CN104261754B - 一种建材废渣生产的墙体保温材料及其制备方法 - Google Patents

一种建材废渣生产的墙体保温材料及其制备方法 Download PDF

Info

Publication number
CN104261754B
CN104261754B CN201410436226.6A CN201410436226A CN104261754B CN 104261754 B CN104261754 B CN 104261754B CN 201410436226 A CN201410436226 A CN 201410436226A CN 104261754 B CN104261754 B CN 104261754B
Authority
CN
China
Prior art keywords
waste residue
building materials
heat insulation
add
insulation material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410436226.6A
Other languages
English (en)
Other versions
CN104261754A (zh
Inventor
李根固
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Huiming Construction Group Co Ltd
Original Assignee
Anhui Huiming Construction Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Huiming Construction Group Co Ltd filed Critical Anhui Huiming Construction Group Co Ltd
Priority to CN201410436226.6A priority Critical patent/CN104261754B/zh
Publication of CN104261754A publication Critical patent/CN104261754A/zh
Application granted granted Critical
Publication of CN104261754B publication Critical patent/CN104261754B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种建材废渣生产的墙体保温材料，其是由下述重量份的原料制得：改性建材废渣5-15，白水泥80-100，浮石70-90，凹凸棒土粉10-15，竹炭粉2-4，单烷基醚磷酸酯1-2，硅丙乳液10-15，草酸钠1-2，甘露醇1-3，麦芽糖醇0.5-1，羟丙基甲基纤维素醚2-4；本发明的墙体保温材料合理回收利用建材废渣生产墙体保温材料，在保证保温隔热效果的前提下，达到节能环保的目的。

Description

一种建材废渣生产的墙体保温材料及其制备方法
技术领域
本发明涉及建筑材料领域，具体涉及一种建材废渣生产的墙体保温材料及其制备方法。
背景技术
墙体保温材料作为影响建筑节能一个重要因素，其开发与应用已经越来越受到世界各国的普遍重视。合理开发墙体保温材料，有效再回收利用建筑工业产生的废渣废料，既能大量节约墙体材料，又能达到节约资源，减少环境污染的目的，符合国家节能环保的政策。
发明内容
本发明的目的是提供一种建材废渣生产的墙体保温材料。
本发明是通过以下技术方案实现的：
一种建材废渣生产的墙体保温材料，其是由下述重量份的原料制得：
改性建材废渣5-15，白水泥80-100，浮石70-90，凹凸棒土粉10-15，竹炭粉2-4，单烷基醚磷酸酯1-2，硅丙乳液10-15，草酸钠1-2，甘露醇1-3，麦芽糖醇0.5-1，羟丙基甲基纤维素醚2-4；
改性建材废渣由下列重量份的原料制成：
陶瓷废渣5-10，大理石废渣10-15，硼石膏1-2，液体石蜡0.5-1.5，油酸0.2-0.5，三异丙醇胺1-2，酒石酸钠1-3，铝酸酯偶联剂0.2-0.5；
改性建材废渣的制备方法是：
将陶瓷废渣、大理石废渣和硼石膏混合后800-1000℃煅烧2-4h，冷却后加入适量4-6%醋酸溶液，加入三异丙醇胺和酒石酸钠，200-400r/min搅拌1-2h，干燥后研磨均匀，过50-100目筛，再加入铝酸酯偶联剂，100-150℃，400-600r/min搅拌20-40min，加入液体石蜡和油酸，同样条件下搅拌20-40min，即得；
一种建材废渣生产的墙体保温材料的制备方法，包括以下步骤：
（1）将硅丙乳液、单烷基醚磷酸酯和羟丙基甲基纤维素醚混合后800-1000r/min搅拌15-30min，喷雾干燥后得到活性粉体；
（2）将凹凸棒土粉和竹炭粉混合后400-600℃煅烧1-2h，冷却后加入甘露醇、麦芽糖醇和草酸钠，混合后研磨均匀，过100-200目筛，加入活性粉体和其余原料，搅拌均匀后分装，即得。
本发明的优点是：
1.合理回收利用建材废渣生产墙体保温材料，节约资源，减少环境污染与生态破坏的隐患；
2.耐水、耐腐蚀性好，使用寿命长，耐候性好；
3.产品质量稳定，适用于多种使用环境。
具体实施方式
本发明非限定实施例如下：
实施例1
一种建材废渣生产的墙体保温材料，由下列重量(kg)的组分原料制备而成：
改性建材废渣10，白水泥90，浮石80，凹凸棒土粉12，竹炭粉3，单烷基醚磷酸酯1.5，硅丙乳液12，草酸钠1.5，甘露醇2，麦芽糖醇0.8，羟丙基甲基纤维素醚3；
其中，改性建材废渣由下列重量（kg）的原料制成：
陶瓷废渣7，大理石废渣12，硼石膏1.5，液体石蜡1，油酸0.3，三异丙醇胺1.5，酒石酸钠2，铝酸酯偶联剂0.4；
改性建材废渣的制备方法：
将陶瓷废渣、大理石废渣和硼石膏混合后800℃煅烧3h，冷却后加入适量4%醋酸溶液，加入三异丙醇胺和酒石酸钠，200r/min搅拌2h，干燥后研磨均匀，过100目筛，再加入铝酸酯偶联剂，100℃，600r/min搅拌30min，加入液体石蜡和油酸，同样条件下搅拌30min，即得。
建材废渣生产的墙体保温材料的制备方法包括以下步骤：
（1）将硅丙乳液、单烷基醚磷酸酯和羟丙基甲基纤维素醚混合后1000r/min搅拌15min，喷雾干燥后得到活性粉体；
（2）将凹凸棒土粉和竹炭粉混合后400℃煅烧2h，冷却后加入甘露醇、麦芽糖醇和草酸钠，混合后研磨均匀，过100目筛，加入活性粉体和其余原料，搅拌均匀后分装，即得。
实施例为干粉材料，使用时需在施工现场加水调制成料浆，即可施工。
依据DB34/T1279-2010进行产品性能测试，上述实施的测试结果如下：
干表观密度（kg/m3）：283；
线性收缩率（%）：0.15；
抗压强度（MPa）：0.97；
粘结强度（KPa）：85；
导热系数（w/m﹒k）：0.062；
软化系数：0.63。

Claims (1)

1.一种建材废渣生产的墙体保温材料，其特征在于，其是由下述重量份的原料制得：改性建材废渣5-15，白水泥80-100，浮石70-90，凹凸棒土粉10-15，竹炭粉2-4，单烷基醚磷酸酯1-2，硅丙乳液10-15，草酸钠1-2，甘露醇1-3，麦芽糖醇0.5-1，羟丙基甲基纤维素醚2-4；所述改性建材废渣由下列重量份的原料制成：陶瓷废渣5-10，大理石废渣10-15，硼石膏1-2，液体石蜡0.5-1.5，油酸0.2-0.5，三异丙醇胺1-2，酒石酸钠1-3，铝酸酯偶联剂0.2-0.5；
所述改性建材废渣的制备方法是：将陶瓷废渣、大理石废渣和硼石膏混合后800-1000℃煅烧2-4h，冷却后加入适量4-6%醋酸溶液，加入三异丙醇胺和酒石酸钠，200-400r/min搅拌1-2h，干燥后研磨均匀，过50-100目筛，再加入铝酸酯偶联剂，100-150℃，400-600r/min搅拌20-40min，加入液体石蜡和油酸，同样条件下搅拌20-40min，即得；
所述的一种建材废渣生产的墙体保温材料的制备方法，包括以下步骤：
（1）将硅丙乳液、单烷基醚磷酸酯和羟丙基甲基纤维素醚混合后800-1000r/min搅拌15-30min，喷雾干燥后得到活性粉体；
（2）将凹凸棒土粉和竹炭粉混合后400-600℃煅烧1-2h，冷却后加入甘露醇、麦芽糖醇和草酸钠，混合后研磨均匀，过100-200目筛，加入活性粉体和其余原料，搅拌均匀后分装，即得。
CN201410436226.6A 2014-08-29 2014-08-29 一种建材废渣生产的墙体保温材料及其制备方法 Expired - Fee Related CN104261754B (zh)