CN104556180A - 一种冰晶石的生产方法 - Google Patents
一种冰晶石的生产方法 Download PDFInfo
- Publication number
- CN104556180A CN104556180A CN201410744647.5A CN201410744647A CN104556180A CN 104556180 A CN104556180 A CN 104556180A CN 201410744647 A CN201410744647 A CN 201410744647A CN 104556180 A CN104556180 A CN 104556180A
- Authority
- CN
- China
- Prior art keywords
- cryolite
- solution
- sodium aluminum
- aluminum fluoride
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种冰晶石的生产方法,尤其是一种利用磷肥副产合成冰晶石的方法,通过氟硅酸溶液用氨水中和,用压滤机分离形成的氟化铵溶液和硅酸,分离得到的氟化铵清液用硫酸调节pH值,将调节后的溶液送入冰晶石合成槽,加热至95℃,保湿15分钟;加入硫酸铝溶液,加完料后,迅速升温;加入硫酸钠,保温搅拌反应60分钟,用离心分离除去硫酸铵母液;将含20%左右水的冰晶石进行气流干燥;干燥完成后即得到冰晶石产品;本发明中所述的方法采用磷肥副产物为原料进行化学反应得到的冰晶石质量好、生产成本低,同时能有效的保护环境。
Description
技术领域
本发明涉及一种冰晶石的生产方法,尤其是一种利用磷肥副产合成冰晶石的方法。
背景技术
冰晶石主要用作炼铝的助溶剂,也可以用作农作物的杀虫剂,搪瓷乳白剂,玻璃和搪瓷生产用的遮光剂和助溶剂,树脂橡胶的耐磨填充剂。还可以同于铁合金和沸腾钢的生产。冰晶石有少量的天然矿床,目前,冰晶石工业化的生产方法主要有纯碱氟氯酸法、粘土盐卤法、氟硅酸生产冰晶石联产白炭黑法等,这些方法均需要占用一定的氟资源,生产成本相对较高,并且现行工艺都存在程度不同的环境污染。
发明内容
本发明要解决的技术问题是提供一种冰晶石的生产方法,以提高产品质量,降低生产成本,同时降低对环境的污染。
本发明的技术方案是:一种冰晶石的生产方法,包括以下步骤:
1) 将10~12%的氟硅酸溶液用17~18%的氨水中和,氨水的加入量以控制溶液的pH值在8.0~8.5之间为准,保持搅拌反应1小时;
2) 用压滤机分离形成的氟化铵溶液和硅酸,分离得到的氟化铵清液用硫酸调节至pH值5.0~5.5;
3) 将调节后的溶液送入冰晶石合成槽,加热至90~95℃,保湿15分钟;
4) 加入化学计量95%的硫酸铝溶液,加完料后,迅速升温至80~85℃;
5) 加入化学计量105%的硫酸钠,保温搅拌反应45~60分钟,控制合成液的最终pH值为3.0;
6) 用离心分离除去硫酸铵母液;
7) 将含20%左右水的冰晶石在100~110℃下进行气流干燥;干燥完成后即得到冰晶石产品。
本发明的有益效果:本发明中所述的方法采用磷肥副产物为原料进行化学反应得到的冰晶石质量好、生产成本低,同时能有效的保护环境。
具体实施方式
实施例一
1) 将10%的氟硅酸溶液用17%的氨水中和,氨水的加入量以控制溶液的pH值为8.0,保持搅拌反应1小时;
2) 用压滤机分离形成的氟化铵溶液和硅酸,分离得到的氟化铵清液用硫酸调节至pH值5.0;
3) 将调节后的溶液送入冰晶石合成槽,加热至90℃,保湿15分钟;
4) 加入化学计量95%的硫酸铝溶液,加完料后,迅速升温至80℃;
5) 加入化学计量105%的硫酸钠,保温搅拌反应45分钟,控制合成液的最终pH值为3.0;
6) 用离心分离除去硫酸铵母液;
7) 将含20%左右水的冰晶石在110℃下进行气流干燥;干燥完成后即得到冰晶石产品。
实施例二
1) 将11%的氟硅酸溶液用17.5%的氨水中和,氨水的加入量以控制溶液的pH值为8.2,保持搅拌反应1小时;
2) 用压滤机分离形成的氟化铵溶液和硅酸,分离得到的氟化铵清液用硫酸调节至pH值5.2;
3) 将调节后的溶液送入冰晶石合成槽,加热至92℃,保湿15分钟;
4) 加入化学计量95%的硫酸铝溶液,加完料后,迅速升温至82℃;
5) 加入化学计量105%的硫酸钠,保温搅拌反应50分钟,控制合成液的最终pH值为3.0;
6) 用离心分离除去硫酸铵母液;
7) 将含20%左右水的冰晶石在105℃下进行气流干燥;干燥完成后即得到冰晶石产品。
实施例三
1) 将12%的氟硅酸溶液用18%的氨水中和,氨水的加入量以控制溶液的pH值为8.5,保持搅拌反应1小时;
2) 用压滤机分离形成的氟化铵溶液和硅酸,分离得到的氟化铵清液用硫酸调节至pH值5.5;
3) 将调节后的溶液送入冰晶石合成槽,加热至95℃,保湿15分钟;
4) 加入化学计量95%的硫酸铝溶液,加完料后,迅速升温至85℃;
5) 加入化学计量105%的硫酸钠,保温搅拌反应60分钟,控制合成液的最终pH值为3.0;
6) 用离心分离除去硫酸铵母液;
7) 将含20%左右水的冰晶石在100℃下进行气流干燥;干燥完成后即得到冰晶石产品。
Claims (1)
1.一种冰晶石的生产方法,包括以下步骤:
将10~12%的氟硅酸溶液用17~18%的氨水中和,氨水的加入量以控制溶液的pH值在8.0~8.5之间为准,保持搅拌反应1小时;
用压滤机分离形成的氟化铵溶液和硅酸,分离得到的氟化铵清液用硫酸调节至pH值5.0~5.5;
将调节后的溶液送入冰晶石合成槽,加热至90~95℃,保湿15分钟;
加入化学计量95%的硫酸铝溶液,加完料后,迅速升温至80~85℃;
加入化学计量105%的硫酸钠,保温搅拌反应45~60分钟,控制合成液的最终pH值为3.0;
用离心分离除去硫酸铵母液;
将含20%左右水的冰晶石在100~110℃下进行气流干燥;干燥完成后即得到冰晶石产品。