CN102154932A - 一种比重小的石头纸 - Google Patents
一种比重小的石头纸 Download PDFInfo
- Publication number
- CN102154932A CN102154932A CN2011100561500A CN201110056150A CN102154932A CN 102154932 A CN102154932 A CN 102154932A CN 2011100561500 A CN2011100561500 A CN 2011100561500A CN 201110056150 A CN201110056150 A CN 201110056150A CN 102154932 A CN102154932 A CN 102154932A
- Authority
- CN
- China
- Prior art keywords
- base paper
- weight
- paper layer
- parts
- lithopone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种比重小的石头纸，涉及合成纸类。由基纸层及涂布层组成，涂布层涂覆于基纸层上；基纸层由合成树脂和拌料组成，合成树脂的重量份数为15～30，拌料的重量份数为70～85；合成树脂为聚乳酸、或EVA、或PP、或PE或它们中的任意两种的组合；拌料为空心玻璃珠、或粉煤灰、或它们的组合；涂布层的成份包括丙烯酸树脂、立德粉及去离子水，各自占的重量份数是：丙烯酸树脂20～40，立德粉20～40，去离子水30～50。其有益效果是：拌料为空心玻璃珠、或粉煤灰，其比重轻，分散性好，立德粉的遮盖性也好，便于减轻纸张的重量，提高纸张质量，降低制造成本。
Description
技术领域
本发明涉及石头纸，尤指一种比重小的石头纸。
背景技术
纸产品的需求量及消费量不断增加，这与社会文明的进步和人类生活水平的不断提高相关。传统造纸技术至少有以下不足： 1、造纸的主要原料为树木制成的木浆，造纸行业耗用了大量宝贵的森林资源，是导致地球生态失衡的一个重要因素。2、造纸行业还耗用大量的水资源和能源。3、各种纸的生产大多采用湿法生产，通过一系列的化学方法和物理方法来生产纸浆，排放大量的酸、碱废液，污染土壤与水体，使人类赖以生存的环境遭到破坏与威胁，而对酸、碱废液的达标处理需要耗费大量投入，治理难度大，致使生产成本提高。4、生产方法复杂，设备投资大。
全球环保问题越来越突出，森林资源不断减少，对传统纸张及其制作技术提出了挑战。石头纸之类的合成纸应运而生，并正在应用到各行各业。但是，目前生产的石头纸比传统纸要重，因而使石头纸的应用受到局限。造成石头纸比重大的原因较多，其中之一是石头纸以人造树脂及碳酸钙粉为主要原料，碳酸钙粉（包括重质碳酸钙粉和轻质碳酸钙粉）的比重较大，且碳酸钙粉一般占75%左右，致使石头纸比重增加。
发明内容
本发明旨在针对传统造纸技术及目前石头纸的上述不足，提供一种比重小的石头纸，其比重接近传统纸张，综合性能优越，普遍适用等等。
为了达到上述目的，完成上述任务，本发明一种比重小的石头纸采用如下技术方案。
构造本发明一种比重小的石头纸，由基纸层及涂布层组成，涂布层涂覆于基纸层上；
基纸层由合成树脂和拌料组成，合成树脂的重量份数为15～30，拌料的重量份数为70～85；合成树脂为聚乳酸、或EVA、或PP、或PE或它们中的任意两种的组合；拌料为空心玻璃珠、或粉煤灰，或它们的组合；
涂布层的成份包括丙稀酸树脂、立德粉及去离子水，各自占的重量份数是：丙稀酸树脂20～40，立德粉20～40，去离子水30～50；
其加工步骤是：
、将拌料热烘脱水，使其中的水份含量的重量百分比小于或等于0.2%，并搅拌均匀；
对上述技术方案进行进一步阐述：
空心玻璃珠的粒度即颗粒的直径为等于或小于1微米。
粉煤灰的细度等于或大于200目。
立德粉的细度等于或大于600目。
基纸层的厚度为0.02～2毫米。
本发明一种比重小的石头纸，其有益效果是：
其一，拌料为空心玻璃珠、或粉煤灰，其比重轻，分散性好，立德粉的遮盖性也好，便于减轻纸张的重量，提高纸张质量，降低制造成本。
其二，环保型。可生物降解，属环境友好性材料，不会造成白色污染。
其三，不含重金属，不含邻苯二甲酸盐，不会产生增塑剂释出的危险。能作为文化、食品及卫生用纸。
其四，柔韧好，耐折耐撕裂性好，能作为笔记本及课本用纸等。
具体实施方式
下面，介绍本发明的具体实施方式。
实施例一：
本发明一种比重小的石头纸，由基纸层及涂布层组成，涂布层涂覆于基纸层上。
基纸层由合成树脂和拌料组成，合成树脂的重量份数为15，拌料的重量份数为70；合成树脂为聚乳酸、或EVA、或PP、或PE或它们中的任意两种的组合；拌料为空心玻璃珠、或粉煤灰、或它们的组合。
涂布层的成份包括丙稀酸树脂、立德粉及去离子水，各自占的重量份数是：丙稀酸树脂20，立德粉20，去离子水30。
其加工步骤是：
、将拌料热烘脱水，使其中的水份含量的重量百分比小于或等于0.2%，并搅拌均匀；
空心玻璃珠的粒度即颗粒的直径为等于或小于1微米。
粉煤灰的细度等于或大于200目。
立德粉的细度等于或大于600目。
基纸层的厚度为0.02～2毫米。
实施例二：
构造本发明一种比重小的石头纸，由基纸层及涂布层组成，涂布层涂覆于基纸层上。
基纸层由合成树脂和拌料组成，合成树脂的重量份数为22，拌料的重量份数为77；合成树脂为聚乳酸、或EVA、或PP、或PE或它们中的任意两种的组合；拌料为空心玻璃珠、或粉煤灰、或它们的组合。
涂布层的成份包括丙稀酸树脂、立德粉及去离子水，各自占的重量份数是：丙稀酸树脂30，立德粉30，去离子水40。
其加工步骤是：
空心玻璃珠的粒度即颗粒的直径为等于或小于1微米。
粉煤灰的细度等于或大于200目。
立德粉的细度等于或大于600目。
基纸层的厚度为0.02～2毫米。
实施例三：
本发明一种比重小的石头纸，由基纸层及涂布层组成，涂布层涂覆于基纸层上。
基纸层由合成树脂和拌料组成，合成树脂的重量份数为30，拌料的重量份数为85；合成树脂为聚乳酸、或EVA、或PP、或PE或它们中的任意两种的组合；拌料为空心玻璃珠、或粉煤灰、或它们的组合。
涂布层的成份包括丙稀酸树脂、立德粉及去离子水，各自占的重量份数是：丙稀酸树脂40，立德粉40，去离子水50。
其加工步骤是：
空心玻璃珠的粒度即颗粒的直径为等于或小于1微米。
粉煤灰的细度等于或大于200目。
立德粉的细度等于或大于600目。
基纸层的厚度为0.02～2毫米。
上述的具体实施方式仅是本发明的较佳实施例。需要指出的是，本行业的技术人员在本发明技术方案的指导下，可以做出一些变形与改良。这些变形与改良都是本发明保护的范围。
Claims (5)
1.一种比重小的石头纸，由基纸层及涂布层组成，涂布层涂覆于基纸层上；其特征在于：
基纸层由合成树脂和拌料组成，合成树脂的重量份数为15～30，拌料的重量份数为70～85；合成树脂为聚乳酸、或EVA、或PP、或PE或它们中的任意两种的组合；拌料为空心玻璃珠、或粉煤灰、或它们的组合；
涂布层的成份包括丙稀酸树脂、立德粉及去离子水，各自占的重量份数是：丙稀酸树脂20～40，立德粉20～40，去离子水30～50；
其加工步骤是：
、将拌料热烘脱水，使其中的水份含量的重量百分比小于或等于0.2%，并搅拌均匀；
2.根据权利要求1所述的一种比重小的石头纸，其特征在于：空心玻璃珠的粒度即颗粒的直径为等于或小于1微米。
3.根据权利要求1所述的一种比重小的石头纸，其特征在于：粉煤灰的细度等于或大于200目。
4.根据权利要求所述1的一种比重小的石头纸，其特征在于：立德粉的细度等于或大于600目。
5.根据权利要求所述1的一种比重小的石头纸，其特征在于：基纸层的厚度为0.02～2毫米。