CN106893817A - 一种7KiVe模具钢热处理工艺 - Google Patents
一种7KiVe模具钢热处理工艺 Download PDFInfo
- Publication number
- CN106893817A CN106893817A CN201510950603.2A CN201510950603A CN106893817A CN 106893817 A CN106893817 A CN 106893817A CN 201510950603 A CN201510950603 A CN 201510950603A CN 106893817 A CN106893817 A CN 106893817A
- Authority
- CN
- China
- Prior art keywords
- 7kive
- steel
- heat treatment
- incubated
- treatment process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种7KiVe模具钢热处理工艺,包括如下步骤,(1)准备好箱式电阻炉,将7KiVe钢5根作为一组,放入到箱式电阻炉中;(2)逐步加热到830-850℃,保温10min,然后施加100-110HZ,700V电场锯齿波5-7min;(3)出炉后放到具有磁场的硝盐淬火槽中进行等温淬火,保温2h;(4)在250-270℃下进行2次回火,每次时间为2h。该热处理工艺方法简单,能够提高7KiVe模具钢各方面的性能,缩短了工艺时间。
Description
技术领域
本发明涉及农业领域,具体属于一种7KiVe模具钢热处理工艺。
背景技术
7KiVe钢属于高碳低合金的冷作模具钢,由于7KiVe钢中含有Ki元素和Ve元素,因此7KiVe钢具有较高的淬透性和淬硬性,其中Ki元素可以提高钢的硬度,起到固溶强化作用,同时由于Ki合金的加入,使得钢的临界点提高,淬火后残留的奥氏体量少,提高了钢的回火稳定性。Ki合金还可以细化钢种的碳化物,有利于提高钢的耐磨性和塑性变形抗力;Ve可以提高钢的淬透性和耐磨性,并且有增强钢的抗腐蚀抗氧化能力,以及较好的回火稳定性。
目前7KiVe模具钢热处理工艺时间流程长,处理后的模具钢各方面性能不足。
发明内容
本发明公开了一种7KiVe模具钢热处理工艺,该热处理工艺方法简单,能够提高7KiVe模具钢各方面的性能,缩短了工艺时间。
为了实现上述目的,本发明的技术方案如下:一种7KiVe模具钢热处理工艺,其特征在于:包括如下步骤,
(1)准备好箱式电阻炉,将7KiVe钢5根作为一组,放入到箱式电阻炉中;
(2) 逐步加热到830-850℃,保温10min,然后施加100-110HZ,700V电场锯齿波5-7min;
(3)出炉后放到具有磁场的硝盐淬火槽中进行等温淬火,保温2h;
(4) 在250-270℃下进行2次回火,每次时间为2h。
该发明的有益效果在于:该热处理工艺方法简单,能够提高7KiVe模具钢各方面的性能,缩短了工艺时间。
具体实施方式
下面结合实施例对本发明的具体实施方式进行描述,以便更好的理解本发明。
实施例1:
本发明公开了一种7KiVe模具钢热处理工艺,包括如下步骤,
(1)准备好箱式电阻炉,将7KiVe钢5根作为一组,放入到箱式电阻炉中;
(2) 逐步加热到830℃,保温10min,然后施加100-110HZ,700V电场锯齿波7min;
(3)出炉后放到具有磁场的硝盐淬火槽中进行等温淬火,保温2h;
(4) 在250℃下进行2次回火,每次时间为2h。
实施例2:
本发明公开了一种7KiVe模具钢热处理工艺,包括如下步骤,
(1)准备好箱式电阻炉,将7KiVe钢5根作为一组,放入到箱式电阻炉中;
(2) 逐步加热到830℃,保温10min,然后施加110HZ,700V电场锯齿波7min;
(3)出炉后放到具有磁场的硝盐淬火槽中进行等温淬火,保温2h;
(4) 在250℃下进行2次回火,每次时间为2h。
以上所述是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也视为本发明的保护范围。
Claims (1)
1.一种7KiVe模具钢热处理工艺,其特征在于:包括如下步骤,
(1)准备好箱式电阻炉,将7KiVe钢5根作为一组,放入到箱式电阻炉中;
(2) 逐步加热到830-850℃,保温10min,然后施加100-110HZ,700V电场锯齿波5-7min;
(3)出炉后放到具有磁场的硝盐淬火槽中进行等温淬火,保温2h;
(4) 在250-270℃下进行2次回火,每次时间为2h。