CN104909692A - 一种防霉防蛀混合型保温砂浆及其制备方法 - Google Patents
一种防霉防蛀混合型保温砂浆及其制备方法 Download PDFInfo
- Publication number
- CN104909692A CN104909692A CN201510282798.8A CN201510282798A CN104909692A CN 104909692 A CN104909692 A CN 104909692A CN 201510282798 A CN201510282798 A CN 201510282798A CN 104909692 A CN104909692 A CN 104909692A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- thermal insulation
- moth
- insulation mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防霉防蛀混合型保温砂浆，其特征在于，由下列重量份的原料制备制成：水泥34-38、石膏10-13、玻化微珠20-23、VAE可再分散性乳胶粉2-4、木质素磺酸钠0.6-0.8、羟乙基纤维素1-1.5、樟木油0.05-0.1、黄原胶2-4、重钙13-15、膨胀石墨6-8、石棉粉2-3、硫酸铜1-1.5、增效剂8-10；本发明在普通玻化微珠保温砂浆的基础上，添加樟木油具有防虫蛀功效，硫酸铜防霉变，添加膨胀石墨，具有良好的润滑性，增加流动性以及砂浆的和易性，提高了施工性能；添加增效剂，增强了产品的防火、抗裂、耐高温性能；本发明防霉防虫蛀防水，耐老化性能好，施工简单，便于操作。
Description
技术领域
本发明涉及建筑保温材料领域，特别是一种防霉防蛀混合型保温砂浆及其制备方法。
背景技术
近年来外墙外保温工程的推广应用，对节能减排政策的落实起到积极的作用，尤其是高层建筑保温工程施工中的防火安全问题更为突出，这就为无机不燃保温砂浆的工程应用提供了前所未有的契机。无机保温砂浆为无机胶凝材料、适当比例的轻骨料，并填加可再分散乳胶粉、纤维素醚等外加剂混合制成。现有无机胶凝材料浆体施工后内部含气量低，而且防水性能不理想，从而导致无机保温砂浆遇水后保温性能大大下降，久而久之产生霉变以及虫蛀。
现有的保温砂浆不仅需要具有除基本的保温隔热功能外，还希望可以通过复合添加剂的调整，还具有其他功能，如防水、耐火、防霉、防蛀等。本发明在普通保温砂浆的基础上，添加樟木油具有防虫蛀功效，硫酸铜防霉变，添加膨胀石墨，具有良好的润滑性，增加流动性以及砂浆的和易性，提高了施工性能；添加增效剂，提高了阻燃防火性，抗裂性以及耐高温性能。
发明内容
本发明的目的是提供一种防霉防蛀混合型保温砂浆及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种防霉防蛀混合型保温砂浆，由下列重量份的原料制备制成：水泥34-38、石膏10-13、玻化微珠20-23、VAE可再分散性乳胶粉2-4、木质素磺酸钠0.6-0.8、羟乙基纤维素1-1.5、樟木油0.05-0.1、黄原胶2-4、重钙13-15、膨胀石墨6-8、石棉粉2-3、硫酸铜1-1.5、增效剂8-10；
所述增效剂由以下重量份的原料制备而成：农作物秸秆45-50、水性聚氨酯20-24、碳化硅3-5、聚丙烯纤维2-3、丙烯酸甲酯7-9、油酸丁酯4-6、氢氧化铝4-5、200目莫来粉7-9、聚乙二醇3-5、环氧大豆油2-3、羟丙基甲基纤维素醚 1-2、水20-25；制备方法如下：首先将农作物秸秆干燥后粉碎成100-200目粉末，与氢氧化铝、200目莫来粉、碳化硅、聚丙烯纤维混合均匀形成混合粉料，然后将聚乙二醇溶于水中，加入丙烯酸乙酯、油酸丁酯，加热至50℃-60℃，反应1-1.5小时，冷却至室温，加入其余剩余成分，以300-400转/分的速度搅拌8-10分钟后加入混合粉料，以500-600转/分的速度搅拌20-30分钟得到混合浆料，最后将混合浆料泵入喷雾干燥设备中，控制进风温度 120-150℃、出风温度 80-100℃，即可制成增效剂。
本发明所述一种防霉防蛀混合型保温砂浆，由以下具体步骤制成：首先将重钙、膨胀石墨、石棉粉混合后研磨40-60分钟，形成200-300目粉末，然后与其他剩余成分混合，加入到双轴卧式搅拌釜中，以300-400转/分钟匀速搅拌15-20分钟，包装即得到保温砂浆预拌料。
本发明的有益效果是：本发明在普通玻化微珠保温砂浆的基础上，添加樟木油具有防虫蛀功效，硫酸铜防霉变，添加膨胀石墨，具有良好的润滑性，增加流动性以及砂浆的和易性，提高了施工性能；添加增效剂，具有良好的抗裂性以及耐高温性能，能够增强产品的抗裂防火阻燃性，采用农作物秸秆为基料，节能环保；本发明防霉防虫蛀防水，耐老化性能好，施工简单，便于操作。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种防霉防蛀混合型保温砂浆，由下列重量份（公斤）的原料制备制成：水泥34、石膏10、玻化微珠20、VAE可再分散性乳胶粉2、木质素磺酸钠0.6、羟乙基纤维素1、樟木油0.05、黄原胶2、重钙13、膨胀石墨6、石棉粉2、硫酸铜1、增效剂8；
所述增效剂由以下重量份（公斤）的原料制备而成：农作物秸秆45、水性聚氨酯20、碳化硅3、聚丙烯纤维2、丙烯酸甲酯7、油酸丁酯4、氢氧化铝4、200目莫来粉7、聚乙二醇3、环氧大豆油2、羟丙基甲基纤维素醚 1、水20；制备方法如下：首先将农作物秸秆干燥后粉碎成100-200目粉末，与氢氧化铝、200目莫来粉、碳化硅、聚丙烯纤维混合均匀形成混合粉料，然后将聚乙二醇溶于水中，加入丙烯酸乙酯、油酸丁酯，加热至50℃-60℃，反应1-1.5小时，冷却至室温，加入其余剩余成分，以300-400转/分的速度搅拌8-10分钟后加入混合粉料，以500-600转/分的速度搅拌20-30分钟得到混合浆料，最后将混合浆料泵入喷雾干燥设备中，控制进风温度 120-150℃、出风温度 80-100℃，即可制成增效剂。
本发明所述一种防霉防蛀混合型保温砂浆，由以下具体步骤制成：首先将重钙、膨胀石墨、石棉粉混合后研磨40-60分钟，形成200-300目粉末，然后与其他剩余成分混合，加入到双轴卧式搅拌釜中，以300-400转/分钟匀速搅拌15-20分钟，包装即得到保温砂浆预拌料。
本发明保温砂浆采用现配现用的方式，使用时将保温砂浆加入0.8倍量的水搅拌均匀形成膏状物质即可使用。
经各种试验测定，本发明保温砂浆各项性能为 ：堆积密度为271 kg/m3，导热系数为0.051W/m.K，抗压强度为0.32Mpa，线性收缩率为0.26%。
Claims (2)
1.一种防霉防蛀混合型保温砂浆，其特征在于，由下列重量份的原料制备制成：水泥34-38、石膏10-13、玻化微珠20-23、VAE可再分散性乳胶粉2-4、木质素磺酸钠0.6-0.8、羟乙基纤维素1-1.5、樟木油0.05-0.1、黄原胶2-4、重钙13-15、膨胀石墨6-8、石棉粉2-3、硫酸铜1-1.5、增效剂8-10；
所述增效剂由以下重量份的原料制备而成：农作物秸秆45-50、水性聚氨酯20-24、碳化硅3-5、聚丙烯纤维2-3、丙烯酸甲酯7-9、油酸丁酯4-6、氢氧化铝4-5、200目莫来粉7-9、聚乙二醇3-5、环氧大豆油2-3、羟丙基甲基纤维素醚 1-2、水20-25；制备方法如下：首先将农作物秸秆干燥后粉碎成100-200目粉末，与氢氧化铝、200目莫来粉、碳化硅、聚丙烯纤维混合均匀形成混合粉料，然后将聚乙二醇溶于水中，加入丙烯酸乙酯、油酸丁酯，加热至50℃-60℃，反应1-1.5小时，冷却至室温，加入其余剩余成分，以300-400转/分的速度搅拌8-10分钟后加入混合粉料，以500-600转/分的速度搅拌20-30分钟得到混合浆料，最后将混合浆料泵入喷雾干燥设备中，控制进风温度 120-150℃、出风温度 80-100℃，即可制成增效剂。
2.根据权利要求1所述一种防霉防蛀混合型保温砂浆，其特征在于，由以下具体步骤制成：首先将重钙、膨胀石墨、石棉粉混合后研磨40-60分钟，形成200-300目粉末，然后与其他剩余成分混合，加入到双轴卧式搅拌釜中，以300-400转/分钟匀速搅拌15-20分钟，包装即得到保温砂浆预拌料。