CN106272892A - A kind of boccaro slip casting strand mud manufacture method - Google Patents
A kind of boccaro slip casting strand mud manufacture method Download PDFInfo
- Publication number
- CN106272892A CN106272892A CN201610691450.9A CN201610691450A CN106272892A CN 106272892 A CN106272892 A CN 106272892A CN 201610691450 A CN201610691450 A CN 201610691450A CN 106272892 A CN106272892 A CN 106272892A
- Authority
- CN
- China
- Prior art keywords
- mud
- slip casting
- boccaro
- manufacture method
- casting strand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of boccaro slip casting strand mud manufacture method, including Raw material processing, molding, fires, and molding comprises the following steps: the mud of two or more the most deployed colors is injected simultaneously in gypsum mold by (1) in proportion；(2) turn clockwise gypsum mold, and rotary speed is 15r/min, after often rotating 10 seconds, quiet to 2 ~ 3 seconds, amounts to rotation 2 ~ 3 minutes；(3) continuing after gypsum mold stops the rotation to inject mud, wait to fill, mould inner wall mud forms the thickness required, pours out waste mud.
Description
Technical field
The present invention relates to a kind of method utilizing strand grout technique preparation strand tire porcelain, belong to strand tire porcelain technology of preparing neck
Territory.
Background technology
Strand tire porcelain is also known as " stirring tire porcelain ", and its strand tread sample is pure and fresh bright and clear, brief graceful, the most reproducible, has the skill of uniqueness
Art sense, strand tire porcelain especially attractive spot is that each strand tire works are all unique, the most similar absolutely not phase
With.
Strand tire technology in producing porcelain refers to rub up together by the china clay of two or more different colours, and strand forms different color mutually
Decorative pattern, then water a clear frit after molding and reburn into porcelain.In strand tire technique, the skill and technique of molding is generally divided into three kinds:
The splicing of throwing, slice, slip casting.
The operating process of wherein slip casting skill and technique is that the mud of the different colours modulated successively is poured into preparation respectively in advance
In good mould regular or irregular rock, form grain pattern.The grain pattern being spliced to form compared to throwing and slice, edge
Ratio is milder, and the mud of different colours also can be fused together, and forms new color, and color is the mildest appropriate.
But the shortcoming that this skill and technique is maximum, that is, have no idea to control completely the flowing of mud, it is impossible to control the decorative pattern formed.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, it is provided that a kind of decorative pattern transmutability twisting tire porcelain and controllability are high, texture
Abundant expression forms, creates the boccaro slip casting strand mud manufacture method of new artistic expression.
For realizing the object of the invention, it is provided that techniques below scheme: a kind of boccaro slip casting strand mud manufacture method, including raw material
Processing, molding, fire, it is characterised in that molding comprises the following steps:
(1) mud of two or more the most deployed colors is injected simultaneously in gypsum mold in proportion；
(2) turn clockwise gypsum mold, and rotary speed is 15r/min, often rotates after 10 seconds, quiet to 2 ~ 3 seconds, amount to rotation 2 ~
3 minutes；
(3) continuing after gypsum mold stops the rotation to inject mud, wait to fill, mould inner wall mud forms the thickness required, pours out
Waste mud.
As preferably, the mud injection rate during the gypsum mold that turns clockwise is 35% ~ 45%.
As preferably, the pug concentration of the mud of two or more colors is 60% ~ 62%, and density is 1.5kg/m.
As preferably, when preparing entire body strand tire porcelain, the colour mixture waste mud of recovery can use again in slip casting.
As preferably, the mud of two or more colors injects flow velocity and sequentially successively decreases 2cm/s, and maximum flow velocity is 10cm/
s。
As preferably, the color of mud is the purple three kinds of colors of reddish yellow.
The method have the benefit that the defect that instant invention overcomes prior art slip casting method, synthesized by several different mud
One flows in gypsum mold, rotates plaster model with rotating disk, produces the decorative pattern needed for difference, and this moulding process is the newest
The ceramic practice of grain husk, can produce the product of a lot of different decorative pattern.
Detailed description of the invention
Embodiment 1: a kind of boccaro slip casting strand mud manufacture method, including Raw material processing, molding, fires, it is characterised in that
Molding comprises the following steps:
(1) mud of purple for the most deployed reddish yellow three kinds of colors is injected simultaneously in gypsum mold in proportion；
(2) turn clockwise gypsum mold, and rotary speed is 15r/min, often rotates after 10 seconds, quiet to 2 ~ 3 seconds, amount to rotation 2 ~
3 minutes；
(3) continuing after gypsum mold stops the rotation to inject mud, wait to fill, mould inner wall mud forms the thickness required, pours out
Waste mud.
The mud injection rate during gypsum mold that turns clockwise is 35% ~ 45%.The mud of the mud of two or more colors
Material concentration is 60% ~ 62%, and density is 1.5kg/m.When preparing entire body strand tire porcelain, the colour mixture waste mud of recovery can be noted again
Slurry uses.
The mud of three kinds of colors injects flow velocity and sequentially successively decreases 2cm/s, and maximum flow velocity is 10cm/s.
The mud container of the purple three kinds of colors of reddish yellow is hung on the aerial of differing heights, by plastic conduit to gypsum mold
Carrying out slip casting, plastic conduit is provided with flow control valve, the height of red mud is higher than half meter of yellow mud, and yellow mud is high
Degree is higher than half meter of purple mud.
Claims (6)
1. a boccaro slip casting strand mud manufacture method, including Raw material processing, molding, fires, it is characterised in that molding includes following
Step:
(1) mud of two or more the most deployed colors is injected simultaneously in gypsum mold in proportion；
(2) turn clockwise gypsum mold, and rotary speed is 15r/min, often rotates after 10 seconds, quiet to 2 ~ 3 seconds, amount to rotation 2 ~
3 minutes；
(3) continuing after gypsum mold stops the rotation to inject mud, wait to fill, mould inner wall mud forms the thickness required, pours out
Waste mud.
A kind of boccaro slip casting strand mud manufacture method the most according to claim 1, it is characterised in that turn clockwise plaster mold
Mud injection rate during tool is 35% ~ 45%.
A kind of boccaro slip casting strand mud manufacture method the most according to claim 1, it is characterised in that two or more colors
The pug concentration of mud is 60% ~ 62%, and density is 1.5kg/m.
A kind of boccaro slip casting strand mud manufacture method the most according to claim 1, it is characterised in that at preparation entire body strand tire porcelain
Time, the colour mixture waste mud of recovery can use again in slip casting.
A kind of boccaro slip casting strand mud manufacture method the most according to claim 1, it is characterised in that two or more colors
Mud injects flow velocity and sequentially successively decreases 2cm/s, and maximum flow velocity is 10cm/s.
A kind of boccaro slip casting strand mud manufacture method the most according to claim 1, it is characterised in that the color of mud is reddish yellow
Purple three kinds of colors.