CN107427347B - 局部或全口义齿的制造方法以及根据此方法获得的义齿 - Google Patents
局部或全口义齿的制造方法以及根据此方法获得的义齿 Download PDFInfo
- Publication number
- CN107427347B CN107427347B CN201680017802.0A CN201680017802A CN107427347B CN 107427347 B CN107427347 B CN 107427347B CN 201680017802 A CN201680017802 A CN 201680017802A CN 107427347 B CN107427347 B CN 107427347B
- Authority
- CN
- China
- Prior art keywords
- denture
- dental
- composition
- base
- virtual model
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种用于制造牙齿的假体的模制品,例如局部义齿或全口义齿的方法,模制品由至少一个义齿或一个义齿齿弧的生产制造的实心体模型制造为多层的,其中,义齿在内部的牙颈侧上具有髓腔,髓腔中填充有牙本质颜色的、能够聚合的组合物。这种组合物随后在至少一个步骤中聚合。具有牙本质颜色的组合物的至少一个义齿以其颈侧放置在义齿基托的牙齿侧的表面上并且共同压合。随后,获得的局部义齿或全口义齿在光固化装置中完全地固化。同样地,本发明的主体是一种通过根据本发明的方法获得的假体模制品。
Description
技术领域
本发明涉及一种用于制造牙齿的假体的模制品的方法,例如局部义齿或全口义齿,模制品由至少一个义齿或一个齿弧的、生产制造的实心体模型制造为多层的,其中义齿在内部的牙颈侧具有髓腔,髓腔中填充有牙本质颜色的、能够聚合的组合物。这种组合物随后在至少一个步骤中聚合。具有牙本质颜色的组合物的至少一个义齿以其颈侧放置在义齿基托的牙齿侧的表面上并且共同压合。随后,获得的局部义齿或全口义齿在光固化装置中完全地固化。同样地,本发明的主体是能够通过根据本发明的方法获得的假体的模制品。
背景技术
除手工制造技术以外,数字化的制造方法在牙科领域中赢得越来越高的重要性。义齿,如牙冠和牙桥,从几年前就已经在铣削方法中借助CAD-CAM技术消减式地生产。
此外,用于制造牙冠、牙桥和模型的生产方法,例如金属粉末的SLS(selectivelaser sintering选择性激光烧结)和塑料粉末的SLM(selective laser melting选择性激光熔化)以及在聚合物基础上的牙齿产品(例如临时仪器、假体、KFO装置、咬合夹板、钻孔模具或牙齿模型)的立体光刻越来越具重要性。
在这种情况下,在丙烯酸酯基础上借助RP方法制造义齿到目前为止仍遭受很大的局限性。目前为止,多颜色的义齿或者由不同的用于高品质且美观的义齿的制造的聚合材料(例如用于牙釉质和牙本质)构成的义齿,只能借助于复杂的具有多个材料室的RP设备或者借助复杂的粘合和接合技术制造。
DE102011102095A1公开了多件式义齿的制造,其中借助于生产方法制造至少两个、尤其是3+n个通过至少一个接触面彼此连接的单独的部件。从而DE102011102095A1公开一种义齿,该义齿通过结合所述至少两个或多个生产制造的相邻的单独部件而制造。这种生产制造的相邻的单独部件的缺点在于,单独的部件必须非常匹配地制造,以避免在义齿中的内部表面。这样的内部表面,不等同于内部的边界表面,而是能够通过收缩或者通过拉伸在生产制造之后产生。这种内部表面或者裂缝影响半透明材料的美观以及影响义齿的美观及卫生。
DE102007010624A1公开了一种由至少两种不同的可凝固的物质立体光刻地制造出模制品的方法,该方法通过在可侵入到物质中的支架的底面上凝固有可凝固的物质的层的方式实现。为了执行这种费时的方法,需要使用一种具有特殊的容器构造的复杂的装置。
发明内容
本发明的目的在于,提供一种经济的方法,该方法允许借助一种生产方法,例如快速原型法,高品质并且美观地制造义齿。另外的目的在于,简化方法并且缩短方法的时间。目的还在于,提供一种高品质美观的义齿,其具有类似于牙釉质的美观性并且具有半透明性以及仿制类似于天然的牙齿的牙本质颜色的核。优选地,经济的方法应该能够实现多层的或多颜色的义齿的制造。
这些目的通过根据权利要求1的方法以及通过假体的模制品,尤其是根据权利要求12的局部义齿或全口义齿实现。
令人惊喜的是,能够研发一种方法,其实现了借助于快速原型法并且结合可聚合牙齿组合物的经典加工经济并且有效地制造义齿的部件的方法。
该目的如此根据本发明地解决,即,首先如图1所示数字化地设计局部义齿或全口义齿。随后借助文件分割(划分数字数据)将义齿拆分为义齿基托的部分,参见图2a;和义齿的部分,参见图2b。
具有隐含的切割边缘的义齿的数据记录最初在软件上(现有技术)是一个敞开的外壳(仅由表面1组成)并且能够标记为一个敞开的表面外壳。此表面具有一个朝向义齿底座的等同于髓腔的开口,如图1中所示。
纯粹的表面外壳-等同于表面的模型的数字数据-由描述了牙齿的几何形状点的连接构成。散点图的点数字化地如此连接,即形成三角形。如此获得一个由不同大小的三角形构成的表面。三角形的大小符合牙齿的几何形状,也就是没有三角形的标准尺寸。由于数字化的形成,表面外壳的壁厚为零,也就是说表面外壳具有0mm的壁厚。
由义齿的纯粹的表面外壳-表面的模型的数字数据-在使用相应的软件的情况下产生一个实心模型(图4a)。这表面的数字数据(2-维)到3维空间的扩充(3-维,即所谓的3D模型)而进行。其被称为“壁厚”。
壁厚是在局部/全口义齿的结构建立期间确定的并且描述了美观的牙齿曲线。壁厚优选处于0.005mm到牙齿中心的范围内,例如从0.005mm-5mm。第二个选择是,获得一个内部不具有用于填充牙本质颜色的、牙齿的组合物的髓腔(同义词:空穴)的义齿。这种实心模型随后借助于软件被拆分为多个平行的层,其在接下来的打印过程中是必须的。实心模型优选地在软件中被切成分别具有大约5到200μm层厚的平行的层。义齿能够优选地由至少一种或由不同种的、有颜色的类似于牙釉质的光固化的材料借助于快速原型法(RP-Verfahren)制造而成。为了经济的制造,多个单独的牙齿有利地连接成为一个齿弧并且同时被挤压。对于非常高品质的局部/全口义齿能够单独地挤压每个牙齿,其中优选将牙齿至少颈侧(对齐地)彼此连接。
义齿基托(底座)同样能够借助生产方法制造,如RP-方法。义齿基托由一种牙龈色的、可聚合的牙科组合物制造而成。
尤其优选地以一种或多种流动性的、牙本质颜色的、光固化的、牙齿的组合物完全地填充空穴,即生产的牙齿的髓腔及生产的齿弧的凹穴。能够逐层地或者在一个步骤中全部层地-除最外层地-同时进行固化。
接下来以未固化和选择性固化的组合物填充的空穴,即义齿或齿弧的多个义齿的髓腔与义齿基托共同压合,在这种情况下,能够去除可能发生的残留的或溢出的可光固化的组合物。随后,压合的义齿基托和齿弧能够在光固化装置中固化。义齿基托在此必须还具有一个分散层或者借助例如palabond事先激活表面。在这种固化中所有组件持久地并且无间隙边缘的彼此粘合并且同时产生义齿材料的最终强度。
这种调质(post-curing)以及粘合借助于由光引发剂确定波长的强光完成,例如波长为385nm(Lucirin TPO光引发剂)或波长为100-600nm(樟脑醌光引发剂)。适合的光固化设备例如为Heraeus Kulzer GmbH的试验室灯HiLite Power。
优选以立体光刻法或DLP法(借助UV或可见光固化液态的单体的方法)作为RP-方法用于根据本发明的局部/全口义齿的制造。此外,能够考虑的用于义齿和义齿基托的制造的生产制作方法及结构制作方法包含有激光烧结或3D印刷,例如熔融沉积建模。
本发明的主体是一种用于制造牙科假体的模制品,例如局部义齿或全口义齿、义齿或齿弧的方法,以及根据所述方法获得的相应假体的模制品,模制品包含至少一个义齿或多个义齿和义齿基托(底座),义齿优选地结合为一个齿弧,其中
(A)1.(i)提供所述至少一个义齿的和/或多个义齿的表面的虚拟的模型的数字数据,其中至少一个义齿的表面形成内部放置的髓腔和/或多个义齿的表面分别不相关地形成髓腔或者形成一个共同的髓腔,尤其该内部放置的髓腔能够至少局部至完全地在内部的齿弧上延伸,并且
1.(ii)提供义齿底座的表面的虚拟的模型的数字数据,或者
2.(i)提供包含至少一个义齿和/或多个义齿、尤其是齿弧以及包含义齿基托的模制品的表面的虚拟的模型的数字数据(STL数据),
2.(ii)表面的虚拟的模型的数字数据(文件分割)分成
-至少一个义齿或多个义齿的表面的虚拟的模型的数字数据,
-其中至少一个义齿的表面形成内部放置的髓腔和/或多个义齿的表面分别不相关地形成髓腔或者形成一个共同的髓腔,内部放置的髓腔尤其能够至少局部至完全地在内部的齿弧上延伸,和分成
-义齿基座的表面的虚拟的模型的数字数据,并且
(iii)通过在表面的虚拟的模型中计算出一个在义齿或多个义齿的表面的内侧的限定的薄厚和通过获得至少一个义齿或多个义齿的虚拟的实心模型的方式,使得具有内部放置的髓腔的至少一个义齿和/或多个义齿的表面的虚拟的模型的数字数据借助于软件、基于至少一个义齿的表面的虚拟的模型的数据地转变为一个虚拟的实心模型的数字数据,尤其从而减少内部放置的髓腔4,并且可选择地
(iv)至少一个义齿或多个义齿的、尤其是齿弧的虚拟的实心体模型数字化地拆分为多个平行的层(薄片、切片),其中优选地获得用于执行生产方法的层的数字数据(x、y、z数据),
(v)步骤(ii)中的义齿基托(底座)的表面的虚拟的模型的数字数据作为具有封闭的表面的虚拟的模型的数据存在,或者在区域(2.2)中封闭,或者在至少一个区域中产生一个封闭的表面,在该区域中分成至少一个义齿或多个义齿的、尤其是齿弧的虚拟模型和义齿基托的虚拟模型,并且可选择地
(vi)义齿基托的虚拟模型数字化地拆分为多个平行的层,其中优选地获得用于执行生产方法的层的数字数据(x、y、z数据),
(vii)以(iii)、(iv)、(v)、(vi)或者(v)、(vi)、(iii)、(iv)的排列顺序执行步骤组合(iii)和(iv),或者(v)和(vi)。
(B)(viii)在生成或附加的方法中,至少一个义齿或多个义齿、尤其是齿弧的制造以及义齿基托的制造彼此不相关,
(ix)将至少一个义齿或多个义齿、尤其是齿弧,和义齿基托结合成牙科假体的模制品,如局部义齿或全口义齿,并且
(x)获得具有至少一个义齿和一个义齿基托(底座)的牙科假体的模制品。
牙齿和义齿基托的表面的虚拟的模型能够由现有技术中的相应的已知的方法借助于计算机程序的应用地产生并且作为数字数据提供。
(A)(i)中的模制品的表面的虚拟的模型的数字数据(STL数据)能够在已知的类型和方式中获得和/或制造。例如通过扫描部分缺牙或没有牙的颌骨、压痕或具有或不具有牙齿的模型获得和制造。数字牙齿能够根据数字图书馆用于生成模制品表面的虚拟的模型的数字数据(STL数据)或者义齿的模型的数字数据,从而调整义齿的牙颈区域。
在获得、制作或者提供包含至少一个假牙的模制品的表面的数据之后,表面的虚拟的模型的数字数据被划分(文件分割)。可选择地,义齿和义齿底座的模型的数字数据分隔地存在并且个性化地匹配在颈侧和牙齿侧区域中。
根据本发明的层相当于限定了层厚的薄片。这些层或薄片通过所谓的切割获得。这些根据本发明的层包含例如在DLP方法中获得的切片,也包含例如在FDM方法中通过轨道的沉积获得的层。
在文件分割之后,在朝向义齿底座的接触面处产生了一个用于至少一个义齿、多个义齿或者齿弧的表面的虚拟的模型的敞开的髓腔,其能够通过义齿底座的再次的填补被封闭。
义齿底座的虚拟模型计算作为实心模型10并且以数字的方式分割成多个平行的层。同样地,在文件分割之后,义齿底座的表面在虚拟的至少一个义齿、多个义齿或齿弧被切断的区域中具有一个开口,其在义齿基托的虚拟的模型中被封闭。此外,义齿基托的虚拟的模型作为实心模型计算并且随后优选地被切割为多个平行的层,其为RP方法提供数据。打印过程需要参考数字数据并且考虑到体积收缩。
在步骤(v)中存在的义齿基托(底座)的表面的虚拟的模型的数字数据,优选地在一个嵌入有至少一个义齿或多个义齿、尤其是齿弧的虚拟的模型的区域中,显示出一个在至少一个义齿或齿弧的各自的牙颈的区域中与实心模型的颈侧的、底面和/或内部的表面的形状配合的匹配和/或材料配合的匹配。至少一个义齿1.2的齿颈区域尤其优选地相当于相应的作为阳模形成的义齿底座的牙齿侧区域2.2的阴模。根据本发明,所有牙齿的所有的区域1.2和2.2分别地设计成阴模和阳模。根据一个尤其优选的实施例,多个义齿6(1至n)的所有齿颈区域分别适应于义齿底座的外部的表面的牙齿侧的区域2.2(1至n)。所有义齿以这种方式限定地分派给义齿底座的一个无牙的区域,从而出现一个钥匙/锁类型的编码。因此,义齿和义齿底座之间的连接点优选地存在一种凹陷和相应成型的配合件的形式的明确的匹配。
在具有限定的壁厚的至少一个义齿或齿弧的虚拟的实心模型的产生过程中,表面的外面尺寸没有变化。壁厚向内仅延伸到牙齿的内部并且避免在表面的内部形成髓腔或孔穴,如果必要的话壁厚为零,也就是说,实心模型的表面在牙颈的区域中相当于义齿基托的表面的阴模。
在步骤B中制造义齿和义齿基托的真实的模型。
在步骤(v)中的义齿基托的数据模型能够优选地在执行步骤(vi)之前转变为实心模型。可选择地,义齿基托的数字的模型能够在执行完步骤(vi)之后、在拆分为多个层的期间或在拆分为多个层之后转变为全面的层。还可以考虑在打印路径中进行转变。根据本发明的制造优选地以RP方法完成,在该方法中同时对聚合物组合物的整体的层进行聚合。
在步骤A(iii)中,虚拟的实心模型中的壁厚优选地生成为大于等于0.005mm小于3mm,尤其生成为大于等于0.025mm的壁厚,优选壁厚从0.025mm直至没有内部髓腔的实心模型,其中实心模型的齿颈的内部的表面在各自的牙颈的区域中相当于义齿基托的牙齿侧的、外部表面的阴模。壁厚优选地处于0.05至5mm之间,优选从0.075至2.5mm。根据实施例,能够在一个义齿中设置髓腔,在每个义齿中都设置一个髓腔或者在齿弧中设置一个跨越所有义齿的共同的髓腔。如果要制造特别美观、高品质的义齿,那么能够优选地为门牙区域的每颗牙齿都设置一个髓腔,而齿弧的其他牙齿设置一个共同的髓腔。为了制造尤其廉价的义齿,所有义齿的齿弧能够只具有一个髓腔。技术人员明确,根据本发明的方法的每个可想到组合都能够制造并且是可实现的。由此,具有上述壁厚的齿弧的义齿也是本发明的主体。
此外,在根据本发明的方法的步骤(iii)中获得的虚拟的实心模型还具有髓腔,髓腔的尺寸尤其取决于壁厚。
生产制造的至少一个义齿、多个义齿和/或齿弧的在生产方法中制造的壁厚优选大于等于0.025mm,优选壁厚是0.05mm至5mm,进一步优选是0.075mm至2mm或者直至没有内部髓腔的实心体,其中实心体的齿颈的内部的表面在分别的牙颈区域中相当于义齿基托的牙齿侧的外部的表面的阴模。可选择地,齿弧在至少两个义齿上具有一个共同的髓腔。优选地,门牙区域的各个义齿分别具有一个髓腔。
根据特别优选的选择方案,通过两个或者多个义齿分别解剖学方位地连接并且形成齿弧的至少一部分,从而形成一个虚拟的实心模型,尤其是2至16颗牙齿分别解剖学方位地连接,从而形成作为上颌骨或下颌骨的虚拟的实心模型的齿弧。
依照根据本发明的方法,两个或多个生产制造的义齿解剖学方位地连接并且形成齿弧的至少一部分,尤其制造2至16颗牙齿,其分别人体解剖学方位地连接,形成上颌骨或者下颌骨的齿弧。根据该方法获得的齿弧也是本发明的主体。
义齿、齿弧和/或义齿基托(底座)的数字层优选具有5至200μm的层厚度(z-数据),优选层厚度是25至200μm,进一步优选是25至100μm,尤其优选是25至50μm。
假体的模制品的制造同义齿一样,也就是说具有髓腔的义齿的制造和/或义齿基座的制造优选地在一种包括光化学聚合化(辐射固化)、立体光刻和/或3D印刷的生产方法中完成。在一个特别优选的实施例中,在一种借助于平面光调制器的、具有均匀化的光量分布的生产方法中完成制造,例如快速原型方法,在该方法中具有均匀化的光量分布,特别是如DE102012224005A1所公开的,具有一种LED投影仪,在投影仪中光量分布被均匀化。根据这种方法,可聚合的组合物的整个层,也就是说至少一个义齿、义齿基托的层能够借助曝光步骤或闪光曝光分别地聚合化。在快速原型方法中,除了UV/Vis激光、UV/VIS-LED投影仪、紫外线(UV)激光以外,还能够使用UV-LED投影仪以及具有长波光线,例如波长为420-430nm的LED投影仪。
根据本发明的方法优选地包含生产制造义齿、多个义齿、齿弧和/或义齿基托的步骤,其中包含有单体和/或聚合物的液态的组合物通过光源完成光化学的聚合的触发。优选地,使用尤其具有波长为100至600nm、优选为180至440nm的辐射的投影仪或激光***作为光源,优选地使用具有波长大约为385nm或340nm的辐射的LED投影仪,或者使用具有波长在220至440nm之间的辐射的激光***。
同样地,本发明的主体在于一种方法,其中
a)在一种生产方法中,由具有髓腔的虚拟的实心模型制造出至少一个具有一个髓腔的义齿或者制造出具有至少一个髓腔甚至每颗牙分别具有一个髓腔的多个义齿,尤其是齿弧,或者
b)在一种生产方法中,由可选择地包括至少一个具有髓腔的义齿的虚拟的实心模型甚至由内部存在不具有髓腔的至少一个义齿的实心模型,制造出至少一个义齿或多个义齿,尤其是齿弧,其中实心模型的表面在不具有内部的髓腔的义齿的、尤其是齿弧的各自的牙颈的颈侧区域中相当于义齿基托的区域的齿侧的、外表面的阴模。
同样地,本发明的主体在于一种方法,这种方法在执行了方法步骤(B)中的步骤(iii)之后
-至少一个义齿具有髓腔,或者多个义齿、尤其是齿弧具有至少一个髓腔甚至每颗牙都具有一个髓腔,使用至少一个或多个流动性的、牙本质颜色的、可聚合化的、牙齿的组合物一步地或多步骤地至少局部地填充至少一个髓腔,可选地该牙科组合物至少部分地聚合,并且在接下来的步骤中完成
(ix)通过至少一个义齿或多个义齿,尤其是齿弧的牙颈区域与义齿基托的相应地牙齿侧区域的压合,将至少一个义齿或多个义齿、尤其是齿弧与义齿基托结合成一个牙齿的假体的模制品,例如局部/全口义齿并且
(x)获得局部义齿或全口义齿的牙齿的假体的模制品。在此尤其优选,在压合之后将局部/全口义齿中的组合物借助于UV和/或VIS光进一步地聚合化。
局部的聚合化能够在执行步骤(B)(iii)之后并且在执行步骤(ix)之前完成。
优选地使用至少一个或多个流动性的、牙本质颜色的、可UV/VIS聚合化的、牙齿的组合物至少局部地填充至少一个髓腔并且一步地或多步骤地以UV和/或VIS光聚合化所述组合物。填充能够一步地或者多步骤地,例如1至20步骤地完成,其中组合物的聚合化同样地能够一次地或多次地完成。
根据本发明中的结合优选地(ix)借助于至少一个义齿或多个义齿、尤其是齿弧和义齿基托的
a)压合并且随后聚合化牙本质颜色的、牙齿的组合物,或者
b)粘合,c)彼此熔化,d)焊接和/或
e)彼此收缩构成为牙齿的假体的模制品。
相应地,方法的一个尤其优选的方法步骤为
(a)在至少一个义齿的髓腔中或在多个义齿、尤其是齿弧的髓腔(多个髓腔)中填充可聚合的、牙齿的、尤其可流动的组合物,并且
(b)聚合化该组合物,并且可选择地重复步骤a)和b),并且
(c)在颈侧区域中将至少一个义齿或多个义齿、尤其是齿弧和义齿基托的相应的牙齿侧的区域结合或者尤其是
(c)在颈侧区域中将至少一个义齿或多个义齿、尤其是齿弧和义齿基托的相应的牙齿侧的区域结合并且聚合化该组合物,其中通过结合和可选择的聚合化将至少一个义齿或多个义齿与义齿基托(9)连接。
通过根据本发明的方法能够完成单个的方法步骤的自动化甚至所有方法步骤的自动化。尤其能够局部地或全部地对步骤(A)、(B),尤其步骤(viii)、(ix),优选步骤(ix)a、b、c或d和/或e进行自动化。
无边缘间隙地完成义齿、多个义齿或齿弧与义齿底座的连接。
在根据本发明的方法中,优选以一种或多种可流动的、牙本质颜色的组合物作为可聚合的、牙齿的组合物使用,其包含单体、尤其是二(甲基)丙烯酯以及可选的填充剂,尤其是包含牙科玻璃。此外,组合物优选地包括102至106mPas的粘度。优选在承受248秒的持久的负载后黏度为2*102mPas,负载在构建期间大约为5*105mPas并且在静态中大约为106mPas。
根据本发明的方法允许在一个自动化的方法中以特定的方式对提供假体的选定的区域中的形状和/或牙齿颜色和/或牙龈颜色以及曲线及层次进行调节。在此,各自的牙本质颜色最好匹配于义齿或齿弧的生产制造的外壳的牙齿颜色。因此,在保有对牙齿修复的最高的美观的需求的同时,根据本发明的方法允许在自动化的方法中完成局部或全口义齿的修复的非常经济的制作。以这种方式,能够完成牙齿颜色的调整,使之匹配于剩余牙齿。
举例来说,用于义齿的生产制造的牙齿的可聚合的组合物、光固化的牙本质颜色的组合物以及用于义齿基托的生产制造的组合物能够包含以下组成。优选使用用于制造上述义齿部分的光固化的组合物。
典型的组合物包含(a)至少一个可固化的单体和/或聚合物组分以及可选择地包含(b)至少一个填充组分。单体在总组合物中的份额能够高达100%的重量百分比,优选重量百分比为40到99.99%,尤其是50至99.99%或者98%到99.99%,其中还能够包含0.01至2%的重量百分比的引发剂、稳定剂或辅料。
在这种情况下,一种作为填充组分(b)的组合物含有总填充材料份额,其相对于总组合物占10至98%的质量百分比,尤其是占60至95%的重量百分比,其中尤其包含(b.1)重量百分比为10-35%、尤其为10至30%、优选为10至25%、特别优选为15至25%的硅烷化的氧化物粒子和/或(b.2)至少一个牙科玻璃,其重量百分比为0到75%重量百分比,尤其为10至65%重量百分比,尤其优选为40至60%重量百分比,以及45至50或50-65%重量百分比,其中优选使用由50至90%的粗粒牙齿玻璃和10至50%细的牙齿玻璃组成的混合的牙齿玻璃,其中关于平均粒径(d50值),细的和粗的牙齿玻璃的比为30:1至1:30,并且可选择地还包括(b.3)颗粒大小为1到50nm的重量百分比为0.5至10%的未凝集的纳米填充物。
总组合物中的(a)单体的份额能够为2至90%的重量百分比,优选5至80的重量百分比,其中组合物可选择地包含至少0.1重量百分比的引发剂,尤其是0.1至2重量百分比的引发剂。
优选地,从单体混合物(i)、(ii)和(iii)中选择一个或多个单体作为组合物的(a)可固化的或可聚合化的单体和/或聚合物组分:
(i)组别甲基丙烯酸缩水甘油酯(bisglycidylacrylate)、烷氧基化的季戊四醇四丙烯酸酯alkoxylated pentaerythritol tetraacylate、TCD-di-HEMA或TCD-di-HEA,以及其衍生物中的至少一种单体,相对于总组合物其重量百分比尤其为2至20%重量百分比,特别是2至10%的重量百分比,和
(ii)相对于总组合物,至少为5至80%的双功能交联剂UDMA(二甲基丙烯酸二氨基甲酸酯)和/或脂族二丙烯酸酯,尤其是25至75%的重量百分比,和
(iii)相对于总组合物,可选择的剩余的TEDMA(三甲基乙二醇二甲基丙烯酸甲酯)和/或另外的多功能的交联剂,尤其是0至15%的重量百分比,优选为0.01至10%的重量百分比,
其中(i)、(ii)、(iii)整体能够占牙齿材料的5至90%重量百分比,优选占50至85%的重量百分比,c)至多为1%的引发剂和可选择的(b)至少一种填充组分,其在组合物中填充直到100%重量百分比,如硅酸。除了可聚合的单体,在总组合物中能够包含重量百分比为100%的颗粒有机聚合物。
未凝聚的纳米填料是已知的并且例如在WO0130305A1或在DE19617931A1中以SiO2作为例子描述。未凝聚的纳米填料最好是在组别SiO2、ZrO2、TiO2、Al2O3以及在至少两种这些物质的混合物中选择。他们能够如在DE19617931A1中所描述地被分散在有机溶剂中,也能够加入到水或含水的溶剂混合物中。
钡玻璃粉末、优选钡玻璃-铝-硼硅酸盐玻璃、和/或锶玻璃粉末尤其适合作为牙齿玻璃使用。粗的牙齿玻璃的平均粒径优选是5到10μm,尤其是7μm,并且细的牙齿玻璃的平均粒径为0.5到2μm,尤其是1μm。可选择的现存的其他牙齿玻璃的平均颗粒大小例如为2至5μm或10至50μm。
因此,填充物能够包括具有三种或更多的颗粒部分的牙齿玻璃。填充物还能够包含另外的、在牙科领域的惯用的传统的填充材料,如石英陶瓷、玻璃陶瓷或其混合物。此外,复合材料能够包含用于提高辐射不透明度的填充材料。
牙科材料优选包含作为可固化的单体和/或聚合物组分的以下的所谓单体或聚合物:
作为单体能够考虑在牙科领域中常见的单体:例如可自由基聚合的单体,如(单甲基)丙烯酸酯、甲基-、乙基-、丁基-、苄基-、糠醇-或苯基(甲基)丙烯酸酯;多功能单体,如多功能丙烯酸酯以及甲基丙烯酸酯,例如双酚A二(甲基)丙烯酸酯、Bis-GMA(由甲基丙烯酸和双酚a二缩水甘油醚的加成产物)、UDMA(聚氨酯二甲基丙烯酸酯),如由2羟乙基甲基丙烯酸酯和2,2,4-六底异氰酸酯的加成产物、2-、3-或4乙烯基乙二醇二(甲基)丙烯酸酯、癸二醇二(甲基)丙烯酸酯、十二烷二(甲基)丙烯酸酯、己基癸醇二(甲基)丙烯酸酯、三羟甲基丙烷三(甲基)丙烯酸酯、季戊四醇四(甲基)丙烯酸酯以及丁二醇二甲基丙烯酸酯。尤其优选Bis-GMA、TEDMA(三乙基乙二醇二甲基丙烯酸酯)、UDMA(聚氨酯二甲基丙烯酸酯)、TCD-di-HEMA(双(甲基丙烯酰氧基乙基)三环[5.2.1.02.6]癸烷)和TCD-di-HEA(双(丙烯酰氧基甲基)三环[5.2.1.02.6]癸烷)。
能够从以下物质或其混合物中选择至少一个单体作为优选的交联单体:2,2-双-4-(3甲基丙烯酰氧基-2-羟丙基)-苯基丙烷(Bis-GMA),即甲基丙烯酸缩水甘油酯和双酚A(含OH基团)的反应物,和7,7,9-三甲基-4,13-二氧代-3,14-二氧杂-5,12-二氮杂十六烷-1,16-二基二甲基丙烯酸酯(UDMA),即由2摩尔2羟乙基甲基丙烯酸酯(HDMA)和1摩尔2,2,4-三甲基六亚甲基二异氰酸酯(含氨基甲酸酯基团)反应的聚氨酯二甲基丙烯酸酯。此外,甲基丙烯酸缩水甘油酯与其它双酚,例如双酚B(2,2'-双-(4-羟基苯基)丁烷)、双酚F(4,4'-双(羟基苯基)-甲烷)、(2,2'-甲基苯酚)或4,4'-二羟基二苯基的反应产物,以及2摩尔HEMA或2-羟丙酯(甲基)丙烯酸与特别是1摩尔已知的二异氰酸酯(例如六亚甲基二异氰酸酯、间苯二甲基二异氰酸酯或甲苯二异氰酸酯)的反应产物也是非常适合作为交联单体的。
除了TEDMA和UDMA之外,可以想到以下多功能的交联剂:二(甲基)丙烯酸二甘醇酯、三羟甲基丙烷三(甲基)丙烯酸酯、四(甲基)丙烯酸季戊四醇酯以及二(甲基)丙烯酸丁二醇酯、1,10-癸二醇二(甲基)丙烯酸酯、1,12-十二烷二醇二(甲基)丙烯酸酯。
牙齿材料优选地包含以下的单体和/或聚合物作为可固化的单体和/或聚合物组分:一种或多种具有或不具有酸官能团的烯属不饱和化合物。例如丙烯酸酯、甲基丙烯酸酯、羟基官能的丙烯酸酯、羟基官能的甲基丙烯酸酯及其混合物。以及单-、双-、聚(甲基)丙烯酸酯,也就是丙烯酸酯和甲基丙烯酸甲酯,如(甲基)丙烯酸甲酯、丙烯酸乙酯、甲基丙烯酸异丙酯、丙烯酸正己酯、丙烯酸硬脂基酯、丙烯酸烯丙酯、甘油三丙烯酸酯、乙二醇二丙烯酸酯、二甘醇二丙烯酸酯、三甘醇二甲基丙烯酸酯、1,3-丙二醇(甲基)丙烯酸酯、三羟甲基丙烷三丙烯酸酯、1,2,4-丁三醇三甲基丙烯酸酯、1,4-环己二醇二丙烯酸酯,季戊四醇四(甲基)丙烯酸酯、山梨糖醇六丙烯酸酯、四氢糠基(甲基)丙烯酸酯、双[1-(2丙烯酰氧基)]对乙氧基苯基二甲基甲烷,双[1-(3-丙烯酰氧基-2-羟基)]对-丙氧基苯基二甲基甲烷、乙氧基化双酚A二(甲基)丙烯酸酯和三甲基异氰脲酸酯异氰脲酸酯三甲基丙烯酸酯、(甲基)丙烯酰胺(即丙烯酰胺和甲基丙烯酰胺),如(甲基)丙烯酰胺、亚甲基-(甲基)丙烯酰胺和双丙酮(甲基)丙烯酰胺;聚氨酯(甲基)丙烯酸酯;聚乙二醇(优选分子量为200-500g/mol)的(甲基)丙烯酸酯,丙烯酸酯化单体和乙烯基化合物如苯乙烯、邻苯二甲酸二烯丙酯、二乙烯基琥珀酸酯、己二酸二乙烯酯和邻苯二甲酸二乙烯基酯的可共聚合的混合物。其他适合的可自由基聚合的化合物包含硅氧烷官能的(甲基)丙烯酸酯和氟聚合物官能的(甲基)丙烯酸酯或者在需要的情况下使用两种或多种可自由基聚合的化合物。
可聚合的组分还能够在单个分子中包含羟基和烯键式不饱和基团。这种材料的实例包含(甲基)丙烯酸羟烷基酯,如2-羟乙酯(甲基)丙烯酸酯和2羟丙基(甲基)丙烯酸酯;甘油单-或二(甲基)丙烯酸酯;三羟甲基丙烷单-或二(甲基)丙烯酸酯;季戊四醇单-,二-和三(甲基)丙烯酸酯;山梨糖醇单-,二-,三-,四-或五(甲基)丙烯酸酯和2,2-双[4-(2-羟基-3-甲基丙烯酰氧基丙氧基)苯基]丙烷(BisGMA)或烯属不饱和化合物的混合物。可固化或可聚合的组分能够包含PEGDMA(分子量约为400g/mol的聚乙二醇二甲基丙烯酸酯),GDMA(二甲基丙烯酸甘油酯),TEGDMA(三甘醇二甲基丙烯酸酯)和/或包含NPGDMA(新戊二醇二甲基丙烯酸酯)以及它们的混合物。
复合材料包括用于引发聚合的聚合引发剂,例如用于自由基聚合的引发剂。根据使用的引发剂的类型,混合物能够通过辐射冷交联,即UV-或VIS-交联,或者能够通过加热而聚合。
可以使用已知的过氧化物,例如过氧化二苯甲酰、过氧化二壬酰、过辛酸叔丁酯或过苯甲酸叔丁酯,还可以使用α,α'-偶氮-双(异丁基乙酯)、苯频哪醇和2,2'-二甲基苯并二辛醇作为温度诱导聚合的引发剂。温度诱导聚合的引发剂能够根据本发明地用于固化牙本质颜色的组合物和/或用于义齿与义齿底座的粘合。
举例而言,能够考虑的光引发剂有苯甲酰基醚或苯甲酰基酯、苯偶酰单酮、酰基膦氧化物或脂族和芳族的1,2-二酮化合物,例如2,2-二乙氧基苯乙酮9,10-菲醌、二乙酰基、呋喃、茴香胺、4,4'-二氯二苯甲酮和4,4'-二烷氧基苯甲醚或樟脑醌。光引发剂优选与还原剂一起使用。还原剂的实例为胺类,如脂族或芳族的叔胺,例如N,N-二甲基对甲苯胺或三乙醇胺、氰基乙基甲基苯胺、三乙胺,N,N-二甲基苯胺、N-甲基二苯胺、N,N-二甲基对N-二甲苯胺、N,N-3,5-四甲基苯胺和4-二甲基氨基苯甲酸乙酯或有机亚磷酸酯。常见的光引发剂体系例如为樟脑醌加上乙基-4-(N,N-二甲基氨基)苯甲酸酯、2-(乙基己基)-4-(N,N-二甲氨基)苯甲酸甲酯或N,N-二甲基丙烯酸乙酯。
2,4,6-三甲基苯甲酰基二苯基膦氧化物特别适合作为紫外光诱导聚合的引发剂。UV光引发剂能够单独使用,也能够和可见光的引发剂、冷固化用的引发剂和/或用于温度诱导固化的引发剂组合地使用。
自由基形成的体系,例如苯甲酰基或过氧化月桂酰胺和胺类,如N,N-二甲基对-联苯胺或N,N-二甲基-对甲苯胺组合用作冷聚合的引发剂。也能够使用双固化体系,例如具有胺类和过氧化物的光引发剂。基于混合物的总质量,引发剂优选以0.01至1%重量百分比的量使用。用于冷聚合的引发剂能够根据本发明地用于固化牙本质颜色的组合物或用于义齿和义齿底座的粘合。
在冷聚合中能够有利的是,将复合材料细分为两个组分,两个组分设计为通过混合而固化。还能够如此制备材料,即能够通过VIS和/或UV光固化也能够通过混合两种组分而固化。牙本质颜色的材料的两个组分能够存在于两种膏剂中,或者作为粉末/液体体系存在。根据反应需求或聚合体系,聚合所需的自由基的引发剂体系被分为两种膏剂,或包含在液体组分(A)和/或粉末组分(B)中。相关细节是本领域技术人员已知的。例如,在用于冷聚合的基础混合物中,引发剂体系通常存在于两种组分中,即液体组分和粉末组分中,并且因此在混合所述组分时被组合。在用于热聚合的基础混合物中,引发剂通常存在于聚合物组分中,也就是存在于粉末组分中。引发剂仅在混合时进入液体单体组分中。因此,能够设置假体原材料,在这种原材料中引发剂组分(c)存在于粉末状组分(B)中,特别是以过氧化物、庚酮、过酸酯和/或偶氮化合物的形式存在。在此能够涉及到在粉末组分的生产期间不反应的引发剂组分的残余物,例如涉及到过氧化物,如过氧化二苯甲酰。
原则上能够考虑这样的物质作为用于冷聚合的或自动聚合的起始混合物的聚合反应的引发剂,即借助这种引发剂能够引发自由基的聚合化反应。优选的引发剂是过氧化物,例如过氧化二苯甲酰、过氧化二月桂酰和二叔丁基过氧化物,以及偶氮化合物,如偶氮二异丁腈(AIBN)。
因此也能够考虑LPO:二月桂酰过氧化物、BPO:过氧化二苯甲酰、t-BPEH:叔丁基-2-乙基己酸酯、AIBN:2,2'-偶氮二异丁腈、DTBP:二叔丁基过氧化物。
为了通过过氧化物加速自由基聚合的引发,能够添加适当的活化剂,例如芳族的胺类。举例而言,适当的胺为N,N-二甲基对甲苯胺、N,N-二羟基乙基-对-甲苯胺和对二苄基氨基苯甲酸二乙酯。在此,胺通常用作用为共引发剂,并且通常以基于总组合物的至多0.5%的重量百分比的量存在。
此外,氧化还原体系也适合作为自由基的引发体系,尤其是过氧化二苯甲酰、二月桂酰基或樟脑醌与胺类的混合物,胺类如N,N-二甲基-对-甲苯胺、N,N'-二羟基乙基-对甲苯胺和对-二甲基氨基苯甲酸二乙酯。此外,这样的物质也能够作为氧化还原体系应用,其除了过氧化物还包含抗坏血酸或其衍生物、巴比妥酸或巴比妥酸衍生物或作为还原剂的亚磺酸。在一个有利的实施方案中,占总组合物的0.01至1%的重量百分比的这种氧化还原体系分别包括(份额例如为0.01至10%的重量百分比的)巴比妥酸或硫代巴比妥酸,或巴比妥酸或硫代巴比妥酸的衍生物;包含(份额例如为0.1至8%的重量百分比的)至少一种铜盐或铜络合物;以及包含(份额例如为0.05至7%的重量百分比的)至少一种具有电离原子卤素原子的化合物。举例而言,上述氧化还原体系的适当成分为1-苄基-5-苯基巴比妥酸、乙酰丙酮铜和苄基二丁基氯化铵。
在室温或略微升高的温度下和在轻微的压力下,为了避免形成气泡,优选通过氧化还原诱导的自由基的聚合进行组合物的固化。例如使用与铜和氯离子结合的巴比妥酸作为在室温下进行聚合的引发剂。这种体系的特征在于高的颜色稳定性。
用于生产制造至少一个义齿的液体的组合物优选地包含至少一种单体,特别是至少一种二(甲基)丙烯酸酯,组合物特别优选地包含UDMA、乙氧基化双酚A和可选地包含如热解二氧化硅的牙齿玻璃。
生产制造的义齿(6)优选地具有>50%的半透明度。特别优选地,聚合的牙本质颜色的牙齿组合物具有大于等于35%的半透明度和/或至少一个生产制造的义齿或齿弧具有大于等于55%和小于65%的半透明度。
用于生产制造义齿基托(底座)的液体的组合物优选地包含至少一个单体,尤其是至少一种二(甲基)丙烯酸酯和可选择地包含填料(例如d50<2μm的牙齿玻璃)和可选择地包含热解的硅酸。
本发明的主体还有假体的模制品,尤其是选自义齿、多个义齿、齿弧的牙科假体模制品,模制品包含多个义齿、义齿基托(底座)和/或局部/全口义齿以及临时的假体模制品包含临时的多个义齿、临时的齿弧、临时的义齿底座和/或临时的局部/全口义齿(分别为真实模型)。
同样地,本发明的主体还有在根据本发明的方法中包含牙齿玻璃的可流动的、牙本质颜色的、可聚合的、牙齿组合物的用途。
此外,本发明的主体还有由根据权利要求中的任一项的方法获得的局部或全口义齿的用途
(i)作为临时的义齿,或者
(ii)作为一个临时的义齿的真实的模型,用于根据患者的牙齿情况调整临时的义齿,或者
(iii)作为一个临时的义齿的真实的模型,用于根据患者的牙齿情况调整临时的义齿并且用于扫描如此调整的临时的义齿以及可选择地为了患者的局部义齿或全口义齿的生产制造调整至少一个义齿或多个义齿的虚拟的模型,尤其是调整齿弧的虚拟的模型。
附图说明
示意性的附图1至4描绘了本发明的一个实施例,本发明不局限于这个实施例。
图1示出了切开的全口义齿0及假体的模制品的表面0的虚拟的模型的数字数据;
图2a示出了文件分割后的义齿基托(底座)2;
图2b示出了文件分割后的义齿1;
图3示出了真实的全口义齿5的剖视图,其具有嵌在义齿基托9上的限定的壁厚7的义齿6和在髓腔4内的聚合的组合物8;
图4a示出了具有限定的壁厚3/7a和髓腔4的虚拟的义齿1的剖视图;
图4b示出了具有限定的壁厚7b和髓腔4的真实的义齿6的剖视图;
图4c示出了具有局部填充有牙本质颜色的、未聚合的组合物12的真实的义齿6的剖视图。
具体实施方式
图1示出了一个由假体的模制品的表面0的虚拟的模型的数字数据获得的切开的全口义齿0。随后,这个数据由软件分成(文件分割)在图2a中作为义齿底座2示出的义齿基托(底座)的数字数据和在图2b中作为义齿的表面外壳示出的义齿1的数字数据。在齿颈处(底面不可见的)有义齿的颈部区域1.2。图1中进一步示出了义齿基托(在牙龈上的)的牙龈表面2.3。
额外地,在图2a中示出了牙槽区域2.2,在牙槽区域中分为至少一个义齿1或多个义齿1的虚拟的模型和义齿基托2的虚拟的模型,或者可选择地在这个区域里有闭合的牙槽表面2.2。在区域2.2中嵌有义齿的颈侧区域1.2,尤其是通过义齿和义齿基托互相挤压后的多余的牙科组合物12的聚合而嵌入。
图3示出了一个制成的具有义齿6的真实的全口义齿5的剖视图。义齿具有限定的壁厚7和在髓腔4中的聚合的组合物8。义齿6嵌在义齿底座9上。
在图4a至4c中示出了义齿1的制造的不同的阶段。图4a示出了通过实心模型11的牙齿的虚拟的模型1的一个截面图,其中虚拟的模型具有构建的限定的壁厚3和残留的髓腔或空穴4。1.2示出了牙齿的颈侧区域。如图4b所示,在立体光刻的方法中由这个实心模型制造具有限定的壁厚7和髓腔4的真实的义齿6。图4c示出了另外的方法步骤,在此步骤中将牙齿的牙本质颜色的组合物12填充到义齿6的髓腔4中。组合物12能够聚合并且随后能够在髓腔中填充另外的牙齿组合物12。当填充髓腔时,将义齿6放置在义齿基托9上,挤压并且通过UV光聚合。如此制造的局部义齿或全口义齿5能够在光炉中后续调质。
接下来提供两种典型的组合物,一种在生成方法中用于制造义齿6和义齿底座9的牙科可聚合的组合物(表1)和一种牙本质颜色的组合物(表2)。
表1:底座和牙釉质组合物的例子
表2:牙本质颜色的组合物的例子(可流动的)
附图标记说明
0 假体的模制品的表面虚拟模型的数字数据(表面外壳)
1 至少一个义齿的表面(表面外壳)
1.2 义齿的颈侧区域(牙颈)
2 义齿基托(底座)的表面虚拟模型的数字数据(表面外壳)
2.2 牙齿侧区域,在这个区域中分成至少一个义齿1或多个义齿1的虚拟模型和义齿基托2的虚拟模型或者可选择地在这个区域内形成闭合的牙齿侧表面2.2
2.3 义齿基托的牙龈表面(牙龈上面的牙龈侧表面)
3 限定的壁厚,在实心模型11中的数字的壁厚
4 在义齿内部的髓腔,同义词:空穴、凹穴
5 假体的模制品
6 义齿或多个义齿
7 一个义齿/多个义齿的壁厚(1/6)(7a:一个虚拟义齿/多个虚拟义齿的壁厚,7b:一个真实义齿/多个真实义齿的壁厚)
8 在髓腔4中的牙本质颜色的聚合的组合物
9 义齿基托(底座)
10 义齿基托2的虚拟的实心模型,尤其实心模型10数字地拆解为多个平行的层,并且义齿基托9以一种生成方法制造
11 至少一个义齿、多个义齿、齿弧的虚拟的实心模型
12 牙本质颜色的、未聚合的组合物
Claims (13)
1.用于制造牙齿的假体的模制品(5)的方法,所述模制品包含至少一个义齿(6)和一个义齿基托(9),其中
(A)1.(i)提供所述至少一个义齿(1)的表面的虚拟模型的数字数据,并且
(ii)提供所述义齿底座的表面的虚拟模型的数字数据,或者
2.(i)提供包含所述至少一个义齿(1)及所述义齿基托(2)的模制品的表面(0)的虚拟模型的数字数据,
(ii)将所述表面(0)的虚拟模型的数字数据分成所述至少一个义齿(1)的表面的虚拟模型的数字数据,和所述义齿基托(2)的表面的虚拟模型的数字数据,
-其中各自的所述至少一个义齿(1)的表面构成一个内部的髓腔,并且
(iii)通过在所述至少一个义齿(1)的表面的虚拟的模型中计算出在所述表面的内侧的限定的薄厚(3)和通过获得所述至少一个义齿(1)的虚拟的实心模型(11)的方式,使得具有内部放置的髓腔(4)的所述至少一个义齿(1)的表面的虚拟的模型的所述数字数据,基于表面(1)的虚拟的模型的数据地转变为一个虚拟的实心模型(11)的数字数据,并且
(iv)所述至少一个义齿(1)的虚拟的实心模型(11)数字化地拆分为多个平行的层,
(v)步骤(ii)中的所述义齿基托(2)的表面的虚拟的模型的数字数据作为在区域(2.2)中具有封闭的表面的虚拟的模型的数据存在,或者在区域(2.2)中封闭,或者在至少一个区域(2.2)中产生封闭的表面(2.2),在所述区域中分成所述至少一个义齿(1)的虚拟的模型和所述义齿基托(2)的虚拟的模型,并且
(vi)所述义齿基托(2)的虚拟模型数字化地拆分为多个平行的层,
(vii)以(iii)、(iv)、(v)和(vi)或者(v)、(vi)、(iii)和(iv)的排列顺序执行步骤组合(iii)和(iv),或者(v)和(vi),
(B)(viii)在生成方法中,所述至少一个义齿(6)的制造以及所述义齿基托(9)的制造彼此不相关,并且
至少部分地以可聚合的、牙齿的组合物填充具有髓腔(4)的所述至少一个义齿(6),
(ix)结合所述至少一个义齿(6)和所述义齿基托(9)成为牙齿的假体的模制品(5),并且
(x)获得具有至少一个义齿(6)和一个义齿基托(9)的牙齿的假体的模制品(5)。
2.根据权利要求1所述的方法,其特征在于,
(i)虚拟的所述实心模型(11)的壁厚至少在0.005毫米到5毫米之间。
3.根据权利要求1所述的方法,其特征在于,两个或多个义齿(1)通过分别解剖学方位上的连接并且形成齿弧的至少一部分从而形成虚拟的实心模型(11)。
4.根据权利要求1所述的方法,其特征在于,数字的平行的层具有5μm至200μm的层厚度(z-数据)。
5.根据权利要求1所述的方法,其特征在于,所述生成方法包含光化学聚合、立体光刻和/或3D印刷。
6.根据权利要求1所述的方法,其特征在于,所述生成方法基于液体的组合物的由光源触发的光化学聚合,所述组合物包含单体和聚合物。
7.根据权利要求1所述的方法,其特征在于,在执行方法步骤(B)中的步骤(viii)之后,多个义齿(6)具有至少一个髓腔(4)或甚至每个牙齿分别具有一个髓腔(4),所述至少一个髓腔(4)至少部分填充有可聚合的、牙齿的组合物,牙齿的组合物可选择地局部地聚合,并且在另外的步骤中通过所述至少一个义齿(6)以其颈侧区域和义齿基托的相应的牙齿侧区域(2.2)的接合完成了
(ix)结合所述至少一个义齿(6)和所述义齿基托(9)成为牙齿的假体的模制品(5),并且
(x)获得局部义齿或全口义齿的牙齿的假体的模制品(5)。
8.根据权利要求1所述的方法,其特征在于,由此进行(ix)结合,即所述至少一个义齿(6)和所述义齿基托(9)
a)接合并且随后聚合所述牙齿的组合物,
b)粘合,
c)互相熔化,
d)焊接和/或
e)收缩。
9.根据权利要求1所述的方法,其特征在于,
(a)在所述至少一个义齿(6)的髓腔(4)中填充可聚合的、牙齿的组合物,并且
(b)聚合所述组合物,并且可选择地重复步骤a)和b),并且
(c)在颈侧区域中结合所述至少一个义齿(6)和所述义齿基托(9)的相应的牙齿侧的区域(2.2)或者
(c)在颈侧区域中结合所述至少一个义齿(6)和所述义齿基托(9)的相应的牙齿侧的区域(2.2)并且聚合所述组合物,其中通过结合和可选择的聚合,使所述至少一个义齿(6)与所述义齿基托(9)连接。
10.根据权利要求7至9中任一项所述的方法,其特征在于,所述可聚合的、牙齿的组合物是流动性的、牙本质颜色的组合物。
11.由根据权利要求1所述的方法获得的假体的模制品,其中所述模制品是局部义齿或全口义齿。
12.在根据权利要求1所述的方法中具有牙科玻璃的流动性的、牙本质颜色的、可聚合的、牙齿的组合物的用途。
13.由根据权利要求1所述的方法获得的局部义齿或全口义齿的用途,其用途为
(i)作为临时的义齿,或者
(ii)作为一个临时的义齿的真实的模型,用于根据患者的牙齿情况调整所述临时的义齿,或者
(iii)作为一个临时的义齿的真实的模型,用于根据患者的牙齿情况调整所述临时的义齿并且用于扫描如此调整的所述临时的义齿以及可选地为了患者的局部义齿或全口义齿的生产制造调整至少一个义齿(1)的虚拟的模型和义齿基托(2)的虚拟的模型。