CN105237824A - 一种轻量化雨靴及其制备方法 - Google Patents
一种轻量化雨靴及其制备方法 Download PDFInfo
- Publication number
- CN105237824A CN105237824A CN201510747173.4A CN201510747173A CN105237824A CN 105237824 A CN105237824 A CN 105237824A CN 201510747173 A CN201510747173 A CN 201510747173A CN 105237824 A CN105237824 A CN 105237824A
- Authority
- CN
- China
- Prior art keywords
- lightweight
- parts
- galosh
- preparation
- sulphur
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于雨靴材料制备领域,特别涉及一种轻量化雨靴及制备方法。本发明基于天然橡胶改性制备成轻质雨靴材料,各组分为,天然橡胶70~75份、丁苯橡胶25~30份、高苯乙烯4~6份、硫磺2~2.5份、促进剂M0.2~0.25份、促进剂D0.2~0.3份、碳酸锌4~5份、硬脂酸0.5~1份、防老剂22460.3~0.6份、铝合金阻隔防爆材料20~30份、聚乙二醇2~3份、纤维粉10~20份、炭黑2~3份、C5树脂2~4份,兼顾材料的轻质特点和力学使用性能。
Description
技术领域
本发明属于雨靴材料制备领域,特别涉及一种轻量化雨靴及制备方法。
背景技术
雨靴是下雨和泥泞时穿的一种高至踝节部的橡胶或塑料套鞋,是雨天出行绝佳装备,主要特点是能防水,用于雨天和泥泞道路上的步行,一般情况下靴长不到膝盖,材质主要是橡胶。
现有的雨靴材料重量较重,穿起来不方便;发泡橡胶具有比非发泡橡胶更轻的性能,已有的橡胶经发泡后虽然重量较轻,但是力学性能却不尽理想,只能使用于使用性能要求较低的雨靴材料,使用寿命有限。因此,需要提供一种具有轻质特点和牢固力学性能的雨靴材料。
发明内容
本发明所要解决的技术问题在于:提供一种兼顾轻质特点和力学使用性能的雨靴材料,该轻量化雨靴(鞋面和鞋底)材料各组分按重量份数计算为:
本发明还提供了一种上述雨靴材料的制备工艺:
将塑炼达标(可塑度为0.4,停放保持12小时)的胶料投入密炼机中,加入各填料(除了硫磺;铝合金阻隔防爆材料需人工粉碎后加入),90℃混炼7至8分钟,混炼后85℃开炼并加入硫磺,待硫磺和胶料混合完全后,再打三角包5至8次,加硫好的胶料进入炼胶机60~70℃翻炼均匀,打卷后进入五辊机,根据雨靴鞋面或鞋底的不同规格压延成型,辊温由下而上分别为75℃、80℃、85℃、90℃、95℃。
本发明的有益效果在于:本发明基于天然橡胶改性制备成轻质雨靴材料,通过丁苯橡胶的加入提高了雨靴材料的耐磨和耐热性;通过高苯乙烯增加了硫化靴的硬度和挺性,并且增加了橡胶的抗撕裂强度和耐磨性。
本发明采用铝合金阻隔防爆材料作为橡胶填料,该填料内部本身具有蜂窝状结构,赋予复合橡胶材料轻质的特点;并且本发明中通过合理的助剂复配,不仅起到了改善橡胶加工性能、使用性能的目的,同时也促进了铝合金阻隔防爆材料在橡胶体系中的相容性,确保了雨靴的使用寿命。
具体实施方式
实施例1
一种轻量化雨靴材料,各组分按重量份数计算为:
制备工艺:
将塑炼达标(可塑度为0.4,停放保持12小时)的胶料投入密炼机中,加入各填料(除了硫磺;铝合金阻隔防爆材料需人工粉碎后加入),90℃混炼7至8分钟,混炼后85℃开炼并加入硫磺,待硫磺和胶料混合完全后,再打三角包5至8次,加硫好的胶料进入炼胶机60~70℃翻炼均匀,打卷后进入五辊机压延成型,辊温由下而上分别为75℃、80℃、85℃、90℃、95℃。
比较例1
与实施例1相比,未加入铝合金阻隔防爆材料,其余工艺与实施例1相同:
一种轻量化雨靴材料,各组分按重量份数计算为:
制备工艺如实施例1。
比较例2
与实施例1相比,复合材料制备中加入的助剂略有变化(“促进剂D”换成“促进剂DM”,并且将配方中的C5树脂省去),其余工艺与实施例1相同:
一种轻量化雨靴材料,各组分按重量份数计算为:
制备工艺如实施例1。
比较例3
与实施例1相比,复合材料制备中加入的助剂略有变化(具体为:硫磺、硬脂酸、聚乙二醇的用量有所变化),其余工艺与实施例1相同:
一种轻量化雨靴材料,各组分按重量份数计算为:
制备工艺如实施例1。
比较例4
与实施例1相比,将配方中的“炭黑”省去,其余工艺与实施例1相同:
制备工艺如实施例1。
对上述各实施例、比较例中橡胶材料产品的邵氏硬度、拉伸强度、扯断伸长率和密度进行测试,测试结果如表1:
表1
邵氏硬度(A) | 拉伸强度(MPa) | 扯断伸长率(%) | 密度(g/cm3) | |
实施例1 | 97 | 17.2 | 660 | 0.96 |
比较例1 | 97 | 17.8 | 680 | 1.31 |
比较例2 | 94 | 10.4 | 360 | 0.97 |
比较例3 | 95 | 12.4 | 410 | 0.97 |
比较例4 | 96 | 10.2 | 350 | 0.98 |
Claims (7)
1.一种轻量化雨靴,其特征在于:所述的轻量化雨靴的鞋面和鞋底材料中,各组分按重量份数计算为,
2.如权利要求1所述的轻量化雨靴的制备方法,其特征在于:所述制备方法为,
将塑炼达标的胶料投入密炼机中,加入除硫磺外的各填料,混炼7至8分钟,混炼后开炼并加入硫磺,待硫磺和胶料混合完全后,再打三角包5至8次,加硫好的胶料进入炼胶机翻炼均匀,打卷后进入五辊机压延成型。
3.如权利要求2所述的轻量化雨靴的制备方法,其特征在于:塑炼达标是指,胶料可塑度达到0.4,并停放保持12小时。
4.如权利要求2所述的轻量化雨靴的制备方法,其特征在于:所述混炼的温度为90℃。
5.如权利要求2所述的轻量化雨靴的制备方法,其特征在于:所述开炼的温度为85℃。
6.如权利要求2所述的轻量化雨靴的制备方法,其特征在于:所述翻炼的温度为60~70℃。
7.如权利要求2所述的轻量化雨靴的制备方法,其特征在于:所述五辊机的辊温由下而上分别为75℃、80℃、85℃、90℃、95℃。