CN106045450A - Decorating coating for indoor wall - Google Patents
Decorating coating for indoor wall Download PDFInfo
- Publication number
- CN106045450A CN106045450A CN201610358781.0A CN201610358781A CN106045450A CN 106045450 A CN106045450 A CN 106045450A CN 201610358781 A CN201610358781 A CN 201610358781A CN 106045450 A CN106045450 A CN 106045450A
- Authority
- CN
- China
- Prior art keywords
- parts
- calcium
- water
- temperature
- quartz
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses decorating coating for an indoor wall. The decorating coating comprises, by weight, 32-35 parts of river sand particles, 5-8 parts of coal cinder, 4-6 parts of light concrete, 5-7 parts of latex powder, 3-5 parts of fly ash, 2-4 parts of hematite, 1-3 parts of quartz, 3-5 parts of calcium silicate, 2-3 parts of magnesium oxide, 3-5 parts of maize yellow, 2-4 parts of benzoic acid, 4-6 parts of silica sol, 0.5-0.8 part of wooden-calcium, 8-10 parts of water reducing agent and 50-60 parts of water. By the arrangement, the decorating coating is good in adhering force, less prone to falling, visually attractive, low in manufacturing cost, simple and practical.
Description
Technical field
The present invention relates to building materials field, particularly belong to a kind of indoor wall decorative paint.
Background technology
For beautifying the environment in family, traditional mode is wallpaper on the wall, wallpaper is of long duration there will be fade, viscous
Knot power is poor, easy to crack, even comes off.It is coated with the various coating with aesthetic feeling color, especially at present on indoor body of wall
It is poor with the cohesive force of cement indoor wall, big containing zest, it is hazardous to the human body, and cost is high, also directly affect knot
Close the performances such as intensity.
Summary of the invention
It is an object of the invention to provide a kind of indoor wall decorative paint, cohesive force is good, difficult drop-off, embossment visual appearance
Effect, cost of manufacture is low, the most practical.
Technical scheme is as follows:
A kind of indoor wall decorative paint, is made up of the following component of following weight portion meter: fluvial sand granule 32-35 part, coal slag
5-8 part, lightweight concrete 4-6 part, latex powder 5-7 part, flyash 3-5 part, bloodstone 2-4 part, quartz 1-3 part, calcium silicates 3-5
Part, magnesium oxide 2-3 part, maize 3-5 part, benzoic acid 2-4 part, Ludox 4-6 part, wood calcium 0.5-0.8 part, water reducer 8-10
Part, water 50-60 part；Its preparation method comprises the steps:
(1) coal slag, flyash, bloodstone, quartz, calcium silicates are inserted in pulverizer and pulverized fully, then inserted by ground product
Concentrating in concentration tank, thickening temperature is 2-4 DEG C, then concentrate carries out after dried at a temperature of 120-140 DEG C powder
Broken mix with maize, benzoic acid again, carry out steam pressure fermentation stage after mixing, boost phase: from 0.5 MPa～1 MPa, boosting
Process time is 0.5～0.8h；In the constant temperature and pressure stage: pressure remains 1 MPa, temperature remains 200～250 DEG C, and the time is
1.5～1.8h；Buck stage: drop to normal pressure from 1MPa, dip time is 1～2h, then it is standby to be ground into powder；
(2) after fluvial sand granule, lightweight concrete, latex powder, magnesium oxide, wood calcium and water mix and blend, slurry is obtained, at 60-80
Foamed time 60-70min at a temperature of DEG C；Foaming disposed slurry；
(3) being mixed with other remaining ingredients by the product obtained in above-mentioned steps (1), (2), in together adding agitator, stirring is mixed
Closing, and be heated to 90-110 DEG C, the persistent period is 1.5-2 h, is then poured out by the mixture in agitator, to obtain final product.
A kind of indoor wall decorative paint, is made up of the following component of following weight portion meter: fluvial sand granule 34 parts, coal slag
7 parts, lightweight concrete 5 parts, latex powder 6 parts, 4 parts of flyash, bloodstone 3 parts, 2 parts of quartz, calcium silicates 4 parts, magnesium oxide 2.5
Part, maize 4 parts, 3 parts of benzoic acid, Ludox 5 parts, wood calcium 0.6 part, water reducer 9 parts, 55 parts of water.
In the present invention, the cooperation of each material achieves preferable effect, and fire protecting performance is more preferable, and range of application is wider.The present invention adopts
Coordinate with benzoic acid, Ludox, containing latex powder, wood calcium etc. in product of the present invention, it to major part material such as timber, metal,
Glass, plastics, rubber, leather, pottery, fiber etc. have good bonding force.Product after solidification, has excellent chemically-resistant
Corrosivity, thermostability, resistance to acids and bases and good electrical insulating property, have good adhesive force, anticorrosive property and mechanical strength；This
Invention is containing particulate matter, and it is attractive in appearance etc. that brushing presents the art of embossment on interior wall.
The present invention uses technique scheme to provide indoor wall decorative paint, and cohesive force is good, difficult drop-off, and vision is beautiful
Seeing, cost of manufacture is low, the most practical.
Detailed description of the invention
A kind of indoor wall decorative paint, is made up of the following component of following weight portion meter: fluvial sand granule 34 parts, coal slag
7 parts, lightweight concrete 5 parts, latex powder 6 parts, 4 parts of flyash, bloodstone 3 parts, 2 parts of quartz, calcium silicates 4 parts, magnesium oxide 2.5
Part, maize 4 parts, 3 parts of benzoic acid, Ludox 5 parts, wood calcium 0.6 part, water reducer 9 parts, 55 parts of water；Its preparation method include as
Lower step:
(1) coal slag, flyash, bloodstone, quartz, calcium silicates are inserted in pulverizer and pulverized fully, then inserted by ground product
Concentrating in concentration tank, thickening temperature is 2-4 DEG C, then concentrate carries out after dried at a temperature of 120-140 DEG C powder
Broken mix with maize, benzoic acid again, carry out steam pressure fermentation stage after mixing, boost phase: from 0.5MPa～1MPa, liter presses through
The journey time is 0.5～0.8h；In the constant temperature and pressure stage: pressure remains 1MPa, temperature remains 200～250 DEG C, and the time is 1.5
～1.8h；Buck stage: drop to normal pressure from 1MPa, dip time is 1～2h, then it is standby to be ground into powder；
(2) after fluvial sand granule, lightweight concrete, latex powder, magnesium oxide, wood calcium and water mix and blend, slurry is obtained, at 60-80
Foamed time 60-70min at a temperature of DEG C；Foaming disposed slurry；
(3) being mixed with other remaining ingredients by the product obtained in above-mentioned steps (1), (2), in together adding agitator, stirring is mixed
Closing, and be heated to 90-110 DEG C, the persistent period is 1.5-2h, is then poured out by the mixture in agitator, to obtain final product.
Claims (2)
1. an indoor wall decorative paint, it is characterised in that be made up of the following component of following weight portion meter: fluvial sand granule
32-35 part, coal slag 5-8 part, lightweight concrete 4-6 part, latex powder 5-7 part, flyash 3-5 part, bloodstone 2-4 part, quartz
1-3 part, calcium silicates 3-5 part, magnesium oxide 2-3 part, maize 3-5 part, benzoic acid 2-4 part, Ludox 4-6 part, wood calcium 0.5-
0.8 part, water reducer 8-10 part, water 50-60 part；Its preparation method comprises the steps:
(1) coal slag, flyash, bloodstone, quartz, calcium silicates are inserted in pulverizer and pulverized fully, then inserted by ground product
Concentrating in concentration tank, thickening temperature is 2-4 DEG C, then concentrate carries out after dried at a temperature of 120-140 DEG C powder
Broken, finally mix with maize, benzoic acid, carry out steam pressure fermentation stage after mixing, boost phase: from 0.5 MPa～1 MPa,
The boost process time is 0.5～0.8h；In the constant temperature and pressure stage: pressure remains 1 MPa, temperature remains 200～250 DEG C, time
Between be 1.5～1.8h；Buck stage: drop to normal pressure from 1MPa, dip time is 1～2h, then it is standby to be ground into powder；
(2) after fluvial sand granule, lightweight concrete, latex powder, magnesium oxide, wood calcium and water mix and blend, slurry is obtained, at 60-80
Foamed time 60-70min at a temperature of DEG C；Foaming disposed slurry；
(3) being mixed with other remaining ingredients by the product obtained in above-mentioned steps (1), (2), in together adding agitator, stirring is mixed
Closing, and be heated to 90-110 DEG C, the persistent period is 1.5-2 h, is then poured out by the mixture in agitator, to obtain final product.
Indoor wall decorative paint the most according to claim 1, it is characterised in that by the following component of following weight portion meter
Composition: fluvial sand granule 34 parts, coal slag 7 parts, lightweight concrete 5 parts, latex powder 6 parts, 4 parts of flyash, bloodstone 3 parts, quartz 2
Part, calcium silicates 4 parts, magnesium oxide 2.5 parts, maize 4 parts, 3 parts of benzoic acid, Ludox 5 parts, wood calcium 0.6 part, water reducer 9 parts, water
55 parts.