CN104084897B - 一种无尘打磨单面网格砂布及其制备方法 - Google Patents
一种无尘打磨单面网格砂布及其制备方法 Download PDFInfo
- Publication number
- CN104084897B CN104084897B CN201410303662.6A CN201410303662A CN104084897B CN 104084897 B CN104084897 B CN 104084897B CN 201410303662 A CN201410303662 A CN 201410303662A CN 104084897 B CN104084897 B CN 104084897B
- Authority
- CN
- China
- Prior art keywords
- tack coat
- cloth
- matrix
- abrasive cloth
- mesh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种无尘打磨单面网格砂布及其制备方法，无尘打磨单面网格砂布所述包括基体、粘结层A、磨料以及粘结层B；所述的基体为由底布以及耸立在底布一面的毛圈构成的背绒网眼布，所述粘结层A和粘结层B依次涂附在背绒网眼布无绒的一面；所述磨料通过粘结层A和粘结层B附着在背绒网眼布无绒的一面及其网眼内，制备方法为：将背绒网眼布无绒的一面用刮涂法以粘结剂A涂附到基体上，在拉幅机的作用下送入植砂烘干机构进行单面植砂，使磨料植入基体的粘结层A，进行烘干预处理；再用对辊凃附一层粘结剂B，再固化处理；然后对背绒网格砂布进行整形、裁剪等其它后续加工。本发明的网眼砂布减少污染，提高工作效率。
Description
技术领域
本发明涉及一种网格砂布，具体涉及一种无尘打磨单面网格砂布，还涉及该网格砂布的制备方法。
背景技术
目前砂布作为一种磨削工具被广泛运用于各制造行业，可以对金属、木材、塑料、墙体甚至皮革等材料进行打磨、抛光，以达到所需的加工精度或表面质量。其中网格砂布的应用极为广泛，网格砂布由交织的经纬线构成，经纬线上均匀粘附有磨料，使用时将网格砂
布固定于电动工具之上，如打磨机或角磨机，网格砂布随电动工具的转轴旋转达到研磨的目的，但是在研磨过程中会产生大量磨屑，打磨形成的细粉就飘散在周围的环境中，造成环境污染，不仅严重影响操作工人的身体健康，而且打磨形成的细粉飘散在环境中，在一定程度是一种资源的浪费。
发明内容
本发明的目的在于针对现有技术中的不足，提供一种无尘打磨单面网格砂布，粘贴牢固，利于环保。
为解决上述技术问题，本发明采用的技术方案为：一种无尘打磨单面网格砂布，包括基体、粘结层A、磨料以及粘结层B；所述的基体为由地经和地纬编织而成的底布以及耸立在底布一面由绒经或绒纬编织而成的毛圈构成的背绒网眼布，所述粘结层A和粘结层B依次涂附在背绒网眼布无绒的一面；所述磨料通过粘结层A和粘结层B附着在背绒网眼布无绒的一面及其网眼内。
进一步的，所述的背绒网眼布为涤纶织物或者尼龙织物。
进一步的，所述的粘结层A的厚度为3～8um。
进一步的，所述磨料刚玉砂或碳化硅或石英砂或陶瓷中的一种。
进一步的，所述的磨料的粒径为10～1000目。
进一步的，所述的粘结层B的厚度为2～4um。
本发明还提供了一种无尘打磨单面网格砂布的制备方法，包括以下步骤：
（1）将背绒网眼布无绒的一面用刮涂法以厚度3～8um的粘结剂A涂附到基体上，形成粘结层A，粘结剂A只集中在基体的无绒的一面以及基体的侧面；
（2）将步骤（1）得到的背绒网眼布在拉幅机作用下送入植砂烘干机构进行单面植砂，使磨料植入基体树脂层，即粘结层A，植砂量占产品总质量的55～85%，同时进行烘干预处理，烘干温度为80℃～140℃，烘干时间为2～ 8min；
（3）再在步骤（2）已植入磨料并且干燥好的粘结层A上用对辊凃附一层厚度2～4um粘结剂B，形成粘结层B，在70～120℃下固化处理4～8小时；
（4）对步骤（3）的背绒网格砂布进行整形、裁剪及其他后续加工。
进一步的，所述的粘结剂A和粘结剂B的主剂均为水溶性酚醛树脂或环氧树脂或糠醛树脂或糠醇树脂或聚氨酯或醇酸树脂或尿醛树脂中的一种或几种的组合。
本发明的有益效果：
1、本发明的无尘打磨单面网格砂布，背绒丝线直接经编在网眼布的经线或纬线上，保持了原网眼布形状、孔隙，更牢固、均匀、一致、美观。
2、本发明的无尘打磨单面网格砂布在打磨时粉尘通过网孔进入收集装置从而环境污染少、给操作人员提供了一个较好的工作环境；
3、本发明的无尘打磨单面网格砂布工作效率高。
附图说明
图1为本发明的无尘打磨单面网格砂布的剖面图。
具体实施方式
下面结合具体实施例对本发明的技术方案作详细说明。
本发明的一种无尘打磨单面网格砂布，包括基体、粘结层A 2、磨料3以及粘结层B 4；基体为由地经和地纬编织而成的底布11以及耸立在底布一面由绒经或绒纬编织而成的毛圈12构成的背绒网眼布；粘结层A 2和粘结层B 3依次涂附在背绒网眼布无绒的一面；磨料3通过粘结层A 2和粘结层B 3附着在背绒网眼布无绒的一面及其网眼内。
无尘打磨单面网格砂布的制备方法，包括以下步骤：
（1）将背绒网眼布无绒的一面用刮涂法以厚度3～8um的粘结剂A涂附到基体上，形成粘结层A，粘结剂A只集中在基体的无绒的一面以及基体的侧面；
（2）将步骤（1）得到的背绒网眼布在拉幅机作用下送入植砂烘干机构进行单面植砂，使磨料植入基体树脂层，即粘结层A，植砂量占产品总质量的55～85%，同时进行烘干预处理，烘干温度为80℃～140℃，烘干时间为2～ 8min；
（3）再在步骤（2）已植入磨料并且干燥好的粘结层A上用对辊凃附一层厚度2～4um粘结剂B，形成粘结层B，在70～120℃下固化处理4～8小时；
（4）对步骤（3）的背绒网格砂布进行整形、裁剪及其他后续加工。
实施例
1
直径为125mm的圆片形无尘打磨单面网格砂布，以涤纶织物为基体材料，刚玉砂为磨料，制备方法如下：
（1）将背绒网眼布无绒的一面用刮涂法以厚度6um的水溶性酚醛树脂涂附到基体上，形成粘结层A，水溶性酚醛树脂只集中在基体的无绒的一面以及基体的侧面；
（2）将步骤（1）得到的背绒网眼布在拉幅机作用下送入植砂烘干机构进行单面植砂，使磨料植入基体树脂层--粘结层A，植砂量占产品总质量的60%，同时进行烘干预处理，烘干温度为80℃，烘干时间为8min；
（3）再在步骤（2）已植入磨料并且干燥好的粘结层A上用对辊凃附一层厚度4um环氧树脂粘结剂B，形成粘结层B，在120℃下固化处理4小时；
（4）对步骤（3）的背绒网格砂布进行整形、裁剪即得到直径为125mm的圆片形无尘打磨单面网格砂布。
实施例
2
直径为150mm的圆片形无尘打磨单面网格砂布，以尼龙织物为基体材料，100目石英砂为磨料，制备方法如下：
（1）将背绒网眼布无绒的一面用刮涂法以厚度5um的酚醛树脂和环氧树脂的混合物涂附到基体上，形成粘结层A，其中酚醛树脂和环氧树脂的质量比为9:1，酚醛树脂和环氧树脂的混合物只集中在基体的无绒的一面以及基体的侧面；
（2）将步骤（1）得到的背绒网眼布在拉幅机作用下送入植砂烘干机构进行单面植砂，使100目石英砂磨料植入基体树脂层--粘结层A，植砂量占产品总质量的73%，同时进行烘干预处理，烘干温度为100℃，烘干时间为6min；
（3）再在步骤（2）已植入磨料100目石英砂并且干燥好的粘结层A上用对辊凃附一层厚度3um环氧树脂，形成粘结层B，在100℃下固化处理6小时；
（4）对步骤（3）的背绒网格砂布进行整形、裁剪及其他后续加工。
实施例
3
70×125mm的方片形无尘打磨单面网格砂布，以涤纶织物为基体材料，180目碳化硅为磨料，制备方法如下：
（1）将背绒网眼布无绒的一面用刮涂法以厚度4um的酚醛树脂涂附到基体上，形成粘结层A，酚醛树脂只集中在基体的无绒的一面以及基体的侧面；
（2）将步骤（1）得到的背绒网眼布在拉幅机作用下送入植砂烘干机构进行单面植砂，使180目碳化硅磨料植入基体树脂层--粘结层A，植砂量占产品总质量的69%同时进行烘干预处理，烘干温度为120℃，烘干时间为4min；
（3）再在步骤（2）已植入磨料并且干燥好的粘结层A上用对辊凃附一层厚度3um聚氨酯，形成粘结层B，在90℃下固化处理6.5小时；
（4）对步骤（3）的背绒网格砂布进行整形、裁剪及其他后续加工。
实施例
4
70×420mm的方片形无尘打磨单面网格砂布，以尼龙织物为基体材料，320目碳化硅为磨料，制备方法如下：
（1）将背绒网眼布无绒的一面用刮涂法以厚度4um的尿醛树脂涂附到基体上，形成粘结层A，尿醛树脂只集中在基体的无绒的一面以及基体的侧面；
（2）将步骤（1）得到的背绒网眼布在拉幅机作用下送入植砂烘干机构进行单面植砂，使320目碳化硅磨料植入基体树脂层--粘结层A,植砂量占产品总质量的65%，同时进行烘干预处理，烘干温度为140℃，烘干时间为2min；
（3）再在步骤（2）已植入磨料并且干燥好的粘结层A上用对辊凃附一层厚度3um环氧树脂，形成粘结层B，在70℃下固化处理8小时；
（4）对步骤（3）的背绒网格砂布进行整形、裁剪及其他后续加工。
Claims (5)
1.一种无尘打磨单面网格砂布，其特征在于：包括基体、粘结层A、磨料以及粘结层B；所述的基体为由地经和地纬编织而成的底布以及耸立在底布一面由绒经或绒纬编织而成的毛圈构成的背绒网眼布，所述粘结层A和所述粘结层B依次涂附在背绒网眼布无绒的一面；所述磨料通过粘结层A和粘结层B附着在背绒网眼布无绒的一面及其网眼内；
所述无尘打磨单面网格砂布的制备方法，包括以下步骤：
（1）将背绒网眼布无绒的一面用刮涂法以厚度3～8um的粘结剂A涂附到基体上，形成粘结层A，粘结剂A只集中在基体的无绒的一面以及基体的侧面；
（2）将步骤（1）得到的背绒网眼布在拉幅机作用下送入植砂烘干机构进行单面植砂，使磨料植入基体树脂层，即粘结层A，植砂量占产品总质量的55～85%，同时进行烘干预处理，烘干温度为80℃～140℃，烘干时间为2～ 8min；
（3）再在步骤（2）已植入磨料并且干燥好的粘结层A上用对辊凃附一层厚度2～4um粘结剂B，形成粘结层B，在70～120℃下固化处理4～8小时；
（4）对步骤（3）的背绒网格砂布进行整形、裁剪及后续加工。
2.根据权利要求1所述的一种无尘打磨单面网格砂布，其特征在于：所述的背绒网眼布为涤纶织物或者尼龙织物。
3.根据权利要求1或2所述的一种无尘打磨单面网格砂布，其特征在于：所述磨料为刚玉砂或碳化硅或石英砂或陶瓷中的一种或几种。
4.根据权利要求3所述的一种无尘打磨单面网格砂布，其特征在于：所述的磨料的粒径为10～1000目。
5.根据权利要求1或2所述的一种无尘打磨单面网格砂布，其特征在于：所述的粘结剂A和所述的粘结剂B的主剂均为水溶性酚醛树脂或环氧树脂或糠醛树脂或糠醇树脂或聚氨酯或醇酸树脂或尿醛树脂中的一种或几种的组合。