CN104877205A - 一种耐磨防老化橡胶 - Google Patents
一种耐磨防老化橡胶 Download PDFInfo
- Publication number
- CN104877205A CN104877205A CN201510342939.0A CN201510342939A CN104877205A CN 104877205 A CN104877205 A CN 104877205A CN 201510342939 A CN201510342939 A CN 201510342939A CN 104877205 A CN104877205 A CN 104877205A
- Authority
- CN
- China
- Prior art keywords
- rubber
- wear
- produced
- produces
- aging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐磨防老化橡胶,其成分中含有下列物质:端羧基液态丁腈橡胶、丁苯橡胶、辛基酚醛树脂、氧化锌、硬脂酸、4,4′-双(a,a′二甲基苄基)二苯胺、2,2,4-三甲基1,2-二氢化喹啉、玻璃纤维、炭黑N660、陶土、碳酸钙、牛油、松焦油、机油、二硫化二苯并噻唑、2-硫醇基苯并噻唑、二硫化四甲基秋兰姆、N-环己基硫代二甲酰亚胺、硫磺。本发明生产的混炼橡胶,经40℃×72h老化,在2倍放大镜下观察未见裂纹,耐磨防老化性能好。
Description
技术领域
本发明涉及一种橡胶,具体说是一种用于疏浚胶管外覆层的耐磨防老化橡胶。
背景技术
近些年来,疏浚胶管的使用范围有了很大拓展,不仅由于江河湖海的航道清淤和港口建设,而且用于人工造地、岛礁开发、海洋建筑、海底采矿等工程。输导的物料中,含有砾石、岩石、珊瑚等大颗粒物质,传统的疏浚胶管外覆层橡胶不耐磨,而且容易老化,会很快龟裂破损,影响了胶管使用寿命。
发明内容
为了克服现有技术中存在的问题,本发明的目的是提供一种耐磨防老化橡胶,经40℃×72h老化,在2倍放大镜下观察未见裂纹,耐磨防老化性能较好,可以满足疏浚胶管施工需要。
本发明的目的通过以下技术方案实现:
一种耐磨防老化橡胶,其特征在于:该耐磨防老化橡胶含有以下质量分的物质:
端羧基液态丁腈橡胶天然橡胶 70-80
丁苯橡胶 30-20
辛基酚醛树脂 5-10
氧化锌 4-8
硬脂酸 1.5-3.0
二硫化二苯并噻唑 1-1.5
2-硫醇基苯并噻唑 0.6-1.2
二硫化四甲基秋兰姆 0.2-0.4
4,4′-双(a,a′二甲基苄基)二苯胺 1-3
2,2,4-三甲基1,2-二氢化喹啉 1-3
N-环己基硫代二甲酰亚胺 0.1-0.3
玻璃纤维 30-50
炭黑N660 20-35
陶土 10-15
碳酸钙 10-15
工业酯 3.0-6.0
松焦油 3.0-6.0
硫磺 1-3
其中,端羧基液态丁腈橡胶是美国Emerald端羧基液态丁腈橡胶;丁苯橡胶为浙江维泰橡胶有限公司生产的力维泰牌SBR1502橡胶;辛基酚醛树脂为无锡宾王化工厂产。氧化锌为扬州振中锌业有限公司产;硬脂酸为印尼PALMATA 1801公司产;4,4′-双(a,a′二甲基苄基)二苯胺由常州仕诚化工有限公司生产;2,2,4-三甲基1,2-二氢化喹啉为天津科迈化工有限公司生产;二硫醇基苯并噻唑由天津科迈化工有限公司生产;二硫化二苯并噻唑由天津拉勃助剂公司生产;二硫化四甲基秋兰姆 由镇江振邦化工有限公司生产;炭黑N660为江西黑猫炭黑股份有限公司生产;工业酯 由无锡市兴沪石油制品有限公司生产;松焦油为沙县昌盛林产化工有限公司生产;硫磺为镇江润旺化工公司生产。
本发明的橡胶制备方法与现有的制备方法相同。
与现有技术相比,本发明,经40℃×72h老化,在2倍放大镜下观察未见裂纹,耐磨防老化性能较好,本发明适用于疏浚胶管外覆层中。
具体实施方式
下面结合实施例对本发明做详细说明
实施例1
一种耐磨防老化橡胶,含有以下质量分的物质:
端羧基液态丁腈橡胶 75
丁苯橡胶 25
辛基酚醛树脂 6.0
氧化锌 5.0
硬脂酸 1.6
二硫化二苯并噻唑 1.2
2-硫醇基苯并噻唑 0.6
二硫化四甲基秋兰姆 0.2
4,4′-双(a,a′二甲基苄基)二苯胺 1.2
2,2,4-三甲基1,2-二氢化喹啉 1.0
N-环己基硫代二甲酰亚胺 0.1
玻璃纤维 40
炭黑N660 25
陶土 14
碳酸钙 12
工业酯 6.0
松焦油 4.0
硫磺 1.8
端羧基液态丁腈橡胶是美国Emerald端羧基液态丁腈橡胶、丁苯橡胶为浙江维泰橡胶有限公司生产的力维泰牌SBR1502橡胶、辛基酚醛树脂为无锡宾王化工厂产、氧化锌为扬州振中锌业有限公司产、硬脂酸为印尼PALMATA 1801公司产、4,4′-双(a,a′二甲基苄基)二苯胺由常州仕诚化工有限公司生产、2,2,4-三甲基1,2-二氢化喹啉为天津科迈化工有限公司生产、二硫醇基苯并噻唑由天津科迈化工有限公司生产、二硫化二苯并噻唑由天津拉勃助剂公司生产、二硫化四甲基秋兰姆 由镇江振邦化工有限公司生产、炭黑N660为江西黑猫炭黑股份有限公司生产、工业酯 由无锡市兴沪石油制品有限公司生产、松焦油为沙县昌盛林产化工有限公司生产、硫磺为镇江润旺化工公司生产。
验证:上述配方生产的混炼橡胶经40℃×72h老化,在2倍放大镜下观察未见裂纹,耐磨防老化性能较好。
实施例2
又一种耐磨防老化橡胶,含有以下质量分的物质:
端羧基液态丁腈橡胶 80
丁苯橡胶 20
辛基酚醛树脂 10
氧化锌 8
硬脂酸 3.0
二硫化二苯并噻唑 1.5
2-硫醇基苯并噻唑 1.2
二硫化四甲基秋兰姆 0.4
4,4′-双(a,a′二甲基苄基)二苯胺 3
2,2,4-三甲基1,2-二氢化喹啉 3
N-环己基硫代二甲酰亚胺 0.3
玻璃纤维 50
炭黑N660 35
陶土 15
碳酸钙 15
工业酯 6.0
松焦油 6.0
硫磺 3
验证:上述配方生产的混炼橡胶40℃×72h老化,在2倍放大镜下观察未见裂纹,耐磨防老化性能较好。
Claims (4)
1.一种耐磨防老化橡胶,其特征在于:该耐磨防老化橡胶含有以下质量分的物质:
端羧基液态丁腈橡胶 70-80
丁苯橡胶 30-20
辛基酚醛树脂 5-10
氧化锌 4-8
硬脂酸 1.5-3.0
二硫化二苯并噻唑 1-1.5
2-硫醇基苯并噻唑 0.6-1.2
二硫化四甲基秋兰姆 0.2-0.4
4,4′-双(a,a′二甲基苄基)二苯胺 1-3
2,2,4-三甲基1,2-二氢化喹啉 1-3
N-环己基硫代二甲酰亚胺 0.1-0.3
玻璃纤维 30-50
炭黑N660 20-35
陶土 10-15
碳酸钙 10-15
工业酯 3.0-6.0
松焦油 3.0-6.0
硫磺 1-3。
2.根据权利要求1所述的耐磨防老化橡胶,其特征在于:端羧基液态丁腈橡胶是美国Emerald端羧基液态丁腈橡胶;丁苯橡胶为浙江维泰橡胶有限公司生产的力维泰牌SBR1502橡胶;辛基酚醛树脂为无锡宾王化工厂产。
3.根据权利要求1所述的耐磨防老化橡胶,其特征在于:氧化锌为扬州振中锌业有限公司产;硬脂酸为印尼PALMATA 1801公司产;4,4′-双(a,a′二甲基苄基)二苯胺由常州仕诚化工有限公司生产;2,2,4-三甲基1,2-二氢化喹啉为天津科迈化工有限公司生产;二硫醇基苯并噻唑由天津科迈化工有限公司生产;二硫化二苯并噻唑由天津拉勃助剂公司生产;二硫化四甲基秋兰姆 由镇江振邦化工有限公司生产;玻璃纤维由盐城固驰玻璃纤维有限公司生产;炭黑N660为江西黑猫炭黑股份有限公司生产;工业酯 由无锡市兴沪石油制品有限公司生产;松焦油为沙县昌盛林产化工有限公司生产;硫磺为镇江润旺化工公司生产。
4.根据权利要求1所述的耐磨防老化橡胶,其特征在于:该耐臭氧老化橡胶含有以下质量分的物质:
端羧基液态丁腈橡胶 75
丁苯橡胶 25
辛基酚醛树脂 6.0
氧化锌 5.0
硬脂酸 1.6
二硫化二苯并噻唑 1.2
2-硫醇基苯并噻唑 0.6
二硫化四甲基秋兰姆 0.2
4,4′-双(a,a′二甲基苄基)二苯胺 1.2
2,2,4-三甲基1,2-二氢化喹啉 1.0
N-环己基硫代二甲酰亚胺 0.1
玻璃纤维 40
炭黑N660 25
陶土 14
碳酸钙 12
工业酯 6.0
松焦油 4.0
硫磺 1.8。