑰花水。
在上述的远红外离子水中，本远红外离子水的制备方法是：
按质量份数取99份负离子材料和1份乳化剂，加入800份蒸馏水，在40-50℃，2000-2500rpm下恒温搅拌90min，得到负离子水混合液，
按质量份数取100份玫瑰花水，加入到上述混合液中，在常温下搅拌10-15min，使混合物充分融合，
静置24小时以上，过滤除渣后得到远红外离子水。
在上述的远红外离子水中，按质量份数取99份负离子材料和1份乳化剂，加入800份蒸馏水，在40-50℃，2000-2500rpm下恒温搅拌90min，静置分层，滤除固体物，得到负离子水，
按质量份数取100份玫瑰花水，加入到上述负离子水中，在常温下搅拌10-15min，使充分融合，得到远红外离子水。
在上述的远红外离子水中，所述的乳化剂为非离子表面活性剂。
在上述的远红外离子水中，所述的乳化剂包括烷基醇酰胺、多元醇和烷基酚聚氧乙烯醚中一种或几种。
在上述的远红外离子水中，所述的负离子材料的制备方法是：
将海鸥石、托玛琳、欧泊石、麦饭石和六环石分别经纳米研磨机研磨至粒径在100-200纳米之间，然后按35wt％海鸥石纳米粉、25wt％托玛琳纳米粉、20wt％欧泊石纳米粉、10wt％麦饭石纳米粉和10wt％六环石纳米粉在常温，800rpm下搅拌30min制成负离子材料。
在上述的远红外离子水中，所述的玫瑰花水的制备方法是：
将新鲜玫瑰采摘后放入到蒸馏器中，按鲜花重量放入10wt％的食盐，加入鲜花重量10倍的蒸馏水，蒸馏6-10小时，蒸馏液冷凝后进入油水分离器静置分层，分离精油后得到玫瑰花水。
在上述的远红外离子水中，所述的玫瑰花水中含有0.02％-0.03wt％玫瑰精油、0.02％-0.03wt％环肽和0.02％-0.03wt％鞣质。
一种远红外离子水，由负离子水和玫瑰花水组成。
在上述的远红外离子水中，按质量份数取99份负离子材料和1份乳化剂，加入800份蒸馏水，在40-50℃，2000-2500rpm下恒温搅拌90min，静置分层，滤除固体物，得到负离子水，
按质量份数取100份玫瑰花水，加入到上述负离子水中，在常温下搅拌10-15min，使充分融合，得到远红外离子水，
所述的玫瑰花水的制备方法是：
将新鲜玫瑰采摘后放入到蒸馏器中，按鲜花重量放入10wt％的食盐，加入鲜花重量10倍的蒸馏水，蒸馏9小时，蒸馏液冷凝后进入油水分离器静置分层，分离精油后得到玫瑰花水，玫瑰花水，提取玫瑰精油后的重要副产品，具有杀菌、留香、促进皮肤血液循环、增进新陈代谢、补水保湿、滋润防皱、保持肌肤柔嫩光泽的功效，
所述的负离子材料的制备方法是：
将海鸥石、托玛琳、欧泊石、麦饭石、六环石分别经纳米研磨机研磨至粒径在100-200纳米之间，然后按35wt％海鸥石纳米粉、25wt％托玛琳纳米粉、20wt％欧泊石纳米粉、10wt％麦饭石纳米粉和10wt％六环石纳米粉在常温，800rpm下搅拌30min制成负离子材料。
海鸥石，英文名：Health。主要成分为CaO、SiO2以及变价金属Fe；内部结构具有20-60nm的孔隙，故具备强大的吸附功能；当空气中水分子进入海鸥石内部微孔时，水分子被变价铁产生的微电场电离，产生天然负离子，负氧离子浓度达1700个/cm3，同时海鸥石内部含有少量TiO2，故具有光电催化作用，能把空气中的有害细菌、病毒杀灭，根据实验，海鸥石对金黄色葡萄球菌、大肠杆菌、白色念球菌、枯草菌的抗菌率高达90％以上。
托玛琳是一种天然矿石，也叫电气石，能释放远红外线，负离子，含有多种微量元素，能产生0.06ma生物电流，能改善水质，放入托玛琳的水，是弱碱性的小分子团的水，最适合人饮用。水质呈现弱碱性，具有抗氧化作用，有利于人体健康。
欧泊石，又称欧珀、蛋白石，类别是非晶质，属蛋白石宝石类。蛋白石具有独特的天然纳米级微孔结构，有着强大的吸附功能，同时释放天然空气负离子。
麦饭石,中药名。学名为：石英二长岩。麦饭石对生物无毒、无害并具有一定生物活性的复合矿物或药用岩石。具有解毒散结，去腐生肌，除寒祛湿，益肝健胃，活血化瘀，利尿化石，延年益寿之功效。
六环石，生成于奥陶系(距今2亿4千万年)。具有洁净结构，能自然发射远红外线，法向发射率高达0.88，有独特的生物电功能。是一种吸附性强大、抗电磁波、抗化疗、抗肿瘤、抗艾滋病病毒的古沉积岩，六环石富含钙、镁、钠、钾、铁、硒、锌、锶、铜及贵金属锗等人体必需的营养元素，并永久释放负离子。
与现有的技术相比，本发明的优点在于：
1、本远红外离子水含有起保湿作用的玫瑰花水，又含有杀菌抑菌、抗氧化、释放4-16um远红外射线的负离子材料，通过乳化剂作用，将每部分功效成分溶合在一起，形成稳定均相，充分发挥各个成分的作用，具有抗氧化、保湿、抑菌及释放负离子等效果。
2、乳化剂采用非离子表面活性剂，即起到乳化剂作用，又降低混合液粘度。
3、产品制备工艺简单，成本低廉。
具体实施方式
下述实施例中所用的试剂，如无特殊说明，可以从常规生化试剂商店购买得到。
实施例1
一种远红外离子水，包括负离子水和玫瑰花水
按质量份数取99份负离子材料和1份乳化剂，加入800份蒸馏水，在40-50℃，2000rpm下恒温搅拌90min，得到负离子水混合液，按质量份数取100份玫瑰花水，加入到上述混合液中，在常温下搅拌15min，使混合物充分融合，静置24小时，过滤除渣后得到远红外离子水。
乳化剂为非离子表面活性剂，包括烷基醇酰胺、多元醇和烷基酚聚氧乙烯醚中一种或几种。在本实施例中，非离子表面活性剂为6501。
负离子材料的制备方法是：
将海鸥石、托玛琳、欧泊石、麦饭石和六环石分别经纳米研磨机研磨至粒径在100-200纳米之间，然后按35wt％海鸥石纳米粉、25wt％托玛琳纳米粉、20wt％欧泊石纳米粉、10wt％麦饭石纳米粉和10wt％六环石纳米粉在常温，800rpm下搅拌30min制成负离子材料。
玫瑰花水的制备方法是：
将新鲜玫瑰采摘后放入到蒸馏器中，按鲜花重量放入10wt％的食盐，加入鲜花重量10倍的蒸馏水，蒸馏6-10小时，蒸馏液冷凝后进入油水分离器静置分层，分离精油后得到玫瑰花水。玫瑰花水中含有0.02％-0.03wt％玫瑰精油、0.02％-0.03wt％环肽和0.02％-0.03wt％鞣质。
实施例2
一种远红外离子水，包括负离子水和玫瑰花水
按质量份数取99份负离子材料和1份乳化剂，加入800份蒸馏水，在45℃，2500rpm下恒温搅拌90min，得到负离子水混合液，按质量份数取100份玫瑰花水，加入到上述混合液中，在常温下搅拌10min，使混合物充分融合，静置26小时，过滤除渣后得到远红外离子水。
乳化剂为非离子表面活性剂，包括烷基醇酰胺、多元醇和烷基酚聚氧乙烯醚中一种或几种。在本实施例中，非离子表面活性剂为平平加O。
负离子材料的制备方法是：
将海鸥石、托玛琳、欧泊石、麦饭石和六环石分别经纳米研磨机研磨至粒径在100-200纳米之间，然后按35wt％海鸥石纳米粉、25wt％托玛琳纳米粉、20wt％欧泊石纳米粉、10wt％麦饭石纳米粉和10wt％六环石纳米粉在常温，800rpm下搅拌30min制成负离子材料。
玫瑰花水的制备方法是：
将新鲜玫瑰采摘后放入到蒸馏器中，按鲜花重量放入10wt％的食盐，加入鲜花重量10倍的蒸馏水，蒸馏8小时，蒸馏液冷凝后进入油水分离器静置分层，分离精油后得到玫瑰花水。玫瑰花水中含有0.025wt％玫瑰精油、0.025wt％环肽和0.025wt％鞣质。
实施例3
一种远红外离子水，由负离子水和玫瑰花水组成。
按质量份数取99份负离子材料和1份乳化剂，加入800份蒸馏水，在40-50℃，2000-2500rpm下恒温搅拌90min，静置分层，滤除固体物，得到负离子水，按质量份数取100份玫瑰花水，加入到上述负离子水中，在常温下搅拌10-15min，使充分融合，得到远红外离子水。
所述的玫瑰花水的制备方法是：
将新鲜玫瑰采摘后放入到蒸馏器中，按鲜花重量放入10wt％的食盐，加入鲜花重量10倍的蒸馏水，蒸馏9小时，蒸馏液冷凝后进入油水分离器静置分层，分离精油后得到玫瑰花水，
所述的负离子材料的制备方法是：
将海鸥石、托玛琳、欧泊石、麦饭石、六环石分别经纳米研磨机研磨至粒径在100-200纳米之间，然后按35wt％海鸥石纳米粉、25wt％托玛琳纳米粉、20wt％欧泊石纳米粉、10wt％麦饭石纳米粉和10wt％六环石纳米粉在常温，800rpm下搅拌30min制成负离子材料。
本实施例中，乳化剂为非离子表面活性剂Span-20。
实施例4
一种远红外离子水，包括负离子水和玫瑰花水。
本远红外离子水的制备方法是：
按质量份数取99份负离子材料和1份乳化剂，加入800份蒸馏水，在40-50℃，2000-2500rpm下恒温搅拌90min，得到负离子水混合液，按质量份数取100份玫瑰花水，加入到上述混合液中，在常温下搅拌10-15min，使混合物充分融合，静置24小时以上，本实施例中，静置25小时，过滤除渣后得到远红外离子水。
乳化剂为非离子表面活性剂，包括烷基醇酰胺、多元醇和烷基酚聚氧乙烯醚中一种或几种。在本实施例中，非离子表面活性剂为平平加O。
负离子材料的制备方法是：
将海鸥石、托玛琳、欧泊石、麦饭石和六环石分别经纳米研磨机研磨至粒径在100-200纳米之间，然后按35wt％海鸥石纳米粉、25wt％托玛琳纳米粉、20wt％欧泊石纳米粉、10wt％麦饭石纳米粉和10wt％六环石纳米粉在常温，800rpm下搅拌30min制成负离子材料。
玫瑰花水的制备方法是：
将新鲜玫瑰采摘后放入到蒸馏器中，按鲜花重量放入10wt％的食盐，加入鲜花重量10倍的蒸馏水，蒸馏8小时，蒸馏液冷凝后进入油水分离器静置分层，分离精油后得到玫瑰花水。玫瑰花水中含有0.025wt％玫瑰精油、0.025wt％环肽和0.025wt％鞣质。
对比例1
按质量份数取99份负离子材料和1份乳化剂，加入800份蒸馏水，在40-50℃，2000rpm下恒温搅拌90min，得到负离子水混合液，按质量份数取100份薰衣草花水，加入到上述混合液中，在常温下搅拌15min，使混合物充分融合，静置24小时，过滤除渣后得到远红外离子水。
乳化剂为6501。
负离子材料的制备方法是：
将海鸥石、托玛琳、欧泊石、麦饭石和六环石分别经纳米研磨机研磨至粒径在100-200纳米之间，然后按35wt％海鸥石纳米粉、25wt％托玛琳纳米粉、20wt％欧泊石纳米粉、10wt％麦饭石纳米粉和10wt％六环石纳米粉在常温，800rpm下搅拌30min制成负离子材料。
薰衣草花水的制备方法是：
将新鲜薰衣草花采摘后放入到蒸馏器中，按鲜花重量放入10wt％的食盐，加入鲜花重量10倍的蒸馏水，蒸馏6-10小时，蒸馏液冷凝后进入油水分离器静置分层，分离精油后得到薰衣草花水。
对比例2
按质量份数取99份负离子材料和1份乳化剂，加入800份蒸馏水，在40-50℃，2000rpm下恒温搅拌90min，得到负离子水混合液，按质量份数取100份洋甘菊花水，加入到上述混合液中，在常温下搅拌15min，使混合物充分融合，静置24小时，过滤除渣后得到远红外离子水。
乳化剂为6501。
负离子材料的制备方法是：
将海鸥石、托玛琳、欧泊石、麦饭石和六环石分别经纳米研磨机研磨至粒径在100-200纳米之间，然后按35wt％海鸥石纳米粉、25wt％托玛琳纳米粉、20wt％欧泊石纳米粉、10wt％麦饭石纳米粉和10wt％六环石纳米粉在常温，800rpm下搅拌30min制成负离子材料。
洋甘菊花水的制备方法是：
将新鲜洋甘菊花采摘后放入到蒸馏器中，按鲜花重量放入10wt％的食盐，加入鲜花重量10倍的蒸馏水，蒸馏6-10小时，蒸馏液冷凝后进入油水分离器静置分层，分离精油后得到洋甘菊花水。
结果分析
稳定性考察。
对实施例1-4的远红外离子水进行稳定性考察，得出以下结果。
显示实施例1-4的远红外离子水符合稳定性要求。
失水率考察。
对实施例1-4、对比例1-2、去离子水和1wt％甘油采用世界公认的CORNEOMETER(皮肤测试仪)-电容法进行测试。其结果通过设定的湿度测量值[Moisture MeasurementValue(缩写：MMV)]来表示。MMV为0-150的数值。
| 试验项目 | 2h(失水率％) | 4h(失水率％) | 6h(失水率％) | 8h(失水率％) |
| 去离子水 | 14 | 11 | 7 | 6.5 |
| 甘油 | 10 | 7.5 | 4.5 | 4 |
| 实施例1 | 4.5 | 4 | 3.6 | 3.2 |
| 实施例2 | 4.5 | 4.1 | 3.6 | 3.3 |
| 实施例3 | 4.5 | 4 | 3.7 | 3.3 |
| 实施例4 | 4.4 | 4 | 3.5 | 3.1 |
| 对比例1 | 5.5 | 5 | 4 | 3.5 |
| 对比例2 | 5.2 | 4.8 | 4.3 | 3.8 |
从结果看，实施例1-4的失水率明显小于去离子，而对比例1-2的失水率比实施例1-4相对高20％左右，由于对比例1-2的技术特征与实施例4基本相同，不同之处是实施例4采用玫瑰花水，而对比例1和2则是分别采用薰衣草花水和洋甘菊花水，可见在实际应用中玫瑰花水的保湿效果更好。
负离子释放考察。
将实施例1-4、对比例1-2、去离子水和1wt％甘油各10ml喷在面膜纸上并晾干，分别放入60cm*60cm*60cm的密封玻璃箱，进行负离子释放试验。结果如下表。
从结果看，去离子水和甘油水溶液无负离子释放，而实施例1-4的负离子释放值24小时平均值均大于等于1500个/cm3，说明本发明具有负离子释放功能，同时对比例1-2的负离子释放值24小时平均值均大于等于1500个/cm3，说明也具有负离子释放功能，但相对于实施例4，负离子释放值降低15％左右，可见玫瑰花水与负离子水协同能力较强。
抑菌性检验。
供试验菌种为金黄色葡萄球菌、枯草芽孢杆菌和大肠杆菌。培养基为牛肉膏蛋白胨培养基。通过平板稀释涂布法，对菌落进行计数。设定2个组，对照组只有液体培养基和菌种，实验组1在对照组基础上加入实施例1-4和对比例1-2制备的产品，每个重复3次。
结果表明，实施例1-4和对比例1-2制备的产品对金黄色葡萄球菌、枯草芽孢杆菌、大肠杆菌都有明显抑制作用，效果明显优于对照组。另外，对比例1-2的菌落数比实施例4的菌落数高出20-50％，可见玫瑰花水与负离子水的结合抑菌效果更好。
抗氧化试验。
取表明完好无腐烂的苹果，均匀切成8份。制作60cm*60cm*60cm的密封玻璃箱4个。设定2个组，对照组：将1/4份的苹果放入无任何处理的玻璃密封箱内，实验组：将实施例1-4和对比例1-2制备的产品各100ml均匀喷在3个密闭玻璃箱内壁上并晾干，每个玻璃密封箱内分别放入1/8份的苹果，每个重复3次。
结果表明，实施例1-4和对比例1-2制备的产品对苹果切面表面具有抗氧化作用，效果明显优于对照组。
本文中所描述的具体实施例仅仅是对本发明精神作举例说明。本发明所属技术领域的技术人员可以对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代，但并不会偏离本发明的精神或者超越所附权利要求书所定义的范围。
Claims (6)
1.一种远红外离子水，其特征在于，本远红外离子水包括负离子水和玫瑰花水，
本远红外离子水的制备方法是：
按质量份数取99份负离子材料和1份乳化剂，加入800份蒸馏水，在40-50℃，2000-2500rpm下恒温搅拌90min，得到负离子水混合液，
按质量份数取100份玫瑰花水，加入到上述混合液中，在常温下搅拌10-15min，使混合物充分融合，
静置24小时以上，过滤除渣后得到远红外离子水，
所述的玫瑰花水的制备方法是：
将新鲜玫瑰采摘后放入到蒸馏器中，按鲜花重量放入10wt％的食盐，加入鲜花重量10倍的蒸馏水，蒸馏6-10小时，蒸馏液冷凝后进入油水分离器静置分层，分离精油后得到玫瑰花水，
所述的负离子材料的制备方法是：
将海鸥石、托玛琳、欧泊石、麦饭石和六环石分别经纳米研磨机研磨至粒径在100-200纳米之间，然后按35wt％海鸥石纳米粉、25wt％托玛琳纳米粉、20wt％欧泊石纳米粉、10wt％麦饭石纳米粉和10wt％六环石纳米粉在常温，800rpm下搅拌30min制成负离子材料。
2.根据权利要求1所述的远红外离子水，其特征在于，
按质量份数取99份负离子材料和1份乳化剂，加入800份蒸馏水，在40-50℃，2000-2500rpm下恒温搅拌90min，静置分层，滤除固体物，得到负离子水，
按质量份数取100份玫瑰花水，加入到上述负离子水中，在常温下搅拌10-15min，使充分融合，得到远红外离子水。
3.根据权利要求1或2所述的远红外离子水，其特征在于，所述的乳化剂为非离子表面活性剂。
4.根据权利要求3所述的远红外离子水，其特征在于，所述的乳化剂包括烷基醇酰胺、多元醇和烷基酚聚氧乙烯醚中一种或几种。
5.根据权利要求1所述的远红外离子水，其特征在于，所述的玫瑰花水中含有0.02％-0.03wt％玫瑰精油、0.02％-0.03wt％环肽和0.02％-0.03wt％鞣质。
6.一种远红外离子水，其特征在于，由负离子水和玫瑰花水组成，
按质量份数取99份负离子材料和1份乳化剂，加入800份蒸馏水，在40-50℃，2000-2500rpm下恒温搅拌90min，静置分层，滤除固体物，得到负离子水，
按质量份数取100份玫瑰花水，加入到上述负离子水中，在常温下搅拌10-15min，使充分融合，得到远红外离子水，
所述的玫瑰花水的制备方法是：
将新鲜玫瑰采摘后放入到蒸馏器中，按鲜花重量放入10wt％的食盐，加入鲜花重量10倍的蒸馏水，蒸馏9小时，蒸馏液冷凝后进入油水分离器静置分层，分离精油后得到玫瑰花水，
所述的负离子材料的制备方法是：
将海鸥石、托玛琳、欧泊石、麦饭石、六环石分别经纳米研磨机研磨至粒径在100-200纳米之间，然后按35wt％海鸥石纳米粉、25wt％托玛琳纳米粉、20wt％欧泊石纳米粉、10wt％麦饭石纳米粉和10wt％六环石纳米粉在常温，800rpm下搅拌30min制成负离子材料。