CN104877423A - Preparation method for moisture-proof putty powder - Google Patents
Preparation method for moisture-proof putty powder Download PDFInfo
- Publication number
- CN104877423A CN104877423A CN201510285964.XA CN201510285964A CN104877423A CN 104877423 A CN104877423 A CN 104877423A CN 201510285964 A CN201510285964 A CN 201510285964A CN 104877423 A CN104877423 A CN 104877423A
- Authority
- CN
- China
- Prior art keywords
- parts
- putty powder
- palygorskite clay
- sodium chloride
- wilkinite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method for moisture-proof putty powder, and relates to the technical field of building materials. The moisture-proof putty powder is prepared by raw materials including, by weight, 25-40 parts of white cement, 10-15 parts of palygorskite clay, 3-8 parts of bagasse fibers, 0.5-1 part of hydroxypropyl methyl cellulose, 5-10 parts of super absorbent resin, 2.5-3.5 parts of bentonite and 0.5-1 part of sodium chloride. The preparation method includes A, firing the palygorskite clay for standby application; B, smashing the palygorskite clay obtained in the step A to obtain a smashed material; C, putting the smashed material obtained in the step B, the super absorbent resin, the hydroxypropyl methyl cellulose, the bentonite and the bagasse fibers into a blender for stirring to obtain a mixture; D, putting the mixture obtained in the step C into a grinder, and grinding the mixture into 500 meshes to obtain the putty powder. By the preparation method, the problem that existing putty powder does not have a moisture proofing function can be solved.
Description
Technical field
The present invention relates to building material technical field, especially a kind of method prepared for the moistureproof putty powder of wall.
Background technology
Along with the raising of people's quality of life, house decoration more and more obtains the attention of people, putty powder is indispensable material in house decoration, the many employings of existing putty powder be calcium carbonate, talcum powder, the raw materials such as PVOH glue are made, its moisture-proof function is poor, constantly overcast and rainy between the March to April that south China especially Guangxi is annual, atmospheric moisture is large, the wall that family has scraped putty often there will be the globule or the flowing water of cohesion, not only cause not pleasant Damage by Short Circuit and the household supplies also causing household electrical appliance of human body, the mouldy damage of furniture, therefore provide a kind of nontoxic, caking ability is strong and putty powder of environment protection damp-proof and preparation method thereof is those skilled in the art needs the problem of solution badly.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of moistureproof putty powder preparation method, and it can solve the problem of existing putty powder without moisture-proof function.
In order to solve the problem, technical scheme of the present invention is: this moistureproof putty powder preparation method, adopts the raw material of following weight part to make:
White cement: 25 parts to 40 parts; Palygorskite clay: 10 parts to 15 parts; Bagasse fibre: 3 parts to 8 parts; Vltra tears: 0.5 part to 1 part; High hydrophilous resin: 5 parts to 10 parts; Wilkinite: 2.5 parts to 3.5 parts; Sodium chloride: 0.5 part to 1 part;
Comprise the steps:
A. palygorskite clay is placed in earth kiln to fire, time 2 h, temperature 280 degrees Celsius is to 300 degrees Celsius, stand-by;
B. the palygorskite clay that steps A is obtained is put into pulverizer to pulverize, obtain crushed material;
C. crushed material obtained for step B and High hydrophilous resin, Vltra tears, wilkinite, sodium chloride, bagasse fibre are put into stirrer, stir 2 minutes with the speed of 5000 revs/min, obtain compound;
D. the compound that step C is obtained is put into shredder to grind, fineness is 500 orders, to obtain final product.
In technique scheme, scheme can also be more specifically: white cement: 29 parts to 35 parts; Palygorskite clay: 12 parts to 14 parts; Bagasse fibre: 5 parts to 7 parts; Vltra tears: 0.6 part to 0.9 part; High hydrophilous resin: 6 parts to 8 parts; Wilkinite: 2.7 parts to 3 parts; Sodium chloride: 0.6 part to 0.8 part.
Further: white cement: 32 parts; Palygorskite clay: 13 parts; Bagasse fibre: 6 parts; Vltra tears: 0.7 part; High hydrophilous resin: 7 parts; Wilkinite: 3 parts; Sodium chloride: 0.7 part.
Owing to adopting technique scheme, the present invention has following beneficial effect:
1, owing to adding polygorskite powder in white cement, it not only adds the caking ability of putty powder and water tolerance and polygorskite powder drying shrinkage is little, does not produce be full of cracks;
2, owing to adding bagasse fibre, bagasse fibre is as toughner, and it not only adds the splitting resistance of putty and natural environmental-protective;
3, owing to adding Vltra tears, as dispersion agent and stablizer, each raw material is made all to have good intermiscibility in water or organic solvent;
4, owing to adding High hydrophilous resin, play the moisture absorption effect of space air, the room in wet weather kept dry, not only make the pleasant drying also protecting household electrical appliance and household supplies, furniture of human body sensory,
5, owing to adding wilkinite, it has stronger water absorbability and cementability, not only natural environmental-protective and improve water absorbability and the cementability of putty;
6, owing to adding sodium chloride, the wetting ability of sodium chloride and virus killing property, it not only adds the moisture absorption effect of putty powder and plays disinfection.
Embodiment
By embodiment, the present invention is described in further detail below:
Embodiment 1:
This moistureproof putty powder preparation method, adopts the raw material of following weight to make:
White cement: 25 kilograms; Palygorskite clay: 10 kilograms; Bagasse fibre: 3 kilograms; Vltra tears: 0.5 kilogram; High hydrophilous resin: 5 kilograms; Wilkinite: 2.5 kilograms; Sodium chloride: 0.5 kilogram;
Comprise the steps:
A. palygorskite clay is placed in earth kiln to fire, time 2 h, temperature 280 degrees Celsius is to 300 degrees Celsius, stand-by;
B. the palygorskite clay that steps A is obtained is put into pulverizer to pulverize, obtain crushed material;
C. crushed material obtained for step B and High hydrophilous resin, Vltra tears, wilkinite, sodium chloride, bagasse fibre are put into stirrer, stir 2 minutes with the speed of 5000 revs/min, obtain compound;
D. the compound that step C is obtained is put into shredder to grind, fineness is 500 orders, to obtain final product.
Embodiment 2:
This moistureproof putty powder preparation method, adopts the raw material of following weight to make:
White cement: 40 kilograms; Palygorskite clay: 15 kilograms; Bagasse fibre: 8 kilograms; Vltra tears: 1 kilogram; High hydrophilous resin: 10 kilograms; Wilkinite: 3.5 kilograms; Sodium chloride: 1 kilogram; All the other are all identical with embodiment one.
Embodiment 3:
This moistureproof putty powder preparation method, adopts the raw material of following weight to make:
White cement: 29 kilograms; Palygorskite clay: 12 kilograms; Bagasse fibre: 5 kilograms; Vltra tears: 0.6 kilogram; High hydrophilous resin: 6 kilograms; Wilkinite: 2.7 kilograms; Sodium chloride: 0.6 kilogram; All the other are all identical with embodiment one.
Embodiment 4
This moistureproof putty powder preparation method, adopts the raw material of following weight to make:
White cement: 35 kilograms; Palygorskite clay: 14 kilograms; Bagasse fibre 7 kilograms; Vltra tears: 0.9 kilogram; High hydrophilous resin: 8 kilograms; Wilkinite: 3 kilograms; Sodium chloride: 0.8 kilogram; All the other are all identical with embodiment one.
Embodiment 5
This moistureproof putty powder preparation method, adopts the raw material of following weight to make:
White cement: 32 kilograms; Palygorskite clay: 13 kilograms; Bagasse fibre: 6 kilograms; Vltra tears: 0.7 kilogram; High hydrophilous resin: 7 kilograms; Wilkinite: 3 kilograms; Sodium chloride: 0.7 kilogram; All the other are all identical with embodiment one.
Claims (3)
1. a moistureproof putty powder preparation method, is characterized in that: adopt the raw material of following weight part to make:
White cement: 25 parts to 40 parts; Palygorskite clay: 10 parts to 15 parts; Bagasse fibre: 3 parts to 8 parts; Vltra tears: 0.5 part to 1 part; High hydrophilous resin: 5 parts to 10 parts; Wilkinite: 2.5 parts to 3.5 parts; Sodium chloride: 0.5 part to 1 part;
Comprise the steps:
A. palygorskite clay is placed in earth kiln to fire, time 2 h, temperature 280 degrees Celsius is to 300 degrees Celsius, stand-by;
B. the palygorskite clay that steps A is obtained is put into pulverizer to pulverize, obtain crushed material;
C. crushed material obtained for step B and High hydrophilous resin, Vltra tears, wilkinite, sodium chloride, bagasse fibre are put into stirrer, stir 2 minutes with the speed of 5000 revs/min, obtain compound;
D. the compound that step C is obtained is put into shredder to grind, fineness is 500 orders, to obtain final product.
2. moistureproof putty powder preparation method according to claim 1, is characterized in that: adopt the raw material of following weight part to make:
White cement: 29 parts to 35 parts; Palygorskite clay: 12 parts to 14 parts; Bagasse fibre: 5 parts to 7 parts; Vltra tears: 0.6 part to 0.9 part; High hydrophilous resin: 6 parts to 8 parts; Wilkinite: 2.7 parts to 3 parts; Sodium chloride: 0.6 part to 0.8 part.
3. moistureproof putty powder preparation method according to claim 1 and 2, is characterized in that: adopt the raw material of following weight part to make:
White cement: 32 parts; Palygorskite clay: 13 parts; Bagasse fibre: 6 parts; Vltra tears: 0.7 part; High hydrophilous resin: 7 parts; Wilkinite: 3 parts; Sodium chloride: 0.7 part.