CN105562060A - 一种含改性分子筛的催化裂化催化剂及其制备方法 - Google Patents
一种含改性分子筛的催化裂化催化剂及其制备方法 Download PDFInfo
- Publication number
- CN105562060A CN105562060A CN201510475250.5A CN201510475250A CN105562060A CN 105562060 A CN105562060 A CN 105562060A CN 201510475250 A CN201510475250 A CN 201510475250A CN 105562060 A CN105562060 A CN 105562060A
- Authority
- CN
- China
- Prior art keywords
- molecular sieve
- iii
- catalytic cracking
- catalyst
- dispersant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种含改性分子筛的催化裂化催化剂及其制备方法。该催化剂以催化剂质量为100%计算,含有10~55%以干基计的改性分子筛、10~80%以干基计的粘土、0~40%以氧化物计的无机氧化物和5~40%以氧化物计的粘结剂;所述的改性分子筛通过下述制备方法获得:将分子筛浆液、含元素周期表ⅢB金属离子的化合物溶液、沉淀剂、有机络合剂和/或分散剂混合,温度5~100℃下,搅拌至少10分钟,得到含有元素周期表中ⅢB元素的沉淀物和分子筛的混合浆液,干燥,经过或不经过焙烧,得到经过ⅢB元素改性的分子筛。本发明公开的催化裂化催化剂具有优良的活性稳定性和抗重金属污染性能。
Description
技术领域
本发明涉及一种催化裂化催化剂,特别是涉及一种具有优良的活性稳定性和抗重金属污染性能的催化裂化催化剂。
背景技术
原油重质化、劣质化程度日益加剧,高效加工重油、掺炼渣油成为炼油企业提高加工能力、获取更高利润的迫切需求。催化裂化是重油加工最重要的工艺,由于其重油转化效率高、产品质量好、非临氢及操作压力低等显著优势,使其在炼厂加工重油工艺中占有举足轻重的地位,是炼油厂利润的主要来源。据统计,目前全世界催化裂化装置共有420套左右,单套催化裂化装置规模最大已达1000万吨/年,总加工能力约7.37亿吨,居二次加工的首位。
由于重油和渣油中含有胶质、沥青质等容易产生焦炭的大分子化合物,而且含有重金属镍、钒等,导致催化裂化平衡催化剂上镍钒含量在10000μg/g已比较常见,而高达15000μg/g的重度污染也不罕见,钒在催化裂化高温水热环境下严重破坏催化剂中的活性组分分子筛的结构,造成催化剂活性降低,使催化裂化产品分布变差。因此,需要开发具有优良的活性、水热稳定性和抗重金属污染的催化剂,以满足重油、渣油裂化对催化剂性能的严格要求。
为了提高催化剂的活性和稳定性,现有技术中一般采用稀土或磷对分子筛进行改性处理,如中国专利CN1169717C公开了一种Y沸石用稀土离子进行改性的方法和产品,该方法用NaY分子筛为原料,先经铵交换,然后进行水热处理,再用含H+、NH4 +和RE3+的溶液处理后,经洗涤、干燥、焙烧,得到改性分子筛产品。中国专利CN1111136C公开了一种含磷和稀土的Y型分子筛的制备方法,是将NaY分子筛先用铵离子和稀土离子交换,进行焙烧,再与磷化合物反应结合上1~10重量%的P2O5,再进行焙烧得到。中国专利CN1209288C公开了一种含磷和稀土的八面沸石的制备方法,是将八面沸石先用铵化合物和磷化合物进行一次交换反应后,然后在交换浆液中引入稀土溶液进一步反应,经过滤、洗涤,再进行焙烧得到。含该沸石的催化剂活性稳定性好,汽油收率高,焦炭产率低,重油裂化能力和抗重金属污染能力强。中国专利CN1026225C公开了一种稀土Y分子筛的制备方法,是将NaY分子筛与稀土离子在水溶液中进行离子交换后,过滤,滤饼在流动的水蒸汽中进行焙烧得到。中国专利CN1069553C公开了一种制备稀土Y型分子筛的方法,是将NaY分子筛与稀土离子进行离子交换后,过滤,滤饼再进行焙烧,焙烧后的产物的1~40%循环返回下一批稀土交换浆液中继续上面所述的操作,其余作为REY分子筛产品用于制备催化剂,如此连续进行,得到稀土Y型分子筛。中国专利CN103058217A公开了一种含稀土的Y分子筛的制备方法,该方法用NaY分子筛为原料,先经铵交换,然后进行水热处理,再用含H+、NH4 +、RE3+和有机溶剂的混合溶液处理后,母液分离、滤饼焙烧,得到改性分子筛产品。中国专利CN1159101C公开了一种含稀土超稳Y沸石的制备方法,该方法将氧化钠含量为3~5重量%的超稳Y沸石与一种稀土化合物溶液混合,制成一种浆液,将得到的浆液在剪应力至少10公斤/厘米2的条件下研磨至少1分钟,得到改性分子筛产品。该方法制备的沸石具有高的水热稳定性、抗钠及抗重金属污染的能力。
CN99105792.9公开了一种含稀土的分子筛及其制备方法,其制备方法包括在25~120℃,将一种以氧化物计,含稀土0.1~40重%的稀土型分子筛与一种含(Ⅰ)中的至少一种物质和(Ⅱ)中的至少一种物质的溶液接触至少0.1小时;(Ⅰ)包括无机酸、无机碱、有机酸或能与铝形成络合物的试剂,(Ⅱ)包括可溶性铵盐、有机酸盐及胺、醇、醛、酮;所述溶液的pH值为3~12。该方法分子筛上首先负载了稀土,之后才与含(Ⅰ)中的至少一种物质和(Ⅱ)中的至少一种物质处理,其目的是为了得到骨架稀土分子筛,其稀土存在于分子筛的骨架上,取代了分子筛骨架上的部分阳离子。
CN200510114495.1公开了一种提高超稳Y型沸石稀土含量的方法,该方法包括:将超稳Y型沸石和浓度为0.01~2N的酸溶液以液固比4~20的比例在20~100℃的温度范围下充分混合,处理10~300分钟后洗涤、过滤,再加入稀土盐溶液进行稀土离子交换,交换后洗涤、过滤、干燥,得到孔道通畅、稀土含量显著提高的稀土超稳Y型沸石。该方法首先采用酸溶液清理Y型沸石孔道,过滤后,沸石分子筛进行稀土交换,其目的是为了提高分子筛中的稀土含量,其稀土存在于分子筛的骨架上,取代了分子筛骨架上的部分阳离子。
CN200610087535.2公开了一种REY分子筛的制备方法,将NaY分子筛与含稀土离子的水溶液接触交换,与外加沉淀剂接触使部分稀土沉淀在分子筛上,再进行水热处理,最后与铵盐水溶液接触,其中的沉淀剂为可溶碳酸盐水溶液或碱性水溶液。该制备方法的实质是通过稀土交换和铵盐交换去除NaY分子筛中的Na+含量,同时引入稀土离子;该制备先将分子筛进行稀土交换,之后采用外加沉淀剂使部分稀土沉淀在分子筛上,之后分子筛过滤、洗涤,滤饼再进行水热处理,铵交换。在制备过程中,稀土主要以离子交换的形式负载到分子筛上,部分没有交换到分子筛上的稀土与沉淀剂作用沉淀下来,采用这种沉淀法制备的含稀土的Y型分子筛,虽然形成了稀土的沉淀物,含有独立相的稀土,但稀土沉淀物的颗粒较大,不利于均匀分散在分子筛表面,也不利于与重金属有效接触、及时捕集重金属,因此其抗重金属污染的能力不足。同时,由于其原料为NaY,稀土交换后的过滤、洗涤、水热处理、铵交换降钠过程也会导致稀土的利用率大大降低。
中国专利CN02103909.7公开了一种用于重油催化裂化的、含抗钒组分的新型稀土超稳Y分子筛制备方法,是以NaY型分子筛为原料,化学脱铝络合剂中含有草酸或草酸盐及其混合物,同时在化学脱铝反应后期引入稀土离子,形成稀土沉淀,再经过水热处理,即可实现超稳化及引入稀土离子和独立相氧化稀土的目的。该方法首先采用化学脱铝络合剂(草酸和/或草酸盐)处理分子筛,使分子筛脱铝,然后采用稀土与络合剂形成包含草酸稀土的稀土沉淀物,该方法中,化学脱铝络合剂(草酸和/或草酸盐)能够与分子筛中的铝络合,但不能够与稀土络合,且该方法所形成的稀土沉淀物颗粒大,在分子筛中的分布不够均匀,因此抗重金属效果相对差。
催化裂化过程中,原料油中的重金属镍、钒等不断沉积在催化剂上,其中,沉积在催化剂上的钒在再生器的有氧、高温和水汽环境下,形成钒酸,破坏催化剂中的活性组分—分子筛的结构,造成分子筛晶体结构的崩塌和分子筛的失活。沉积在催化剂上的重金属镍,会作为脱氢活性中心参与反应过程,使催化裂化反应选择性变差、产生更多的焦炭和干气。因此,需要将镍、钒等及时捕获、钝化,使之转化为稳定的、惰性的化合物,从而达到提高催化剂的抗重金属污染的目的。已经发现,稀土离子与分子筛的钠等阳离子发生离子交换,迁移进入分子筛,能够提高分子筛活性和稳定性,但离子交换后的稀土一旦与钒接触,容易脱离分子筛的骨架结构,形成钒酸稀土,反而使分子筛的结构稳定性变差;而以独立相形式存在的稀土,由于存在位置和存在状态的不同,可用于催化裂化反应过程中捕集重金属,起到抗重金属的作用。因此上述采用稀土离子交换制备的稀土分子筛,不含独立相的稀土,因此其抗重金属污染的能力不足。
采用沉淀法制备的含稀土的Y型分子筛,即使形成了稀土的沉淀物,含有独立相的稀土,但稀土沉淀物的颗粒较大,不利于均匀分散在分子筛表面,也不利于与重金属有效接触、及时捕集重金属。因此,为了满足分子筛催化剂对活性稳定性和抗重金属污染能力的要求,尽管有了近来的催化剂技术,但仍需要具有优良的活性稳定性和抗重金属污染的催化剂新技术。
发明内容
本发明的目的提供一种含有改性分子筛的催化裂化催化剂,该催化剂具有良好抗重金属污染性能,同时具备较好的活性和稳定性。
本发明所公开的一种含改性分子筛的催化裂化催化剂,以催化剂质量为100%计,含有10~55%的以干基计的改性分子筛、10~80%的以干基计的粘土、0~40%的以氧化物计的无机氧化物和5~40%以氧化物计的粘结剂;所述的改性分子筛通过包括下述制备步骤的制备方法获得:(1)将分子筛浆液、(2)含元素周期表ⅢB金属离子的化合物溶液、(3)有机络合剂和/或分散剂、(4)沉淀剂混合,温度5~100℃,优选5~60℃,更好优选在5~40℃,搅拌至少10分钟,优选10min~40min,得到含有元素周期表中ⅢB元素的沉淀物和分子筛的混合浆液,干燥,经过或不经过焙烧,得到经过ⅢB元素改性的分子筛,其中ⅢB元素以氧化物计与分子筛干基的重量比为0.3~10:100,优选0.3~8:100,所述的有机络合剂与ⅢB金属离子的摩尔比为0.3~10:1,优选0.5~6:1,更优选1.0~4:1,所述分散剂与金属离子的摩尔比为0.2~16:1,优选1~11:1,更优选2~7:1。
优选的,本发明所公开的一种含改性分子筛的催化裂化催化剂,以催化剂质量为100%计,含有15~45%的以干基计的改性分子筛、20~65%的以干基计的粘土、5~25%的以氧化物计的无机氧化物和5~30%以氧化物计的粘结剂。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其中改性分子筛的制备方法中,所述的分子筛浆液为本领域技术人员所公知,即将分子筛和水混合打浆后的混合物。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其中改性分子筛的制备方法中,所述的得到含有元素周期表中ⅢB元素的沉淀物和分子筛的混合浆液,干燥,干燥之前,可以对混合浆液过滤,加快干燥速度,也可以不过滤。干燥后经过或不经过焙烧,得到经过ⅢB元素改性分子筛。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其中改性分子筛的制备方法中,所述的ⅢB元素选自钪、钇、镧系稀土元素中的一种或多种。所述的镧系稀土包括镧、铈、镨、钕、钷、钐、铕、钆、铽、镝、钬、铒、铥、镱、镥中一种或多种,例如可以是各种稀土元素的混合物,或高纯度单种稀土,常用的为富镧稀土、富铈稀土、纯镧或纯铈。含ⅢB元素的化合物选自可溶于水或酸的ⅢB元素的卤化物、硝酸盐、硫酸盐、氧化物、氢氧化物的化合物中的一种或多种。以氧化物计的ⅢB元素沉淀物与分子筛干基的重量比为0.3~10:100。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其中改性分子筛的制备方法中,所述的沉淀剂是指在化学沉淀反应中,能够与体系中的ⅢB族金属离子发生化学反应,并且使其生成物在体系中微溶或不溶物质。因此沉淀剂的种类和加入量为本领域技术人员所公知,能够提供或产生氢氧根离子(OH-)、碳酸根离子(CO3 2-)、碳酸氢根离子(HCO3 -)、磷酸根离子(PO4 3-)、磷酸氢根离子(HPO4 2-)、磷酸二氢根离子(H2PO4 -)、草酸根离子(C2O4 2-)的化合物均可以作为本发明的沉淀剂,其加入量满足沉淀反应中的物质摩尔配比即可。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其中改性分子筛的制备方法中,其中所述的沉淀剂优选草酸、草酸铵、碳酸铵、碳酸氢铵、二氧化碳、氨水、磷酸、磷酸氢二铵、磷酸二氢铵、磷酸铵、尿素中的一种或几种。所述的氨水加入量视分子筛浆液的pH值而定,使分子筛浆液pH值保持在6.5~9.0范围内;草酸、草酸铵、碳酸铵、碳酸氢铵、二氧化碳、磷酸、磷酸氢二铵、磷酸二氢铵、磷酸铵、尿素的加入量视ⅢB元素化合物的加入量而定,使上述沉淀剂:ⅢB元素的化合物(氧化物计)的重量比=0.3~5。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其中改性分子筛的制备方法中,所述的有机络合剂选自甲酸、乙酸、己二酸、柠檬酸、酒石酸、苯甲酸、乙二胺四乙酸、水杨酸以及上述酸的盐、以及乙酰丙酮、二乙醇胺、三乙醇胺中的一种或多种,优选柠檬酸、柠檬酸铵、柠檬酸二氢铵、柠檬酸氢二铵、EDTA(乙二胺四乙酸)中的一种或多种。所述的有机络合剂与金属离子的摩尔比为0.3~10:1。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其中改性分子筛的制备方法中,所述的分散剂为本领域技术人员所公知,是一种在分子内同时具有亲油性和亲水性两种相反性质的界面活性剂,可均一分散那些难于溶解于液体的固体颗粒,同时也能防止固体颗粒的沉降和凝聚,形成安定悬浮液所需的物质,其主要作用是降低液-液和固-液间的界面张力,表面活性剂也可作为分散剂;且分散剂不会与ⅢB族金属离子作用形成沉淀。所述的分散剂选自碳原子数为2~8的一元醇或二元醇、聚乙二醇、纤维素衍生物、聚丙烯酰胺及其衍生物、古尔胶中的一种或多种。所述的分散剂与金属离子的摩尔比为0.2~16:1。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其中改性分子筛的制备方法中,所述的纤维素衍生物典型的为羟甲基纤维素钠、甲基羟乙基纤维素、羟丙基甲基纤维素。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其中改性分子筛的制备方法中,所述的碳原子数为2~8的一元醇或二元醇为化学领域技术人员所公知,例如:碳原子数为2的一元醇或多元醇为乙醇、乙二醇,碳原子数为3的一元醇或二元醇为异丙醇、正丙醇、1,3-二丙醇、1,2-二丙醇。本发明优选碳原子数为2~5的一元醇或二元醇;更优选乙醇、乙二醇、异丙醇、丁醇、甲基戊醇中的一种或多种。
本发明所公开的一种含改性分子筛的催化裂化催化剂,所述的分子筛为降钠后的分子筛,即低钠含量的分子筛,优选Na2O质量含量不大于2%。降低分子筛氧化钠含量技术为本领域技术人员所公知,典型的为经铵盐离子交换降钠处理,所述的铵盐选自硫酸铵、硫酸氢铵、硝酸铵、氯化铵、碳酸铵、碳酸氢铵中的一种或多种,铵盐主要用于交换分子筛上的钠,使经过交换后的分子筛具有酸催化活性。其中所述的分子筛优选自Y型分子筛、β分子筛、SAPO分子筛、ZSM分子筛、钛硅分子筛中的一种或几种;其中Y型分子筛,选自USY、REUSY、REHY、HY、NH4Y、REY、含磷Y分子筛。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其中改性分子筛的制备方法中,所述的(1)分子筛浆液、(2)含元素周期表ⅢB金属离子的化合物溶液、(3)有机络合剂和/或分散剂、(4)沉淀剂的加入顺序无特别限制,只要在混合浆液的体系中含有分子筛,加入了含元素周期表ⅢB金属离子的化合物溶液、有机络合剂和/或分散剂、沉淀剂,即可满足本发明的要求。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其中改性分子筛的制备方法中,所述的分子筛浆液、含元素周期表ⅢB金属离子的化合物溶液、有机络合剂和/或分散剂、沉淀剂的混合优选通过下述的之一方式实现:
方式1:将分子筛浆液、沉淀剂、有机络合剂和/或分散剂混合均匀,加入含元素周期表中ⅢB金属离子的化合物溶液,搅拌至少10分钟,其中沉淀剂、有机络合剂和/或分散剂、分子筛浆液混合均匀时对各物料的加入顺序、加入次数不做限定,多种物料可以同时加入,也可以将不同物料分别不限定顺序加入,只要混合均匀即可;
方式2:将含元素周期表中ⅢB金属离子的化合物溶液、分子筛浆液、有机络合剂和/或分散剂混合均匀,加入沉淀剂,搅拌至少10分钟,其中将含元素周期表中ⅢB金属离子的化合物溶液、有机络合剂和/或分散剂、分子筛浆液混合均匀时对各物料的加入方式、加入顺序不做限定,只要混合均匀即可;
方式3:将沉淀剂与含元素周期表中ⅢB金属离子的化合物溶液混合形成ⅢB金属离子沉淀物,ⅢB金属离子沉淀物与分子筛浆液、有机络合剂和/或分散剂中一种或多种混合,加入剩余组分,形成含有ⅢB金属离子沉淀物、分子筛浆液、有机络合剂和/或分散剂的悬浮液,搅拌至少10分钟。本发明更优选方式1和方式2,这两种方式在混合时形成的沉淀物的粒度更小。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其中改性分子筛的制备方法中,所述的有机络合剂和/或分散剂起到分散作用,其主要作用在于降低元素周期表中ⅢB元素沉淀物的颗粒大小;沉淀剂主要用于沉淀元素周期表中的ⅢB元素。有机络合剂、沉淀剂可以直接加入使用,或溶解于水中,形成溶液后使用。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其中改性分子筛的制备方法中,含有元素周期表中ⅢB元素的沉淀物和分子筛的混合浆液干燥采用本领域的通用技术,例如可以过滤干燥或不经过过滤直接喷雾干燥。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其中改性分子筛的制备方法中,所述的含有元素周期表中ⅢB元素的沉淀物和分子筛的混合浆液,经过滤或不过滤,干燥,经过或不经过焙烧,得到经过ⅢB元素改性分子筛。优选经过焙烧处理,焙烧的工艺条件为,在100%水蒸汽气氛下进行分子筛焙烧,焙烧温度450~700℃,焙烧时间0.5~4小时。元素周期表中ⅢB元素的沉淀物在高温焙烧处理过程中,部分ⅢB元素发生固相离子迁移交换到分子筛上去,可以起到提高分子筛活性和稳定分子筛晶体结构的目的,另外的部分以独立相形式存在,起到抗重金属污染的作用。焙烧过程中,存在脱铝和硅迁移,使得分子筛骨架上的Si-O-Al被Si-O-Si所代替,由于Si原子(直径为0.082nm)比Al原子(直径为0.1nm)小,键长变短(Si-O键长0.161nm,Al-O键长0.174nm),晶胞收缩,分子筛结构稳定性提高。焙烧过程中,也同时伴随着离子迁移,其中,ⅢB元素的离子迁移到Y型分子筛方钠石笼中的SⅠ和SⅡ位置,起到稳定分子筛晶体结构和提供酸活性中心的作用,方钠石笼中的Na+离子则迁移到超笼中,在后续的离子交换过程中脱离分子筛。与单纯的高温焙烧相比,在100%水蒸汽气氛下进行水热焙烧,更有利于上述ⅢB元素的离子和Na+离子的迁移,也更有利于保持分子筛的晶体结构和晶胞收缩。
本发明所公开的一种含改性分子筛的催化裂化催化剂,所述的粘土选自常用作催化裂化催化剂组分的粘土中的一种或多种,例如高岭土、多水高岭土、偏高岭土、酸抽提高岭土、碱抽提高岭土、蒙脱土、硅藻土、累托土、埃洛石、皂石、海泡石、凹凸棒土、水滑石、膨润土中的一种或多种,这些粘土为本领域普通技术人员所公知。
本发明所公开的一种含改性分子筛的催化裂化催化剂,所述的无机氧化物不作为粘结剂使用,例如所述的无机氧化物以固体细粉的形式用于催化剂的成胶过程,在成胶过程中保持固体形态;所述的无机氧化物为氧化铝、氧化硅、氧化钛、氧化锆或其混合物中的一种或多种。所述氧化铝选自各种形态的氧化铝和/或水合氧化铝,例如γ-氧化铝、η-氧化铝、θ-氧化铝、一水铝石(Boehmite)、三水铝石(Gibbsite),拜耳石(Bayreite)中的一种或多种,但能够酸溶、酸溶后有粘结剂作用的拟薄水铝石除外。
本发明所公开的一种含改性分子筛的催化裂化催化剂,所述的粘结剂选自裂化催化剂中常用的粘结剂中的一种或多种,例如硅溶胶、铝溶胶、改性硅溶胶、改性铝溶胶、无定形硅铝凝胶、拟薄水铝石中的一种或多种,优选拟薄水铝石和/或铝溶胶。
本发明所公开的一种含改性分子筛的催化裂化催化剂,其制备方法为本领域技术人员所公知,可按照现有裂化催化剂的制备方法进行,这些方法在CN02155601.6、CN00105235.7、CN200910092838.7、CN201110419922.2、CN02103907.0中都有详尽的描述,这里一并作为参考引用。本发明提供的含改性分子筛的催化裂化催化剂的制备方法为:将改性分子筛、粘土、无机氧化物、粘结剂混合打浆,喷雾干燥,即可制备所得的催化剂。将催化裂化催化剂的各个组分混合打浆,其方式多种,可以将各个组分分别形成单独的物料浆液然后混合打浆;也可以将2~3种组分混合后打浆,再将剩余的物料制成2~1股物料浆液,混合打浆,制备成含有多种组分的混合浆液。
本发明所公开的一种含改性分子筛的催化裂化催化剂的制备方法,包括:(1)制备改性分子筛,将分子筛浆液、含元素周期表ⅢB金属离子的化合物溶液、有机络合剂和/或分散剂、沉淀剂混合,温度5~100℃,搅拌至少10分钟,得到含有元素周期表中ⅢB元素的沉淀物和分子筛的混合浆液,干燥,经过或不经过焙烧,得到经过ⅢB元素改性的分子筛,其中以氧化物计的ⅢB元素与分子筛干基的重量比为0.3~10:100,所述的有机络合剂与ⅢB金属离子的摩尔比为0.3~10:1,所述分散剂与金属离子的摩尔比为0.2~16:1;(2)将改性分子筛、粘土、无机氧化物、粘结剂混合打浆,喷雾干燥,制备得到催化剂。
本发明所公开的一种含改性分子筛的催化裂化催化剂的制备方法,也可以有如下的替代方案,该制备方法包括:(1)制备改性分子筛浆液,将分子筛浆液、含元素周期表ⅢB金属离子的化合物溶液、有机络合剂和/或分散剂、沉淀剂混合,温度5~100℃,搅拌至少10分钟,得到含有元素周期表中ⅢB元素的沉淀物和分子筛的混合浆液,其中以氧化物计的ⅢB元素与分子筛干基的重量比为0.3~10:100,所述的有机络合剂与ⅢB金属离子的摩尔比为0.3~10:1,所述分散剂与金属离子的摩尔比为0.2~16:1;(2)将改性分子筛浆液、粘土、无机氧化物、粘结剂混合打浆,喷雾干燥,制备得到催化剂。
本发明所公开的一种含改性分子筛的催化裂化催化剂的制备方法,其中改性分子筛的制备方法中,当得到含有元素周期表中ⅢB元素的沉淀物和分子筛的混合浆液,不用对该浆液进行任何处理,即可用于直接制备催化裂化催化剂;也可对该浆液进行处理,将含有元素周期表中ⅢB元素的沉淀物和分子筛的混合浆液干燥,经过或不经过焙烧,然后再将改性分子筛打浆,或将改性分子筛和其他组分混合共同打浆。当对混合浆液干燥时,其中的干燥为本领域的通用技术,例如可以过滤干燥或不经过过滤直接喷雾干燥。
本发明所公开的催化剂的制备方法还可包括喷雾干燥后的焙烧、洗涤、过滤、干燥的步骤,所述喷雾干燥、焙烧、洗涤、过滤、干燥为现有技术,本发明没有特别要求。
本发明所公开的一种含改性分子筛的催化裂化催化剂,所述的改性分子筛的制备过程中,将分子筛、ⅢB元素的化合物、有机络合剂和/或分散剂、沉淀剂共同加入,由于有机络合剂和/或分散剂的存在,所形成的体系为ⅢB元素沉积在分子筛上提供适宜的反应环境,有利于形成元素周期表中ⅢB元素的超微粒化合物,降低ⅢB元素沉淀物的颗粒度,增大沉淀物的外表面和分散程度,将元素周期表中ⅢB元素沉淀物更均匀地沉积在分子筛上,元素周期表中ⅢB元素以独立相或独立相/离子的混合相态形式存在,起到提高分子筛活性稳定性和抗重金属污染性能的目的。利用该改性分子筛制备催化剂,含有ⅢB元素的沉淀物作为重金属钝化剂,有利于使污染重金属与污染重金属钝化剂及时、有效地接触,避免催化剂微球钝化剂分布不均匀、微球或分子筛局部没有布置钝化剂,从而达到更有效地捕集重金属的目的。本发明所公开的催化剂,具有优良的活性、稳定性和更强的抗重金属污染性能;适用于重油催化裂化,尤其适用于重金属钒含量高的重油催化裂化。所述重油包括但不限于常压渣油、减压渣油、减压瓦斯油、常压瓦斯油、脱沥青油和焦化瓦斯油中的一种或多种。
具体实施方式
下面进一步用实施例说明本发明,但本发明并不仅限于这些例子。
(一)实施例中所用的分析测试方法
1.氧化钠、氧化钇、稀土含量:采用X荧光法分析。
2.分子筛的结晶度、晶胞常数:采用X射线衍射法分析。
3.粒度:采用激光粒度仪法分析。
4.催化剂的活性测定:在华阳公司生产的CSA-B型催化剂评定装置上进行。催化剂预先在800℃、100%水蒸气条件下老化6h或17h后,采用大港轻柴油为原料进行活性测定,反应温度460℃,反应时间70s,催化剂装量5.0g,剂油比3.2。
(二)实施例中所用原料规格
1.NaY分子筛、REUSY分子筛(RE2O3含量4.02%,Na2O含量1.24%)、NH4Y分子筛(Na2O含量1.68%,曾经经过一次水热焙烧)、ZSM-5分子筛(Na2O含量0.10%)、高岭土(灼减14.6%),硅藻土(灼减15.4%),铝溶胶(含氧化铝19.4重%),拟薄水铝石(灼减31.8%),薄水铝石(灼减17.0%),氧化硅(白炭黑,灼减9.91%),氨水(浓度18%),硝酸稀土(RE2O3230.5g/L):均为工业品,采自兰州石化公司催化剂厂。
2.硫酸铵、柠檬酸、柠檬酸铵、乙二醇、乙醇、草酸铵、乙二胺四乙酸、尿素、磷酸氢二铵、硝酸镧、硝酸铈、硝酸钇、甲基羟乙基纤维素:均为化学试剂。
3.盐酸:浓度36%,化学试剂。
4.自制的含钇Y型分子筛浆液Y-1:该分子筛浆液的制备通过如下过程制备:(1)将1000gNaY分子筛(干基)加入7L去离子水中,搅拌状态下,加入350g硫酸铵,用盐酸调节浆液pH值3.4,85℃下搅拌1h,之后过滤、洗涤,得到滤饼。将滤饼(干基计798g)与102g硝酸钇、2.2L去离子水混合,搅拌0.5h,喷雾干燥,在焙烧炉中在100%水蒸汽气氛下进行水热焙烧,焙烧温度600℃,焙烧时间2小时;(2)将步骤(1)所得的分子筛、硫酸铵及水按照分子筛(干基):铵盐:水=1:0.3:5的重量比混合,形成浆液,在75℃、pH=3.5条件下搅拌1小时,即得到自制的含钇Y型分子筛浆液Y-1。
实施例1
在自制的含钇Y型分子筛浆液Y-1中,同时加入16g柠檬酸、4g乙二醇、54g硝酸钇和128g草酸铵,在温度55℃下搅拌20分钟。过滤、洗涤,滤饼在600℃、100%水蒸汽气氛下焙烧2小时,得到本发明改性分子筛Z-1。
将600g(干基)分子筛Z-1加入1.2L去离子水中,经过砂磨处理,得到分子筛浆液Z-1J。将619g铝溶胶、1499g高岭土、2.2L水混合打浆,之后加入分子筛浆液Z-1J,继续搅拌30min,均质后喷雾干燥成型,焙烧、水洗、干燥得到本发明催化剂C-1。
实施例2
将798g(干基计)REUSY分子筛、16g(干基计)ZSM-5分子筛、水按照分子筛(干基):水=1:3的重量比混合打浆,形成分子筛浆液,加入110g乙二胺四乙酸、104mL硝酸稀土,用氨水调节分子筛浆液的pH值在7.5~8.0范围内,再加入23g乙醇,室温(25℃)下搅拌30分钟。过滤、洗涤,滤饼在200℃干燥。得到本发明改性分子筛Z-2。
将600g(干基)分子筛Z-2加入1.2L去离子水中,经过砂磨处理,得到分子筛浆液Z-2J。将619g铝溶胶、1513g硅藻土、2.2L水混合打浆,之后加入分子筛浆液Z-2J,继续搅拌30min,均质后喷雾干燥成型,焙烧、水洗、干燥得到本发明催化剂C-2。
实施例3
将798g(干基计)REUSY分子筛、水按照分子筛(干基):水=1:3的重量比混合,形成浆液,依次加入155g尿素、85g硝酸镧,室温(25℃)下搅拌,用氨水调节分子筛浆液的pH值在6.5~7.0范围内,再加入14g乙二醇,室温(25℃)下继续搅拌1.5小时。250℃干燥。得到本发明改性分子筛Z-3。
将600g(干基)分子筛Z-3加入1.2L去离子水中,经过砂磨处理,得到分子筛浆液Z-3J。将1054g高岭土、587g拟薄水铝石、2.2L水混合打浆,加入60mL盐酸,搅拌1小时,然后加入分子筛浆液Z-3J,搅拌15min,再加入515g铝溶胶,继续搅拌30min成胶,均质后喷雾干燥成型,焙烧、水洗、干燥得到本发明催化剂C-3。
实施例4
将798g(干基计)NH4Y分子筛、水按照分子筛(干基):水=1:5的重量比混合,形成浆液,加入40g柠檬酸铵、277mL硝酸稀土,搅拌15分钟,用氨水调节分子筛浆液的pH值在8.0~9.0范围内,温度35℃下继续搅拌1小时,得到本发明改性分子筛Z-4浆液。
将1030g高岭土、440g拟薄水铝石、120g薄水铝石、2.2L水混合打浆,加入33mL盐酸,搅拌1小时,然后加入600g(干基)改性分子筛Z-4浆液,搅拌15min,再加入619g铝溶胶,继续搅拌30min成胶,均质后喷雾干燥成型,焙烧、水洗、干燥得到本发明催化剂C-4。
实施例5
将798g(干基计)NH4Y分子筛、水按照分子筛(干基):水=1:3.5的重量比混合,形成浆液,加入70g磷酸氢二铵、64硝酸铈,搅拌10分钟,再加入30g乙二醇、15g乙醇,温度15℃下继续搅拌1小时,喷雾干燥,所得分子筛在焙烧炉中在100%水蒸汽气氛下进行水热焙烧,焙烧温度550℃,焙烧时间2.5小时。得到本发明改性分子筛Z-5。
将600g(干基)分子筛Z-5加入1.2L去离子水中,经过砂磨处理,得到分子筛浆液Z-5J。将738g高岭土、220g拟薄水铝石、1.5L水混合打浆,加入19mL盐酸,搅拌1小时,然后加入分子筛浆液Z-5J,搅拌25min,再加入619g铝溶胶,继续搅拌30min成胶,均质后喷雾干燥成型,焙烧、水洗、干燥得到本发明催化剂C-5。
实施例6
将798g(干基计)NH4Y分子筛、水按照分子筛(干基):水=1:5的重量比混合,形成浆液,加入69.2mL硝酸稀土,温度25℃下搅拌10分钟,接着加入16g柠檬酸、3g甲基羟乙基纤维素,温度25℃下搅拌10分钟,再加入64g草酸铵,继续搅拌15分钟,干燥,所得含水的分子筛在焙烧炉中在100%水蒸汽气氛下进行水热焙烧,焙烧温度650℃,焙烧时间2小时。得到本发明改性分子筛Z-6。
将500g(干基)分子筛Z-6加入1.0L去离子水中,经过砂磨处理,得到分子筛浆液Z-6J。将867g高岭土、587g拟薄水铝石、222g氧化硅、2.0L水混合打浆,加入50mL盐酸,搅拌0.5小时,然后加入分子筛浆液Z-6J,搅拌25min,再加入870g铝溶胶,继续搅拌30min成胶,均质后喷雾干燥成型,焙烧、水洗、干燥得到本发明催化剂C-6。
实施例7
将69.2mL硝酸稀土、0.5L水、64g草酸铵混合,温度25℃下搅拌10分钟,接着加入798g(干基计)NH4Y分子筛、16g柠檬酸、3g甲基羟乙基纤维素和水,得到的混合体系中,分子筛(干基):水的重量比为1:5,继续搅拌15分钟,干燥,所得含水的分子筛在焙烧炉中在100%水蒸汽气氛下进行水热焙烧,焙烧温度650℃,焙烧时间2小时。得到本发明改性分子筛Z-7。
将500g(干基)分子筛Z-7加入1.0L去离子水中,经过砂磨处理,得到分子筛浆液Z-7J。将867g高岭土、587g拟薄水铝石、222g氧化硅、2.0L水混合打浆,加入50mL盐酸,搅拌0.5小时,然后加入分子筛浆液Z-7J,搅拌25min,再加入870g铝溶胶,继续搅拌30min成胶,均质后喷雾干燥成型,焙烧、水洗、干燥得到本发明催化剂C-7。
对比例1
在自制的含钇Y型分子筛浆液Y-1中,加入16g柠檬酸、4g乙二醇、54g硝酸钇,在温度55℃下搅拌20分钟。过滤、洗涤,滤饼在600℃、100%水蒸汽气氛下焙烧2小时,得到对比分子筛DZ-1。
将600g(干基)分子筛DZ-1加入1.2L去离子水中,经过砂磨处理,得到分子筛浆液DZ-1J。将619g铝溶胶、1499g高岭土、2.2L水混合打浆,之后加入分子筛浆液DZ-1J,继续搅拌30min,均质后喷雾干燥成型,焙烧、水洗、干燥得到含对比分子筛DZ-1的对比催化剂DC-1。
对比例2
在自制的含钇Y型分子筛浆液Y-1中,加入54g硝酸钇和128g草酸铵,在温度55℃下搅拌20分钟。过滤、洗涤,滤饼在600℃、100%水蒸汽气氛下焙烧2小时,得到对比分子筛DZ-2。
将600g(干基)分子筛DZ-2加入1.2L去离子水中,经过砂磨处理,得到分子筛浆液DZ-2J。将619g铝溶胶、1499g高岭土、2.2L水混合打浆,之后加入分子筛浆液DZ-2J,继续搅拌30min,均质后喷雾干燥成型,焙烧、水洗、干燥得到含对比分子筛DZ-2的对比催化剂DC-2。
对比例3
自制的含钇Y型分子筛浆液Y-1在温度55℃下搅拌20分钟,过滤、洗涤,滤饼在600℃、100%水蒸汽气氛下焙烧2小时,得到对比分子筛DZ-3。
将600g(干基)分子筛DZ-3加入1.2L去离子水中,经过砂磨处理,得到分子筛浆液DZ-3J。将619g铝溶胶、1499g高岭土、2.2L水混合打浆,之后加入分子筛浆液DZ-3J,继续搅拌30min,均质后喷雾干燥成型,焙烧、水洗、干燥得到含对比分子筛DZ-3的对比催化剂DC-3。
对比例4
按照中国专利CN99105792.9公开的含稀土分子筛的制备方法:将798g(干基计)REUSY分子筛、16g(干基计)ZSM-5分子筛、水按照分子筛(干基):水=1:3的重量比混合打浆,形成分子筛浆液,加入110g乙二胺四乙酸,用氨水调节分子筛浆液的pH值在7.5~8.0范围内,再加入23g乙醇,室温(25℃)下搅拌30分钟。过滤、洗涤,滤饼在200℃干燥,制得对比分子筛DZ-4。
将600g(干基)分子筛DZ-4加入1.2L去离子水中,经过砂磨处理,得到分子筛浆液DZ-4J。将619g铝溶胶、1513g硅藻土、2.2L水混合打浆,之后加入分子筛浆液DZ-4J,继续搅拌30min,均质后喷雾干燥成型,焙烧、水洗、干燥得到含对比分子筛DZ-4的对比催化剂DC-4。
对比例5
将798g(干基计)REUSY分子筛、水按照分子筛(干基):水=1:3的重量比混合,形成浆液,加入85g硝酸镧,室温(25℃)下搅拌,用氨水调节分子筛浆液的pH值在6.5~7.0范围内,室温(25℃)下继续搅拌1.5小时。250℃干燥,制得对比分子筛DZ-5。
将600g(干基)分子筛DZ-5加入1.2L去离子水中,经过砂磨处理,得到分子筛浆液DZ-5J。将1054g高岭土、587g拟薄水铝石、2.2L水混合打浆,加入60mL盐酸,搅拌1小时,然后加入分子筛浆液DZ-5J,搅拌15min,再加入515g铝溶胶,继续搅拌30min成胶,均质后喷雾干燥成型,焙烧、水洗、干燥得到含对比分子筛DZ-5的对比催化剂DC-5。
对比例6
将798g(干基计)NH4Y分子筛、水按照分子筛(干基):水=1:5的重量比混合,形成浆液,搅拌15分钟,温度35℃下继续搅拌1小时,制得对比分子筛DZ-6浆液。
将1030g高岭土、440g拟薄水铝石、120g薄水铝石、2.2L水混合打浆,加入33mL盐酸,搅拌1小时,然后加入600g(干基)分子筛DZ-6浆液,搅拌15min,再加入619g铝溶胶,继续搅拌30min成胶,均质后喷雾干燥成型,焙烧、水洗、干燥得到含对比分子筛DZ-6的对比催化剂DC-6。
对比例7
将798g(干基计)NH4Y分子筛、水按照分子筛(干基):水=1:3.5的重量比混合,形成浆液,加入70g磷酸氢二铵、64硝酸铈,搅拌10分钟,温度15℃下继续搅拌1小时,喷雾干燥,所得分子筛在焙烧炉中在100%水蒸汽气氛下进行水热焙烧,焙烧温度550℃,焙烧时间2.5小时,制得对比分子筛DZ-7。
将600g(干基)分子筛DZ-7加入1.2L去离子水中,经过砂磨处理,得到分子筛浆液DZ-7J。将738g高岭土、220g拟薄水铝石、1.5L水混合打浆,加入19mL盐酸,搅拌1小时,然后加入分子筛浆液DZ-7J,搅拌25min,再加入619g铝溶胶,继续搅拌30min成胶,均质后喷雾干燥成型,焙烧、水洗、干燥得到含对比分子筛DZ-7的对比催化剂DC-7。
对比例8
按照中国专利CN200510114495.1公开的一种提高超稳Y型沸石稀土含量的方法,将798g(干基计)NH4Y分子筛在600℃、100%水蒸汽气氛下焙烧1.5小时得到超稳Y分子筛,超稳Y分子筛与水按照分子筛(干基):水=1:5的重量比混合,形成浆液,加入40g柠檬酸铵,温度35℃下搅拌1小时,然后洗涤、过滤、取出滤饼,将滤饼按照分子筛(干基):水=1:5的重量比混合,搅拌,再加入277mL硝酸稀土,温度35℃下继续搅拌1小时,过滤、干燥,制得对比分子筛DZ-8。
将600g(干基)分子筛DZ-8加入1.5L去离子水中,经过砂磨处理,得到分子筛浆液DZ-8J。将1030g高岭土、440g拟薄水铝石、120g薄水铝石、2.2L水混合打浆,加入50mL盐酸,搅拌1小时,然后加入分子筛浆液DZ-8J,搅拌15min,再加入619g铝溶胶,继续搅拌30min成胶,均质后喷雾干燥成型,焙烧、水洗、干燥得到含对比分子筛DZ-8的对比催化剂DC-8。
对比例9
按照中国专利CN02103909.7公开的一种用于重油催化裂化的、含抗钒组分的新型稀土超稳Y分子筛制备方法,将798g(干基计)NH4Y分子筛、水按照分子筛(干基):水=1:5的重量比混合,形成浆液,加入64g草酸铵,温度25℃下搅拌0.5小时,再加入69.2mL硝酸稀土,继续充分搅拌15分钟,过滤、水洗,所得含水的分子筛在焙烧炉中,在100%水蒸汽气氛下进行水热焙烧,焙烧温度650℃,焙烧时间2小时。制得对比分子筛DZ-9。
将500g(干基)分子筛DZ-9加入1.0L去离子水中,经过砂磨处理,得到分子筛浆液DZ-9J。将867g高岭土、587g拟薄水铝石、222g氧化硅、2.0L水混合打浆,加入50mL盐酸,搅拌0.5小时,然后加入分子筛浆液DZ-9J,搅拌25min,再加入870g铝溶胶,继续搅拌30min成胶,均质后喷雾干燥成型,焙烧、水洗、干燥得到含对比分子筛DZ-9的对比催化剂DC-9。
采用实施例1~7制备的分子筛Z-1~Z-7和采用对比例1~9制备的分子筛DZ-1~DZ-9,其物化性质分析测试结果列于表1中。
表1改性分子筛的性质
表1结果表明,与采用对比例1制备的分子筛DZ-1相比,采用实施例1制备的分子筛Z-1,氧化钠含量、结晶度、晶胞常数与对比分子筛DZ-1相当,但分子筛的氧化钇含量远高于DZ-11.49wt%,说明本发明改性分子筛制备过程中沉淀剂是不可缺少的,有利于元素周期表中ⅢB元素沉淀在分子筛上。与采用实施例4制备的分子筛Z-4相比,采用对比例8制备的分子筛DZ-8,由于稀土离子交换后,进行过滤,未交换到分子筛上的稀土存在流失进入滤液的现象,因此分子筛的稀土含量低,稀土的利用率低;对比分子筛DZ-8所含有的稀土是通过离子交换进入分子筛的,这种稀土使分子筛在水热焙烧过程中晶胞不容易收缩,因此其晶胞常数高于采用实施例4所制备的分子筛Z-4;另外,与采用实施例4制备的分子筛Z-4相比,采用对比例8制备的分子筛DZ-8增加了分子筛的过滤处理过程,制备工艺相对复杂。与采用实施例6制备的分子筛Z-6相比,采用对比例9制备的分子筛DZ-9,由于分子筛加入稀土后,也进行过滤,因此也存在稀土的流失和分子筛制备工艺相对复杂的问题;在采用实施例6制备分子筛Z-6的过程中,草酸铵主要用作稀土的沉淀剂,而采用对比例9制备分子筛DZ-9的过程中,草酸铵首先作为脱铝剂,脱除分子筛上的铝,然后与稀土反应,使稀土沉淀下来。
为了考察催化剂的裂化活性和水热稳定性,将采用实施例1~7制备的催化剂C-1~C-7和采用对比例1~9制备的对比催化剂DC-1~DC-9,分别测试催化剂经过17h水蒸汽老化后的活性,测试结果列于表2。
为了考察催化剂的抗重金属污染能力,将上述催化剂采用等体积浸渍法,分别浸渍5000μg/gV、3000μg/gNi(相对于催化剂),经钒、镍污染的催化剂在800℃、100%水蒸汽条件下处理6h,测试钒、镍污染催化剂6h水蒸汽老化后的活性,测试结果列于表2。
表2中,用活性保留率R1表征催化剂的抗重金属污染能力。定义:活性保留率R1=钒、镍污染6h水蒸汽老化活性/17h水蒸汽老化活性×100%。
表2结果表明,与采用对比例1~9制备的对比催化剂DC-1~DC-9相比,本发明实施例1~7制备的催化剂C-1~C-7,其活性保留率R1均提高,说明本发明改性分子筛催化剂具有更强的抗钒、镍污染能力。
与采用对比例1制备的催化剂DC-1相比,以本发明实施例1制备的分子筛Z-1为活性组分制备的催化剂C-1,其17h活性明显高于含有对比例1制备的分子筛的对比催化剂DC-1,高4个百分点;催化剂污染钒、镍后,以本发明实施例1制备的催化剂C-1,其钒、镍污染催化剂6h水蒸汽老化后的活性明显高于对比催化剂DC-111个百分点,活性保留率R1提高了11个百分点,说明本发明含沉淀钇的催化剂具有更高的活性稳定性和抗钒、镍污染能力。与采用对比例2制备的催化剂DC-2相比,以本发明实施例1制备的催化剂
表2催化剂的活性和抗重金属性能
C-1,其17h活性与采用对比例2制备的对比催化剂DC-2相当,但催化剂污染钒、镍后,以本发明实施例1制备的催化剂C-1,其钒、镍污染催化剂6h水蒸汽老化后的活性明显高于对比催化剂(DC-2)5个百分点,活性保留率R1提高了7个百分点,说明本发明采用有机络合剂和分散剂制备的含有沉淀钇的分子筛催化剂具有更高的抗钒、镍污染能力。与采用对比例3制备的催化剂DC-3相比,以本发明实施例1制备的催化剂C-1,其17h活性明显高于采用对比例3制备的对比催化剂DC-3,高11个百分点;催化剂污染钒、镍后,以本发明实施例1制备的催化剂C-1,其钒、镍污染催化剂6h水蒸汽老化后的活性明显高于对比催化剂(DC-3)16个百分点,活性保留率R1提高了11个百分点,说明本发明含沉淀钇的催化剂具有更高的活性稳定性和抗钒、镍污染能力。
与采用对比例4制备的对比催化剂DC-4相比,以本发明实施例2制备的催化剂C-2,其17h活性明显高于对比催化剂DC-4,高10个百分点;催化剂污染钒、镍后,以本发明实施例2制备的催化剂C-2,其钒、镍污染催化剂6h水蒸汽老化后的活性明显高于对比催化剂(DC-4)16个百分点,活性保留率R1提高了14个百分点,说明本发明含沉淀稀土的催化剂具有更高的活性稳定性和抗钒、镍污染能力。
与采用对比例5制备的催化剂DC-5相比,以本发明实施例3制备的催化剂C-3,其17h活性高于采用对比例5制备的对比催化剂,高2个百分点;催化剂污染钒、镍后,以本发明实施例3制备的催化剂C-3,其钒、镍污染催化剂6h水蒸汽老化后的活性明显高于对比催化剂(DC-5)9个百分点,活性保留率R1提高了11个百分点,说明本发明采用分散剂和尿素、氨水沉淀剂制备的分子筛催化剂比只采用氨水沉淀技术制备的分子筛催化剂具有更高的活性稳定性和抗钒、镍污染能力。
与采用对比例6制备的催化剂DC-6相比,以本发明实施例4制备的催化剂C-4,其17h活性明显高于对比催化剂DC-6,高20个百分点;催化剂污染钒、镍后,以本发明实施例4制备的催化剂C-4,其钒、镍污染催化剂6h水蒸汽老化后的活性明显高于对比催化剂(DC-6)24个百分点,活性保留率R1提高了15个百分点,说明本发明制备的催化剂比不含沉淀稀土的催化剂具有更高的活性稳定性和抗钒、镍污染能力。
与采用对比例7制备的催化剂DC-7相比,以本发明实施例5制备的催化剂C-5,其17h活性与对比催化剂DC-7相当;催化剂污染钒、镍后,以本发明实施例5制备的催化剂C-5,其钒、镍污染催化剂6h水蒸汽老化后的活性高于对比催化剂(DC-7)5个百分点,活性保留率R1提高了9个百分点,说明本发明采用分散剂制备的催化剂比不采用分散剂的磷酸稀土沉淀技术制备的催化剂具有更高的活性稳定性和抗钒、镍污染能力。
与采用对比例8制备的催化剂DC-8相比,污染钒、镍后,以本发明实施例4制备的催化剂C-4,其钒、镍污染催化剂6h水蒸汽老化后的活性明显高于对比催化剂(DC-8)6个百分点,活性保留率R1提高了9个百分点,说明本发明制备的催化剂比不含沉淀稀土的催化剂具有更高的活性稳定性和抗钒、镍污染能力。
与采用对比例9制备的催化剂DC-9相比,污染钒、镍后,分别以本发明实施例6、7制备的催化剂C-6、C-7,其钒、镍污染催化剂6h水蒸汽老化后的活性明显高于对比催化剂(DC-9)4~5个百分点,活性保留率R1分别提高了10个百分点和7百分点,说明本发明采用络合剂和分散剂制备的催化剂比采用现有技术中国专利CN02103909.7方法制备的催化剂具有更高的活性稳定性和抗钒、镍污染能力。
本发明实施例所提供的改性分子筛的制备方法,由于ⅢB元素沉淀物与分子筛混合在一起,没有单独分开,所以没有办法单独测试实施例1~7的ⅢB元素沉淀物的粒度,为了表征采用本发明方法制备的ⅢB元素沉淀物的粒度,本发明实施例8~9,对比例10提供了不加入分子筛,ⅢB元素沉淀物的制备和粒度的定量数据。
实施例8
将2g柠檬酸、2.48mL硝酸稀土和75mL去离子水混合,形成均匀的溶液,再加入2g草酸铵,搅拌15分钟,形成含稀土的沉淀物浆液CD-1。
实施例9
将2g柠檬酸、2.48mL硝酸稀土和75mL去离子水混合,形成均匀的溶液,再加入2g乙醇,搅拌15分钟,形成含稀土的沉淀物浆液CD-2。
对比例10
除了将实施例8中不加入2g柠檬酸之外,其它条件同实施例8,制得对比含稀土的沉淀物浆液DCD-1。
分别对采用实施例8、9和对比例10制备的含稀土的沉淀物浆液CD-1、CD-2、DCD-1测试稀土沉淀的粒度,结果列于表3。
表3稀土沉淀的粒度
表3结果表明,与采用对比例10制备的含稀土的沉淀物DCD-1相比,采用实施例8、9制备的含稀土的沉淀物CD-1、CD-2粒度变小,说明本发明有机络合剂、分散剂能够有效降低稀土与沉淀剂反应所形成的沉淀物的颗粒大小。
当然,本发明还可有其它多种实施例,在不背离本发明精神及其实质的情况下,熟悉本领域的技术人员可根据本发明作出各种相应的改变和变形,但这些相应的改变和变形都应属于本发明权利要求的保护范围。
Claims (16)
1.一种含有改性分子筛的催化裂化催化剂,以催化剂质量为100%计,含有10~55%的以干基计的改性分子筛、10~80%的以干基计的粘土、0~40%的以氧化物计的无机氧化物和5~40%以氧化物计的粘结剂;其特征在于所述的改性分子筛通过包括下述制备步骤的制备方法获得:将(1)分子筛浆液、(2)含元素周期表ⅢB金属离子的化合物溶液、(3)有机络合剂和/或分散剂、(4)沉淀剂混合,温度5~100℃,搅拌至少10分钟,得到含有元素周期表中ⅢB元素的沉淀物和分子筛的混合浆液,干燥,经过或不经过焙烧,得到经过ⅢB元素改性的分子筛,其中以氧化物计的ⅢB元素与分子筛干基的重量比为0.3~10:100,所述的有机络合剂与ⅢB金属离子的摩尔比为0.3~10:1,所述分散剂与金属离子的摩尔比为0.2~16:1。
2.根据权利要求1所述的催化裂化催化剂,其特征在于以催化剂质量为100%计,含有15~45%的以干基计的改性分子筛、20~65%的以干基计的粘土、5~25%的以氧化物计的无机氧化物和5~30%以氧化物计的粘结剂。
3.根据权利要求1或2所述的催化裂化催化剂,其特征在于所述的改性分子筛的制备中,将(1)分子筛浆液、(2)含元素周期表ⅢB金属离子的化合物溶液、(3)有机络合剂和/或分散剂、(4)沉淀剂混合,在温度5~60℃下,搅拌10min~40min,得到含有元素周期表中ⅢB元素的沉淀物和分子筛的混合浆液。
4.根据权利要求1或2所述的催化裂化催化剂,其特征在于所述的以氧化物计的ⅢB元素与分子筛干基的重量比为0.3~8:100。
5.根据权利要求1或2所述的催化裂化催化剂,其特征在于所述的有机络合剂与ⅢB金属离子的摩尔比为0.5~6:1,优选1.0~4:1;所述分散剂与金属离子的摩尔比为1~11:1,优选2~7:1。
6.根据权利要求1或2所述的催化裂化催化剂,其特征在于所述的沉淀剂为在化学沉淀反应中,能够与体系中的ⅢB族金属离子发生化学反应,并且使其生成物在体系中微溶或不溶的物质。
7.根据权利要求1或2所述的催化裂化催化剂,其特征在于所述的沉淀剂为能够提供或产生氢氧根离子、碳酸根离子、碳酸氢根离子、磷酸根离子、磷酸氢根离子、磷酸二氢根离子、草酸根离子的化合物。
8.根据权利要求1或2所述的催化裂化催化剂,其特征在于所述的沉淀剂为草酸、草酸铵、碳酸铵、碳酸氢铵、二氧化碳、氨水、磷酸、磷酸氢二铵、磷酸二氢铵、磷酸铵、尿素中的一种或几种。
9.根据权利要求1或2所述的催化裂化催化剂,其特征在于所述的有机络合剂选自甲酸、乙酸、己二酸、柠檬酸、酒石酸、苯甲酸、乙二胺四乙酸、水杨酸以及上述酸的盐、以及乙酰丙酮、二乙醇胺、三乙醇胺中的一种或多种,优选柠檬酸、柠檬酸铵、柠檬酸二氢铵、柠檬酸氢二铵、乙二胺四乙酸中的一种或多种。
10.根据权利要求1或2所述的催化裂化催化剂,其特征在于所述的分散剂为在分子内同时具有亲油性和亲水性两种相反性质的界面活性剂,可均一分散那些难于溶解于液体的固体颗粒,同时也能防止固体颗粒的沉降和凝聚,形成安定悬浮液所需的物质,且分散剂不会与ⅢB族金属离子作用形成沉淀。
11.根据权利要求1或2所述的催化裂化催化剂,其特征在于所述的分散剂选自碳原子数为2~8的一元醇或二元醇、聚乙二醇、纤维素衍生物、聚丙烯酰胺及其衍生物、古尔胶中的一种或多种。
12.根据权利要求11所述的催化裂化催化剂,其特征在于所述的纤维素衍生物为羟甲基纤维素钠、甲基羟乙基纤维素、羟丙基甲基纤维素;所述的碳原子数为2~8的一元醇或二元醇为乙醇、乙二醇、异丙醇、丁醇、甲基戊醇中的一种或多种。
13.根据权利要求1或2所述的催化裂化催化剂,其特征在于所述的(1)分子筛浆液、(2)含元素周期表ⅢB金属离子的化合物溶液、(3)有机络合剂和/或分散剂、(4)沉淀剂的混合通过以下任意一种方式实现:
方式1:将分子筛浆液、沉淀剂、有机络合剂和/或分散剂混合均匀,加入含元素周期表中ⅢB金属离子的化合物溶液,搅拌至少10分钟;
方式2:将含元素周期表中ⅢB金属离子的化合物溶液、分子筛浆液、有机络合剂和/或分散剂混合均匀,加入沉淀剂,搅拌至少10分钟;
方式3:将沉淀剂与含元素周期表中ⅢB金属离子的化合物溶液混合形成ⅢB金属离子沉淀物,ⅢB金属离子沉淀物与分子筛浆液、有机络合剂和/或分散剂中一种或多种混合,加入剩余组分,形成含有ⅢB金属离子沉淀物、分子筛浆液、有机络合剂和/或分散剂的悬浮液,搅拌至少10分钟。
14.根据权利要求1或2所述的催化裂化催化剂,其特征在于所述的分子筛焙烧工艺条件为,在100%水蒸汽气氛下进行分子筛焙烧,焙烧温度450~700℃,焙烧时间0.5~4小时。
15.一种权利要求1所述的含改性分子筛的催化裂化催化剂的制备方法,其特征在于该制备方法包括:(1)制备改性分子筛,将分子筛浆液、含元素周期表ⅢB金属离子的化合物溶液、有机络合剂和/或分散剂、沉淀剂混合,温度5~100℃,搅拌至少10分钟,得到含有元素周期表中ⅢB元素的沉淀物和分子筛的混合浆液,干燥,经过或不经过焙烧,得到经过ⅢB元素改性的分子筛,其中以氧化物计的ⅢB元素与分子筛干基的重量比为0.3~10:100,所述的有机络合剂与ⅢB金属离子的摩尔比为0.3~10:1,所述分散剂与金属离子的摩尔比为0.2~16:1;(2)将改性分子筛、粘土、无机氧化物、粘结剂混合打浆,喷雾干燥,制备得到催化剂。
16.一种权利要求1所述的含改性分子筛的催化裂化催化剂的制备方法,其特征在于该制备方法包括:(1)制备改性分子筛浆液,将分子筛浆液、含元素周期表ⅢB金属离子的化合物溶液、有机络合剂和/或分散剂、沉淀剂混合,温度5~100℃,搅拌至少10分钟,得到含有元素周期表中ⅢB元素的沉淀物和分子筛的混合浆液,其中以氧化物计的ⅢB元素与分子筛干基的重量比为0.3~10:100,所述的有机络合剂与ⅢB金属离子的摩尔比为0.3~10:1,所述分散剂与金属离子的摩尔比为0.2~16:1;(2)将改性分子筛浆液、粘土、无机氧化物、粘结剂混合打浆,喷雾干燥,制备得到催化剂。