CN105712661A - 一种无机保温材料的制备方法 - Google Patents
一种无机保温材料的制备方法 Download PDFInfo
- Publication number
- CN105712661A CN105712661A CN201510382479.4A CN201510382479A CN105712661A CN 105712661 A CN105712661 A CN 105712661A CN 201510382479 A CN201510382479 A CN 201510382479A CN 105712661 A CN105712661 A CN 105712661A
- Authority
- CN
- China
- Prior art keywords
- preparation
- silicon dioxide
- flyash
- polystyrene resin
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种无机保温材料的制备方法,无机保温材料,包括二氧化硅、玻璃纤维、木棉纤维、聚苯乙烯树脂、氢氧化钙、二甲基硅油、粉煤灰和水;制备方法,包括以下几个步骤:(A)原料准备;(B)制备混合物料;(C)将玻璃纤维和木棉纤维置于搅拌机中,搅拌;(D)将步骤(B)和步骤(C)中得到的物料置于搅拌机中搅拌,最后将浆料置于模具成型机成型,烘干,脱模。本发明利用粉煤灰作为原料环保又经济,制备方法简单,制备出来的保温材料,对人体及环境不会带来危害,便于运输和施工;保温效果好。
Description
技术领域
本发明涉及一种无机保温材料的制备方法,属于无机材料领域。
背景技术
目前保温材料多处于单一结构,如岩棉、玻璃纤维、陶瓷纤维等及制品属纤维状结构,珍珠岩、陶瓷微珠等属于颗粒微孔结构。这些单一结构的保温材料使用过程中都存在着保温性能因材料结构和施工而大大降低的问题。
目前保温市场上采用聚苯板、密度聚苯板和保温砂浆的保温材料在技术上都存在自身无法克服的缺陷和不尽如人意的部分,聚苯板是从石油中提炼出的有机材料,受温度影响敏感,分子活动非常活跃,所以在使用和施工过程中会出现翘曲、开裂的问题,而保温砂浆仅有水泥加聚苯颗粒外加粘结剂混合而成,利用这几种组分组成的保温板材在使用中由于水泥黏结物间存在微传导,会在一定时间的积聚,墙体储存冷热空气达到一定值,使内墙成为冷、热桥体,将冷、热气流导入室内,导致室内的冷热气流传到进室内,最终破坏室内空间的恒温条件,因此,为解决上述问题,特提供一种新的技术方案来满足需求。
发明内容
本发明目的是,用来弥补现有技术的不足,而提供一种保温效果好的无机保温材料及其制备方法。
为了实现上述目的,本发明的技术方案如下:
一种无机保温材料,以重量份数计,包括二氧化硅20-30份、玻璃纤维30-40份、木棉纤维10-20份、聚苯乙烯树脂30-40份、氢氧化钙4-6份、二甲基硅油5-7份、粉煤灰20-30份和水30-40份。
所述的无机保温材料,以重量份数计,包括二氧化硅30份、玻璃纤维30份、羧甲基纤维素10份、二氯二氟甲烷3份、聚苯乙烯树脂40份、氢氧化钙6份、二甲基硅油7份、粉煤灰40份和水20份。
所述的无机保温材料,以重量份数计,包括二氧化硅20份、玻璃纤维30份、木棉纤维10份、聚苯乙烯树脂30份、氢氧化钙4份、二甲基硅油5份、粉煤灰20份和水30份。
所述的一种无机保温材料的制备方法,包括以下几个步骤:
(A)将二氧化硅20-30份、玻璃纤维30-40份、木棉纤维10-20份、聚苯乙烯树脂30-40份、氢氧化钙4-6份、二甲基硅油5-7份、粉煤灰20-30份和水30-40份按照所需比例准备好备用,其中粉煤灰和二氧化硅粉碎至200-300目备用;
(B)将水置于反应釜中加热,待水温达到200℃时,加入聚苯乙烯树脂和二氯二氟甲烷进行搅拌,搅拌速率为80-90转/min,待聚苯乙烯树脂完全溶解后,停止加热,同时加入二甲基硅油搅拌5-10min,再加入氧化钙和粉煤灰,搅拌10-15min后,最后加入二氧化硅,搅拌10-20min,待自然冷却后得到混合物料;
(C)将玻璃纤维和羧甲基纤维素置于搅拌机中,在常温条件下进行搅拌混合,搅拌时间为30-40min,搅拌速率为70-90转/min,搅拌完成后静置24h或置于消泡池中自然消泡1-2h;
(D)将步骤(B)中得到的混合物料和步骤(C)中得到的物料置于搅拌机中通过搅拌混合,搅拌速率为50转/min,搅拌时间为50min,得到浆料,最后将制得的浆料置于模具成型机成型,烘干,脱模后即可得到成品无机保温材料,所述烘干时的温度为100-120℃。
本发明的有益效果如下:
原料粉煤灰是工业废渣,木棉是天然的植物纤维,保暖性好,利用粉煤灰、木棉纤维作为原料环保又经济,制备方法简单,制备出来的保温材料,对人体及环境不会带来危害,便于运输和施工;保温效果好。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
实施例1:
本实施例中,所述的无机保温材料,以重量份数计,包括二氧化硅30份、玻璃纤维30份、木棉纤维10份、聚苯乙烯树脂40份、氢氧化钙6份、二甲基硅油7份、粉煤灰30份和水30份。
所述的一种无机保温材料的制备方法,包括以下几个步骤:
(A)将二氧化硅30份、玻璃纤维30份、木棉纤维10份、聚苯乙烯树脂40份、氢氧化钙6份、二甲基硅油7份、粉煤灰30份和水30份按照所需比例准备好备用,其中粉煤灰和二氧化硅粉碎至200目备用,玻璃纤维长度为10mm;
(B)将水置于反应釜中加热,待水温达到200℃时,加入聚苯乙烯树脂和二氯二氟甲烷进行搅拌,搅拌速率为80转/min,待聚苯乙烯树脂完全溶解后,停止加热,同时加入二甲基硅油搅拌10min,再加入氧化钙和粉煤灰,搅拌10min后,最后加入二氧化硅,搅拌10min,待自然冷却后得到混合物料;
(C)将玻璃纤维和羧甲基纤维素置于搅拌机中,在常温条件下进行搅拌混合,搅拌时间为30min,搅拌速率为70转/min,搅拌完成后静置24h或置于消泡池中自然消泡2h;
(D)将步骤(B)中得到的混合物料和步骤(C)中得到的物料置于搅拌机中通过搅拌混合,搅拌速率为50转/min,搅拌时间为50min,得到浆料,最后将制得的浆料置于模具成型机成型,烘干,脱模后即可得到成品无机保温材料,所述烘干时的温度为120℃。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.一种无机保温材料的制备方法,其特征在于,以重量份数计,包括二氧化硅20-30份、玻璃纤维30-40份、木棉纤维10-20份、聚苯乙烯树脂30-40份、氢氧化钙4-6份、二甲基硅油5-7份、粉煤灰20-30份和水30-40份。
2.根据权利要求1所述的一种无机保温材料的制备方法,其特征在于,包括以下几个步骤:
(A)将二氧化硅20-30份、玻璃纤维30-40份、木棉纤维10-20份、聚苯乙烯树脂30-40份、氢氧化钙4-6份、二甲基硅油5-7份、粉煤灰20-30份和水30-40份按照所需比例准备好备用,其中粉煤灰和二氧化硅粉碎至200-300目备用;
(B)将水置于反应釜中加热,待水温达到200℃时,加入聚苯乙烯树脂进行搅拌,搅拌速率为80-90转/min,待聚苯乙烯树脂完全溶解后,停止加热,同时加入二甲基硅油搅拌5-10min,再加入氧化钙和粉煤灰,搅拌10-15min后,最后加入二氧化硅,搅拌10-20min,待自然冷却后得到混合物料;
(C)将玻璃纤维和木棉纤维置于搅拌机中,在常温条件下进行搅拌混合,搅拌时间为30-40min,搅拌速率为70-90转/min,搅拌完成后静置24h或置于消泡池中自然消泡1-2h;
(D)将步骤(B)中得到的混合物料和步骤(C)中得到的物料置于搅拌机中通过搅拌混合,搅拌速率为50转/min,搅拌时间为50min,得到浆料,最后将制得的浆料置于模具成型机成型,烘干,脱模后即可得到成品无机保温材料,所述烘干时的温度为100-120℃。