CN104909693A - 一种适合外墙材料的环保保温砂浆及其制备方法 - Google Patents

一种适合外墙材料的环保保温砂浆及其制备方法 Download PDF

Info

Publication number
CN104909693A
CN104909693A CN201510283117.XA CN201510283117A CN104909693A CN 104909693 A CN104909693 A CN 104909693A CN 201510283117 A CN201510283117 A CN 201510283117A CN 104909693 A CN104909693 A CN 104909693A
Authority
CN
China
Prior art keywords
parts
powder
environmentally friendly
minute
wall material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510283117.XA
Other languages
English (en)
Inventor
黄二华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Rui He Decorative Engineering Co Ltd
Original Assignee
Hefei Rui He Decorative Engineering Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Rui He Decorative Engineering Co Ltd filed Critical Hefei Rui He Decorative Engineering Co Ltd
Priority to CN201510283117.XA priority Critical patent/CN104909693A/zh
Publication of CN104909693A publication Critical patent/CN104909693A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种适合外墙材料的环保保温砂浆，其特征在于，由下列重量份的原料制备制成：玻化微珠40-45、聚苯乙烯泡沫微粒2-3、轻烧氧化镁4-6、亚麻纤维2-3、聚丙烯纤维1-2、普通硅酸盐水泥30-35、红土12-14、建筑胶粉2-3、高温煅烧石膏6-8、羟丙甲纤维素1-2、十二烷基二甲基氧化胺1-2、增效剂8-10；本发明配方合理，将玻化微珠、聚苯颗粒等多种保温材料添加到本发明中，添加红土，密度低，强度高；添加增效剂，具有良好的抗裂性以及耐高温性能，能够增强产品的抗裂防火阻燃性，采用农作物秸秆为基料，节能环保；本发明燃烧级别高，保温效果高，施工简单，使用时兑水搅拌均匀即可使用。

Description

一种适合外墙材料的环保保温砂浆及其制备方法
技术领域
本发明涉及建筑保温材料领域，特别是一种适合外墙材料的环保保温砂浆及其制备方法。
背景技术
外墙保温***在现代建筑尤其是高层建筑中起到了相当重要的作用，但外墙保温***一般使用普通膨胀珍珠岩和聚苯颗粒作为保温砂浆轻骨料，保温效果及施工方法仍有改进空间。近年来外墙外保温工程的推广应用，对节能减排政策的落实起到积极的作用。但是在工程施工过程中也暴露出了一定的问题，特别是保温材料的防火安全，尤其是高层建筑保温工程施工中的防火安全问题更为突出。本发明在配方中添加玻化微珠、聚苯颗粒等混合，融合多种类型保温材料的优点，通过添加特殊工艺制程的在增效剂，具有良好的抗裂性以及耐高温性能，能够增强产品的抗裂防火阻燃性，同时采用农作物秸秆为基料，节能环保。
发明内容
本发明的目的是提供一种适合外墙材料的环保保温砂浆及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种适合外墙材料的环保保温砂浆，由下列重量份的原料制备制成：玻化微珠40-45、聚苯乙烯泡沫微粒2-3、轻烧氧化镁4-6、亚麻纤维2-3、聚丙烯纤维1-2、普通硅酸盐水泥30-35、红土12-14、建筑胶粉2-3、高温煅烧石膏6-8、羟丙甲纤维素1-2、十二烷基二甲基氧化胺1-2、增效剂8-10；
所述增效剂由以下重量份的原料制备而成：农作物秸秆45-50、水性聚氨酯20-24、碳化硅3-5、聚丙烯纤维2-3、丙烯酸甲酯7-9、油酸丁酯4-6、氢氧化铝4-5、200目莫来粉7-9、聚乙二醇3-5、环氧大豆油2-3、羟丙基甲基纤维素醚 1-2、水20-25；制备方法如下：首先将农作物秸秆干燥后粉碎成100-200目粉末，与氢氧化铝、200目莫来粉、碳化硅、聚丙烯纤维混合均匀形成混合粉料，然后将聚乙二醇溶于水中，加入丙烯酸乙酯、油酸丁酯，加热至50℃-60℃，反应1-1.5小时，冷却至室温，加入其余剩余成分，以300-400转/分的速度搅拌8-10分钟后加入混合粉料，以500-600转/分的速度搅拌20-30分钟得到混合浆料，最后将混合浆料泵入喷雾干燥设备中，控制进风温度 120-150℃、出风温度 80-100℃，即可制成增效剂。
本发明所述一种适合外墙材料的环保保温砂浆，由以下具体步骤制成：首先将轻烧氧化镁、高温煅烧石膏、红土混合后研磨40-60分钟，形成200-300目粉末，然后与其他剩余成分混合，加入到双轴卧式搅拌釜中，以300-400转/分钟匀速搅拌15-20分钟，包装即得到保温砂浆预拌料。
本发明的有益效果是：本发明配方合理，将玻化微珠、聚苯颗粒等多种保温材料添加到本发明中，添加红土，密度低，强度高；添加增效剂，具有良好的抗裂性以及耐高温性能，能够增强产品的抗裂防火阻燃性，采用农作物秸秆为基料，节能环保；本发明燃烧级别高，保温效果高，施工简单，使用时兑水搅拌均匀即可使用。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种适合外墙材料的环保保温砂浆，由下列重量份（公斤）的原料制备制成：玻化微珠40、聚苯乙烯泡沫微粒2、轻烧氧化镁4、亚麻纤维2、聚丙烯纤维1、普通硅酸盐水泥30、红土12、建筑胶粉2、高温煅烧石膏6、羟丙甲纤维素1、十二烷基二甲基氧化胺1、增效剂8；
所述增效剂由以下重量份（公斤）的原料制备而成：农作物秸秆45、水性聚氨酯20、碳化硅3、聚丙烯纤维2、丙烯酸甲酯7、油酸丁酯4、氢氧化铝4、200目莫来粉7、聚乙二醇3、环氧大豆油2、羟丙基甲基纤维素醚 1、水20；制备方法如下：首先将农作物秸秆干燥后粉碎成100-200目粉末，与氢氧化铝、200目莫来粉、碳化硅、聚丙烯纤维混合均匀形成混合粉料，然后将聚乙二醇溶于水中，加入丙烯酸乙酯、油酸丁酯，加热至50℃-60℃，反应1-1.5小时，冷却至室温，加入其余剩余成分，以300-400转/分的速度搅拌8-10分钟后加入混合粉料，以500-600转/分的速度搅拌20-30分钟得到混合浆料，最后将混合浆料泵入喷雾干燥设备中，控制进风温度 120-150℃、出风温度 80-100℃，即可制成增效剂。
本发明所述一种适合外墙材料的环保保温砂浆，由以下具体步骤制成：首先将轻烧氧化镁、高温煅烧石膏、红土混合后研磨40-60分钟，形成200-300目粉末，然后与其他剩余成分混合，加入到双轴卧式搅拌釜中，以300-400转/分钟匀速搅拌15-20分钟，包装即得到保温砂浆预拌料。
本发明保温砂浆采用现配现用的方式，使用时将保温砂浆加入0.8倍量的水搅拌均匀形成膏状物质即可使用。
经各种试验测定，本发明保温砂浆各项性能为 ：堆积密度为272kg/m3，导热系数为0.057W/m.K，抗压强度为0.24Mpa，线性收缩率为0.28%。

Claims (2)

1.一种适合外墙材料的环保保温砂浆，其特征在于，由下列重量份的原料制备制成：玻化微珠40-45、聚苯乙烯泡沫微粒2-3、轻烧氧化镁4-6、亚麻纤维2-3、聚丙烯纤维1-2、普通硅酸盐水泥30-35、红土12-14、建筑胶粉2-3、高温煅烧石膏6-8、羟丙甲纤维素1-2、十二烷基二甲基氧化胺1-2、增效剂8-10；
所述增效剂由以下重量份的原料制备而成：农作物秸秆45-50、水性聚氨酯20-24、碳化硅3-5、聚丙烯纤维2-3、丙烯酸甲酯7-9、油酸丁酯4-6、氢氧化铝4-5、200目莫来粉7-9、聚乙二醇3-5、环氧大豆油2-3、羟丙基甲基纤维素醚 1-2、水20-25；制备方法如下：首先将农作物秸秆干燥后粉碎成100-200目粉末，与氢氧化铝、200目莫来粉、碳化硅、聚丙烯纤维混合均匀形成混合粉料，然后将聚乙二醇溶于水中，加入丙烯酸乙酯、油酸丁酯，加热至50℃-60℃，反应1-1.5小时，冷却至室温，加入其余剩余成分，以300-400转/分的速度搅拌8-10分钟后加入混合粉料，以500-600转/分的速度搅拌20-30分钟得到混合浆料，最后将混合浆料泵入喷雾干燥设备中，控制进风温度 120-150℃、出风温度 80-100℃，即可制成增效剂。
2.根据权利要求1所述一种适合外墙材料的环保保温砂浆，其特征在于，由以下具体步骤制成：首先将轻烧氧化镁、高温煅烧石膏、红土混合后研磨40-60分钟，形成200-300目粉末，然后与其他剩余成分混合，加入到双轴卧式搅拌釜中，以300-400转/分钟匀速搅拌15-20分钟，包装即得到保温砂浆预拌料。
CN201510283117.XA 2015-05-29 2015-05-29 一种适合外墙材料的环保保温砂浆及其制备方法 Pending CN104909693A (zh)