CN105038537A - Waterproof corrosion-resistant coating used on roof - Google Patents
Waterproof corrosion-resistant coating used on roof Download PDFInfo
- Publication number
- CN105038537A CN105038537A CN201410604594.7A CN201410604594A CN105038537A CN 105038537 A CN105038537 A CN 105038537A CN 201410604594 A CN201410604594 A CN 201410604594A CN 105038537 A CN105038537 A CN 105038537A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- pressure
- roof
- resistant coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof corrosion-resistant coating used on roof, wherein the coating includes following raw materials: 40-44 parts of short oil alkyd resin, 10-12 parts of dimethyl benzene, 2-4 parts of zinc stearate, 5-6 parts of lime slurry, 2.5-4.5 parts of organic soil, 5-7 parts of sodium-based bentonite, 0.4-0.8 parts of defoaming agent, 0.2-0.8 parts of a flatting agent, 0.2-0.4 parts of organic tin drier, 2-4 parts of a suspending agent, 1.5-2.5 parts of lignin sulfonic acid, 1-2 parts of ethyl acetate, 2-4 parts of sodium borate, 5-7 parts of water-soluble urea-formaldehyde resin adhesive, 1-2 parts of nano-grade ceramic powder and 30-40 parts of deionized water. The coating, when being dried, can form a continuous coating layer, which is excellent in ductility and breaking strength, is good in resistance of acid and alkali, is excellent in weather resistance, is convenient to construct, is free of environment pollution, and is an excellent material used in roof waterproofing.
Description
Technical field
The present invention relates to architectural decoration coating material field, specifically belong to a kind of roof waterproof corrosion resistant coating.
Background technology
Coating refers to that a class is applied to body surface and can forms the general name of the material of tough and tensile protective membrane.Generally by be used for inner wall of building, exterior wall, ceiling and ground coating be called building coating.Building coating is an important class in coating.Building coating is by the type classification of base-material: can be divided into organic coating, inorganic paint, organic-inorganic composite coating.Solvent difference that organic coating uses due to it, is divided into again organic solvent type coatings and organic water borne (comprising water-latex type and water-soluble) coating two class.
For the coating on roof, raise variety much in market, but all have the shortcomings such as expensive, waterproof, corrosion resistant, environmental-protecting performance are poor, energy consumption is high, and various performance index parameter is not good.
Summary of the invention
The object of this invention is to provide a kind of roof waterproof corrosion resistant coating, successional coating can be formed after dried coating film, coating has good unit elongation and breaking tenacity, acidproof, alkali resistance good, have excellent weather resistance, easy construction, non-environmental-pollution, as roof waterproof use be a kind of comparatively ideal material.
The technical solution used in the present invention is as follows:
A kind of roof waterproof corrosion resistant coating, by weight, is made up of following raw material:
Short-oil alkyd 40-44, dimethylbenzene 10-12, Zinic stearas 2-4, lime white 5-6, organophilic clay 2.5-4.5, sodium bentonite 5-7, defoamer 0.4-0.8, flow agent 0.2-0.8, organotin siccative 0.2-0.4, suspension agent 2-4, lignosulfonic acid 1.5-2.5, ethyl acetate 1-2, Sodium Tetraborate 2-4, water-soluble urea-formaldehyde resin glue 5-7, nanometer scale ceramics powder 1-2, deionized water 30-40;
Its concrete preparation method is as follows:
Each component mixes by weight, and fully stirs, and then leaves standstill 40-60min, then be slowly heated to 75-85 DEG C and fully stir, carry out vacuum, boosting, constant temperature and pressure and buck stage again, the parameter in each stage and process are: vacuum: 0 ~ 0.04MPa, and the pumpdown time is 0.8 ~ 0.9h; Boosting: 0.08 ~ 1.0MPa, pressure rising time is 1.2 ~ 1.8h; Constant temperature and pressure: 0.7MPa, constant voltage time is 3 ~ 5h, and thermostat temperature is 145 ~ 160 DEG C; Step-down: drop to normal pressure, dip time is 1.2 ~ 1.5h; Finally obtained finished product coating.
The present invention is with short-oil alkyd major ingredient, simultaneously with dimethylbenzene, Zinic stearas, lime white for auxiliary material, and make intermolecular adsorptive power stronger by vacuum, boosting, constant temperature and pressure and buck stage, successional coating can be formed after dried coating film, coating has good unit elongation and breaking tenacity, acidproof, alkali resistance good, have excellent weather resistance, easy construction, non-environmental-pollution, as roof waterproof use be a kind of comparatively ideal material.
Embodiment
A kind of roof waterproof corrosion resistant coating, is made up of following raw material:
Short-oil alkyd 40-44, dimethylbenzene 10-12, Zinic stearas 2-4, lime white 5-6, organophilic clay 2.5-4.5, sodium bentonite 5-7, defoamer 0.4-0.8, flow agent 0.2-0.8, organotin siccative 0.2-0.4, suspension agent 2-4, lignosulfonic acid 1.5-2.5, ethyl acetate 1-2, Sodium Tetraborate 2-4, water-soluble urea-formaldehyde resin glue 5-7, nanometer scale ceramics powder 1-2, deionized water 30-40;
Its concrete preparation method is as follows:
Each component mixes by weight, and fully stirs, and then leaves standstill 40-60min, then be slowly heated to 75-85 DEG C and fully stir, carry out vacuum, boosting, constant temperature and pressure and buck stage again, the parameter in each stage and process are: vacuum: 0 ~ 0.04MPa, and the pumpdown time is 0.8 ~ 0.9h; Boosting: 0.08 ~ 1.0MPa, pressure rising time is 1.2 ~ 1.8h; Constant temperature and pressure: 0.7MPa, constant voltage time is 3 ~ 5h, and thermostat temperature is 145 ~ 160 DEG C; Step-down: drop to normal pressure, dip time is 1.2 ~ 1.5h; Finally obtained finished product coating.
Claims (1)
1. a roof waterproof corrosion resistant coating, by weight, is characterized in that, is made up of following raw material:
Short-oil alkyd 40-44, dimethylbenzene 10-12, Zinic stearas 2-4, lime white 5-6, organophilic clay 2.5-4.5, sodium bentonite 5-7, defoamer 0.4-0.8, flow agent 0.2-0.8, organotin siccative 0.2-0.4, suspension agent 2-4, lignosulfonic acid 1.5-2.5, ethyl acetate 1-2, Sodium Tetraborate 2-4, water-soluble urea-formaldehyde resin glue 5-7, nanometer scale ceramics powder 1-2, deionized water 30-40;
Its concrete preparation method is as follows: each component mixes by weight, and fully stir, then 40-60min is left standstill, then be slowly heated to 75-85 DEG C and fully stir, carry out vacuum, boosting, constant temperature and pressure and buck stage again, the parameter in each stage and process are: vacuum: 0 ~ 0.04MPa, and the pumpdown time is 0.8 ~ 0.9h; Boosting: 0.08 ~ 1.0MPa, pressure rising time is 1.2 ~ 1.8h; Constant temperature and pressure: 0.7MPa, constant voltage time is 3 ~ 5h, and thermostat temperature is 145 ~ 160 DEG C; Step-down: drop to normal pressure, dip time is 1.2 ~ 1.5h; Finally obtained finished product coating.