CN107268157A - One kind weaving towel fabric - Google Patents

One kind weaving towel fabric Download PDF

Info

Publication number
CN107268157A
CN107268157A CN201610227985.0A CN201610227985A CN107268157A CN 107268157 A CN107268157 A CN 107268157A CN 201610227985 A CN201610227985 A CN 201610227985A CN 107268157 A CN107268157 A CN 107268157A
Authority
CN
China
Prior art keywords
fabric
layer
fibre
yarn
towel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610227985.0A
Other languages
Chinese (zh)
Other versions
CN107268157B (en
Inventor
张红艳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yueyang Pola Fabritex Srl
Original Assignee
Yueyang Pola Fabritex Srl
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yueyang Pola Fabritex Srl filed Critical Yueyang Pola Fabritex Srl
Priority to CN201610227985.0A priority Critical patent/CN107268157B/en
Publication of CN107268157A publication Critical patent/CN107268157A/en
Application granted granted Critical
Publication of CN107268157B publication Critical patent/CN107268157B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

One kind weaving towel fabric, including three layers of complex textile layer, shell fabric is consistent with lower floor fabric structure thereon, include warp thread and weft yarn, the warp thread cotton fiber is made with blend polyester, and weft yarn is made up of china-hemp fibers and abaca fibre with cotton fiber blending, the mean breadth in gap is more than the mean breadth in the gap between 100 μm, the yarn of weft yarn more than 80 μm between the yarn of its warp thread；And intermediate layer fabric is molded between upper layer of fabric and layer fabric, it is integral by cotton thread weaving, the middle fabric layer is formed by fibre-forming polymer and cotton fiber blending, netted face is formed thereon, and fiber hole is formed on netted face, and one layer of bamboo fibre or alginate fibre layer are formed by spun lacing on the two sides of intermediate layer fabric.Towel product of the present invention is fluffy, the full abundant, comfortable feel of outward appearance, good water absorption, and effectively increases capillary effect, further improves feel and product quality.

Description

One kind weaving towel fabric
Technical field
The present invention relates to textile technology field, and in particular to one kind can be used for make bath towel, towel or The weaving face fabric of other water absorbing fabrics.
Background technology
Towel cloth, is usually used in manufacturing towel and bath towel etc., to ensure flexibility, comfortableness and water imbibition Etc. use requirement, and with the continuous social and economic development, consumer to the demand more and more higher of product, Towel focuses on its feature, with prior art as the necessity of life while its practicality is pursued The towel of production can not increasingly meet the demand of masses.
It is substantially all at present using Quality Pure Cotton Yarn Production as raw material, using different tension force double-beam, length beating technology weaving Produce, it is desirable to flexible, durable, and with certain water imbibition, based on this, also use Man-made fabric directly carries out being weaved or being carried out hybrid woven, such as nylon, polyamide fibre and the like. But it is due to the limitation that raw material have in itself, the fabric of this class is in uvioresistant and antibiosis Feature it is poor, in use, it is impossible to meet that anti-mildew is antibacterial, moisture absorption ventilative, shielding ultraviolet rays Deng functional requirement, while also in the presence of the defect that color fastness is low when dyeing, easily fade, it is impossible to meet consumption The consumption demand that person is increasingly lifted.
The content of the invention
Technical problem solved by the invention is to provide a kind of weaving towel fabric, to solve above-mentioned technology Defect in background.
Technical problem solved by the invention is realized using following technical scheme：
One kind weaving towel fabric, is three layers of complex textile layer, including upper strata fabric, lower floor's fabric and in Between tissue layer：
Upper strata fabric is consistent with lower floor fabric structure, including warp thread and weft yarn, and the warp thread is cotton fiber With the mixed yarn that the terylene line density that blending is made in any proportion is 20~25tex, and weft yarn is that function is fine The mixed yarn that the line density that dimension is made with cotton fiber in 30: 70~35: 65 ratio blending is 17~20tex, its The mean breadth in gap is more than the mean breadth in the gap between 100 μm, the yarn of weft yarn between the yarn of warp thread More than 80 μm, and the functional fibre is the composite fibre of china-hemp fibers and abaca fibre, its mixing ratio Example is 80: 20~85: 15.
In above-mentioned fabrics fabric, upper strata fabric and lower floor's fabric include ground tissue and terry loop layer, its Ground is organized as base layer material, cylindrical, and terry loop layer is molded on ground tissue surface, is provided with Jacquard weave face, the fabric total tightness degree of ground tissue part is 95%~120%, and the fabric of looped pile layer segment is always tight Spend for 75%~90%.
Its intermediate layer fabric is molded between upper layer of fabric and layer fabric, is weaved by cotton thread integral, The middle fabric layer is formed by fibre-forming polymer and cotton fiber blending, forms netted face thereon, and Fiber hole is formed on netted face, and one layer of bamboo is formed by spun lacing on the two sides of intermediate layer fabric Fiber or alginate fibre layer.
In the present invention, the breadth after the towel cloth shaping is 20~30cm, and expansion is fixed to cylinder A diameter of 13~16cm after shape.
In the present invention, in order to improve the overall performance of fibre-forming polymer, the fibre-forming polymer can pass through The mode of chemical immersion is processed, and the component of its immersion chemical reagent includes the original of following component Material：
The raw material of said components is dissolved completely in the mixed liquor of propyl alcohol and acrylic acid mass ratio 3: 1 when using In, then middle fabric layer is immersed in the water bath with thermostatic control of 70~80 DEG C of progress in above-mentioned solution 120min~300min, and 5~8g/L bleeding agent is added when water-bath process proceeds to half, water-bath is complete Rinsed well after and carry out bleaching and dyeing processing.
In the present invention, the fire retardant is boron compound, hibbsite, with chemical combination containing halogen One kind in the antimony oxide of thing.
In the present invention, the hydrophilic softener is polyalcohols softening agent.
Beneficial effect：Product of the present invention is fluffy, and the full abundant, comfortable feel of outward appearance, water imbibition are good, together When the superperformance such as also have ventilative nice and cool, soft elegant, body drapability excellent, with certain Intensity and toughness, cloth in itself can also effective antibacterial and mouldproof, have certain stop to ultraviolet and radiation Performance, is widely portable to prepare high-grade towel, bath towel and some household textiles.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are readily apparent from Solution, with reference to specific embodiment, is expanded on further the present invention.
In the present embodiment, weaving face fabric includes upper strata fabric, lower floor's fabric and middle fabric layer, upper strata Fabric is consistent with lower floor fabric structure, including warp thread and weft yarn, warp thread in braiding using 80% cotton Fiber and terylene carry out blending, and the mixed yarn that line density is 20~25tex is made.Weft yarn is china-hemp fibers The blending that the line density being made with abaca fibre and cotton fiber in 26: 4: 70 ratio blending is 17~20tex Yarn.The mean breadth in gap is more than the flat of the gap between 100 μm, the yarn of weft yarn between the yarn of its warp thread Equal width is more than 80 μm.
Then upper strata fabric, lower floor's fabric are respectively processed, organized with being processed into and terry loop layer two Rotating fields, the loom that its ground tissue passes through is made into cylindrical shape, and terry loop layer is molded on ground tissue surface, table Face carries out sanding processing, and in the jacquard weave face of being provided with, the fabric total tightness degree of ground tissue part for 95%~ 120%, and the fabric total tightness degree of looped pile layer segment is 75%~90%
And intermediate fabric shell fabric is formed by fibre-forming polymer and cotton fiber blending, netted face is above formed, And fiber hole is formed on netted face, and form one by spun lacing on the two sides of intermediate layer fabric Layer bamboo fibre or alginate fibre layer, whole intermediate fabric shell fabric is by making the side of reagent chemical immersion by oneself Formula is processed, and it, which makes medicament by oneself, includes the raw material of following components：
In the mixed liquor that the raw material of said components is dissolved completely in 300 parts of propyl alcohol and acrylic acid 3: 1, then Middle fabric layer is immersed in the water bath with thermostatic control 240min of 70~80 DEG C of progress in above-mentioned solution, and in water-bath Process adds 6g/L bleeding agent when proceeding to half, rinsed well after the completion of water-bath and carry out bleaching and dyeing It is intermediate fabric fabric after processing.Each function ingredients effectively can be molded over fibre by this water-bath working process Tie up in hole and fixed, and contact layer is used as by bamboo fibre or alginate fibre layer, can effectively reduce phase Close the decay of component.
Above-mentioned intermediate fabric fabric is arranged between upper strata fabric and lower floor's fabric, knitted by cotton thread Make together, the breadth after its shaping is 20~30cm, expansion is fixed to a diameter of after cylindrical shape 13~16cm, after the fabric after shaping is cleaned up with 100 DEG C of water, with 30 DEG C of water soaking and washing Get product within 30 minutes.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.One's own profession The technical staff of industry is it should be appreciated that the present invention is not limited to the above embodiments, above-described embodiment and explanation Merely illustrating the principles of the invention described in book, without departing from the spirit and scope of the present invention, Various changes and modifications of the present invention are possible, and these changes and improvements both fall within claimed invention model In enclosing.The scope of the present invention is defined by the appended claims and its equivalents.

Claims (5)

1. one kind weaving towel fabric, is three layers of complex textile layer, including upper strata fabric, lower floor's fabric and Middle fabric layer, it is characterised in that：
Upper strata fabric is consistent with lower floor fabric structure, including warp thread and weft yarn, and the warp thread is cotton fiber With the mixed yarn that the terylene line density that blending is made in any proportion is 20~25tex, and weft yarn is that function is fine The mixed yarn that the line density that dimension is made with cotton fiber in 30: 70~35: 65 ratio blending is 17~20tex, its The mean breadth in gap is more than the mean breadth in the gap between 100 μm, the yarn of weft yarn between the yarn of warp thread More than 80 μm, and the functional fibre is the composite fibre of china-hemp fibers and abaca fibre, its mixing ratio Example is 80: 20~85: 15.
In above-mentioned fabrics fabric, upper strata fabric and lower floor's fabric include ground tissue and terry loop layer, its Ground is organized as base layer material, cylindrical, and terry loop layer is molded on ground tissue surface, is provided with Jacquard weave face, the fabric total tightness degree of ground tissue part is 95%~120%, and the fabric of looped pile layer segment is always tight Spend for 75%~90%.
Its intermediate layer fabric is molded between upper layer of fabric and layer fabric, is weaved by cotton thread integral, The middle fabric layer is formed by fibre-forming polymer and cotton fiber blending, forms netted face thereon, and Fiber hole is formed on netted face, and one layer of bamboo is formed by spun lacing on the two sides of intermediate layer fabric Fiber or alginate fibre layer.
2. a kind of weaving towel fabric according to claim 1, it is characterised in that the towel is knitted Breadth after thing shaping is 20~30cm, and expansion is fixed to a diameter of 13~16cm after cylindrical shape.
3. a kind of weaving towel fabric according to claim 1, it is characterised in that described poly- into fibre Compound can be processed by the mode of chemical immersion, and the component of its immersion chemical reagent is included such as The raw material of lower component：
The raw material of said components is dissolved completely in the mixed liquor of propyl alcohol and acrylic acid mass ratio 3: 1 when using In, then middle fabric layer is immersed in the water bath with thermostatic control of 70~80 DEG C of progress in above-mentioned solution 120min~300min, and 5~8g/L bleeding agent is added when water-bath process proceeds to half, water-bath is complete Rinsed well after and carry out bleaching and dyeing processing.
4. a kind of weaving towel fabric according to claim 3, it is characterised in that the fire retardant It is a kind of in boron compound, hibbsite, the antimony oxide with halogen contained compound
5. a kind of weaving towel fabric according to claim 3, it is characterised in that the hydrophily Softening agent is polyalcohols softening agent.
CN201610227985.0A 2016-04-07 2016-04-07 A kind of weaving towel fabric Active CN107268157B (en)