CN103570321A - 一种经济型无机保温砂浆及生产方法 - Google Patents
一种经济型无机保温砂浆及生产方法 Download PDFInfo
- Publication number
- CN103570321A CN103570321A CN201210280475.1A CN201210280475A CN103570321A CN 103570321 A CN103570321 A CN 103570321A CN 201210280475 A CN201210280475 A CN 201210280475A CN 103570321 A CN103570321 A CN 103570321A
- Authority
- CN
- China
- Prior art keywords
- powder
- cement
- inorganic
- heat insulation
- mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种经济型无机保温砂浆及生产方法,其由无机胶凝材料、无机隔热骨料、有机添加剂三组分组成,各组分的重量配比为:无机胶凝材料50%~70%,无机隔热骨料30%~50%,有机添加剂0.8%~1.5%;无机胶凝材料为粉煤灰、矿渣粉、钢渣粉、石灰粉、石膏粉和水泥的混合物,有机添加剂为纤维素醚、可再分散胶粉、聚丙烯短纤维的混合物,重量配比为15%~25%∶70%~55%∶15%~20%。生产方法:将各原料按预定配比计量称重,然后将所有原料混合均匀,包装,即成。本发明之经济型无机保温砂浆不仅成本低,而且具有很好的保温隔热效果,用其抹面后,不会出现空鼓、开裂、龟裂、脱落等现象。
Description
技术领域
本发明涉及一种经济型墙体和屋面无机保温砂浆,具体地说,涉及一种低成本、无污染的建筑节能无机保温砂浆。
技术背景
目前,在墙体上使用的保温砂浆都是以水泥为主要胶凝材料,添加适当的有机添加剂而成,有的为提高和易性和粘结性在水泥中添加适当的粉煤灰和灰钙,我们知道水泥是高能耗、高污染产品,而保温砂浆是用量很大的一种产品。同时,工业废料如粉煤灰、脱硫石膏、钢渣、矿渣等作为大宗工业废渣,它的处理和综合利用已陪受世界各国关注。
发明内容
本发明的目的在于提供一种生产能耗低,成本低,保温效果好的无机保温砂浆,用其抹面后,不会出现空鼓、开裂、龟裂、脱落等现象,同时提高墙体的保温性能。
本发明的目的是通过下述方案实现的:其由无机胶凝材料、无机隔热骨料、有机添加剂三组分组成,各组分的重量配比为:无机胶凝材料50%~70%,无机隔热骨料30%~50%,有机添加剂0.8%~1.5%。
无机胶凝材料为粉煤灰、矿渣粉、钢渣粉、石灰粉、石膏粉和水泥的混合物,他们的重量配比为粉煤灰∶(矿渣粉+钢渣粉)∶(石膏粉+石灰粉+水泥)=40%~70%∶15%~30%∶15%~30%。
粉煤灰为电厂的一级、二级粉煤灰,或磨细的湿排灰及低等灰,矿渣粉与钢渣粉重量配比0%~100%∶100%~0%,石膏粉为天然二水石膏粉、或脱硫石膏粉、或硬石膏粉,粉末粒度60目~500目,水泥为水泥熟料或各种32.5以上标号水泥,石膏粉∶石灰∶水泥重量配比为20%~30%∶30%~50%∶20%~40%。
无机隔热骨料为膨胀玻化微珠、膨胀珍珠岩、海泡石、蛭石、陶粒、空心玻璃微珠中一种或几种的混合物,有机添加剂为纤维素醚、可再分散胶粉、聚丙烯短纤维的混合物,纤维素醚的分子量一般不少于10万,聚丙烯短纤维的长度在6mm~9mm之间,纤维素醚、可再分散胶粉、聚丙烯短纤维重量配比为15%~25%∶70%~55%∶15%~20%。
经济型无机保温砂浆及生产方法,将各原料按预定配比计量混合均匀,包装,即成。
具体实施方式
实施例1:
二级粉煤灰360公斤,矿渣粉120公斤,石灰48公斤,脱硫石膏30公斤,42.5号水泥36公斤,膨胀玻化微珠400公斤,20万分子量的纤维素醚2.5公斤,可再分散胶粉10公斤,9毫米长聚丙烯短纤维2公斤,混合包装。
检测结果
实施例2:
二级粉煤灰300公斤,矿渣粉100公斤,钢渣粉80公斤,石灰50公斤,脱硫石膏40公斤,42.5号水泥24公斤,膨胀玻化微珠400公斤,20万分子量的纤维素醚2.5公斤,可再分散胶粉10公斤,9毫米长聚丙烯短纤维2公斤,混合包装。
检测结果
实施例3:
二级粉煤灰310公斤,矿渣粉100公斤,钢渣粉20公斤,石灰30公斤,脱硫石膏54公斤,42.5号水泥30公斤,膨胀玻化微珠450公斤,20万分子量的纤维素醚2公斤,可再分散胶粉10公斤,9毫米长聚丙烯短纤维2公斤,混合包装。
检测结果
实施例4:
二级粉煤灰360公斤,矿渣粉120公斤,石灰48公斤,脱硫石膏30公斤,42.5号水泥36公斤,膨胀玻化微珠400公斤,20万分子量的纤维素醚1.5公斤,可再分散胶粉13公斤,9毫米长聚丙烯短纤维1.5公斤,混合包装。
检测结果
Claims (5)
1.一种经济型无机保温砂浆,其特征在于,其由无机胶凝材料、无机隔热骨料、有机添加剂三组分组成,各组分的重量配比为:无机胶凝材料50%~70%,无机隔热骨料30%~50%,有机添加剂0.8%~1.5%。
2.根据权利要求1所述无机胶凝材料为粉煤灰、矿渣粉、钢渣粉、石灰粉、石膏粉和水泥的混合物,他们的重量配比为粉煤灰∶(矿渣粉+钢渣粉)∶(石膏粉+石灰粉+水泥)=40%~70%∶15%~30%∶15%~30%。
3.根据权利要求2所述的粉煤灰为电厂的一级、二级粉煤灰,或磨细的湿排灰及低等灰,矿渣粉与钢渣粉重量配比0%~100%∶100%~0%,石膏粉为天然二水石膏粉、或脱硫石膏粉、或硬石膏粉,粉末粒度60目~500目,水泥为水泥熟料或各种32.5以上标号水泥,石膏粉∶石灰∶水泥重量配比为20%~30%∶30%~50%∶20%~40%。
4.根据权利要求1所述无机隔热骨料为膨胀玻化微珠、膨胀珍珠岩、海泡石、蛭石、陶粒、空心玻璃微珠中一种或几种的混合物,有机添加剂为纤维素醚、可再分散胶粉、聚丙烯短纤维的混合物,纤维素醚的分子量一般不少于10万,聚丙烯短纤维的长度在6mm~9mm之间,纤维素醚、可再分散胶粉、聚丙烯短纤维重量配比为15%~25%∶70%~55%∶15%~20%。
5.根据权利要求1~4所述的经济形无机保温砂浆及生产方法,其特征在于,将各原料按预定配比计量混合均匀,包装,即成。