CN105367014A - 一种复合硅酸盐保温板及其制备方法 - Google Patents
一种复合硅酸盐保温板及其制备方法 Download PDFInfo
- Publication number
- CN105367014A CN105367014A CN201510834190.1A CN201510834190A CN105367014A CN 105367014 A CN105367014 A CN 105367014A CN 201510834190 A CN201510834190 A CN 201510834190A CN 105367014 A CN105367014 A CN 105367014A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- composite
- silicate heat
- heat insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种复合硅酸盐保温板及其制备方法，包括：水泥25-35份、粉煤灰15-25份、硅灰石粉5-10份、表面活性剂2-5份、高效减水剂6-8份、抗裂纤维6-8份、防水剂1-5份、增稠剂3-5份、柔性剂3-5份和复合粘接剂2-5份。按比例将水泥、粉煤灰、硅灰石粉、表面活性剂、高效减水剂、抗裂纤维、防水剂和增稠剂，搅拌混合均匀静置12-15小时；加入柔性剂和复合粘结剂混匀，形成胶凝体浆料；胶凝体浆料成型。本发明具有良好的保温性能，同时，它还具有优良的隔音、吸声、防火效果。
Description
技术领域
本发明涉及一种建筑保温***用的复合硅酸盐保温板及其生产方法。
背景技术
随着对节能、隔音、防火、环保要求的不断提高，建筑围护结构的节能技术日益成熟，内外墙保温技术由于具有消除“热桥”的优势和良好的热舒适性，因此得到广泛的应用。
目前用于建筑物围护结构外墙保温的产品中普遍为现场粘贴或机械固定保温板，然后用抗裂砂浆铺设网格布，再做涂料面或石材面。由于现场配制工艺作业烦琐，配制的质量难以控制，且是现场作业，受天气、环境、时间等影响比较大。特别是在外墙粘贴石材饰面层时，安全、成本、工期等方面都不理想。
发明内容
本发明旨在解决现有技术存在的缺陷和问题，提供一种综合性能良好的复合保温板。
本发明其中一个技术方案是：一种复合硅酸盐保温板，包括：水泥25-35份、粉煤灰15-25份、硅灰石粉5-10份、表面活性剂2-5份、高效减水剂6-8份、抗裂纤维6-8份、防水剂1-5份、增稠剂3-5份、柔性剂3-5份和复合粘接剂2-5份。
优选地，水泥25份、粉煤灰15份、硅灰石粉5份、表面活性剂2份、高效减水剂6份、抗裂纤维6份、防水剂1份、增稠剂3份、柔性剂3份和复合粘接剂2份。
优选地，水泥35份、粉煤灰25份、硅灰石粉10份、表面活性剂5份、高效减水剂8份、抗裂纤维8份、防水剂5份、增稠剂5份、柔性剂5份和复合粘接剂5份。
优选地，水泥30份、粉煤灰20份、硅灰石粉8份、表面活性剂3份、高效减水剂7份、抗裂纤维7份、防水剂3份、增稠剂4份、柔性剂4份和复合粘接剂4份。
优选地，柔性剂为聚乙烯丙纶。
优选地，表面活性剂为琥珀酸二辛酯磺酸钠或/和十二烷基磺酸钠。
优选地，防水剂为无机铝盐防水剂，增稠剂为甲基纤维素、羟丙基甲基纤维素、羧甲基纤维素钠或羟乙基纤维素中的任意一种或两种以上。
本发明另外一个技术主题的技术方案为：一种复合硅酸盐保温板的制备方法，该方法包括以下步骤：
(1)、按比例将水泥、粉煤灰、硅灰石粉、表面活性剂、高效减水剂、抗裂纤维、防水剂和增稠剂，搅拌混合均匀静置12-15小时；
(2)加入柔性剂和复合粘结剂混匀，形成胶凝体浆料；
(3)胶凝体浆料成型。
本发明的优点和有益效果在于：本发明通过确定合理的配方和工艺过程中工艺参数的控制，最终保证了产品成型性能及力学性能，解决了技术上的难点。主要有三个特点：本发明具有良好的保温性能，同时，它还具有优良的隔音、吸声、防火效果。
具体实施方式
下面结合实施例对本发明的具体实施方式作进一步描述，以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明其中一个技术方案是：一种复合硅酸盐保温板，包括：水泥25-35份、粉煤灰15-25份、硅灰石粉5-10份、表面活性剂2-5份、高效减水剂6-8份、抗裂纤维6-8份、防水剂1-5份、增稠剂3-5份、柔性剂3-5份和复合粘接剂2-5份。
优选地，水泥25份、粉煤灰15份、硅灰石粉5份、表面活性剂2份、高效减水剂6份、抗裂纤维6份、防水剂1份、增稠剂3份、柔性剂3份和复合粘接剂2份。
优选地，水泥35份、粉煤灰25份、硅灰石粉10份、表面活性剂5份、高效减水剂8份、抗裂纤维8份、防水剂5份、增稠剂5份、柔性剂5份和复合粘接剂5份。
优选地，水泥30份、粉煤灰20份、硅灰石粉8份、表面活性剂3份、高效减水剂7份、抗裂纤维7份、防水剂3份、增稠剂4份、柔性剂4份和复合粘接剂4份。
优选地，柔性剂为聚乙烯丙纶。
优选地，表面活性剂为琥珀酸二辛酯磺酸钠或/和十二烷基磺酸钠。
优选地，防水剂为无机铝盐防水剂，增稠剂为甲基纤维素、羟丙基甲基纤维素、羧甲基纤维素钠或羟乙基纤维素中的任意一种或两种以上。
本发明另外一个技术主题的技术方案为：一种复合硅酸盐保温板的制备方法，该方法包括以下步骤：
(1)、按比例将水泥、粉煤灰、硅灰石粉、表面活性剂、高效减水剂、抗裂纤维、防水剂和增稠剂，搅拌混合均匀静置12-15小时；
(2)加入柔性剂和复合粘结剂混匀，形成胶凝体浆料；
(3)胶凝体浆料成型。
以上所述仅是本发明的优先实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (8)
1.一种复合硅酸盐保温板，其特征在于,包括：水泥25-35份、粉煤灰15-25份、硅灰石粉5-10份、表面活性剂2-5份、高效减水剂6-8份、抗裂纤维6-8份、防水剂1-5份、增稠剂3-5份、柔性剂3-5份和复合粘接剂2-5份。
2.根据权利要求1所述的复合硅酸盐保温板，其特征在于，水泥25份、粉煤灰15份、硅灰石粉5份、表面活性剂2份、高效减水剂6份、抗裂纤维6份、防水剂1份、增稠剂3份、柔性剂3份和复合粘接剂2份。
3.根据权利要求1所述的复合硅酸盐保温板，其特征在于，水泥35份、粉煤灰25份、硅灰石粉10份、表面活性剂5份、高效减水剂8份、抗裂纤维8份、防水剂5份、增稠剂5份、柔性剂5份和复合粘接剂5份。
4.根据权利要求1所述的复合硅酸盐保温板，其特征在于，水泥30份、粉煤灰20份、硅灰石粉8份、表面活性剂3份、高效减水剂7份、抗裂纤维7份、防水剂3份、增稠剂4份、柔性剂4份和复合粘接剂4份。
5.根据权利要求1所述的复合硅酸盐保温板，其特征在于，柔性剂为聚乙烯丙纶。
6.根据权利要求1所述的复合硅酸盐保温板，其特征在于，表面活性剂为琥珀酸二辛酯磺酸钠或/和十二烷基磺酸钠。
7.根据权利要求1所述的复合硅酸盐保温板，其特征在于，防水剂为无机铝盐防水剂，增稠剂为甲基纤维素、羟丙基甲基纤维素、羧甲基纤维素钠或羟乙基纤维素中的任意一种或两种以上。
8.一种权利要求1-7任一项所述的复合硅酸盐保温板的制备方法，其特征在于，该方法包括以下步骤：
(1)、按比例将水泥、粉煤灰、硅灰石粉、表面活性剂、高效减水剂、抗裂纤维、防水剂和增稠剂，搅拌混合均匀静置12-15小时；
(2)加入柔性剂和复合粘结剂混匀，形成胶凝体浆料；
(3)胶凝体浆料成型。