CN105088811A - 一种提高面料表面柔韧性的组合物面料 - Google Patents
一种提高面料表面柔韧性的组合物面料 Download PDFInfo
- Publication number
- CN105088811A CN105088811A CN201410185652.7A CN201410185652A CN105088811A CN 105088811 A CN105088811 A CN 105088811A CN 201410185652 A CN201410185652 A CN 201410185652A CN 105088811 A CN105088811 A CN 105088811A
- Authority
- CN
- China
- Prior art keywords
- fabric
- alkyl ester
- acid alkyl
- composition
- web surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种提高面料表面柔韧性的组合物面料,其创新点在于:组合物面料包括聚甲烯酸烷基酯、聚苯乙烯和乙烯醋酸乙烯酯构成的共聚物,共聚物的交替度为80%以上。本发明的这种面料组合物,不仅具有良好的耐磨性,耐油性和阻燃性等,并且柔韧性大大提高,在压花加工面料时制备的面料的表面不会发生破裂现象;本发明工艺简单,生产成本低,节约能源,生产安全无污染;本产品中交联剂和润滑剂的使用,使得组合物面料具有的柔韧性度得到提高,方便制作工艺。
Description
技术领域
本发明涉及一种组合物面料,尤其涉及一种提高面料表面柔韧性的组合物面料,属于纺织面料领域。
背景技术
通常我们所称的皮革大体可分为天然皮革和人造皮革。天然皮革由动物的皮毛加工而成,因此其产量有限,成本高,不能进行连续生产,并且也不能保证其颜色的多样性和质量的一致性等。但人造皮革可具有与天然皮革类似的性质,在人造皮革中使用如无纺布或织物的纤维材料作为基层织物,然后在上述基层织物上覆盖有机化合物合成面料,这样人造皮革就起到了弥补天然皮革的上述问题的作用。
目前,主要使用聚氯乙烯和聚烯烃等来制备人造皮革,特别是,由于含卤素的材料的使用受到限制,聚烯烃的使用增加。与皮革相比,人造革易于老化磨损,因含有大量化学原料而对人身健康产生危害,而且用其制作的衣包因不耐用而逐渐失去市场,慢慢的会被其他原料取代。然而,由于人造革所使用的合成树脂不同,基材种类不同,生产工艺方法不同,有无发泡及用途的不同,人造革可以分为许多种类。通常使用的聚氯乙烯和聚烯烃等制备的面料具有差的耐磨性、差的耐油性和差的阻燃性等,并且柔韧性太低,在压花加工面料时制备的面料的表面会破裂。
发明内容
本发明的目的是提供一种提高面料表面柔韧性的组合物面料,以解决上述现有技术中尚未解决的难题。
本发明采用的技术方案为:一种提高面料表面柔韧性的组合物面料,其创新点在于:所述组合物面料包括聚甲烯酸烷基酯、聚苯乙烯和乙烯醋酸乙烯酯构成的共聚物,共聚物的交替度为80%以上。
进一步的,所述聚甲烯酸烷基酯的单体为由1~5种C8~C20甲烯酸烷基酯或其混合物构成。
进一步的,所述聚甲烯酸烷基酯的单体为由2~3种C10~C15甲烯酸烷基酯及其混合物构成。
进一步的,所述聚甲烯酸烷基酯的单体为由C12~C14甲烯酸烷基酯及其混合物构成。
进一步的,所述聚甲烯酸烷基酯的单体为由C12甲烯酸烷基酯构成。
进一步的,所述乙烯醋酸乙烯的含量为40~50wt%。
进一步的,所述面料组合物中还包括有交联剂和润滑剂。
有益效果:本发明的这种面料组合物,不仅具有良好的耐磨性,耐油性和阻燃性等,并且柔韧性大大提高,在压花加工面料时制备的面料的表面不会发生破裂现象;本发明工艺简单,生产成本低,节约能源,生产安全无污染;本产品中交联剂和润滑剂的使用,使得组合物面料具有的柔韧性度得到提高,方便制作工艺。
具体实施方式
下面的实施列可以使本专业技术人员更全面的理解本发明,但并不因此将本发明限制在所述的实施例范围之中。
实施例1
一种提高面料表面柔韧性的组合物面料,包括聚甲烯酸烷基酯、聚苯乙烯和乙烯醋酸乙烯酯构成的共聚物,共聚物的交替度为80%,其中,聚甲烯酸烷基酯的单体为由5种C8~C20甲烯酸烷基酯及其混合物构成,乙烯醋酸乙烯的含量为50wt%。
在本实施例中,本产品不仅具有良好的耐磨性,耐油性和阻燃性等,并且柔韧性大大提高,在压花加工面料时制备的面料的表面不会发生破裂现象。
Claims (7)
1.一种提高面料表面柔韧性的组合物面料,其特征在于:所述组合物面料包括聚甲烯酸烷基酯、聚苯乙烯和乙烯醋酸乙烯酯构成的共聚物,共聚物的交替度为80%以上。
2.根据权利要求1所述的提高面料表面柔韧性的组合物面料,其特征在于:所述聚甲烯酸烷基酯的单体为由1~5种C8~C20甲烯酸烷基酯或其混合物构成。
3.根据权利要求1所述的提高面料表面柔韧性的组合物面料,其特征在于:所述聚甲烯酸烷基酯的单体为由2~3种C10~C15甲烯酸烷基酯及其混合物构成。
4.根据权利要求1所述的提高面料表面柔韧性的组合物面料,其特征在于:所述聚甲烯酸烷基酯的单体为由C12~C14甲烯酸烷基酯及其混合物构成。
5.根据权利要求1所述的提高面料表面柔韧性的组合物面料,其特征在于:所述聚甲烯酸烷基酯的单体为由C12甲烯酸烷基酯构成。
6.根据权利要求1所述的提高面料表面柔韧性的组合物面料,其特征在于:所述乙烯醋酸乙烯的含量为40~50wt%。
7.根据权利要求1所述的提高面料表面柔韧性的组合物面料,其特征在于:所述面料组合物中还包括有交联剂和润滑剂。