CN106467992A - 一种可降解回收再利用布基材及其制备方法 - Google Patents
一种可降解回收再利用布基材及其制备方法 Download PDFInfo
- Publication number
- CN106467992A CN106467992A CN201510540214.2A CN201510540214A CN106467992A CN 106467992 A CN106467992 A CN 106467992A CN 201510540214 A CN201510540214 A CN 201510540214A CN 106467992 A CN106467992 A CN 106467992A
- Authority
- CN
- China
- Prior art keywords
- fabric
- cloth
- base material
- starching
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种可降解回收再利用布基材及其制备方法,含有经纱、纬纱、浆料,以天丝纤维为原料制成经纱、纬纱,以机织织造方法制成原布,原布再经工艺处理后两面上有浆料成为布基材。该基材具有较好的耐热性能,使用中延展率小,不易起皱,表面平整度高。产品失效后可回收再利用,也可在自然环境条件下,被土壤中微生物降解,不会产生有毒物质,避免污染环境,且天丝纤维的原材料为针叶树材,可再生且成本低。
Description
技术领域
本发明涉及涂附磨具领域,特别是一种可降解回收再利用布基材及其制备方法。
背景技术
改革开放以来,国民经济得到快速增长,“科技创新,自主创新”已成为目前国内工业发展的主流,我国工业正逐步向集约型、节能减排、低碳的方向发展。基体是涂附磨具的三个组成部分之一,是磨料和粘结剂的承载体。涂附磨具的基体有以下几个方面的要求:对粘结剂具有很强的粘结能力,有一定的可挠曲性、抗拉强度、较小的延伸率和表面平整。随着工业的发展新型合成金属材料的涌现、加工精度要求的提高及人们可持续发展、环境保护意识的提升,对于涂附磨具的基体有了新的要求。一方面,在新合成金属加工领域,对涂附磨具要求更高的抗拉强度、耐高温性。因为金属磨削加工中产生的温度比较高、切削力大,如果基体材料热熔点和抗拉强度低,在加工过程中发生明显形变或断裂,会造成砂布表面磨粒脱落,涂附磨具失效,缩短使用寿命,影响产品加工精度。当前,国内涂附磨具以一些粗粒、精确度不高的砂带产品为主,与世界同行存在较大差距,难以满足金属产品加工的精度要求。另一方面是,涂附磨具砂带类产品在使用失效后,采用涤纶纤维制作的基体在自然环境条件下难以降解,存在难以处理回收的问题,对环境造成污染,且合成纤维依赖的石油资源逐渐枯竭,纺织纤维原料供应缺口很大,必须充分利用生物质资源、农作物废弃资源和废弃纺织物再生资源,进一步开拓纤维原料新视野。为了解决上述问题,科研单位的科技人员不断地研究与探索,研发新型的高质量、可降解的涂附磨具基体,虽然在技术上取得了一定的进展,但在实际运用中仍然存在着尚未克服的技术难题。
发明内容
本发明的目的在于克服以上不足,提供一种可降解回收再利用布基材,天丝纤维(国内商品名,国际上称为lyocell纤维)材料制成的基材具有热变形点高,使用中延展率小,不易起皱,表面平整度高等特点。在产品失效后可回收,通过氧化胺完全溶解再利用,也可在自然环境条件下,被土壤中微生物降解,不会产生有毒物质,避免占用空间,污染环境,且天丝的原材料为针叶树为主的木浆,是可再生资源。
本发明解决其技术问题所采用的技术方案是:含有经纱、纬纱、浆料,以天丝纤维为原料制成经纱、纬纱,以机织织造方法制成原布,原布再经工艺处理后两面上有浆料成为布基材。
所述一种可降解回收再利用布基材按如下方法制作:
机织织造-检查-刮毛、烧毛-退浆、煮炼、水洗-染色、拉幅定型-上浆-压光
一、机织织造
以天丝纤维为原料纯纺成纱线,以天丝纱线作为经纱及纬纱在织机上织成可降解基材的原布。
原布主要质量指标:
重量(g/m2):120-160 织物组织:平纹或斜纹
经纬密度(根/cm)20.5-40 经纬纱号数(dtex)295-150
织物厚度(mm):0.3-0.7:
二、检查
对原布的抗拉强度、延伸率和表面质量进行检查,挑出油污、卷边、结块等缺陷瑕疵布。
三、刮毛、烧毛
原布通过刮毛机,去除表面杂质,刷掉织物表面尘埃和纱头,并使绒毛竖立以便烧毛。经过刮毛后的原布经过烧毛机去除织物表面绒毛,使织物表面光洁。
四、退浆、煮炼、水洗
1.将上道工序处理后的织物,浸入碱槽,使织物浸透碱液;
2.将浸透碱液后的织物置于90-100℃蒸汽环境下,保温2-3个小时,以分解浆料;
3.将蒸煮后的织物浸入中和槽中和,再进入清洗槽,清洗表面浆料分解物。
4.将清洗干净后的织物,通过烘燥机干燥。
五、染色、拉幅定型
1.采用直接染色处理方法,先用40-60℃温水润湿,后投入温度为70-95℃染液中30-60分钟染色,再进行固色。
2.将染色后的织物用烘燥机烘干。
3.定型温度195±5℃。
六、上浆
1.采用酚醛树脂、丙烯酸树脂对织物作背面上浆,用橡胶胶乳对织物作正面上浆,以刮浆法上浆。
2.烘干上浆后的织物,保持水分含量10-15%。
七、压光
将烘干后的织物,采用压光机进行压光,使得基体表面平整,浆膜和织物挤压结实及降低延伸率。
可降解回收再利用布基材主要技术指标:
重量(g/m2):120-160 伸长率(600N)(%):3-5
厚度(mm):0.3-0.7: 断裂伸长率(%):5-10
抗拉强度(经向)(N/5cm): 900-1600
本发明解决其技术问题所采用的原理是:天丝原料来自木材,可自然再生。在产品失效后,可生化降解,不会对环境造成污染。在性能上天丝纤维耐热温度最高可达300度,而且再经过上浆等工艺处理过后具有极强的抗拉抗变形性能,耐高温、不易变形、使用过程中延展率极小。
本发明的有益效果是:该布基材具有较好的耐热性能,使用中延展率小,不易起皱,表面平整度高。产品失效后可回收再利用,也可在自然环境条件下,被土壤中微生物降解不会产生有毒物质,避免对污染环境,且天丝纤维的原材料为针叶树材,可再生且成本低。
附图说明
下面是结合附图和实施例对本发明进一步描述;
图1是一种可降解回收再利用布基材的结构示意图。
在图中,1.经纱、2.纬纱、3.浆料。
具体实施方式
在图1中,以天丝纤维为原料制成经纱1、纬纱2,以机织织造方法制成原布,再经过后期加工处理成为基材,原布两面有浆料3。
所述一种可降解回收再利用基材按如下方法制作:
织造-检查-刮毛、烧毛-退浆、煮炼-染色、拉幅定型-上浆-压光
一、机织织造
以天丝纤维为原料纺成纱线,以上述纱线作为经纱及纬纱在织机上织成可降解基材的原布。
原布主要质量指标:
重量(g/m2):120-160 织物组织:平纹或斜纹
经纬密度(根/cm)20.5-40 经纬纱号数(dtex)295-150
织物厚度(mm):0.3-0.7:
二、检查
对原布进行抗拉强度、延伸率和表面质量检查,挑出油污、卷边等缺陷瑕疵布。
三、刮毛、烧毛
原布通过刮毛机,去除表面杂质,刷去织物表面尘埃和纱头,并使绒毛竖立以便烧毛。经过刮毛后的原布经过烧毛机去除织物表面绒毛,使织物表面光洁。
四、退浆、煮炼
1.将上道工序处理后的织物,浸入碱槽,使织物浸透碱液;
2.将浸透碱液后的织物置于90-100℃蒸汽环境下,保温2-3个小时,以分解浆料;
3.将蒸煮后的织物浸入中和槽中和,再进入清洗槽,清洗表面浆料分解物。
4.将清洗干净后的织物,通过烘燥机干燥。
五、染色、拉幅定型
1.采用直接染色处理方法,先用40-60℃温水润湿,后投入温度为70-95℃染液中进行30-60分钟染色,再进行固色处理。
2.将染色后的织物用烘燥机烘干。
六、上浆
1.采用酚醛树脂、丙烯酸树脂对织物背面上浆,用橡胶胶乳对织物正面上浆,以刮浆法上浆。
2.烘干上浆后的织物,保持水分含量10-15%。
七、压光
将烘干后的织物,采用压光机进行压光,使得基体表面平整,浆膜和织物挤压结实以降低延伸率。
可降解回收再利用布基材主要技术指标:
重量(g/m2):120-160 伸长率(600N)(%):3-5
厚度(mm):0.3-0.7: 断裂伸长率(%):5-10
抗拉强度(经向)(N/5cm): 900-1600
天丝原料来自木材,可自然再生,生产工艺成熟成本低廉与棉相同。在使用后,可生化降解回收再利用,所用氧化剂氧化胺回收率达99%以上,不会在回收生产中对环境造成污染。在性能上天丝纤维耐热温度可达300度,再经过上浆和压光等工艺处理过后具有更强的抗拉、抗变形、耐高温性能,拉幅定型和压光可降低使用过程中延展率。产品失效废弃后,可在自然环境条件下,日光和微生物作用下迅速老化,被土壤中微生物降解,不会产生有毒物质,避免污染环境。
Claims (2)
1.一种可降解回收再利用布基材及其制备方法,含有经纱、纬纱、浆料,其特征是:以天丝纤维为原料制成经纱、纬纱,以机织织造方法制成原布,原布再经工艺处理后两面上有浆料成为布基材。
2.权利要求1所述的一种可降解回收再利用布基材及其制备方法,其特征包括以下步骤:
机织织造-检查-刮毛、烧毛-退浆、煮炼-染色、拉幅定型-上浆-压光
第一步骤:机织织造
以天丝纤维为原料纯纺成纱线,以天丝纱线作为经纱及纬纱在织机上织成可降解基材的原布。
原布主要质量指标:
重量(g/m2): 120-160 织物组织:平纹或斜纹
经纬密度(根/cm) 20.5-40 经纬纱号数(dtex)295-150
织物厚度(mm): 0.3-0.7:
第二步骤:检查
对抗拉强度、延伸率和表面质量进行检查,挑出油污、卷边、结块等缺陷疵布。
第三步骤:刮毛、烧毛
原布通过刮毛机,去除表面杂质,刷掉织物表面尘埃和纱头,并使绒毛竖立以便烧毛。经过刮毛后的原布经过烧毛机去除织物表面绒毛,使织物表面光洁。
第四步骤:退浆、煮炼
1.将上道工序处理后的织物,浸入碱槽,使织物浸透碱液;
2.将浸透碱液后的织物置于90-100℃蒸汽环境下,保温2-3个小时,以分解浆料;
3.将蒸煮后的织物浸入中和槽中和,再进入清洗槽,清洗表面浆料分解物。
4.将清洗干净后的织物,通过烘燥机干燥。
第五步骤:染色、拉幅定型
1.采用直接染色处理方法,先用40-60℃温水润湿,后投入温度为70-95℃染液中30-60分钟染色,再进行固色。
2.将染色后的织物用烘燥机烘干。
第六步骤:上浆
1.采用酚醛树脂、丙烯酸树脂对织物作背面上浆,用橡胶胶乳对织物正面上浆,以刮浆法上浆。
2.烘干上浆后的织物,保持水分含量10-15%。
第七步骤:压光
将烘干后的织物,采用压光机进行压光,使得基材表面平整,浆膜和织物挤压结实及降低延伸率。