CN107129215A - A kind of environment-protection ground face brick and preparation method thereof - Google Patents
A kind of environment-protection ground face brick and preparation method thereof Download PDFInfo
- Publication number
- CN107129215A CN107129215A CN201710471096.3A CN201710471096A CN107129215A CN 107129215 A CN107129215 A CN 107129215A CN 201710471096 A CN201710471096 A CN 201710471096A CN 107129215 A CN107129215 A CN 107129215A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- ground face
- face brick
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of environment-protection ground face brick, include the component of following parts by weight：3~10 parts of 15~30 parts of cement, 10~20 parts of diatom ooze, 30~40 parts of quartz sand, 6~8 parts of bamboo fibre, 8~17 parts of silica gel, 5~9 parts of aluminium hydroxide, 1~3 part of talcum powder, 2~4 parts of graphite, 3~6 parts of carbon black, 4~8 parts of stalk powder, 5~10 parts of toughener, 8~15 parts of fire retardant, 0.8~1.5 part of antioxidant and plant extraction liquid.The environmentally friendly floor tile has the function of the pernicious gases such as formaldehyde adsorption using natural material as raw material environmental protection.
Description
Technical field
The invention belongs to building material technical field, and in particular to a kind of environment-protection ground face brick and preparation method thereof.
Background technology
At present, people require more and more higher for the healthy, safe and nontoxic etc. of living environment, and much fit up, decoration material
All contain substantial amounts of artificial synthesized chemicals in material, so as to frequently result in formaldehyde, and then trigger respiratory disease, even
It is the malignant diseases such as even more serious leukaemia, have much causes leukaemia every year because decoration material quality is unqualified
Report.
In the case, carry out having research for safe and healthy, nontoxic environment-friendly materials, be current environment-friendly materials technology
Important subject and content in field, people have also carried out substantial amounts of research to this, and achieve many achievements.
On the other hand, people also increasingly advocate natural material, it is desirable to artificial synthesizedization is reduced in decoration material
The use of product, but remain to keep original basic performance.And diatom ooze is exactly a kind of natural environment-friendly materials, it has strong
Health, environmental protection, safe and nontoxic, releasing negative oxygen ion, many excellent effects of regulation humidity etc. and as in current environment-friendly materials field
Research emphasis, people be based on diatom ooze based on, have developed multiple product, achieve good technique effect.
The content of the invention
The invention provides a kind of environment-protection ground face brick and preparation method thereof, the environmentally friendly floor tile is using natural material as original
Expect environmental protection, and with the function of the pernicious gases such as formaldehyde adsorption.
In order to solve the problem of prior art is present, adopt the following technical scheme that：
A kind of environment-protection ground face brick, includes the component of following parts by weight：15~30 parts of cement, 10~20 parts of diatom ooze, quartz sand
30~40 parts, 6~8 parts of bamboo fibre, 8~17 parts of silica gel, 5~9 parts of aluminium hydroxide, 1~3 part of talcum powder, 2~4 parts of graphite, carbon black
3~6 parts, 4~8 parts of stalk powder, 5~10 parts of toughener, 8~15 parts of fire retardant, 0.8~1.5 part of antioxidant and plant extract
3~10 parts of liquid.
It is preferred that, the environment-protection ground face brick includes the component of following parts by weight：18~25 parts of cement, diatom ooze 13~
18 parts, 32~35 parts of quartz sand, 6~8 parts of bamboo fibre, 10~15 parts of silica gel, 6~8 parts of aluminium hydroxide, 1~3 part of talcum powder, stone
2~4 parts of ink, 3~6 parts of carbon black, 5~7 parts of stalk powder, 7~9 parts of toughener, 12~14 parts of fire retardant, antioxidant 0.8~1.5
5~8 parts of part and plant extraction liquid.
It is preferred that, the environment-protection ground face brick includes the component of following parts by weight：23 parts of cement, 15 parts of diatom ooze, quartz
33 parts of sand, 7 parts of bamboo fibre, 12 parts of silica gel, 7 parts of aluminium hydroxide, 2 parts of talcum powder, 3 parts of graphite, 5 parts of carbon black, 6 parts of stalk powder,
7 parts of 8 parts of toughener, 13 parts of fire retardant, 1.3 parts of antioxidant and plant extraction liquid.
It is preferred that, the plant extraction liquid is epipremnum aureum, aloe, the mixed extract of bracketplant.
It is preferred that, stalk is mixed using the one or several kinds of of maize straw, soybean stalk, wheat stalk and broomcorn straw
Compound.
A kind of method for preparing the environment-protection ground face brick, comprises the following steps：
Step one, various raw materials are weighed, it is standby；
Step 2, high mixer is put into by aluminium hydroxide and cement, quartz sand, and 20~30 points are dried under 120~135 degrees Celsius
Storage is incubated after clock, blowing, it is standby；
Step 3, is put into ball milling 2~4 hours in ball mill by graphite, carbon black and bamboo fibre, obtains the first mix powder；
Step 4, the sodium carbonate that sodium hydroxide solution and mass fraction that mass fraction is 30% are 40% is sequentially placed into by starch
15 minutes and 35 minutes in solution, then it is washed with deionized water to neutral and dry, you can obtain modified starch；
Step 5, by the first mix powder, modified starch, cement, diatom ooze, quartz sand, silica gel, aluminium hydroxide, talcum powder,
Stalk powder, toughener, fire retardant, antioxidant and plant extraction liquid are put into high mixer, and mixture temperature is 60~70 degrees Celsius, is mixed
Conjunction obtains mixed material in 5~8 minutes；
Step 6, mixed material is put into twin (double) screw extruder, is extruded, you can obtain finished product.
It is preferred that, extruder temperature is 180~200 degrees Celsius in the step 6, and rotating speed is 500~720rpm.
It is preferred that, in the step 6, extruding is carried out under vacuum -0.12~-0.05MPa vacuum condition.
Compared with prior art, it has the advantages that the present invention：
（1）Environment-protection ground face brick of the present invention, adds diatom ooze, and diatom ooze is exactly a kind of natural environment-friendly materials, its
With many excellent effects such as healthy, environmentally friendly, safe and nontoxic, releasing negative oxygen ion, regulation humidity so that the environment-protection ground
Face brick, which has, eliminates formaldehyde, purification air, regulation humidity, releasing negative oxygen ion, fire protection flame retarding, the self-cleaning, deodorization and sterilization of metope etc.
Function；
（2）Environment-protection ground face brick of the present invention, also added stalk powder, toughener, fire retardant, antioxidant and plant and carries
Liquid is taken, cost is reduced, the functions such as the anti-flammability of the environment-protection ground face brick is added, extends its service life；
（3）The preparation method of environment-protection ground face brick of the present invention is simple, is adapted to promote.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.These embodiments be merely to illustrate the present invention and without
In limitation the scope of the present invention.
Embodiment 1
The present embodiment is related to a kind of environment-protection ground face brick, includes the component of following parts by weight：15 parts of cement, 10 parts of diatom ooze, stone
30 parts of sand, 6 parts of bamboo fibre, 8 parts of silica gel, 5 parts of aluminium hydroxide, 1 part of talcum powder, 2 parts of graphite, 3 parts of carbon black, 4 parts of stalk powder,
3 parts of 5 parts of toughener, 8 parts of fire retardant, 0.8 part of antioxidant and plant extraction liquid.
Wherein, the plant extraction liquid is epipremnum aureum, aloe, the mixed extract of bracketplant.
Wherein, stalk uses maize straw.
A kind of method for preparing the environment-protection ground face brick, comprises the following steps：
Step one, various raw materials are weighed, it is standby；
Step 2, high mixer is put into by aluminium hydroxide and cement, quartz sand, is dried 20~30 minutes at one hundred and twenty degrees centigrade, blowing
Insulation storage, standby afterwards；
Step 3, is put into ball milling 2 hours in ball mill by graphite, carbon black and bamboo fibre, obtains the first mix powder；
Step 4, the sodium carbonate that sodium hydroxide solution and mass fraction that mass fraction is 30% are 40% is sequentially placed into by starch
15 minutes and 35 minutes in solution, then it is washed with deionized water to neutral and dry, you can obtain modified starch；
Step 5, by the first mix powder, modified starch, cement, diatom ooze, quartz sand, silica gel, aluminium hydroxide, talcum powder,
Stalk powder, toughener, fire retardant, antioxidant and plant extraction liquid are put into high mixer, and mixture temperature is 60 degrees Celsius, mixing 5
Minute obtains mixed material；
Step 6, mixed material is put into twin (double) screw extruder, is extruded, you can obtain finished product.
Wherein, extruder temperature is 180 degrees Celsius in the step 6, and rotating speed is 500rpm.
Embodiment 2
The present embodiment is related to a kind of environment-protection ground face brick, includes the component of following parts by weight：30 parts of cement, 20 parts of diatom ooze, stone
40 parts of sand, 8 parts of bamboo fibre, 17 parts of silica gel, 9 parts of aluminium hydroxide, 3 parts of talcum powder, 4 parts of graphite, 6 parts of carbon black, stalk powder 8
Part, 10 parts of toughener, 15 parts of fire retardant, 1.5 parts of antioxidant and 10 parts of plant extraction liquid.
Wherein, the plant extraction liquid is epipremnum aureum, aloe, the mixed extract of bracketplant.
Wherein, stalk uses the mixture of maize straw, soybean stalk, wheat stalk and broomcorn straw.
A kind of method for preparing the environment-protection ground face brick, comprises the following steps：
Step one, various raw materials are weighed, it is standby；
Step 2, high mixer is put into by aluminium hydroxide and cement, quartz sand, is dried 30 minutes under 135 degrees Celsius, is protected after blowing
It is gentle to put, it is standby；
Step 3, is put into ball milling 4 hours in ball mill by graphite, carbon black and bamboo fibre, obtains the first mix powder；
Step 4, the sodium carbonate that sodium hydroxide solution and mass fraction that mass fraction is 30% are 40% is sequentially placed into by starch
15 minutes and 35 minutes in solution, then it is washed with deionized water to neutral and dry, you can obtain modified starch；
Step 5, by the first mix powder, modified starch, cement, diatom ooze, quartz sand, silica gel, aluminium hydroxide, talcum powder,
Stalk powder, toughener, fire retardant, antioxidant and plant extraction liquid are put into high mixer, and mixture temperature is 70 degrees Celsius, mixing 8
Minute obtains mixed material；
Step 6, mixed material is put into twin (double) screw extruder, is extruded, you can obtain finished product.
Wherein, extruder temperature is 200 degrees Celsius in the step 6, and rotating speed is 720rpm.
Embodiment 3
The present embodiment is related to a kind of environment-protection ground face brick, includes the component of following parts by weight：18 parts of cement, 13 parts of diatom ooze, stone
32 parts of sand, 6 parts of bamboo fibre, 10 parts of silica gel, 6 parts of aluminium hydroxide, 1 part of talcum powder, 2 parts of graphite, 3 parts of carbon black, stalk powder 5
Part, 7 parts of toughener, 12 parts of fire retardant, 0.8 part of antioxidant and 5 parts of plant extraction liquid.
Wherein, the plant extraction liquid is epipremnum aureum, aloe, the mixed extract of bracketplant.
Wherein, stalk uses maize straw, the mixture of soybean stalk.
A kind of method for preparing the environment-protection ground face brick, comprises the following steps：
Step one, various raw materials are weighed, it is standby；
Step 2, high mixer is put into by aluminium hydroxide and cement, quartz sand, is dried 25 minutes under 125 degrees Celsius, is protected after blowing
It is gentle to put, it is standby；
Step 3, is put into ball milling 3 hours in ball mill by graphite, carbon black and bamboo fibre, obtains the first mix powder；
Step 4, the sodium carbonate that sodium hydroxide solution and mass fraction that mass fraction is 30% are 40% is sequentially placed into by starch
15 minutes and 35 minutes in solution, then it is washed with deionized water to neutral and dry, you can obtain modified starch；
Step 5, by the first mix powder, modified starch, cement, diatom ooze, quartz sand, silica gel, aluminium hydroxide, talcum powder,
Stalk powder, toughener, fire retardant, antioxidant and plant extraction liquid are put into high mixer, and mixture temperature is 65 degrees Celsius, mixing 6
Minute obtains mixed material；
Step 6, mixed material is put into twin (double) screw extruder, is extruded, you can obtain finished product.
Wherein, extruder temperature is 190 degrees Celsius in the step 6, and rotating speed is 600rpm.
Embodiment 4
The present embodiment is related to a kind of environment-protection ground face brick, includes the component of following parts by weight：25 parts of cement, 18 parts of diatom ooze, stone
35 parts of sand, 8 parts of bamboo fibre, 15 parts of silica gel, 8 parts of aluminium hydroxide, 3 parts of talcum powder, 4 parts of graphite, 6 parts of carbon black, stalk powder 7
Part, 9 parts of toughener, 14 parts of fire retardant, 1.5 parts of antioxidant and 8 parts of plant extraction liquid.
Wherein, the plant extraction liquid is epipremnum aureum, aloe, the mixed extract of bracketplant.
Wherein, stalk uses maize straw, the mixture of soybean stalk.
A kind of method for preparing the environment-protection ground face brick, comprises the following steps：
Step one, various raw materials are weighed, it is standby；
Step 2, high mixer is put into by aluminium hydroxide and cement, quartz sand, is dried 25 minutes under 125 degrees Celsius, is protected after blowing
It is gentle to put, it is standby；
Step 3, is put into ball milling 3 hours in ball mill by graphite, carbon black and bamboo fibre, obtains the first mix powder；
Step 4, the sodium carbonate that sodium hydroxide solution and mass fraction that mass fraction is 30% are 40% is sequentially placed into by starch
15 minutes and 35 minutes in solution, then it is washed with deionized water to neutral and dry, you can obtain modified starch；
Step 5, by the first mix powder, modified starch, cement, diatom ooze, quartz sand, silica gel, aluminium hydroxide, talcum powder,
Stalk powder, toughener, fire retardant, antioxidant and plant extraction liquid are put into high mixer, and mixture temperature is 65 degrees Celsius, mixing 6
Minute obtains mixed material；
Step 6, mixed material is put into twin (double) screw extruder, is extruded, you can obtain finished product.
Wherein, extruder temperature is 190 degrees Celsius in the step 6, and rotating speed is 600rpm.
Embodiment 5
The present embodiment is related to a kind of environment-protection ground face brick, includes the component of following parts by weight：23 parts of cement, 15 parts of diatom ooze, stone
33 parts of sand, 7 parts of bamboo fibre, 12 parts of silica gel, 7 parts of aluminium hydroxide, 2 parts of talcum powder, 3 parts of graphite, 5 parts of carbon black, stalk powder 6
Part, 8 parts of toughener, 13 parts of fire retardant, 1.3 parts of antioxidant and 7 parts of plant extraction liquid.
Wherein, the plant extraction liquid is epipremnum aureum, aloe, the mixed extract of bracketplant.
Wherein, stalk uses maize straw, the mixture of soybean stalk.
A kind of method for preparing the environment-protection ground face brick, comprises the following steps：
Step one, various raw materials are weighed, it is standby；
Step 2, high mixer is put into by aluminium hydroxide and cement, quartz sand, is dried 25 minutes under 125 degrees Celsius, is protected after blowing
It is gentle to put, it is standby；
Step 3, is put into ball milling 3 hours in ball mill by graphite, carbon black and bamboo fibre, obtains the first mix powder；
Step 4, the sodium carbonate that sodium hydroxide solution and mass fraction that mass fraction is 30% are 40% is sequentially placed into by starch
15 minutes and 35 minutes in solution, then it is washed with deionized water to neutral and dry, you can obtain modified starch；
Step 5, by the first mix powder, modified starch, cement, diatom ooze, quartz sand, silica gel, aluminium hydroxide, talcum powder,
Stalk powder, toughener, fire retardant, antioxidant and plant extraction liquid are put into high mixer, and mixture temperature is 65 degrees Celsius, mixing 6
Minute obtains mixed material；
Step 6, mixed material is put into twin (double) screw extruder, is extruded, you can obtain finished product.
Wherein, extruder temperature is 190 degrees Celsius in the step 6, and rotating speed is 600rpm.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (8)
1. a kind of environment-protection ground face brick, it is characterised in that include the component of following parts by weight：15~30 parts of cement, diatom ooze 10
~20 parts, 30~40 parts of quartz sand, 6~8 parts of bamboo fibre, 8~17 parts of silica gel, 5~9 parts of aluminium hydroxide, 1~3 part of talcum powder, stone
2~4 parts of ink, 3~6 parts of carbon black, 4~8 parts of stalk powder, 5~10 parts of toughener, 8~15 parts of fire retardant, antioxidant 0.8~1.5
3~10 parts of part and plant extraction liquid.
2. environment-protection ground face brick according to claim 1, it is characterised in that include the component of following parts by weight：Cement 18
~25 parts, 13~18 parts of diatom ooze, 32~35 parts of quartz sand, 6~8 parts of bamboo fibre, 10~15 parts of silica gel, aluminium hydroxide 6~8
Part, 1~3 part of talcum powder, 2~4 parts of graphite, 3~6 parts of carbon black, 5~7 parts of stalk powder, 7~9 parts of toughener, fire retardant 12~
5~8 parts of 14 parts, 0.8~1.5 part of antioxidant and plant extraction liquid.
3. environment-protection ground face brick according to claim 1, it is characterised in that include the component of following parts by weight：Cement 23
Part, 15 parts of diatom ooze, 33 parts of quartz sand, 7 parts of bamboo fibre, 12 parts of silica gel, 7 parts of aluminium hydroxide, 2 parts of talcum powder, 3 parts of graphite, charcoal
7 parts of black 5 parts, 6 parts of stalk powder, 8 parts of toughener, 13 parts of fire retardant, 1.3 parts of antioxidant and plant extraction liquid.
4. environment-protection ground face brick according to claim 1, it is characterised in that the plant extraction liquid is epipremnum aureum, aloe, hung
Blue mixed extract.
5. environment-protection ground face brick according to claim 1, it is characterised in that the stalk uses maize straw, big beanstalk
One or several kinds of mixtures of stalk, wheat stalk and broomcorn straw.
6. a kind of method for preparing any one of Claims 1 to 5 environment-protection ground face brick, it is characterised in that including following step
Suddenly：
Step one, various raw materials are weighed, it is standby；
Step 2, high mixer is put into by aluminium hydroxide and cement, quartz sand, and 20~30 points are dried under 120~135 degrees Celsius
Storage is incubated after clock, blowing, it is standby；
Step 3, is put into ball milling 2~4 hours in ball mill by graphite, carbon black and bamboo fibre, obtains the first mix powder；
Step 4, the sodium carbonate that sodium hydroxide solution and mass fraction that mass fraction is 30% are 40% is sequentially placed into by starch
15 minutes and 35 minutes in solution, then it is washed with deionized water to neutral and dry, you can obtain modified starch；
Step 5, by the first mix powder, modified starch, cement, diatom ooze, quartz sand, silica gel, aluminium hydroxide, talcum powder,
Stalk powder, toughener, fire retardant, antioxidant and plant extraction liquid are put into high mixer, and mixture temperature is 60~70 degrees Celsius, is mixed
Conjunction obtains mixed material in 5~8 minutes；
Step 6, mixed material is put into twin (double) screw extruder, is extruded, you can obtain finished product.
7. preparation method according to claim 6, it is characterised in that extruder temperature is 180~200 in the step 6
Degree Celsius, rotating speed is 500~720rpm.
8. preparation method according to claim 6, it is characterised in that in the step 6, extruding is in vacuum -0.12
Carried out under~-0.05MPa vacuum condition.